CN112795777A - 一种用于冶金球团生产的有机复合型膨润土生产工艺 - Google Patents
一种用于冶金球团生产的有机复合型膨润土生产工艺 Download PDFInfo
- Publication number
- CN112795777A CN112795777A CN202110243156.2A CN202110243156A CN112795777A CN 112795777 A CN112795777 A CN 112795777A CN 202110243156 A CN202110243156 A CN 202110243156A CN 112795777 A CN112795777 A CN 112795777A
- Authority
- CN
- China
- Prior art keywords
- bentonite
- metallurgical
- organic
- organic composite
- sodium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种用于冶金球团生产的有机复合型膨润土生产工艺，其特征是：首先将钙基膨润土钠化，制得成品钠基膨润土；在钠基膨润土中添加一定量的有机粘接粉剂，制得有机复合球团膨润土；将羧甲基淀粉钠(CMS‑Na)和聚丙烯酰胺(PAM)在搅拌机中充分拌匀制成有机粘接粉剂；羧甲基淀粉钠(CMS‑Na)是一种有机物，是一种水溶性阴离子高分子化合物；聚丙烯酰胺筒称PAM，是易溶于水的高分子量的阴离子性的聚丙烯酰胺，将钠基膨润土与有机粘接粉剂充分搅拌，制得有机复合型膨润土；生产冶金球团时，将有机复合型膨润土按一定浓度调制成泥浆，再用泥浆泵喷洒在旋转的造球机造球盘中冶金粉末上造球；有机物燃烧后对冶金产品质量无影响，也不污染环境。
Description
技术领域
一种用于冶金球团生产的有机复合型膨润土生产工艺，属非金属矿物材料技术领域。
背景技术
在冶金熔炼或其它需要粉末造球的企业中，冶金粉末需得添加一种粘合剂造球，目前国内国外都用膨润土作为粘合剂，但是，添加非金属矿物膨润土太多会降低冶金球团品位，增加炉下矿渣量和整体冶金熔炼能耗；国内冶金粉末球团生产中膨润土的配入量太大，其平均配入量按重量百分比计算在2.5-4％左右，与国外低于1％的水平相比，存在明显的差距；怎样才可既能减少膨润土的添加量，又要能满足铁粉及其它冶金球团的各种性能要求，研制一种用于冶金球团生产的有机复合型膨润土，制得的冶金球团才能满足冶金球团的落下强度、抗压强度和爆裂温度等各项要求。
发明内容
为了解决认上问题，本发明涉及一种用于冶金球团生产的有机复合型膨润土生产工艺，本产品可大幅减少冶金球团造球时所需膨润土的使用量。
为了解决以上技术问题，本发明特征是：首先采用钙基膨润土中添加纯碱溶液挤压钠化的方法，再烘干后研细制得钠基膨润土成品。
在钠基膨润土中添加一定量的有机粘接粉剂，制得用于冶金球团生产的有机复合型膨润土。
有机粘接粉剂的制备方法是将有机粘接剂羧甲基淀粉钠(CMS-Na) 75％和聚丙烯酰胺(PAM) 25％，放入搅拌机中充分拌匀制成有机粘接粉剂；这类有机粘接剂的化学物理性质，如高温流变性、分解和燃烧温度均能满足球团的使用要求。
羧甲基淀粉钠(CMS-Na)是一种有机物，是一种阴离子淀粉醚，化学式为[C10H1908Na]n，白色或黄色粉末，是能溶于冷水的电解质；是变性淀粉的一种，属醚类淀粉，是一种水溶性阴离子高分子化合物；它无臭、无味、无毒、不易霉变，当取代度大于0.2时易溶于水；简称CMC-Na，为纤维状或颗粒状粉末，有吸湿性，易于分散在水中形成透明的胶体溶液，经高温烧灭后主要生成二氧化碳和水。
要求工业用羧甲基淀粉钠(CMS-Na) 易溶于冷水。
聚丙烯酰胺筒称PAM，要求聚丙烯酰胺(PAM) 为易溶于水的高分子量的阴离子性的聚丙烯酰胺，可以采用专业制蚊香或佛香用的聚丙烯酰胺(PAM) ，高温烧灭后生成二氧化碳和水。
用于冶金球团生产的有机复合型膨润土的制备方法是将钠基膨润土与有机粘接粉剂充分混合，制得用于冶金球团生产的有机复合型膨润土。
有机粘结粉剂添加量为钠基膨润土重量百分比的1-2％。
生产冶金球团时，首先将用于冶金球团生产的有机复合型膨润土按10-15％浓度调制成膨润土泥浆，再用泥浆泵经泥浆管喷头，均匀的喷洒在旋转的造球机造球盘中冶金粉末上造球。
喷洒在造球盘中的有机复合型膨润土泥浆添加量可从原钠基膨润土添加量重量百分比3-4％降到1.0-1.5％左右，而这些有机物燃烧后主要生成二氧化碳和水，对冶金产品质量并无影响，同时也不会造成环境污染。
一种用于冶金球团生产的有机复合型膨润土具有以下创新点。
使用有机复合型膨润土造球可使原料成球性能明显改善，还可降低造球对原料粒度的要求。
有机复合型膨润土的用量大幅下降，从原添加量(重量百分比)3-4％降到1.0-1.5％左右，而有机物燃烧后主要生成二氧化碳和水，对冶金产品质量并无影响，同时也不会造成环境污染。
