CN112588015B - 制备光催化空气净化棒状二氧化硅颗粒复合纤维毡的方法 - Google Patents
制备光催化空气净化棒状二氧化硅颗粒复合纤维毡的方法 Download PDFInfo
- Publication number
- CN112588015B CN112588015B CN202011336227.5A CN202011336227A CN112588015B CN 112588015 B CN112588015 B CN 112588015B CN 202011336227 A CN202011336227 A CN 202011336227A CN 112588015 B CN112588015 B CN 112588015B
- Authority
- CN
- China
- Prior art keywords
- photocatalytic
- silicon dioxide
- fibrofelt
- fiber
- precursor solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了制备光催化空气净化棒状二氧化硅颗粒复合纤维毡的方法,包括如下步骤:配置氧化钛前驱体溶液;将光催化纳米颗粒用去离子水分散,超声震荡得到分散液,将纤维毡浸渍于分散液中超声,然后烘干;将纤维毡放入氧化钛前驱体溶液中,随后放入微波快速反应合成器中进行退火,即得纤维表面被均匀的棒状光催化复合纳米颗粒包覆的复合纤维毡。本发明将氧化钛颗粒以前驱体混合液的形式分散附着在纤维表面,复合纤维毡特殊三维网状结构均匀负载紧密包覆光催化颗粒,增大了原有单一超细纤维的比表面积,增加了催化剂与细菌微生物的接触面积和参与氧化还原反应的活性位点数量,更高效捕获空气中的微生物颗粒实现快速光催化响应,实现光催化抗菌灭活。
Description
技术领域
本发明属于空气过滤纤维毡技术领域,具体涉及制备棒状二氧化硅光催化颗粒复合纤维毡的方法。
背景技术
在商场、学校、写字楼、车厢、飞机舱、船舱等空气相对不流通的室内公共空间,大多采用空气内循环模式,不具备颗粒物拦截、TVOC 催化、灭菌等功效,细菌、病毒等容易随空气中的悬浮颗粒物、气溶胶进行传播,从而引发群体性传染事件。纤维过滤毡可以利用其纤维搭建的三维网络结构来通过物理拦截和静电吸附捕获细小颗粒污染物,但纤维过滤毡对空气中存在病毒微生物无能为力,并且当条件合适时一些微生物可以在纤维过滤毡表面生存并繁殖。二氧化硅、石墨烯和还原氧化石墨烯等光触媒纳米颗粒利用光催化机理具有良好的空气杀菌能力,并且在实验室中被大量的研究其空气净化作用,但截止目前缺少使得光触媒可以在可见光条件下和空气净化滤材介质有效融合短时间内起到杀菌净化空气的作用。因此,开发出高性能光触煤和纤维毡复合空气净化滤材是一个亟待解决的问题。
发明内容
综上所述,本发明的目的在于提供制备光催化空气净化棒状二氧化硅颗粒复合纤维毡的方法,以达到优异的空气过滤和可见光条件下的快速光催化抗菌响应。
为达到上述目的,本发明提供如下技术方案:制备光催化空气净化棒状二氧化硅颗粒复合纤维毡的方法,包括如下步骤:
步骤1,配置二氧化硅前驱体溶液;
步骤2,将5mg/mL的光催化纳米颗粒用去离子水分散为50mL,超声震荡30min,得到分散液,将纤维毡浸渍于分散液中超声5min,然后烘干,烘干条件为130℃保持18min,浸渍烘干重复三次;
