CN112175417A - 一种新型涂料用纳米级液体钛白粉 - Google Patents

一种新型涂料用纳米级液体钛白粉 Download PDF

Info

Publication number
CN112175417A
CN112175417A CN202011028245.7A CN202011028245A CN112175417A CN 112175417 A CN112175417 A CN 112175417A CN 202011028245 A CN202011028245 A CN 202011028245A CN 112175417 A CN112175417 A CN 112175417A
Authority
CN
China
Prior art keywords
parts
powder
titanium dioxide
resistant
calcium carbonate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202011028245.7A
Other languages
English (en)
Inventor
许荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN202011028245.7A priority Critical patent/CN112175417A/zh
Publication of CN112175417A publication Critical patent/CN112175417A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种新型涂料用纳米级液体钛白粉，涉及钛白粉技术领域，该新型涂料用纳米级液体钛白粉，包括如下重量份的原料：二氧化钛颗粒60‑80份、碳酸钙粉体100‑120份、耐磨耐酸粉末50‑70份、去离子水660‑880份、活化剂6‑16份、阻燃剂8‑20份。该新型造纸用纳米级液体钛白粉，能够提升二氧化钛粉体对碳酸钙纳米粉体的包覆率，使用的碳酸钙粉体和二氧化钛粉体均研磨呈纳米级，可以进一步的保障包裹效果，在制备的过程中加入耐磨耐酸粉末，使得制备后的纳米级液体钛白粉在使用后，具有良好的耐磨效果，同时，加入的阻燃剂，使得纳米级液体钛白粉在使用后，具有阻燃性，进而制备出具有品质优良的液体钛白粉。

Description

一种新型涂料用纳米级液体钛白粉
技术领域
本发明涉及钛白粉技术领域，特别的为一种新型涂料用纳米级液体钛白粉。
背景技术
钛白粉被认为是世界上性能最好的一种颜料，广泛应用于涂料、塑料、造纸、印刷油墨、化纤、橡胶、化妆品等工业，钛白粉主要成分为二氧化钛的白色颜料，学名为二氧化钛，分子式为TiO2是一种多晶化合物，其质点呈规则排列，具有格子构造，但是现有技术中制备的液体钛白粉，在制备的过程中，二氧化钛对矿物粉体的包覆率不佳，造成制备的液体钛白粉质量不佳，且制备的液体钛白粉，在使用后，极易受到磨损，也缺少阻燃作用，无法满足使用者的需求。
发明内容
本发明提供的发明目的在于提供一种新型涂料用纳米级液体钛白粉，在制备时，能够提升二氧化钛粉体对碳酸钙纳米粉体的包覆率，同时，作为涂料使用后，能够起到耐磨和阻燃效果。
为实现以上目的，本发明通过以下技术方案予以实现：一种新型涂料用纳米级液体钛白粉，包括如下重量份的原料：二氧化钛颗粒60-80份、碳酸钙粉体100-120份、耐磨耐酸粉末50-70份、去离子水660-880份、活化剂6-16份、阻燃剂8-20份。
