CN112194988B - Preparation method of outdoor advertisement vehicle body sticker - Google Patents
Preparation method of outdoor advertisement vehicle body sticker Download PDFInfo
- Publication number
- CN112194988B CN112194988B CN201910609031.XA CN201910609031A CN112194988B CN 112194988 B CN112194988 B CN 112194988B CN 201910609031 A CN201910609031 A CN 201910609031A CN 112194988 B CN112194988 B CN 112194988B
- Authority
- CN
- China
- Prior art keywords
- parts
- layer
- vehicle body
- body sticker
- substrate layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a preparation method of an outdoor advertisement vehicle body sticker, which comprises a substrate layer, a back adhesive layer and a release layer, wherein one side of the substrate layer is coated on the back adhesive layer, the side, opposite to the substrate layer, of the back adhesive layer is provided with the release layer, and the glue solution is prepared through the following steps: uniformly mixing 20-35 parts of methyl methacrylate, 10-30 parts of styrene, 10-20 parts of butyl acrylate, 0.5-1.5 parts of sodium carbonate, 1-5 parts of hexachlorocyclotriphosphazene and 50-80 parts of deionized water, heating to 75-90 ℃, dropwise adding 0.5-1.5 parts of 4,4' -azobis (4-cyanopentanoic acid) and 1-5 parts of acrylic acid into the mixed system, and reacting for 3-5 hours; s2, cooling to room temperature, adding 1-5 parts of aluminum isopropoxide, 1-3 parts of a curing agent, 0.2-1 part of triglycerol monostearate and 0.1-1 part of hydroquinone, and uniformly mixing to obtain a glue solution; and S3, uniformly coating the glue solution on the substrate layer, and drying to obtain the back glue layer. The outdoor advertising vehicle body sticker is easy to peel off and free of residual glue, and meanwhile, the peeling force changes little after the outdoor advertising vehicle body sticker is attached for a long time.
Description
Technical Field
The invention belongs to the technical field of adhesive tapes, and particularly relates to a preparation method of an outdoor advertisement vehicle body sticker.
Background
In recent years, the development of digital spray-painting materials using PVC as a base material is very rapid, and the application is quite wide. Because the PVC has poor bonding force with the adhesive layer and low peel strength, the processing performance and the service performance of the product are influenced to a certain extent. Suitable adhesives are key factors in increasing the peel strength of such products.
The existing partial advertisement stickers, such as car stickers and water-based high-brightness PVC, are all provided with a PVC film, an adhesive layer and release paper. Although the outdoor vehicle sticker can also be used as an indoor ink-jet material, the ink-jet ink used by the vehicle sticker product is solvent-based, so that the vehicle sticker has pollution to the operation and use environment and is not suitable for indoor use. In addition, most of the existing car stickers adopt oily pressure-sensitive adhesives, although the weather resistance is excellent, the car stickers do not age and have adhesive residue, the car stickers are easy to pollute the environment in the production process, and the car stickers do not meet the current national environmental protection requirements. In order to meet the requirement of environmental protection, the existing advertisement vehicle sticker widely adopts water-based pressure-sensitive adhesive, however, the water-based pressure-sensitive adhesive is easy to remain adhesive when the advertisement is removed, and great inconvenience is caused for use. Therefore, how to develop a car body sticker without adhesive residue becomes a research direction for those skilled in the art.
Disclosure of Invention
The invention aims to provide a preparation method of an outdoor advertisement vehicle body sticker, the outdoor advertisement vehicle body sticker prepared by the method is easy to peel off, has no adhesive residue, is suitable for outdoor long-time use, does not need to consider the adhesive residue phenomenon generated when the advertisement sticker is replaced, and greatly reduces the probability of damage to the advertisement sticker and a vehicle body.
In order to achieve the purpose, the invention adopts the technical scheme that: the utility model provides a preparation method that outdoor advertisement automobile body pasted, includes substrate layer, gum layer and leaves the type layer, coating in the gum layer on the one side of substrate layer, the one side that the gum layer carried on the back the substrate layer mutually is equipped with leaves the type layer, the gum layer is dried by the coating of glue solution and is obtained, and this glue solution is made through following step:
s1, uniformly mixing 20-35 parts of methyl methacrylate, 10-30 parts of styrene, 10-20 parts of butyl acrylate, 0.5-1.5 parts of sodium carbonate, 1-5 parts of hexachlorocyclotriphosphazene and 50-80 parts of deionized water, heating to 75-90 ℃, dropwise adding 0.5-1.5 parts of 4,4' -azobis (4-cyanopentanoic acid) and 1-5 parts of acrylic acid into the mixed system, and reacting for 3-5 hours;
s2, cooling to room temperature, adding 1-5 parts of aluminum isopropoxide, 1-3 parts of a curing agent, 0.2-1 part of triglycerol monostearate and 0.1-1 part of hydroquinone, and uniformly mixing to obtain a glue solution;
and S3, uniformly coating the glue solution on the substrate layer, and drying to obtain the back glue layer.