步骤3,将步骤2中的纤维毡放入步骤1中的二氧化硅前驱体溶液中,随后放入微波快速反应合成器中进行退火,即得棒状二氧化硅光催化颗粒复合纤维毡。
进一步的,步骤1配置二氧化硅前驱体溶液的方法为:将二氧化硅硅源溶解在去离子水里面,通过加入氨水控制沉淀析出,将沉淀抽滤并烘干,沉淀为硅氨络合物,再取沉淀抽滤的硅氨络合物加氨水和水配置成摩尔浓度为1 -2.5 mol/L的二氧化硅前驱体溶液。
进一步的,步骤2中二氧化硅硅源为三氯氢硅、四氯化硅、二氯二氢硅和硅烷其中的一种或几种。
进一步的,步骤2中光催化纳米颗粒为石墨烯、氧化石墨烯、还原氧化石墨烯或石墨烯量子点中的一种或几种,颗粒直径为20-200nm。
进一步的,步骤2中超细玻璃纤维为玻璃纤维或玄武岩纤维,平均纤维直径为0.5-4μm。
进一步的,步骤3的二氧化硅前驱体溶液中加入偶联剂,偶联剂选用KH560、三甲基氯硅烷、六甲基二硅烷中的一种或几种。
进一步的,步骤3的微波快速反应加热温度为155-225℃,反应时间为5-8min。
进一步的,步骤3中的退火工艺为H2氛围285℃-400℃退火1.5-3h。
本发明的有益效果在于:
1、本发明将二氧化硅纳米颗粒以前驱体混合液的形式分散附着在纤维表面,同时将光催化纳米颗粒和纤维一同置于二氧化硅前驱体溶液微波超声分散,在不破坏复合纤维毡特殊三维网状结构的前提下,保留其优异的空气过滤性能的同时去均匀负载和紧密包覆的光催化纳米颗粒。
2、二氧化硅结构中的硅原子位于正四面体的中心,四个氧原子位于正四面体的四个顶角上,许多个这样的四面体又通过顶角的氧原子相连,每个氧原子为两个四面体共有,使得二氧化硅成为一种坚硬、脆性、难溶的无色透明的固体。同时,二氧化硅是酸性氧化物,不跟一般酸反应。这些都可以有效提高制得复合纤维毡的抗菌杀菌效果和抗老化性能。
3、通过负载光催化纳米颗粒后的纤维毡,光催化剂二氧化硅在石墨烯基体上的均匀分散并附着在复合纤维毡表面,增加了催化剂与细菌微生物的接触面积,一定程度上增加了参与氧化还原反应的活性位点数量,以便更高效率捕获空气中的微生物颗粒实现快速光催化响应。
4、通过石墨烯量子点的引入,石墨烯量子点作为一种零维石墨烯材料,相较于氧化石墨烯和还原氧化石墨烯有更小的粒径,其晶格结构与石墨烯无异,但比表面积比石墨烯更大,活性也更高。除此以外,石墨烯量子点还具有良好的水溶性、无毒性及稳定的光致发光特性等,且属于碳材料,一定条件下可大量获得。同时石墨烯量子点外观极小因此内部电子在各个方向上的运动都会受到限制,从而表现出量子限域效应和边界效应,使其表现出更出色的电子传输能力,从而延长载流子寿命,所以能有效的较低二氧化硅的光生载流子对的复合,使得于复合纤维毡能在可见光的条件下在短时间内对大肠杆菌和金黄色葡萄球菌实现光催化抗菌灭活。
附图说明
图1为对比实施例制得的超细玻璃纤维复合毡放大20000显微组织图;
图2为实施例2制得的超细玻璃纤维复合毡放大20000倍显微组织图。
具体实施方式
以下实施例制备光催化空气净化棒状二氧化硅颗粒复合纤维毡的方法,但本实施例不能用于限制本发明,凡是采用本发明的相似方法及其相似变化,均应列入本发明的保护范围。