作为本发明进一步的方案：包括如下重量份的原料：二氧化钛颗粒58-78份、碳酸钙粉体98-118份、耐磨耐酸粉末48-68份、去离子水658-878份、活化剂8-14份、阻燃剂10-18份。
作为本发明进一步的方案：二氧化钛颗粒56-76份、碳酸钙粉体96-116份、耐磨耐酸粉末46-66份、去离子水656-876份、活化剂10-12份、阻燃剂12-16份。
作为本发明进一步的方案：二氧化钛颗粒70份、碳酸钙粉体110份、耐磨耐酸粉末60份、去离子水770份、活化剂11份、阻燃剂14份。
作为本发明进一步的方案：所述耐磨耐酸粉末为铸石粉与白刚玉的混合物，且混合比例为铸石粉：白刚玉＝3：1。
作为本发明进一步的方案：所述活化剂为磷酸丙二胺、聚乙烯亚胺、磷酸乙二胺中的一种或者多种按任意比例混合。
作为本发明进一步的方案：所述阻燃剂为正丁醇、醋酸丁酯、珍珠岩中的一种或者多种按任意比例混合。
一种新型涂料用纳米级液体钛白粉的制备方法，包括以下步骤：
S1、将二氧化钛颗粒、碳酸钙粉体、耐磨耐酸粉末分别通过纳米级研磨机进行研磨，得到纳米粉末备用。
S2、将获得的碳酸钙纳米粉末与活化剂通过搅拌机进行充分混合，得到表面活化后的碳酸钙纳米粉末。
S3、将表面活化后的碳酸钙纳米粉末与去离子水通过搅拌机混合均匀，然后加入纳米耐磨耐酸粉末和阻燃剂继续搅拌至完全充分混合，得到混合溶液。
S4、向混合溶液内加入纳米级二氧化钛粉末，充分搅拌，制备得到纳米级液体钛白粉。
作为本发明进一步的方案：将根据S2中的操作步骤，混合碳酸钙纳米粉末与活化剂时，温度保持在90-112℃，搅拌机的转速为500-600r/min，搅拌时间为5-10min。
作为本发明进一步的方案：将根据S2中的操作步骤，制备合溶液时，温度保持在90-120℃，搅拌机的转速为800-1200r/min，搅拌时间为5-8min。
本发明提供了一种新型涂料用纳米级液体钛白粉。具备以下有益效果：
本发明中，通过加入活化剂，能够对碳酸钙粉体进行表面活化的处理，活化剂具有助磨作用，促进碳酸钙粉体表面产生活化离子，进而提升二氧化钛粉体对碳酸钙纳米粉体的包覆率，使用的碳酸钙粉体和二氧化钛粉体均研磨呈纳米级，可以进一步的保障包裹效果，在制备的过程中加入耐磨耐酸粉末，使得制备后的纳米级液体钛白粉在使用后，具有良好的耐磨效果，同时，加入的阻燃剂，使得纳米级液体钛白粉在使用后，具有阻燃性，进而制备出具有品质优良的液体钛白粉。
具体实施方式
以下参照具体的实施例来说明本发明。本领域技术人员能够理解，这些实施例仅用于说明本发明，其不以任何方式限制本发明的范围。
实施例1：
一种新型涂料用纳米级液体钛白粉，包括如下重量份的原料：二氧化钛颗粒60份、碳酸钙粉体100份、耐磨耐酸粉末50份、去离子水660份、活化剂6份、阻燃剂8份，二氧化钛具有无毒、最佳的不透明性、最佳白度和光亮度的特性，是制备液体钛白粉的重要成份，碳酸钙是一种无机化合物，无有害成份，活化剂能够对碳酸钙粉体进行表面活化的处理，活化剂具有助磨作用，促进碳酸钙粉体表面产生活化离子，进而提升二氧化钛粉体对碳酸钙纳米粉体的包覆率，加入的耐磨耐酸粉末，使得制备后的纳米级液体钛白粉在使用后，具有良好的耐磨效果，同时，加入的阻燃剂，使得纳米级液体钛白粉在使用后，具有阻燃性，进而制备出具有品质优良的液体钛白粉。
具体的，耐磨耐酸粉末为铸石粉与白刚玉的混合物，且混合比例为铸石粉：白刚玉＝3：1。
具体的，活化剂为磷酸丙二胺、聚乙烯亚胺、磷酸乙二胺中的一种或者多种按任意比例混合。
具体的，阻燃剂为正丁醇、醋酸丁酯、珍珠岩中的一种或者多种按任意比例混合。
一种新型涂料用纳米级液体钛白粉的制备方法，包括以下步骤：
步骤一、将二氧化钛颗粒、碳酸钙粉体、耐磨耐酸粉末分别通过纳米级研磨机进行研磨，得到纳米粉末备用，使用的碳酸钙粉体和二氧化钛粉体均研磨呈纳米级，可以进一步的保障后续包裹效果。
