CN112724746A - 一种温变计时油墨及标签 - Google Patents
一种温变计时油墨及标签 Download PDFInfo
- Publication number
- CN112724746A CN112724746A CN202011594677.4A CN202011594677A CN112724746A CN 112724746 A CN112724746 A CN 112724746A CN 202011594677 A CN202011594677 A CN 202011594677A CN 112724746 A CN112724746 A CN 112724746A
- Authority
- CN
- China
- Prior art keywords
- temperature
- ink
- solvent blue
- color
- timing ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种温变计时油墨及标签，所述温变计时油墨包括成膜树脂、蒽醌类染料和光产酸剂，所述光产酸剂光照生成路易斯酸，所述路易斯酸与所述蒽醌类染料反应呈现出第一颜色，所述温变计时油墨光照后受热由第一颜色转变为第二颜色。此外，本发明还提供了包括上述温变计时油墨层的标签，具有启动便捷、体积小、结构简单、成本低廉、方便量产、颜色变化对比明显的优点。
Description
技术领域
本发明涉及温度监测及应用技术领域，特别涉及一种温变计时油墨及标签。
背景技术
目前，食品生鲜等快消品、血液制品、疫苗等冷链产品在运输和储存过程中需要保持一定的温度范围，这些制品不仅在制备过程中需要低温环境，产品在出厂后要经过一系列的冷链运输环节才能达到消费者手中，每一个环节都是一个潜在的风险点，冷链环节中的任一环节温度超标都可能导致较为严重的后果。同时运输或是储存中若出现问题，责任方认定也较难。
现有技术中，如中国专利申请号为CN200420078916.0的专利提到使用简易温度计的毛细管作用原理，制成一种当环境温度超过设定温度的可变色的装置，该装置体积相对较大而冷链产品体积相对较小，同时该装置关键部件易碎不易使用。另外英国Timestrip公司在中国申请的专利公开号为CN1533518A的专利中提出了一种变色标签装置，将装有溶剂的囊压破后溶液逐渐渗透至观测区，一经使用则会在短者几分钟，迟者数小时的时间内失效，其只能计量冷链运输时间，而不能计量冷链环境是否超过设定的危险温度，同时该产品存在结构复杂、成本高、体积较大的问题，限制了其推广应用。目前WHO官方在疫苗温度监控领域推荐使用的疫苗热标签VVM(Vaccine Vial Monitor)则存在低温生产、低温运输带来的成本问题及失效颜色对比不明显的问题。苏州华实在中国申请的专利公开号为CN103903509B的专利公开中采用两个叠层分别储运，而在使用时组合在一起的方式，这个使用方式对客户来说增加了设备的投入及使用时贴合精度的要求，也限制了其推广应用。
因此，有必要提出一种启动便捷、体积小、结构简单、成本低廉、方便量产、颜色变化对比明显的温变计时油墨及标签。
发明内容
本发明的目的在于针对现有技术中存在的以上技术问题，提出一种结构简单、体积小、量产方便并可实现计时功能的温变计时油墨及标签。
本发明采用的技术方案如下：
一种温变计时油墨，包括成膜树脂、蒽醌类染料和光产酸剂，光产酸剂光照生成路易斯酸，路易斯酸与蒽醌类染料反应呈现出第一颜色，所述温变计时油墨光照后受热由第一颜色转变为第二颜色。