纤维准备:对比实施例和实施例1-2的超细玻璃纤维选取的原料为按质量比称取63份石英砂、6.5份纯碱、3份钾长石、5钠长石、7份方解石、5硼砂、4白云石、1.5份碳酸钡、1份氧化锌和4份平板废玻璃,然后将选取制备超细玻璃纤维的原料混合均匀后投入到1460℃的窑炉中高温熔融成透明均匀的玻璃液,其中熔融均匀的玻璃液温度为1160℃,然后将透明均匀的玻璃液通过2条料道分别流过温度为1000℃、材质为PtRh10的铂铑合金漏板1和温度为990℃、材质为GH4169钴镍合金漏板2分别形成一次玻璃纤维丝,合金漏板1形成的一次玻璃纤维丝再经过温度为1020℃火焰喷吹炉头1形成叩解度为39±1的超细玻璃纤维;合金漏板2形成的一次玻璃纤维丝再经过温度为1005℃火焰喷吹炉头2形成叩解度为32±1的超细玻璃纤维。
实施例3的玄武岩纤维选取质量百分比组分为SiO2:53.5%,Al2O3:15%,Fe2O3:4%,FeO:7%,CaO:8%,Na2O:5.5%,K2O:2%,MgO:3.5%和TiO2:1.5%的纯天然玄武岩作为原料,经在1475℃的窑炉中高温熔融成均匀的熔浆,然后通过料道1250℃的玄武岩熔浆流入材质为PtRh10的400孔铂铑合金漏板,最后经过快速拉丝形成玄武岩纤维。
对比实施例:参见公开号CN111905452A实施例2制备出的一种光催化空气净化用超细玻璃纤维棉毡可以达到在可见光的条件下1h降解85%的10mg/L的罗丹明B溶液,定量80g/m2,过滤阻力125Pa,过滤效率80%,透气量190 L/m2·min。
实施例1-3按照如下步骤实施:
制备光催化空气净化棒状二氧化硅颗粒复合纤维毡的方法,包括如下步骤:
步骤1,配置二氧化硅前驱体溶液:将二氯二氢硅和硅烷的混合物溶解在去离子水里面,通过加入氨水控制沉淀析出,将沉淀抽滤并烘干,沉淀为硅氨络合物,再取沉淀抽滤的硅氨络合物加氨水和水配置成最佳摩尔浓度为2mol/L的二氧化硅前驱体溶液;
步骤2,将5mg/mL的光催化纳米颗粒用去离子水分散为50mL,超声震荡30min,得到分散液,将超细纤维放入分散液中超声5min,然后烘干,烘干条件为130℃保持18min,浸渍烘干重复三次;
步骤3,将步骤2中的超细纤维放入步骤1中二氧化硅前驱体溶液中,随后放入微波快速反应合成器进行退火,即得纳米棒状光催化颗粒复合纤维毡。
实施例1
步骤2中二氧化硅硅源为二氯二氢硅和硅烷。步骤2中光催化纳米颗粒为纳米氧化石墨烯,颗粒直径为55nm。步骤2中超细纤维为平均直径为2.5μm的超细玻璃纤维。步骤3的氧化钛前驱体溶液中加入粘接剂。步骤3的微波快速反应加热温度为175℃,反应时间为7min。步骤3中的退火工艺为H2氛围280℃退火2.5 h。最终制备出的光催化空气净化棒状氧化钛颗粒复合纤维毡的光催化降解性能达到在可见光的条件下45min降解94%的10mg/L的罗丹明B溶液;空气过滤性能达到定量91 g/m2,过滤阻力104Pa,过滤效率94%和透气量243L/m2·min;力学性能达到沿纤维长度方向为23N/25mm,沿纤维宽度方向为13N/25mm;结构特点为纤维表面被的棒状包覆,比表面积由原有单一超细玻璃纤维的2.3641 m2/g增大到均匀包覆棒状光催化复合纳米颗粒的7.9365 m2/g。
实施例2