步骤二、将获得的碳酸钙纳米粉末与活化剂通过搅拌机进行充分混合，得到表面活化后的碳酸钙纳米粉末，混合碳酸钙纳米粉末与活化剂时，温度保持在90-112℃，搅拌机的转速为500-600r/min，搅拌时间为5-10min，在混合过程中对物料施加的机械能和活化剂的双重作用，可以使碳酸钙纳米粉末的表面被高度活化。
步骤三、将表面活化后的碳酸钙纳米粉末与去离子水通过搅拌机混合均匀，然后加入纳米耐磨耐酸粉末和阻燃剂继续搅拌至完全充分混合，得到混合溶液，制备合溶液时，温度保持在90-120℃，搅拌机的转速为800-1200r/min，搅拌时间为5-8min，使得溶液能够充分的混合均匀。
步骤四、向混合溶液内加入纳米级二氧化钛粉末，充分搅拌，制备得到纳米级液体钛白粉，制备的纳米级液体钛白粉具有优良的品质。
实施例2：
一种新型涂料用纳米级液体钛白粉，包括如下重量份的原料：二氧化钛颗粒80份、碳酸钙粉体120份、耐磨耐酸粉末70份、去离子水880份、活化剂16份、阻燃剂20份，二氧化钛具有无毒、最佳的不透明性、最佳白度和光亮度的特性，是制备液体钛白粉的重要成份，碳酸钙是一种无机化合物，无有害成份，活化剂能够对碳酸钙粉体进行表面活化的处理，活化剂具有助磨作用，促进碳酸钙粉体表面产生活化离子，进而提升二氧化钛粉体对碳酸钙纳米粉体的包覆率，加入的耐磨耐酸粉末，使得制备后的纳米级液体钛白粉在使用后，具有良好的耐磨效果，同时，加入的阻燃剂，使得纳米级液体钛白粉在使用后，具有阻燃性，进而制备出具有品质优良的液体钛白粉。
具体的，耐磨耐酸粉末为铸石粉与白刚玉的混合物，且混合比例为铸石粉：白刚玉＝3：1。
具体的，活化剂为磷酸丙二胺、聚乙烯亚胺、磷酸乙二胺中的一种或者多种按任意比例混合。
具体的，阻燃剂为正丁醇、醋酸丁酯、珍珠岩中的一种或者多种按任意比例混合。
一种新型涂料用纳米级液体钛白粉的制备方法，包括以下步骤：
步骤一、将二氧化钛颗粒、碳酸钙粉体、耐磨耐酸粉末分别通过纳米级研磨机进行研磨，得到纳米粉末备用，使用的碳酸钙粉体和二氧化钛粉体均研磨呈纳米级，可以进一步的保障后续包裹效果。
步骤二、将获得的碳酸钙纳米粉末与活化剂通过搅拌机进行充分混合，得到表面活化后的碳酸钙纳米粉末，混合碳酸钙纳米粉末与活化剂时，温度保持在90-112℃，搅拌机的转速为500-600r/min，搅拌时间为5-10min，在混合过程中对物料施加的机械能和活化剂的双重作用，可以使碳酸钙纳米粉末的表面被高度活化。
步骤三、将表面活化后的碳酸钙纳米粉末与去离子水通过搅拌机混合均匀，然后加入纳米耐磨耐酸粉末和阻燃剂继续搅拌至完全充分混合，得到混合溶液，制备合溶液时，温度保持在90-120℃，搅拌机的转速为800-1200r/min，搅拌时间为5-8min，使得溶液能够充分的混合均匀。
步骤四、向混合溶液内加入纳米级二氧化钛粉末，充分搅拌，制备得到纳米级液体钛白粉，制备的纳米级液体钛白粉具有优良的品质。
实施例3：
一种新型涂料用纳米级液体钛白粉，包括如下重量份的原料：二氧化钛颗粒58份、碳酸钙粉体98份、耐磨耐酸粉末48份、去离子水658份、活化剂8份、阻燃剂10份，二氧化钛具有无毒、最佳的不透明性、最佳白度和光亮度的特性，是制备液体钛白粉的重要成份，碳酸钙是一种无机化合物，无有害成份，活化剂能够对碳酸钙粉体进行表面活化的处理，活化剂具有助磨作用，促进碳酸钙粉体表面产生活化离子，进而提升二氧化钛粉体对碳酸钙纳米粉体的包覆率，加入的耐磨耐酸粉末，使得制备后的纳米级液体钛白粉在使用后，具有良好的耐磨效果，同时，加入的阻燃剂，使得纳米级液体钛白粉在使用后，具有阻燃性，进而制备出具有品质优良的液体钛白粉。