优选地，蒽醌类染料占成膜树脂的重量比例为1～50％，光产酸剂占成膜树脂的重量比例为1～10％。
优选地，成膜树脂选自丙烯酸树脂、聚氨酯、有机硅、聚酯中的一种或多种。
优选地，蒽醌类染料选自溶剂蓝11、溶剂蓝36、溶剂蓝35、溶剂蓝68、溶剂蓝70、溶剂蓝78、溶剂蓝97、溶剂蓝104、溶剂蓝122、溶剂蓝359中的一种或多种。
优选地，光产酸剂选自二芳基碘鎓盐、三芳基硫鎓盐、烷基硫鎓盐、铁芳烃盐、磺酰氧基酮及三芳基硅氧醚中的一种或多种。
优选地，温变计时油墨还包括中和剂、流平剂、消泡剂、触变剂和填充料中的一种或者多种。
优选地，中和剂选自环氧类树脂及其单体和衍生改性物中的一种或者多种。
优选地，流平剂、消泡剂选自有机硅类，丙烯酸类以及其改性类中的一种或多种。
优选地，触变剂选自气相二氧化硅，有机膨润土，氢化蓖麻油，聚酰胺蜡中的一种或多种。
优选地，填充料选自有机消光粉、无机消光粉、硫酸钡、碳酸钙中的一种或多种。
本发明还提供了一种标签，包括油墨层，所述油墨层中的油墨为上述温变计时油墨。
本发明的温变计时油墨，在紫外线的激发下启动，受热后能够指示颜色变化。且由该油墨制成的标签，印刷简便，一次印刷即可完成，成品可以常温存储，节约能耗，使用时紫外线激发，启动便捷，具有结构简单、操作方便、材料选择广、易推广应用的优点。
附图说明
通过参照本发明的实施方案的图示说明可以更好地理解本发明，在附图中：
图1是本发明标签的结构示意图。
具体实施方式
在以下的描述中，为了达到解释说明的目的以对本发明有一个全面的认识，阐述了大量的具体细节，然而，很明显的，对本领域技术人员而言，无需这些具体细节也可以实现本发明。本发明所列举的说明性的示例实施方案仅为了说明，并不对本发明造成限制。因此，本发明的保护范围并不受具体实施方案所限，仅以所附的权利要求书的范围为准。
下面将结合附图对本发明的温变计时油墨及标签做详细说明。
正如现有技术所述，现有的感温计时标签在原料制备以及组装上存在着较大难度，且成本较高，售价昂贵，在批量应用上难以实现。
为了解决上述问题，本发明提供了一种温变计时油墨，包括成膜树脂、蒽醌类染料和光产酸剂，光产酸剂光照生成路易斯酸，路易斯酸与蒽醌类染料反应呈现出第一颜色，温变计时油墨光照后受热由第一颜色转变为第二颜色。本发明的温变计时油墨，在紫外线的激发下启动，受热后能够指示颜色变化，具有启动便捷、体积小、结构简单、成本低廉、方便量产、颜色变化对比明显的优点。
本发明温度计时油墨的变色原理：蒽醌类染料在酸性环境中被还原，可生成蒽酚及其异构体蒽酮，呈现出第一颜色；蒽酮在受热后又易氧化为蒽醌，呈现出第二颜色。具体地，在本发明中，温变计时油墨中的光产酸剂在光照下生成路易斯酸，路易斯酸攻击蒽醌类染料，使其还原为蒽酚及其异构体蒽酮，颜色立即发生变化，由蓝色立即变为红色，此时温变计时油墨呈现出第一颜色：红色。此后，随着温度时间的累积，颜色又由红色缓慢的还原至初始的蓝色，即受热后的温变计时油墨完成由第一颜色到第二颜色的转变。该颜色变化反应是不可逆、一次性、不可重复的。
在本发明中，成膜树脂主要用于提供油墨的主体骨架。成膜树脂选自丙烯酸树脂、聚氨酯、有机硅、聚酯中的一种或多种。
蒽醌类染料为主要变色体，可以选自溶剂蓝11、溶剂蓝36、溶剂蓝35、溶剂蓝68、溶剂蓝70、溶剂蓝78、溶剂蓝97、溶剂蓝104、溶剂蓝122、溶剂蓝359中的一种或多种。在本发明中，蒽醌类染料占成膜树脂的重量比例为1～50％。若蒽醌类染料占成膜树脂的重量比例小于1％，蒽醌类染料含量过少，导致温变计时油墨变色不明显；若蒽醌类染料占成膜树脂的重量比例大于50％，染料含量较多，导致无法成膜。