The technical scheme of further improvement in the technical scheme is as follows:
1. in the scheme, the adding ratio of the methyl methacrylate to the styrene is 2: 1-1: 1.
2. In the scheme, the curing agent is selected from one of curing agent S01-5, curing agent MH2844 and curing agent T-31.
3. In the above scheme, the base material layer is a PVC layer.
4. In the scheme, the thickness of the base material layer is 70-120 μm.
5. In the scheme, the thickness of the gum layer is 15-30 μm.
Due to the application of the technical scheme, compared with the prior art, the invention has the following advantages:
1. according to the preparation method of the outdoor advertisement vehicle body sticker, the sodium carbonate and hexachlorocyclotriphosphazene are added into methyl methacrylate, styrene, butyl acrylate, acrylic acid and 4,4' -azobis (4-cyanovaleric acid), so that the advertisement vehicle body sticker is easy to peel off, has no adhesive residue, is suitable for outdoor long-time use, does not need to consider the adhesive residue phenomenon generated when the advertisement sticker is replaced, and greatly reduces the probability of damage to the advertisement sticker and the vehicle body.
2. According to the preparation method of the outdoor advertising vehicle body sticker, the triglycerol monostearate is further added, so that the peeling force of the vehicle body sticker quickly reaches a stable state and cannot increase along with the increase of time, the phenomenon of difficult peeling cannot occur when the outdoor advertising vehicle body sticker is attached to a vehicle body for a long time, and the subsequent replacement is facilitated.
Drawings
FIG. 1 is a schematic view of the outdoor advertisement vehicle body sticker structure.
In the above drawings: 1. a substrate layer; 2. a back glue layer; 3. and a release layer.
Detailed Description
In the description of this patent, it is noted that the terms "center", "upper", "lower", "left", "right", "vertical", "horizontal", "inner", "outer", etc., indicate orientations or positional relationships based on the orientations or positional relationships shown in the drawings, and are only for convenience in describing the present invention and simplifying the description, but do not indicate or imply that the device or element being referred to must have a particular orientation, be constructed and operated in a particular orientation, and thus should not be construed as limiting the present invention; the terms "first," "second," and "third" are used for descriptive purposes only and are not to be construed as indicating or implying relative importance; furthermore, unless expressly stated or limited otherwise, the terms "mounted," "connected," and "connected" are to be construed broadly, as they may be fixedly connected, detachably connected, or integrally connected, for example; can be mechanically or electrically connected; they may be connected directly or indirectly through intervening media, or they may be interconnected between two elements. The meaning of the above terms in this patent may be specifically understood by those of ordinary skill in the art.
The invention is further described below with reference to the following examples:
examples 1 to 4: the utility model provides a preparation method that outdoor advertisement automobile body pasted, includes substrate layer 1, gum layer 2 and release layer 3, coat in gum layer 2 on the one side of substrate layer 1, the one side that the backing layer 2 is carried on the back in the body layer 1 is equipped with release layer 3, the gum layer is dried by the coating of glue solution and is obtained, and this glue solution is made through following step:
s1, uniformly mixing 20-35 parts of methyl methacrylate, 10-30 parts of styrene, 10-20 parts of butyl acrylate, 0.5-1.5 parts of sodium carbonate, 1-5 parts of hexachlorocyclotriphosphazene and 50-80 parts of deionized water, heating to 75-90 ℃, dropwise adding 0.5-1.5 parts of 4,4' -azobis (4-cyanopentanoic acid) and 1-5 parts of acrylic acid into the mixed system, and reacting for 3-5 hours;
s2, cooling to room temperature, adding 1-5 parts of aluminum isopropoxide, 1-3 parts of a curing agent, 0.2-1 part of triglycerol monostearate and 0.1-1 part of hydroquinone, and uniformly mixing to obtain a glue solution;
and S3, uniformly coating the glue solution on the substrate layer, and drying to obtain the back glue layer.
