CN112646243A - 一种医用抗菌手套的制备方法 - Google Patents
一种医用抗菌手套的制备方法 Download PDFInfo
- Publication number
- CN112646243A CN112646243A CN202011562843.2A CN202011562843A CN112646243A CN 112646243 A CN112646243 A CN 112646243A CN 202011562843 A CN202011562843 A CN 202011562843A CN 112646243 A CN112646243 A CN 112646243A
- Authority
- CN
- China
- Prior art keywords
- nano
- parts
- zinc oxide
- drying
- steps
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种医用抗菌手套的制备方法,包括以下步骤:氧化锌改性;制备抗菌剂:纳米氧化锌、纳米氧化铜、纳米二氧化硅、纳米二氧化钛、纳米碳酸钙、纳米三氧化二铝、肉豆蔻酸异丙酯、对甲氧基肉桂酸辛酯、海藻酸丙二酯、喹诺酮通过搅拌机搅拌;天然橡胶、羧基丁腈橡胶、炭黑、硬脂酸、硫磺、氧化锌、纳米氧化银、除味剂在200‑250℃温度下混合2小时;将步骤S2和步骤S3中的物料进行混合搅拌,得到橡胶乳;模具烘干后,先浸渍凝固剂,之后烘干模具;接着模具浸渍上述配制好的橡胶乳;再经过110℃、10‑15min的高温干燥;最后冷却,把手套从模具上脱下,即得到半成品;喷淋含有纳米银的抗菌溶液,然后烘干,即可得到成品。本发明,抗菌效果好。
Description
技术领域
本发明涉及抗菌手套技术领域,具体是一种医用抗菌手套的制备方法。
背景技术
随着生活节奏的加快、工作压力的加大及环境问题的日益严峻,各种传染病盛行,给人们的身体健康带来了严重威胁,切断传染病传播是解决这一问题的有效途径。目前各种传染病都是通过空气或接触方式传播的,而接触方式是疾病传染的主要渠道。为避免通过接触方式的病菌传播,在医疗、医药、卫生防护等方面都会使用一次性手套。医用手套是众多一次性手套中的一种,其在出厂前一般都会进行消毒处理,但是从手套出厂到医生使用往往还需要一定的时间,如何对手套进行有效的抗菌处理,使其抗菌时间延长,是该领域一直在不断探索的技术问题。
现有的医用手套主要是采用乳胶、硅胶、PVC塑料等材料制成,这些材料综合性能不佳,在穿戴时容易与手的表皮附着,摩擦力大,使用不方便,且多含有有毒有害的物质,容易引起皮肤过敏反应。另外由于其手套自身物质即为细菌的营养成份,所以容易引起细菌或微生物的滋生和繁衍,增加了医生和病人感染疾病的危险。为了解决这一问题,现有技术中一般是往手套基质中添加一定量的抗菌物质或成份,但这些物质本身与手套基质材料相溶性较差,容易溶出,且抗菌时效有限,或本身抗菌能力不强,不能有效抑制各种病原体。有些抗菌物质毒性较大,对人体有潜在危害。
发明内容
本发明的目的在于提供一种医用抗菌手套的制备方法,以解决现有技术中的问题。
为实现上述目的,本发明提供如下技术方案:一种医用抗菌手套的制备方法,包括以下步骤:
S1:氧化锌改性:将氧化锌与3-甲基丙烯酰氧基丙基甲基二甲氧基硅烷混合制备改性氧化锌;
S2:制备抗菌剂:纳米氧化锌、纳米氧化铜、纳米二氧化硅、纳米二氧化钛、纳米碳酸钙、纳米三氧化二铝、肉豆蔻酸异丙酯、对甲氧基肉桂酸辛酯、海藻酸丙二酯、喹诺酮通过搅拌机混合搅拌;得到混合物;
S3:天然橡胶、羧基丁腈橡胶、炭黑、硬脂酸、硫磺、氧化锌、纳米氧化银、除味剂在200-250℃温度下混合2小时;
S4:将步骤S2和步骤S3中的物料进行混合搅拌,得到橡胶乳;
S5:模具烘干后,先浸渍凝固剂,之后烘干模具;接着模具浸渍上述配制好的橡胶乳;再经过110℃、10-15min的高温干燥;最后冷却,把手套从模具上脱下,即得到半成品;
S6:喷淋含有纳米银的抗菌溶液,然后烘干,即可得到成品。
优选的,所述步骤S2中搅拌机的搅拌温度为110℃,搅拌机转速为550-650转/min。
优选的,所述步骤S3中各组分的重量份数为:天然橡胶60份、羧基丁腈橡胶25份、炭黑6份、硬脂酸2份、硫磺1.5份、氧化锌2份、纳米氧化银5份、除味剂3份。
优选的,所述步骤S5中凝固剂为重量百分比浓度为10-15%的氯化钙溶液。
优选的,所述步骤S6中烘干的温度设置为55℃,烘干的时间为1-2小时。
与现有技术相比,本发明的有益效果是:通过采用抗菌剂和纳米氧化银的双重作用,对金葡萄菌和大肠杆菌的抗菌率较高,可达99%以上;制备方法简单,原料价格低,生产成本较低,有利于广泛的推广。
附图说明
附图用来提供对本发明的进一步理解,并且构成说明书的一部分,与本发明的实施例一起用于解释本发明,并不构成对本发明的限制。在附图中:
图1为本发明的结构示意图。
具体实施方式