本发明的光产酸剂主要用来提供酸性物质。在紫外线的照射下，光产酸剂会产生酸性物质，与蒽醌类染料反应。光产酸剂选自二芳基碘鎓盐、三芳基硫鎓盐、烷基硫鎓盐、铁芳烃盐、磺酰氧基酮及三芳基硅氧醚中的一种或多种。光产酸剂占成膜树脂的重量比例为1～10％。若光产酸剂的用量小于1％，则无法分解过多的路易斯酸攻击蒽醌类染料，因而无法启动温变计时油墨；若光产酸剂的用量大于10％，则光照后产生的路易斯酸过多，过量的路易斯酸会使受热氧化后的蒽醌还原变色，从而影响温变指示判断。
在本发明一种优选的实施方式中，温变计时油墨还包括中和剂、流平剂、消泡剂、触变剂和填充料中的一种或者多种。
上述中和剂主要用来中和油墨中多余的酸性物质，避免受热氧化后的蒽醌染料在酸性物质作用下再次还原为蒽酮，影响颜色判断。中和剂选自环氧类树脂及其单体和衍生改性物中的一种或者多种，产生的多余质子酸被油墨中环氧树脂或环氧单体中和剂反应掉。
流平剂主要用来提供印刷流平性能，可以为有机硅类，丙烯酸类以及其改性类中的一种或多种，例如可以为毕克化学的BYK333、BYK3500、BYK373、BYK378等。
消泡剂主要用于提供印刷消泡性能，消泡剂选自有机硅类，丙烯酸类以及其改性类中的一种或多种，例如可以为德国迪高消泡剂TEGO N、Foamex805，毕克化学的BYK022、BYK1752、BYK1790、BYK1794等。
触变剂主要用于控制油墨印刷膜厚一致性，触变剂选自气相二氧化硅，有机膨润土，氢化蓖麻油，聚酰胺蜡中的一种或多种。
在本发明的实施方式中，温变计时油墨还包括填充料，填充料用来改变油墨表面粗糙度实现比表面积变化，达到氧化快慢控制效果。填充料选自有机消光粉、无机消光粉、硫酸钡、碳酸钙中的一种或多种。
通过对以上物质进行混合、搅拌、研磨，最终调配成可印刷的温变计时油墨成品。
本发明另一种优选的实施方式中，还提供了一种标签，采用上述温变计时油墨印刷制成，可以采用凹印，凸印，丝印等印刷方式形成温变计时油墨层，进行制作标签，其印刷图案如图1所示，可以是圆形、方形、椭圆、三角形、或多边形、文字、图案等可视化标识，对印刷完图案进行烘干固化。标签使用时采用UV灯进行紫外线激发，使得油墨中光产酸剂产生路易斯酸，路易斯酸与蒽醌类染料反应呈现出第一颜色，标签光照后受热由第一颜色转变为第二颜色。
本发明的标签具有启动便捷、体积小、结构简单、成本低廉、方便量产、颜色变化对比明显的优点。
实施例1
本实施例的温变计时油墨包括：成膜树脂100g，选自日本东洋纺聚酯GK255(40％溶液)；蒽醌类染料30克，选自浙江闰土-分散蓝78；光产酸剂3克，选自深圳优阳科技irgacure-250；中和剂50克，中和剂为台湾长春化工的环氧树脂828。
将以上物质进行混合、搅拌、研磨，最终调配成可印刷的温变计时油墨。然后采用凹印，凸印，丝印等印刷方式形成温变计时油墨层，制作成标签。
实施例2：
与实施例1的不同在于：温变计时油墨还包括1克的流平剂，流平剂选自德国毕克流平剂BYK333；1.2克的消泡剂，消泡剂选自德国迪高消泡剂TEGO N；1克的触变剂，触变剂选自美国卡博特的气相二氧化硅M-5。
实施例3：
与实施例1的不同在于：温变计时油墨还包括1克的流平剂，流平剂选自德国毕克流平剂BYK333；1.2克的消泡剂，消泡剂选自德国迪高消泡剂TEGO N；1克的触变剂，触变剂选自美国卡博特的气相二氧化硅M-5；1.5克的填充料，填充料为德国德固赛消光粉TS-100。
实施例4：