The specific parts by weight of the above components in each example are shown in table 1:
TABLE 1
Components | Example 1 | Example 2 | Example 3 | Example 4 |
Methacrylic acid methyl ester | 20 portions of | 28 portions of | 30 portions of | 35 portions of |
Styrene (meth) acrylic acid ester | 10 portions of | 20 portions of | 15 portions of | 30 portions of |
Acrylic acid butyl ester | 15 portions of | 10 portions of | 20 portions of | 13 portions of |
| 2 portions of | 1 part of | 4 portions of | 5 portions of |
Aluminium isopropoxide | 1 part of | 3 portions of | 5 portions of | 2 portions of |
Sodium carbonate | 0.5 portion | 1.5 parts of | 1 part of | 0.8 portion of |
Phosphonitrilic chloride trimer | 1 part of | 2.5 parts of | 2 portions of | 5 portions of |
4,4' -azobis (4-cyanovaleric acid) | 0.5 portion | 1.2 parts of | 1.5 parts of | 0.8 portion of |
| 3 portions of | 1.5 parts of | 1 part of | 2 portions of |
Deionized water | 60 portions of | 50 portions of | 75 portions of | 80 portions |
Triglycerol monostearate | 0.2 part | 0.5 portion | 0.8 portion of | 1 part of |
Hydroquinone | 0.5 portion | 1 part of | 0.8 portion of | 0.1 part |
In example 1, the ratio of methyl methacrylate to styrene was 2:1, the curing agent was selected from the group consisting of the curing agents S01-5, the thickness of the base layer 1 was 75 μm, and the thickness of the backing layer 2 was 20 μm.
In example 2, the ratio of methyl methacrylate to styrene was 1.4:1, the curing agent was MH2844, the thickness of the base layer 1 was 100 μm, and the thickness of the backing layer 2 was 25 μm.
In example 3, the ratio of methyl methacrylate to styrene was 2:1, the curing agent was selected from the group consisting of curing agents T-31, the thickness of the base layer 1 was 95 μm, and the thickness of the backing layer 2 was 20 μm.
In example 4, the ratio of methyl methacrylate to styrene was 1.17:1, the curing agent was selected from the group consisting of the curing agents S01-5, the thickness of the base layer 1 was 85 μm, and the thickness of the backing layer 2 was 15 μm.
Comparative examples 1 to 2: the utility model provides an outdoor advertisement automobile body subsides, includes substrate layer 1, gum layer 2 and leaves type layer 3, coating in gum layer 2 in the one side of substrate layer 1, gum layer 2 is equipped with from type layer 3 in the one side of substrate layer 1 mutually in the back of the body, the gum layer is dried by the glue solution coating and is obtained, and this glue solution comprises following parts by weight component, as shown in Table 2:
TABLE 2
Components | Comparative example 1 | Comparative example 2 |
Methacrylic acid methyl ester | 25 portions of | 30 portions of |
Styrene (meth) acrylic acid ester | 22 portions of | 15 portions of |
Acrylic acid butyl ester | 10 portions of | 20 portions of |
| 3 portions of | 4 portions of |
| 3 portions of | 2.5 parts of |
Sodium carbonate | - | 1 part of |
Phosphonitrilic chloride trimer | - | 2.5 parts of |
4,4' -azobis (4-cyanovaleric acid) | 1.2 parts of | 1.5 parts of |
Curing agent | 1.8 parts of | 2.1 parts of |
Deionized water | 55 portions of | 60 portions of |
Triglycerol monostearate | 0.5Portions are | - |
Hydroquinone | 1 part of | 0.8 portion of |
Comparative example the procedure was as in example.
The performance of the outdoor advertisement vehicle body sticker prepared in the above examples 1 to 4 and comparative examples 1 to 2 is shown in table 3:
TABLE 3
The test method comprises the following steps:
1. 180-degree peeling force of test sample of peeling force testing machine
(1) A roll-shaped or sheet-shaped sample is taken, and the product is cut into 3-5 strips with the size of 25mm multiplied by 300 mm.
(2) Mirror steel plate: the length is 150 plus or minus 1mm, the width is 50 plus or minus 1mm, and the thickness is 1.5mm-2 mm.
(3) Single-sided tape: tearing off the release material on the sticky tape, gluing the face and can not contact hand or other article, will glue the face and be connected with mirror surface steel sheet's one end, do not exert external pressure with compression roller (2Kg) under the circumstances, make a round trip 3 times with 300 mm/min's speed for glue the face and fully contact with mirror surface steel sheet, sample and mirror surface steel sheet bonding department do not allow the bubble to produce.