为使本发明实施方式的目的、技术方案和优点更加清楚,下面将结合本发明实施方式中的附图,对本发明实施方式中的技术方案进行清楚、完整地描述,显然,所描述的实施方式是本发明一部分实施方式,而不是全部的实施方式。基于本发明中的实施方式,本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施方式,都属于本发明保护的范围。因此,以下对在附图中提供的本发明的实施方式的详细描述并非旨在限制要求保护的本发明的范围,而是仅仅表示本发明的选定实施方式。基于本发明中的实施方式,本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施方式,都属于本发明保护的范围。
请参阅图1,本发明实施例中,一种医用抗菌手套的制备方法,包括以下步骤:
S1:氧化锌改性:将氧化锌与3-甲基丙烯酰氧基丙基甲基二甲氧基硅烷混合制备改性氧化锌;
S2:制备抗菌剂:纳米氧化锌、纳米氧化铜、纳米二氧化硅、纳米二氧化钛、纳米碳酸钙、纳米三氧化二铝、肉豆蔻酸异丙酯、对甲氧基肉桂酸辛酯、海藻酸丙二酯、喹诺酮通过搅拌机混合搅拌;得到混合物;
S3:天然橡胶、羧基丁腈橡胶、炭黑、硬脂酸、硫磺、氧化锌、纳米氧化银、除味剂在200-250℃温度下混合2小时;
S4:将步骤S2和步骤S3中的物料进行混合搅拌,得到橡胶乳;
S5:模具烘干后,先浸渍凝固剂,之后烘干模具;接着模具浸渍上述配制好的橡胶乳;再经过110℃、10-15min的高温干燥;最后冷却,把手套从模具上脱下,即得到半成品;
S6:喷淋含有纳米银的抗菌溶液,然后烘干,即可得到成品。
优选的,所述步骤S2中搅拌机的搅拌温度为110℃,搅拌机转速为550-650转/min。
优选的,所述步骤S3中各组分的重量份数为:天然橡胶60份、羧基丁腈橡胶25份、炭黑6份、硬脂酸2份、硫磺1.5份、氧化锌2份、纳米氧化银5份、除味剂3份。
优选的,所述步骤S5中凝固剂为重量百分比浓度为10-15%的氯化钙溶液。
优选的,所述步骤S6中烘干的温度设置为55℃,烘干的时间为1-2小时。
本发明的工作原理是:氧化锌改性:将氧化锌与3-甲基丙烯酰氧基丙基甲基二甲氧基硅烷混合制备改性氧化锌;制备抗菌剂:纳米氧化锌、纳米氧化铜、纳米二氧化硅、纳米二氧化钛、纳米碳酸钙、纳米三氧化二铝、肉豆蔻酸异丙酯、对甲氧基肉桂酸辛酯、海藻酸丙二酯、喹诺酮通过搅拌机混合搅拌;得到混合物;天然橡胶、羧基丁腈橡胶、炭黑、硬脂酸、硫磺、氧化锌、纳米氧化银、除味剂在200-250℃温度下混合2小时;将步骤S2和步骤S3中的物料进行混合搅拌,得到橡胶乳;模具烘干后,先浸渍凝固剂,之后烘干模具;接着模具浸渍上述配制好的橡胶乳;再经过110℃、10-15min的高温干燥;最后冷却,把手套从模具上脱下,即得到半成品;喷淋含有纳米银的抗菌溶液,然后烘干,即可得到成品;通过采用抗菌剂和纳米氧化银的双重作用,对金葡萄菌和大肠杆菌的抗菌率较高,可达99%以上;制备方法简单,原料价格低,生产成本较低,有利于广泛的推广。
最后应说明的是:以上所述仅为本发明的优选实施例而已,并不用于限制本发明,尽管参照前述实施例对本发明进行了详细的说明,对于本领域的技术人员来说,其依然可以对前述各实施例所记载的技术方案进行修改,或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (5)
1.一种医用抗菌手套的制备方法,其特征在于:包括以下步骤:
S1:氧化锌改性:将氧化锌与3-甲基丙烯酰氧基丙基甲基二甲氧基硅烷混合制备改性氧化锌;
S2:制备抗菌剂:纳米氧化锌、纳米氧化铜、纳米二氧化硅、纳米二氧化钛、纳米碳酸钙、纳米三氧化二铝、肉豆蔻酸异丙酯、对甲氧基肉桂酸辛酯、海藻酸丙二酯、喹诺酮通过搅拌机混合搅拌;得到混合物;
S3:天然橡胶、羧基丁腈橡胶、炭黑、硬脂酸、硫磺、氧化锌、纳米氧化银、除味剂在200-250℃温度下混合2小时;
S4:将步骤S2和步骤S3中的物料进行混合搅拌,得到橡胶乳;
S5:模具烘干后,先浸渍凝固剂,之后烘干模具;接着模具浸渍上述配制好的橡胶乳;再经过110℃、10-15min的高温干燥;最后冷却,把手套从模具上脱下,即得到半成品;
S6:喷淋含有纳米银的抗菌溶液,然后烘干,即可得到成品。
2.根据权利要求1所述的一种医用抗菌手套的制备方法,其特征在于:所述步骤S2中搅拌机的搅拌温度为110℃,搅拌机转速为550-650转/min。
3.根据权利要求1所述的一种医用抗菌手套的制备方法,其特征在于:所述步骤S3中各组分的重量份数为:天然橡胶60份、羧基丁腈橡胶25份、炭黑6份、硬脂酸2份、硫磺1.5份、氧化锌2份、纳米氧化银5份、除味剂3份。
4.根据权利要求1所述的一种医用抗菌手套的制备方法,其特征在于:所述步骤S5中凝固剂为重量百分比浓度为10-15%的氯化钙溶液。
5.根据权利要求1所述的一种医用抗菌手套的制备方法,其特征在于:所述步骤S6中烘干的温度设置为55℃,烘干的时间为1-2小时。