与实施例3的不同在于，蒽醌类染料选自浙江闰土-分散蓝359，填充料的含量为3g。
实施例5：
与实施例3的不同在于，蒽醌类染料选自浙江闰土-分散蓝359，光产酸剂选自深圳优阳科技irgacure-261,填充料的含量为3g。
上述实施例制备的标签，在紫外线的激发下启动，受热后能够指示颜色变化，表1示出了不同实施例的标签在不同温度下的变色时间。
表1标签在不同温度下的变色时间
| -40℃ | 15℃ | 25℃ | 30℃ | |
| 实施例1 | / | 21H | 6.5H | 3.5H |
| 实施例2 | / | 21H | 6.5H | 3.5H |
| 实施例3 | / | 20H | 6H | 3H |
| 实施例4 | / | 17H | 5H | 2.5H |
| 实施例5 | / | 20H | 5.5H | 2H |
由上表可知，本发明的温变计时油墨及由此制备的标签，在紫外线的激发下启动，受热后在不同温度下颜色变化时间不同，可以用来监测温度和时间的变化，具有结构简单、操作方便、材料选择广、易推广应用的优点。可以广泛应用于生鲜食品、血浆制品、疫苗、冷链运输、高低温工作环境时间警示及指示的劳保用品，特殊场所时间限制参观证件，精密仪器设备的温度及运行时间警示及指示等需要监控其存储温度及时间变化及其他温度监测技术领域。
以上结合具体实施例描述了本发明的技术原理。这些描述只是为了解释本发明的原理，而不能以任何方式解释为对本发明保护范围的限制。基于此处的解释，本领域的技术人员不需要付出创造性的劳动即可联想到本发明的其他具体实施方式，这些方式都将落入本发明的保护范围之内。
Claims (11)
1.一种温变计时油墨，其特征在于，包括成膜树脂、蒽醌类染料和光产酸剂，所述光产酸剂光照生成路易斯酸，所述路易斯酸与所述蒽醌类染料反应呈现出第一颜色，所述温变计时油墨光照后受热由第一颜色转变为第二颜色。
2.根据权利要求1所述的一种温变计时油墨，其特征在于，所述蒽醌类染料占所述成膜树脂的重量比例为1～50％，所述光产酸剂占所述成膜树脂的重量比例为1～10％。
3.根据权利要求1所述的一种温变计时油墨，其特征在于，所述成膜树脂选自丙烯酸树脂、聚氨酯、有机硅、聚酯中的一种或多种。
4.根据权利要求1所述的一种温变计时油墨，其特征在于，所述蒽醌类染料选自溶剂蓝11、溶剂蓝36、溶剂蓝35、溶剂蓝68、溶剂蓝70、溶剂蓝78、溶剂蓝97、溶剂蓝104、溶剂蓝122、溶剂蓝359中的一种或多种。
5.根据权利要求1所述的一种温变计时油墨，其特征在于，所述光产酸剂选自二芳基碘鎓盐、三芳基硫鎓盐、烷基硫鎓盐、铁芳烃盐、磺酰氧基酮及三芳基硅氧醚中的一种或多种。
6.根据权利要求1～5任一项所述的一种温变计时油墨，其特征在于，所述温变计时油墨还包括中和剂、流平剂、消泡剂、触变剂和填充料中的一种或者多种。
7.根据权利要求6所述的一种温变计时油墨，其特征在于，所述中和剂选自环氧类树脂及其单体和衍生改性物中的一种或者多种。
8.根据权利要求6所述的一种温变计时油墨，其特征在于，所述流平剂、所述消泡剂选自有机硅类、丙烯酸类以及其改性类中的一种或多种。
9.根据权利要求6所述的一种温变计时油墨，其特征在于，所述触变剂选自气相二氧化硅、有机膨润土、氢化蓖麻油、聚酰胺蜡中的一种或多种。
10.根据权利要求6所述的一种温变计时油墨，其特征在于，所述填充料选自有机消光粉、无机消光粉、硫酸钡、碳酸钙中的一种或多种。
11.一种标签，其特征在于，所述标签包括油墨层，所述油墨层中的油墨为权利要求1～10任一项所述的温变计时油墨。