(4) After the preparation of the sample, the sample is stopped in a specified test environment for 20min and then tested.
(5) The free end of the sample is folded by 180 degrees, the binding surface is stripped from the test plate by 25mm, the free end of the sample and the sample plate are respectively clamped on an upper clamp and a lower clamp, the stripping surface is consistent with the force line of a testing machine, the testing machine continuously strips at the rising speed of 300mm/min +/-10 mm/min, and an automatic recorder draws a stripping curve.
(6) Test data and damage interface locations were recorded and averaged.
2. 180-degree peeling force of sample tested by peeling force tester after aging
(1) The sample preparation method was consistent with that described above.
(2) After the sample and the mirror steel plate are bonded, the mirror steel plate is placed in an environment with high temperature and high humidity of 85 +/-2 ℃ and 85 +/-5% R.H. for 2000H and TC (-40 ℃ -85 ℃ 6H/cycle, 200cycle), and then the mirror steel plate is taken out and stands for 2H, and the test is carried out by using the peel force test method.
(3) Test data and damage interface locations were recorded and averaged.
As shown in the evaluation results of Table 3, the outdoor advertisement car body sticker has excellent peeling performance, has no adhesive residue after long-time sticking, meanwhile, stays for a long time under the environment of high temperature and high humidity, the peeling force quickly reaches a stable state, the peeling force is not continuously increased, the sticking stability is improved, the difficulty in peeling is avoided, the peeling performance of the comparative example 1 is relatively poor, and the peeling force of the comparative example 2 is greatly changed along with the change of temperature and humidity; therefore, the invention not only improves the stripping performance without adhesive residue, but also ensures that the stripping force is almost unchanged and the stripping performance is stable under the condition that the environmental shadow of the outdoor advertisement vehicle body is greatly changed, thereby being suitable for outdoor long-time use, avoiding the adhesive residue phenomenon when the advertisement sticker is replaced and greatly reducing the probability of damage to the advertisement sticker and the vehicle body.
The above embodiments are merely illustrative of the technical ideas and features of the present invention, and the purpose thereof is to enable those skilled in the art to understand the contents of the present invention and implement the present invention, and not to limit the protection scope of the present invention. All equivalent changes and modifications made according to the spirit of the present invention should be covered within the protection scope of the present invention.
Claims (6)
1. A preparation method of an outdoor advertisement vehicle body sticker is characterized by comprising the following steps: including substrate layer (1), gum layer (2) and from type layer (3), coating in gum layer (2) on the one side of substrate layer (1), gum layer (2) are equipped with from type layer (3) in the one side of substrate layer (1) mutually away from, the gum layer is dried by the glue solution coating and is obtained, and this glue solution is made through following step:
s1, uniformly mixing 20-35 parts of methyl methacrylate, 10-30 parts of styrene, 10-20 parts of butyl acrylate, 0.5-1.5 parts of sodium carbonate, 1-5 parts of hexachlorocyclotriphosphazene and 50-80 parts of deionized water, heating to 75-90 ℃, dropwise adding 0.5-1.5 parts of 4,4' -azobis (4-cyanopentanoic acid) and 1-5 parts of acrylic acid into the mixed system, and reacting for 3-5 hours;
s2, cooling to room temperature, adding 1-5 parts of aluminum isopropoxide, 1-3 parts of a curing agent, 0.2-1 part of triglycerol monostearate and 0.1-1 part of hydroquinone, and uniformly mixing to obtain a glue solution;
and S3, uniformly coating the glue solution on the substrate layer (1), and drying to obtain the back glue layer (2).
2. The method for preparing the outdoor advertising vehicle body sticker as claimed in claim 1, wherein: the adding ratio of the methyl methacrylate to the styrene is 2: 1-1: 1.
3. The method for preparing the outdoor advertising vehicle body sticker as claimed in claim 1, wherein: the curing agent is selected from one of curing agent S01-5, curing agent MH2844 and curing agent T-31.
4. The method for preparing the outdoor advertising vehicle body sticker according to any one of claims 1-3, wherein: the base material layer (1) is a PVC layer.
5. The method for preparing the outdoor advertising vehicle body sticker according to any one of claims 1-3, wherein: the thickness of the substrate layer (1) is 70-120 mu m.
6. The method for preparing the outdoor advertising vehicle body sticker according to any one of claims 1-3, wherein: the thickness of the back glue layer (2) is 15-30 μm.