步骤2中,氧化硅硅源为三氯氢硅和硅烷。步骤2中光催化纳米颗粒为石墨烯量子点,颗粒直径为30nm。步骤2中超细纤维为平均直径为2μm的超细玻璃纤维。步骤3的微波快速反应加热温度为185℃,反应时间为6min。步骤3中的退火工艺为H2氛围350℃退火2 h。最终制备出的光催化空气净化纳米棒状颗粒复合纤维毡的光催化降解性能达到在可见光的条件下40min降解98%的10mg/L的罗丹明B溶液;空气过滤性能达到定量95g/m2,过滤阻力97Pa,过滤效率98%和透气量244L/m2·min;力学性能达到沿纤维长度方向为24N/25mm,沿纤维宽度方向为14N/25mm;比表面积由原有单一超细玻璃纤维的2.3641 m2/g增大到均匀包覆棒状光催化复合纳米颗粒的9.8254 m2/g。
实施例3
步骤2中,二氧化硅硅源为为二氯二氢硅和和硅烷。步骤2中光催化纳米颗粒为还原氧化石墨烯,颗粒直径为30nm。步骤2中超细纤维为平均直径为2.5μm的超细玄武岩纤维。步骤3的微波快速反应加热温度为185℃,反应时间为6min。步骤3中的退火工艺为H2氛围350℃退火2h。最终制备出的光催化空气净化纳米棒状颗粒复合纤维毡的光催化降解性能达到在可见光的条件下40min降解96%的10mg/L的罗丹明B溶液;空气过滤性能达到定量91g/m2,过滤阻力100Pa,过滤效率96%和透气量232L/m2·min;力学性能达到沿纤维长度方向为22N/25mm,沿纤维宽度方向为13.5N/25mm;结构特点为纤维表面被均匀的棒状光催化复合纳米颗粒包覆,比表面积由原有单一超细玻璃纤维的2.3641 m2/g增大到均匀包覆棒状光催化复合纳米颗粒的8.9942 m2/g。
最后说明的是,以上优选实施例仅用以说明本发明的技术方案而非限制,尽管通过上述优选实施例已经对本发明进行了详细的描述,但本领域技术人员应当理解,可以在形式上和细节上对其作出各种各样的改变,而不偏离本发明权利要求书所限。
Claims (5)
1.制备光催化空气净化棒状二氧化硅颗粒复合纤维毡的方法,其特征在于,包括如下步骤:
步骤1,配置二氧化硅前驱体溶液;
步骤2,将5mg/mL的光催化纳米颗粒用去离子水分散为50mL,超声震荡30min,得到分散液,将纤维毡浸渍于分散液中超声5min,然后烘干,烘干条件为130℃保持18min,浸渍烘干重复三次,所述光催化纳米颗粒为石墨烯量子点,颗粒直径为20-200nm;
步骤3,将步骤2中的纤维毡放入步骤1中的二氧化硅前驱体溶液中,随后放入微波快速反应合成器中进行退火,微波快速反应为:加热温度为155-225℃,反应时间为5-8min,退火工艺为H2氛围285℃-400℃退火1.5-3h,即得棒状二氧化硅光催化颗粒复合纤维毡。
2.根据权利要求1所述方法,其特征在于,步骤1配置二氧化硅前驱体溶液的方法为:将二氧化硅硅源溶解在去离子水里面,通过加入氨水控制沉淀析出,将沉淀抽滤并烘干,沉淀为硅氨络合物,再取沉淀抽滤的硅氨络合物加氨水和水配置成摩尔浓度为1-2.5 mol/L的二氧化硅前驱体溶液。
3.根据权利要求2所述方法,其特征在于,步骤2中二氧化硅硅源为三氯氢硅、四氯化硅、二氯二氢硅和硅烷其中的一种或几种。
4.根据权利要求1所述方法,其特征在于,步骤2中超细玻璃纤维为玻璃纤维或玄武岩纤维,平均纤维直径为0.5-4μm。
5.根据权利要求1所述方法,其特征在于,步骤3的二氧化硅前驱体溶液中加入偶联剂,偶联剂选用KH560、三甲基氯硅烷、六甲基二硅烷中的一种或几种。