CN112848304B - 一种电场辅助连续面曝光3d打印有序复合材料的制备方法 - Google Patents
一种电场辅助连续面曝光3d打印有序复合材料的制备方法 Download PDFInfo
- Publication number
- CN112848304B CN112848304B CN202110019175.7A CN202110019175A CN112848304B CN 112848304 B CN112848304 B CN 112848304B CN 202110019175 A CN202110019175 A CN 202110019175A CN 112848304 B CN112848304 B CN 112848304B
- Authority
- CN
- China
- Prior art keywords
- printing
- electric field
- slurry
- composite material
- graphene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种电场辅助连续面曝光3D打印有序复合材料的制备方法，所述打印设备包括数字光处理模块，浆料槽，打印平台，外加电场；所述数字处理模块按照打印的模型分层切片，以光束形式穿过复合透氧膜并投射到浆料上实现固化，随着打印平台沿z轴方向逐渐上移，所述外加电场置于浆料槽内部两侧，实现了石墨烯/树脂复合材料的连续打印，且石墨烯片在辅助电场下有序排列实现各向异性/有序复合材料的打印，提高了力学性能与电学性能以及增大了材料的抗弯强度和韧性。
Description
技术领域
本发明涉及3D打印领域，尤其涉及一种电场辅助连续面曝光3D打印有序复合材料的制备方法。
背景技术
目前，3D打印技术已广泛应用于电子、医疗、航天等领域。以数字光处理技术(Digital Light Processing)为核心的光固化3D打印技术具有成型精度高、打印速度快、工艺成熟等优点。其打印材料光敏树脂属于一种高分子聚合物，在光照作用下由液态快速转化为固态而成型。近年来，3D打印用光敏树脂通过在材料中添加纤维、粉末等增强体，或是某些高聚物使得材料在增强性能和实现功能化方面有了长足的发展和进步。然而一些复合材料中增强体的分布并不是可以人为控制，无法更好地利用增强体的特殊性质得到符合要求的材料。
一直以来石墨烯作为一种二维纳米材料以其优异的光学性能、力学性能、导热导电性能受到学术界以及工业界的广泛关注。石墨烯作为添加物被广泛应用于各种复合材料中，但由于工艺限制目前的传统成型和一般的3D打印方法都不能得到石墨烯按照一定规律均匀分布的复合材料，这使得石墨烯本身的性能在材料中的体现大大折扣，也就限制了石墨烯/聚合物复合材料的应用和普及。
针对石墨烯/聚合物复合材料，传统成型工艺有：手糊成型、模压成型、热压罐成型、挤拉成型、缠绕成型等。虽然这些工艺在现有生产中占有一席之地，但是它们也存在着非常明显的缺点。
1、手糊成型：生产效率低、劳动强度大；
2、模压成型与热压罐成型：模具要求高、生产成本大、尺寸受限；
3、挤拉成型：设备投资高、产品截面受限；缠绕成型：投资大、技术要求高。
都不适用于复杂的三维结构，限制了石墨烯/聚合物复合材料的应用和普及。现有的3D打印技术，会造成石墨烯的团聚或沉积，导致成型的材料不能充分发挥石墨烯优良的力学特性和导电特性。
现有技术中并不能实现电场辅助光固化的连续打印，现有的连续打印装置也不能实现打印件内部石墨烯的均匀分布。
因此，亟需解决上述问题。
本背景技术所公开的上述信息仅仅用于增加对本申请背景技术的理解，因此，其可能包括不构成本领域普通技术人员已知的现有技术。
发明内容
为了解决上述问题，本发明提供了一种电场辅助连续面曝光3D打印有序复合材料的制备方法
为实现上述发明目的，本发明采用下述技术方案予以实现：
