CN112724733B - 一种建筑用保温防火抗裂腻子 - Google Patents
一种建筑用保温防火抗裂腻子 Download PDFInfo
- Publication number
- CN112724733B CN112724733B CN202010532422.9A CN202010532422A CN112724733B CN 112724733 B CN112724733 B CN 112724733B CN 202010532422 A CN202010532422 A CN 202010532422A CN 112724733 B CN112724733 B CN 112724733B
- Authority
- CN
- China
- Prior art keywords
- component
- composition
- cement
- powder
- follows
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种建筑用保温防火抗裂腻子，它是由高铝水泥、硫铝酸盐水泥、氯氧镁水泥、漂珠、中空玻化微珠、稻壳粉、锯末等原材料制成。产品不仅具有保温隔热、防火抗裂的功能，而且把稻壳、锯末、粉煤灰等废物加以利用，变废为宝，利国利民，真正实现了保温、防火、抗裂、找平一体化，省工省时，环保节能。
Description
技术领域
本发明涉及建筑涂料技术领域，尤其涉及一种建筑用保温防火抗裂腻子。
背景技术
环保节能是国家大力提倡的，建筑物的防火问题已不能忽视。现有用在建筑物上的腻子材料很多，有抗裂腻子、保温腻子、找平腻子，但没有一款集保温、防火、抗裂为一体的腻子，因此研制出一款既有保温隔热效果，又能达到防火抗裂的多功能腻子势在必行。
发明内容
为解决现有技术中的不足，本发明提供一种建筑用保温防火抗裂腻子的制备方法，它采用有机材料与无机材料复配而成，使该腻子层能达到保温隔热、防火抗裂的功能，并且能让废物加以利用，变废为宝。
为实现上述技术目的，达到上述技术效果，本发明是通过以下技术方案来实现的一种建筑用保温防火抗裂腻子，它是由A、B、C、D四种组份组成，其每种组份重量百分比为A组份25％-28％，B组份28％-32％，C组份10％-15％，D组份为30％-35％。
其中A组份为波美度为23-27度的改性氯化镁水溶液。
①其重量百分比为氯化镁45-55％，水40-50％，改性剂2-5％，其中氯化镁选用纯度在90％以上的无水氯化镁不能用卤片，改性剂为草酸类和磷酸类。
②A组份的生产制造办法为：按重量百分比，先把氯化镁加到水中待完全溶解冷却后再加改性剂搅拌均匀即可。
其中B组份为轻烧氧化镁、高铝水泥。
①其配比按重量百分比计为：轻烧氧化镁80-90％，高铝水泥10-20％，其中轻烧氯化镁选用活性含量为90％以上的轻烧氧化镁，且细度在200-400目之间。
②B组份的生产方法是：把氧化镁和高铝水泥按重量百分比混合均匀即可。
其中C组份材料的组成为：水、VAE乳液、水泥基改性乳液、偶联剂、羟丙基甲基纤维素。
①其各组份的重量百分比为：水30-40％，VAE乳液30-40％，水泥基改性乳液30-40％，偶联剂0.3-0.8％，羟丙基纤维素0.3-0.8％，防腐杀菌剂0.1-0.2％。
②其中VAE乳液选用不与水泥和氧化镁水泥发生不良反应的VAE型乳液。
③C组份的生产制造方法是：按重量百分比在水中先放入羟丙基甲基纤维素、杀菌剂、偶联剂搅拌均匀后，再加入VAE乳液、水泥基乳液搅拌均匀即可。
其中D组份是由硫铝酸盐水泥、粉煤灰、漂珠、中空玻化微珠、陶瓷微珠、稻壳粉或锯末粉组成。
①其重量百分比为：水泥15-25％，粉煤灰20-30％，漂珠20-30％，中空玻化微珠10-18％，陶瓷微珠3-5％，稻壳粉或锯末粉8-13％。
②其中漂珠选用60-120目，中空玻化微珠用30-80目，陶瓷微珠选用200-300目，稻壳或锯末选用20-60目的。
③D组份的生产方法是把上述物质按重量百分比混合均匀即可。