生球强度显著提高，生球抗压强度、落下强度以及球团爆裂温度均能更好地满足球团生产的质量要求。
因造球过程中添加了带有机粘合剂的膨润土，所造冶金球团表面光滑，强度高，干球落下时不易破裂，固不易产生灰尘而污染环境。
使用用于冶金球团生产的有机复合型膨润土造球，提高了冶金球团品位，减少了炉下矿渣量，相对也降低了整体冶炼能源消耗，节约了生产成本。
附图说明
下面结合附图对本发明作进一步说明。
附图是本发明工艺流程图。
具体实施方式
下面结合附图和具体实施方式对本发明作进一步说明。
实施例1：原材料为采购的成品钠化膨润土。
将一定数量的钠化膨润土放于搅拌机中，加入(重量百分比)1％的有机粘接粉剂进行充分搅拌，制得用于冶金球团生产的有机复合型膨润土。
用于冶金球团生产的有机复合型膨润土与水按(重量百分比)15％浓度调制成有机复合型膨润土泥浆，再将泥浆用泥浆泵经泥浆管喷头均匀的喷洒在转动的造球盘中的冶金粉末上造球。
采用此方案制得的冶金球团，其落下强度、抗压强度和爆裂温度圴能达到使用要求。
实施例2：原材料为采购的成品钠化膨润土。
将一定数量的钠化膨润土放于搅拌机中，加入(重量百分比)1.5％的有机粘接粉剂进行充分搅拌，制得用于冶金球团生产的有机复合型膨润土。
用于冶金球团生产的有机复合型膨润土与水按(重量百分比)10％浓度调制成有机复合型膨润土泥浆，再将泥浆用泥浆泵经泥浆管喷头均匀的喷洒在转动的造球盘中的冶金粉末上造球，制得的冶金球团不影响下一步预热、干燥等工序。
采用实施例2方案制得的冶金球团，其落下强度、抗压强度和爆裂温度参数均有所提高。
实施例3：取原矿钙基膨润土晒干或用烘干机脱水，再进入雷蒙磨机研磨，同时加入纯碱2.5-3.5％，羧甲基淀粉钠(CMS-Na)0.8％、聚丙烯酰胺(PAM)0.2％，混合磨细，经风选所得200目细粉，即为用于冶金球团生产的有机复合型膨润土。
用于冶金球团生产的有机复合型膨润土与水按重量百分比10-15％浓度调制成有机复合型膨润土泥浆，再将泥浆用泥浆泵经泥浆管喷头均匀的喷洒在转动的造球盘中的冶金粉末上造球。
按照实施例3方案制得的冶金球团，其落下强度、抗压强度和爆裂温度参数均有进一步提高。
Claims (6)
1.一种用于冶金球团生产的有机复合型膨润土生产工艺，其特征是：首先将钙基膨润土中添加纯碱溶液挤压钠化，再烘干后研细制得钠基膨润土成品，在钠基膨润土中添加一定量的有机粘接粉剂，制得用于冶金球团生产的有机复合型膨润土；有机粘接粉剂的制备方法是将有机粘接剂羧甲基淀粉钠CMS-Na和聚丙烯酰胺PAM，放入搅拌机中充分拌匀制成有机粘接粉剂；这类有机粘接粉剂的化学物理性质，如高温流变性、分解和燃烧温度均能满足球团的使用要求；羧甲基淀粉钠CMS-Na是一种有机物，是一种阴离子淀粉醚，化学式为[C10H1908Na]n，白色或黄色粉末，是能溶于冷水的电解质；是变性淀粉的一种，属醚类淀粉，是一种水溶性阴离子高分子化合物；它无臭、无味、无毒、不易霉变，当取代度大于0.2时易溶于水，简称CMC-Na，为纤维状或颗粒状粉末，有吸湿性，易于分散在水中形成透明的胶体溶液，经高温烧灭后主要生成二氧化碳和水；聚丙烯酰胺筒称PAM，要求聚丙烯酰胺PAM为易溶于水的高分子量的阴离子性的聚丙烯酰胺，可以采用专业制蚊香或佛香用的聚丙烯酰胺(PAM) ，烧灭后生成二氧化碳和水；用于冶金球团生产的有机复合型膨润土的制备方法是将钠基膨润土与有机粘接粉剂充分搅拌，制得用于冶金球团生产的有机复合型膨润土；生产冶金球团时，首先将用于冶金球团生产的有机复合型膨润土调制成膨润土泥浆，再用泥浆泵经泥浆管喷头，均匀的喷洒在旋转的造球机造球盘中冶金粉末上造球，有机复合型膨润土泥浆添加量可从原钠基膨润土添加量重量百分比3-4％降到1.0-1.5％，而这些有机物燃烧后主要生成二氧化碳和水，对冶金产品质量并无影响，同时也不会造成环境污染。
2.根据权利要求1所述的一种用于冶金球团生产的有机复合型膨润土生产工艺，其特征是：有机粘接粉剂是羧甲基淀粉钠CMS-Na75％和聚丙烯酰胺PAM25％的混合物。
3.根据权利要求1所述的一种用于冶金球团生产的有机复合型膨润土生产工艺，其特征是：要求工业用羧甲基淀粉钠CMS-Na 易溶于冷水。
4.根据权利要求1所述的一种用于冶金球团生产的有机复合型膨润土生产工艺，其特征是：有机复合球团膨润土中有机粘结粉剂添加量为钠基膨润土重量百分比的1-2％。
5.根据权利要求1所述的一种用于冶金球团生产的有机复合型膨润土生产工艺，其特征是：经烘干脱水的钙基膨润土中加入纯碱2.5-3.5％、羧甲基淀粉钠CMS-Na 0.8％、聚丙烯酰胺PAM 0.2％，混合磨细，经风选所得200目细粉即为有机复合球团膨润土。
6.根据权利要求1所述的一种用于冶金球团生产的有机复合型膨润土生产工艺，其特征是：用于冶金球团生产的有机复合型膨润土与水按重量百分比10-15％浓度调制成有机复合型膨润土泥浆。