一种电场辅助连续面曝光3D打印有序复合材料的制备方法，所述打印设备包括数字光处理模块，浆料槽，打印平台，高压电源；所述数字处理模块按照打印模型分层切片形状，以光束形式穿过复合透氧膜并投射到浆料中。所述打印平台沿z轴方向逐渐上移，所述高压电源置于浆料槽内部两侧用于提高外加电场；
步骤1：打印模型准备
首先将三维图形以STL文件格式导入至切片软件，在考虑打印时长、材料可固化厚度、精度要求因素后，对模型进行分层切片；然后将切片所得数据制作成视频文件并导入至数字光处理模块；
步骤2：复合材料浆料制备
将一定比例的树脂与石墨烯进行混合，再进行真空除泡，得到所需的复合材料浆料；
步骤3：电场辅助连续面曝光3D打印
首先将打印平台缓缓浸入浆料中，直至打印平台与复合富氧膜的距离略大于成型件与打印窗口之间形成的不固化区域即“死区”厚度；然后，根据需要在指定方向上利用高压电源施加电场；紧接着数字光处理模块将制备好的视频图像投影到浆料上的同时打印平台以一定速度上升，此时，受到紫外光辐照后固化的成型件随着打印平台的上升而不断上升，成型件上升留出的空隙也被四周的浆料迅速填充，整个过程一直处于连续状态；最终视频播放完成的同时，携带着有序排列石墨烯的复合材料成型件也被完整地从浆料中“拖”了出来。
步骤4：打印后处理
打印完成后，取下并清理成型件后进行二次固化。
在本申请的一些实施例中，所述复合透氧膜包括支撑层和低表面能层，支撑层位于低表面层的下部，其选用微孔PET膜来保证支撑强度和一定的透氧性，低表面能层选用PDMS来防止粘附，保证浆料的填充，以固化树脂材料。
在本申请的一些实施例中，所述数字光处理模块，投射光波长为405nm，光源最大功率800mW。
在本申请的一些实施例中，所述复合透氧膜为PDMS/SiO2膜，所述PDMS/SiO2膜，上层为氢氟酸溶液刻蚀掉SiO2的PDMS膜；下层为未刻蚀SiO2的PDMS/SiO2膜。
在本申请的一些实施例中，所述PDMS/SiO2膜的制备方法包括以下步骤：
②取粒径为200nm左右的球状SiO2颗粒与道康宁PDMS预混液，SiO2质量占比为10％-40％，以200r/min-300r/min搅拌2-5min；
②将上述混合溶液放入超声波清洗机中混合15-20min；
③静置冷却后加入PDMS固化剂，固化剂与PDMS预混液质量比为1/10-1/8，以200r/min-300r/min搅拌3-5min；
④在0-8℃温度中静置12-24h，直至完全没有气泡；
⑤利用数控雕刻机，以80-100℃的底板加热、30-50Kpa的气压、320-400km/h将混合溶液打印成膜；
⑥将打印所得膜置于干燥箱中干燥；
⑦将完全固化的SiO2/PDMS混合膜浸入装满SiO2悬浮液的容器中，其中悬浮液中SiO2粒径为2-5μm，利用提拉机器以1-8mm/s匀速竖直向上提拉；
⑧将上述复合膜置于200-250℃中加热60-80h；
⑨用旋涂机将光刻胶SU-8基环氧树脂旋涂在复合膜表面SiO2缝隙中，转速2500-3500r/min、旋涂时间30-60s，再用有机溶剂清洗表面残留的光刻胶；
⑩用紫外固化灯对表面的光刻胶进行固化，时间1-3min；
最终所得的复合透明膜厚度50-100μm，并且氧气透过效率在50barrer以上，紫外光透过率不低于80％，强度不低于20kPa。
在本申请的一些实施例中，所述树脂与石墨烯进行混合，优选球磨混合，球磨参数为转速：300-500r/min；时间：10-12h，优选地，每1h暂停10min。
在本申请的一些实施例中，真空除泡的时间为2h。
在本申请的一些实施例中，所述有序复合材料中石墨烯的添加质量分数为0.1％-5％。
在本申请的一些实施例中，打印速度为10mm/h-100mm/h
在本申请的一些实施例中，利用高压电源施加直流电场，直流恒压电源500V/cm，在微观组织层面对材料中的石墨烯片的排列进行无接触式调整。
在本申请的一些实施例中，所述树脂选用黏度为200-400mPs的树脂，所述石墨烯片使用工业级MLG粉末，片层直径10～50μm、片层厚度3.4～7nm，作为增强体起增强材料导电性和抗弯强度的作用。