生产时把A、B、C、D四种组份按重量百分比配方，分别装袋即可。
使用时按顺序把A组份先加到容器中，再加B组份搅拌均匀后，再加C组份搅拌均匀，最后加D组份搅拌均匀即可使用。使用时最好选用批刮的方式，批刮在建筑物表面，且批刮厚度在1.5-5cm之间。
本发明的有益效果是：
1、本发明是采用有机材料(VAE乳液，水泥基乳液)与无机材料(氯氧镁水泥，高铝水泥)作为凝胶粘接剂，复配起到了刚柔并济的效果，有机材料提高了产品的粘接性，致密性，柔韧性，改善了无机材料的刚性，易开裂等弊端。采用无机材料氯氧镁水泥，高铝水泥复配提高了产品的防火性能，可达A级防火要求，同时降低了成本。
2、采用漂珠、中空玻化微珠、陶瓷微珠、稻壳粉或锯末粉复配添加到粘接剂中起到了很好的保温隔热效果。
3、采用粉煤灰、稻壳粉或锯末粉添加到该产品中，起到了变废为宝、节约成本的效果，同时稻壳粉和锯末粉起到了一定的抗裂作用。
本发明真正实现了保温、防火、抗裂、抹平一体化，且施工方便，省时省工。
下面结合实例说明：
本发明一种建筑用保温防火抗裂腻子，它是由A、B、C、D四组份组成，每组份重量百分比为A组份25％，B组份30％，C组份13％，D组份32％
1、其中A组份为氯化镁水溶液和改性剂，其重量百分比为波美度为25°的氯化镁水溶液98％，20％六偏磷酸钠水溶液2％，生产时按重量百分比搅拌混合均匀即可。
2、其中B组分为轻烧氧化镁、高铝水泥，其重量百分比为轻烧氧化镁85％，高铝水泥15％，生产时搅拌混合均匀即可。
3、其中C组分为水，VAE乳液、水泥基改性乳液，偶联剂，羟丙基甲基纤维素、防腐杀菌剂，其重量百分比为纯净水34％，VAE乳液32％，水泥基改性乳液33％，偶联剂0.4％，羟丙基甲基纤维素0.5％，防腐杀菌剂0.1％，生产时按重量百分比在水中先放入羟丙基甲基纤维素，防腐杀菌剂搅拌均匀后，再放入偶联剂、VAE乳液、水泥基改性乳液搅拌均匀即可。
4、D组分是由硫铝酸盐水泥、粉煤灰、漂珠、中空玻化微珠、陶瓷微珠、改性处理后稻壳粉或锯末粉组成，其重量百分比为：硫铝酸盐水泥25％、粉煤灰27％、漂珠18％、中空玻化微珠15％、陶瓷微珠5％、稻壳粉10％，生产时把上述材料按重量百分比混合均匀即可，批量生产时把A、B、C、D四组分，重量百分比分别装袋密封即可。
使用方法：使用时按顺序先把A组分加到容器中，再把B组分加到A组分中搅拌均匀，再加C组分搅拌均匀，再加D组分搅拌均匀后即可使用，使用时最好现配现用，2小时之内用完。
使用时采用批刮的方式，批刮在建筑物表面，待第一遍表干后，再刮第二遍，且批刮越厚，保温、防火效果更好，每次批刮厚度控制在1.5CM之内。
Claims (2)
1.一种建筑用保温防火抗裂腻子，其特征在于：它是由A组分、B组分、C组分、D组分四组分组成，其中A组分为液料，其重量百分比为：氯化镁5-55％，水40-50％，改性剂2-5％；B组分为粉料，其重量百分比为：轻烧氧化镁80-90％，高铝水泥10-20％；C组分为液料，其重量百分比为：水30-40％，VAE乳液30-40％，水泥基改性乳液30-40％，偶联剂0.3-0.8％，羟丙基纤维素0.3-0.8％，防腐杀菌剂0.1-0.2％；D组分为粉料，其重量百分比为：硫铝酸盐水泥15-25％，粉煤灰20-30％，漂珠20-30％，中空玻化微珠10-18％，陶瓷微珠3-5％，稻壳粉或锯末粉8-13％，A组分、B组分、C组分、D组分四组分在配比中所占的重量百分比为：每种组分在配比中所占的重量百分比为：A组分25％-28％，B组份28％-32％，C组份10％-15％，D组份为30％-35％，使用时使用时的加料顺序为先把A组分加入到容器中，再倒入B组分搅拌均匀后，再加C组分搅拌均匀，最后加D组分搅拌均匀即可使用。
2.根据权利要求书1所述的一种建筑用保温防火抗裂腻子，其特征在于：A组分中选用的氯化镁纯度在90％以上，B组分中选用的氧化镁活性含量在90％以上，C组分中的VAE乳液选用的是不会与硫铝酸盐水泥和氯氧镁水泥发生不良反应的VAE乳液，D组分中选用的水泥为硫铝酸盐水泥。