CN112356417A - 一种五层共挤吹塑法聚乙烯土工膜生产工艺 - Google Patents

一种五层共挤吹塑法聚乙烯土工膜生产工艺 Download PDF

Info

Publication number
CN112356417A
CN112356417A CN202011404177.XA CN202011404177A CN112356417A CN 112356417 A CN112356417 A CN 112356417A CN 202011404177 A CN202011404177 A CN 202011404177A CN 112356417 A CN112356417 A CN 112356417A
Authority
CN
China
Prior art keywords
geomembrane
layer
blow molding
production process
traction
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN202011404177.XA
Other languages
English (en)
Inventor
刘好武
崔占明
杨广庆
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hongxiang New Geo Material Co ltd
Original Assignee
Hongxiang New Geo Material Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hongxiang New Geo Material Co ltd filed Critical Hongxiang New Geo Material Co ltd
Priority to CN202011404177.XA priority Critical patent/CN112356417A/zh
Publication of CN112356417A publication Critical patent/CN112356417A/zh
Withdrawn legal-status Critical Current

Abstract

本发明属于土工膜生产技术领域，特别涉及一种五层共挤吹塑法聚乙烯土工膜生产工艺，包括以下步骤：步骤一：配方原料准备，步骤二：A、B、C、D、E五台螺杆挤出机及机头分别预热，步骤三：预热完成后，分别根据加工需要向五台螺杆挤出机加入相应的称重配比原料，开机生产，加热熔融塑化，步骤四：环形模口挤出，步骤五：吹胀、冷却定型，步骤六：牵引，步骤七：在线测厚，步骤八：剖开，展膜，步骤九：二次牵引，步骤十：卷取，成卷土工膜，步骤十一：检验，包装，入库，本发明采用五层共挤土工膜相当于隐含的五层防渗膜结构，大大提高了土工膜自身的完整性，可称之为“零缺陷”土工膜，性能大大提高。

Description

一种五层共挤吹塑法聚乙烯土工膜生产工艺
技术领域
本发明属于土工膜生产技术领域，特别涉及一种五层共挤吹塑法聚乙烯土工膜生产工艺。
背景技术
目前市面上土工膜生产工艺多为两层共挤法，三层共挤法，上述方法生产的土工膜，特别是粗面土工膜，还存在一定的缺陷，性能也有待提高。
发明内容
本发明提供一种五层共挤吹塑法聚乙烯土工膜生产工艺，可以解决背景技术中所指出的问题。
一种五层共挤吹塑法聚乙烯土工膜生产工艺，包括以下步骤：
步骤一：配方原料准备，
步骤二：A、B、C、D、E五台螺杆挤出机及机头分别预热，
步骤三：预热完成后，分别根据加工需要向五台螺杆挤出机加入相应的称重配比原料，开机生产，加热熔融塑化，
步骤四：环形模口挤出，
步骤五：吹胀、冷却定型，
步骤六：牵引，
步骤七：在线测厚，
步骤八：剖开，展膜，
步骤九：二次牵引，
步骤十：卷取，成卷土工膜，
步骤十一：检验，包装，入库。
优选的，当生产单糙面或双糙面土工膜时，中间B、C、D三层作为防渗主体，A或A、E采用氮气发泡工艺产生具有一定毛糙高度（厚度）的糙面防滑层。
优选的，所述毛糙高度0.25～0.4mm。
本发明提供一种五层共挤吹塑法聚乙烯土工膜生产工艺，五层共挤土工膜相当于隐含的五层防渗膜结构，大大提高了土工膜自身的完整性，可称之为“零缺陷”土工膜，性能大大提高。
具体实施方式
下面对本发明的一个具体实施方式进行详细描述，但应当理解本发明的保护范围并不受具体实施方式的限制。
本发明实施例提供的一种五层共挤吹塑法聚乙烯土工膜生产工艺，包括以下步骤：
步骤一：配方原料准备，
步骤二：A、B、C、D、E五台螺杆挤出机及机头分别预热，
步骤三：预热完成后，分别根据加工需要向五台螺杆挤出机加入相应的称重配比原料，开机生产，加热熔融塑化，
步骤四：环形模口挤出，
步骤五：吹胀、冷却定型，
步骤六：牵引，
步骤七：在线测厚，
步骤八：剖开，展膜，
步骤九：二次牵引，
步骤十：卷取，成卷土工膜，
步骤十一：检验，包装，入库。
当生产单糙面或双糙面土工膜时，中间B、C、D三层作为防渗主体，A或A、E采用氮气发泡工艺产生具有一定毛糙高度（厚度）的糙面防滑层，采用氮气加糙技术，毛糙高度0.25～0.4mm，毛糙高度0.25～0.4mm，糙面高度、稳定性好，界面摩擦系数大，用于坝坡防渗结构稳定。
本生产工艺可生产白色黑色等单一颜色土工膜、黑色/绿色等双色多色土工膜，可生产LDPE/LLDPE/MDPE/HDPE/EVA等多种原料的不同材质层间和混合比例的功能性土工膜，可生产两个纵边预留150mm左右宽度光膜焊接边的糙面土工膜。
以上公开的仅为本发明的几个具体实施例，但是，本发明实施例并非局限于此，任何本领域的技术人员能思之的变化都应落入本发明的保护范围。

Claims (3)

1.一种五层共挤吹塑法聚乙烯土工膜生产工艺，其特征在于：包括以下步骤：
步骤一：配方原料准备，
步骤二：A、B、C、D、E五台螺杆挤出机及机头分别预热，
步骤三：预热完成后，分别根据加工需要向五台螺杆挤出机加入相应的称重配比原料，开机生产，加热熔融塑化，
步骤四：环形模口挤出，
步骤五：吹胀、冷却定型，
步骤六：牵引，
步骤七：在线测厚，
步骤八：剖开，展膜，
步骤九：二次牵引，
步骤十：卷取，成卷土工膜，
步骤十一：检验，包装，入库。
2.如权利要求1所述，一种五层共挤吹塑法聚乙烯土工膜生产工艺，其特征在于：当生产单糙面或双糙面土工膜时，中间B、C、D三层作为防渗主体，A或A、E采用氮气发泡工艺产生具有一定毛糙高度（厚度）的糙面防滑层。
3.如权利要求2所述，一种五层共挤吹塑法聚乙烯土工膜生产工艺，其特征在于：所述毛糙高度0.25～0.4mm。
CN202011404177.XA 2020-12-05 2020-12-05 一种五层共挤吹塑法聚乙烯土工膜生产工艺 Withdrawn CN112356417A (zh)