在本申请的一些实施例中，所述树脂优选为光热双重固化树脂，由于连续打印光固化不能充分固化，所以采用光热双重固化树脂。
在本申请的一些实施例中，所述光热双重固化树脂的二次固化参数为：真空环境下，1℃/min的加热速度加热至100℃，保温1h，继续以1℃/min的加热速度加热至150℃，保温1h，继续以1℃/min的加热速度加热至180℃，保温1h，自然冷却至室温。
在本申请的一些实施例中，为保证打印平台与浆料之间无气泡存在，可采用多种方式放入浆料中，优选以侧置放入浆料有效保证气体的排出，或提前使用浆料润湿打印平台，达到浆料与打印平台的更好贴合。
在本申请的一些实施例中，所述打印设备还包括控制模块，用于根据设定的打印数据控制打印程序。
与现有技术相比，本公开的有益效果是：
通过结合连续面曝光3D打印和电场辅助；可以解决：
1、在表面形貌上对现有的光固化打印进行了优化，可以解决现有光固化技术分层严重的问题，可以做到表面无限细腻。
2、同时可以利用石墨烯片二维材料在辅助电场下有序排列的特点实现各向异性/有序复合材料的打印，以达到提高力学性能与电学性能的目的。
3、实现石墨烯的有序排列，增大了材料的抗弯强度和韧性。
4、通过对复合透氧膜进行优化选择，提高了打印精度，通过选择复合透氧膜为PDMS/SiO2膜，创新地将SiO2混入PDMS中，改善了原先PDMS膜的富氧性能，且不降低PDMS膜的透光性，其次可以改善原先PDMS膜的力学性能，可以配合较大的打印窗口进行大体积产品的打印；还可以对打印时产生的“死区”厚度进行一定范围的调控，最终可以在匹配打印浆料的粘稠性上产生一定效果；复合膜老化速度降低，降低了成本、提高了效率，并可为打印提供充足的氧气；复合膜上的疏水层使得浆料在复合膜上的流动性加强，即打印过程中的浆料填充速度加快。
附图说明
为了更清楚地说明本发明实施例中的技术方案，下面将对实施例中所需要使用的附图作简单地介绍，显而易见地，下面描述中的附图是本发明的一些实施例，对于本领域普通技术人员来讲，在不付出创造性劳动的前提下，还可以根据这些附图获得其他的附图。
图1是本申请的实施例中的打印装置示意图；
图2是本申请实施例中电场辅助连续面曝光3D打印实验装置图；
图3是本申请实施例中石墨烯/树脂复合材料中石墨烯排列示意图；
图4是本申请的石墨烯排列示意图；
图5是本申请的PDMS/SiO2膜的结构示意图。
其中，1、打印平台；2、浆料槽；3、复合富氧膜；4、数字光处理模块；5、死区；6、电极片；7、浆料；8、成型件；9、刻蚀掉SiO2的PDMS膜；10、未刻蚀SiO2的PDMS/SiO2膜；11、控制模块；12、高压电源。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。
本申请的电场辅助连续面曝光3D打印石墨烯/树脂有序复合材料方法，结合了连续面曝光3D打印可以改善成型件表面形貌的特点，以及施加辅助电场操纵导电纳米材料得到有序复合材料的特点。
本申请方法连续的效果是由于渗透到光敏树脂中的氧气会快速消耗树脂中单体固化所需的活性碎片，从而达到阻止或延缓树脂固化的现象；因此，成型件与打印窗口之间会形成不固化的区域，称为“死区”，“死区”的存在，使得成型件与打印窗口之间不会出现粘连现象，从而可以实现连续打印过程。
打印过程中，空气中的氧气分子会透过复合富氧膜进入到浆料槽中的浆料中，并且氧含量随着与复合富氧膜的距离越来越远而越来越小；此时，靠近复合富氧膜的浆料在吸收外界光能的时候会因为高含氧量，这个区域的浆料不会发生固化，这个区域称为“死区”，死区的存在使得成型件与复合富氧膜不会发生粘连，所以打印时不需要剥离操作，从而真正实现了连续打印，理论上，成型件的表面精度可以达到无限细腻。
本申请发明人利用石墨烯较强的介电特性，在电场的作用下，石墨烯产生极化反应，原本随机分布在树脂基体中的石墨烯片会表现出一种有序的排列方式，即排列方向平行于电场方向。极化后，石墨烯可以被看成是电偶极子，此时，作用于石墨烯两端正负电荷的电场力会构成力偶，力偶矩M为
M＝qELsinθ (1)
式中，M是力偶矩，q是石墨烯极化后两端带的电荷，E是施加电场强度，L是石墨烯的长度，θ是石墨烯轴向与电场方向的夹角。由于二维石墨烯具有形状各向异性，所以平行于石墨烯的极化力矩远大于垂直于石墨烯的极化力矩，这种差异会导致其在电场方向产生定向的扭转力，使得石墨烯发生旋转，最终表现为石墨烯在电场的诱导下会呈现出平行于电场方向的有序排列。
实施例1
一种电场辅助连续面曝光3D打印石墨烯/树脂有序复合材料的制备方法，包括以下步骤：
步骤1：打印模型准备
首先将三维图形以STL文件格式导入至切片软件，在考虑打印时长、材料可固化厚度、精度要求因素后，对模型进行分层切片；然后将切片所得数据制作成视频文件并导入至数字光处理模块；
步骤2：复合材料浆料制备
将95wt.％乙氧基化三羟甲基丙烷三丙烯酸酯和5wt.％甲基丙烯酸环氧丙酯混合得到A，将53wt.％环氧树脂828和47wt.％4-甲基六氢苯酐混合得到B，然后40wt.％A和60％wt.B混合得到C，再将99.6wt.％C与0.4wt.％光敏引发剂混合之后，与石墨烯按照质量分数99∶1比例进行球磨混合，球磨参数为转速：500r/min；时间：12h，每1h暂停10min，再进行真空除泡2h，得到所需要的的复合材料浆料；
所述树脂黏度为300mPs，所述石墨烯片使用工业级MLG粉末，片层直径10～50μm、片层厚度3.4～7nm。
步骤3：电场辅助连续面曝光3D打印
首先将打印平台缓缓浸入浆料中，直至打印平台与复合富氧膜的距离略大于成型件与打印窗口之间形成的不固化区域即“死区”厚度；
所述复合透氧膜包括支撑层和低表面能层，支撑层位于低表面层的下部，支撑层为微孔PET膜，低表面能层为PDMS；
然后，根据需要在指定方向上利用高压电源施加直流电场，直流恒压电源500V/cm；紧接着数字光处理模块将制备好的视频图像投影到浆料上的同时打印平台以一定速度上升，数字光处理模块投射光波长为405nm，光源最大功率800mW；此时，受到紫外光辐照后固化的成型件随着打印平台的上升而不断上升，成型件上升留出的空隙也被四周的浆料迅速填充，整个过程一直处于连续状态；最终视频播放完成的同时，携带着有序排列石墨烯的复合材料成型件也被完整地从浆料中“拖”了出来。
步骤4：打印后处理
打印完成后，取下并清理成型件后进行二次固化。
光热双重固化树脂的二次固化参数为：真空环境下，1℃/min的加热速度加热至100℃，保温1h，继续以1℃/min的加热速度加热至150℃，保温1h，继续以1℃/min的加热速度加热至180℃，保温1h，自然冷却至室温。
实施例2
与实施例1不同的是，所述复合透氧膜由PDMS/SiO2组成，其中上层为表面刻蚀的PDMS膜，厚度为10μm；下层为PDMS/SiO2复合膜，厚度为50μm。
测试结果显示，实施例1和2均实现了石墨烯/树脂有序复合材料的连续有序制备，避免了石墨烯在树脂中的沉积和团聚；经测试，具有2wt％含量的石墨烯有序复合材料的电阻率约为无序复合材料的1/16，且在一定范围内，有序复合材料中，石墨烯含量越高，其电阻率越小，表现出优异的电学性能；在力学性能上，有序复合材料在抗弯强度上明显优于无序复合材料，有序复合材料的最大应变为24％，无序复合材料最大为20％。
以上实施例仅用以说明本发明的技术方案，而非对其进行限制；尽管参照前述实施例对本发明进行了详细的说明，对于本领域的普通技术人员来说，依然可以对前述实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换；而这些修改或替换，并不使相应技术方案的本质脱离本发明所要求保护的技术方案的精神和范围。
Claims (8)
1.一种电场辅助连续面曝光3D打印有序复合材料的制备方法，其特征在于，所使用的打印设备包括数字光处理模块，浆料槽，打印平台，高压电源；所述数字光处理模块按照打印模型分层切片形状，以光束形式穿过复合透氧膜并投射到浆料中，所述打印平台沿z轴方向逐渐上移，所述高压电源置于浆料槽内部两侧用于提高外加电场；步骤1：打印模型准备首先将三维图形以STL文件格式导入至切片软件，在考虑打印时长、材料可固化厚度、精度要求因素后，对模型进行分层切片；然后将切片所得数据制作成视频文件并导入至数字光处理模块；步骤2：复合材料浆料制备将一定比例的树脂与石墨烯进行混合，再进行真空除泡，得到所需的复合材料浆料；步骤3：电场辅助连续面曝光3D打印首先将打印平台缓缓浸入浆料中，直至打印平台与复合透氧膜的距离略大于成型件与打印窗口之间形成的不固化区域，即死区厚度；然后，根据需要在指定方向上利用高压电源施加电场；紧接着数字光处理模块将制备好的视频图像投影到浆料上的同时打印平台以一定速度上升，此时，受到紫外光辐照后固化的成型件随着打印平台的上升而不断上升，成型件上升留出的空隙也被四周的浆料迅速填充，整个过程一直处于连续状态；最终视频播放完成的同时，携带着有序排列石墨烯的复合材料成型件也被完整地从浆料中拖了出来；步骤4：打印后处理打印完成后，取下并清理成型件后进行二次固化；
所述复合透氧膜为PDMS/SiO2膜，所述复合透氧膜PDMS/SiO2膜的制备方法包括以下步骤：
①取粒径为200nm左右的球状SiO2颗粒与道康宁PDMS预混液，SiO2质量占比为10％-40％，以200r/min-300r/min搅拌2-5min；②将上述混合溶液放入超声波清洗机中混合15-20min；③静置冷却后加入PDMS固化剂，固化剂与PDMS预混液质量比为1/10-1/8，以200r/min-300r/min搅拌3-5min；④在0-8℃温度中静置12-24h，直至完全没有气泡；⑤利用数控雕刻机，以80-100℃的底板加热、30-50Kpa的气压、320-400km/h将混合溶液打印成膜；⑥将打印所得膜置于干燥箱中干燥；⑦将完全固化的PDMS/SiO2混合膜浸入装满SiO2悬浮液的容器中，其中悬浮液中SiO2粒径为2-5μm，利用提拉机器以1-8mm/s匀速竖直向上提拉；⑧将上述复合膜置于200-250℃中加热60-80h；⑨用旋涂机将光刻胶SU-8基环氧树脂旋涂在复合膜表面SiO2缝隙中，转速2500-3500r/min、旋涂时间30-60s，再用有机溶剂清洗表面残留的光刻胶；⑩用紫外固化灯对表面的光刻胶进行固化，时间1-3min；
将上述复合膜置于氢氟酸溶液中蚀刻5-15min去除表面SiO2，用酒精彻底清洗，干燥箱干燥；最终所得的复合透氧膜厚度50-100μm，并且氧气透过效率在50barrer以上，紫外光透过率不低于80％，强度不低于20kPa。
2.根据权利要求1所述的一种电场辅助连续面曝光3D打印有序复合材料的制备方法，其特征在于，所述数字光处理模块，投射光波长为405nm，光源最大功率800mW。
3.根据权利要求1所述的一种电场辅助连续面曝光3D打印有序复合材料的制备方法，其特征在于，所述树脂与石墨烯进行混合，所述混合为球磨混合，球磨参数为转速为300-500r/min；时间为10-12h，真空除泡的时间为2h。
4.根据权利要求3所述的一种电场辅助连续面曝光3D打印有序复合材料的制备方法，其特征在于，所述有序复合材料中石墨烯的添加质量分数为0.1％-5％。
5.根据权利要求1所述的一种电场辅助连续面曝光3D打印有序复合材料的制备方法，其特征在于，打印速度为10mm/h-100mm/h。
6.根据权利要求1所述的一种电场辅助连续面曝光3D打印有序复合材料的制备方法，其特征在于，利用高压电源施加直流电场，直流恒压电源500V/cm，在微观组织层面对材料中的石墨烯片的排列进行无接触式调整。
7.根据权利要求1-6任一项所述的一种电场辅助连续面曝光3D打印有序复合材料的制备方法，其特征在于，所述树脂光热为双重固化树脂。
8.根据权利要求7所述的一种电场辅助连续面曝光3D打印有序复合材料的制备方法，其特征在于，所述树脂选用黏度为200-400mPa·s的树脂，所述石墨烯片使用工业级MLG粉末，片层直径10～50μm、片层厚度3.4～7nm。