具体的，耐磨耐酸粉末为铸石粉与白刚玉的混合物，且混合比例为铸石粉：白刚玉＝3：1。
具体的，活化剂为磷酸丙二胺、聚乙烯亚胺、磷酸乙二胺中的一种或者多种按任意比例混合。
具体的，阻燃剂为正丁醇、醋酸丁酯、珍珠岩中的一种或者多种按任意比例混合。
一种新型涂料用纳米级液体钛白粉的制备方法，包括以下步骤：
步骤一、将二氧化钛颗粒、碳酸钙粉体、耐磨耐酸粉末分别通过纳米级研磨机进行研磨，得到纳米粉末备用，使用的碳酸钙粉体和二氧化钛粉体均研磨呈纳米级，可以进一步的保障后续包裹效果。
步骤二、将获得的碳酸钙纳米粉末与活化剂通过搅拌机进行充分混合，得到表面活化后的碳酸钙纳米粉末，混合碳酸钙纳米粉末与活化剂时，温度保持在90-112℃，搅拌机的转速为500-600r/min，搅拌时间为5-10min，在混合过程中对物料施加的机械能和活化剂的双重作用，可以使碳酸钙纳米粉末的表面被高度活化。
步骤三、将表面活化后的碳酸钙纳米粉末与去离子水通过搅拌机混合均匀，然后加入纳米耐磨耐酸粉末和阻燃剂继续搅拌至完全充分混合，得到混合溶液，制备合溶液时，温度保持在90-120℃，搅拌机的转速为800-1200r/min，搅拌时间为5-8min，使得溶液能够充分的混合均匀。
步骤四、向混合溶液内加入纳米级二氧化钛粉末，充分搅拌，制备得到纳米级液体钛白粉，制备的纳米级液体钛白粉具有优良的品质。
实施例4：
一种新型涂料用纳米级液体钛白粉，包括如下重量份的原料：二氧化钛颗粒78份、碳酸钙粉体118份、耐磨耐酸粉末68份、去离子水878份、活化剂14份、阻燃剂18份，二氧化钛具有无毒、最佳的不透明性、最佳白度和光亮度的特性，是制备液体钛白粉的重要成份，碳酸钙是一种无机化合物，无有害成份，活化剂能够对碳酸钙粉体进行表面活化的处理，活化剂具有助磨作用，促进碳酸钙粉体表面产生活化离子，进而提升二氧化钛粉体对碳酸钙纳米粉体的包覆率，加入的耐磨耐酸粉末，使得制备后的纳米级液体钛白粉在使用后，具有良好的耐磨效果，同时，加入的阻燃剂，使得纳米级液体钛白粉在使用后，具有阻燃性，进而制备出具有品质优良的液体钛白粉。
具体的，耐磨耐酸粉末为铸石粉与白刚玉的混合物，且混合比例为铸石粉：白刚玉＝3：1。
具体的，活化剂为磷酸丙二胺、聚乙烯亚胺、磷酸乙二胺中的一种或者多种按任意比例混合。
具体的，阻燃剂为正丁醇、醋酸丁酯、珍珠岩中的一种或者多种按任意比例混合。
一种新型涂料用纳米级液体钛白粉的制备方法，包括以下步骤：
步骤一、将二氧化钛颗粒、碳酸钙粉体、耐磨耐酸粉末分别通过纳米级研磨机进行研磨，得到纳米粉末备用，使用的碳酸钙粉体和二氧化钛粉体均研磨呈纳米级，可以进一步的保障后续包裹效果。
步骤二、将获得的碳酸钙纳米粉末与活化剂通过搅拌机进行充分混合，得到表面活化后的碳酸钙纳米粉末，混合碳酸钙纳米粉末与活化剂时，温度保持在90-112℃，搅拌机的转速为500-600r/min，搅拌时间为5-10min，在混合过程中对物料施加的机械能和活化剂的双重作用，可以使碳酸钙纳米粉末的表面被高度活化。
步骤三、将表面活化后的碳酸钙纳米粉末与去离子水通过搅拌机混合均匀，然后加入纳米耐磨耐酸粉末和阻燃剂继续搅拌至完全充分混合，得到混合溶液，制备合溶液时，温度保持在90-120℃，搅拌机的转速为800-1200r/min，搅拌时间为5-8min，使得溶液能够充分的混合均匀。
步骤四、向混合溶液内加入纳米级二氧化钛粉末，充分搅拌，制备得到纳米级液体钛白粉，制备的纳米级液体钛白粉具有优良的品质。
实施例5：
一种新型涂料用纳米级液体钛白粉，包括如下重量份的原料：二氧化钛颗粒56份、碳酸钙粉体96份、耐磨耐酸粉末46份、去离子水656份、活化剂10份、阻燃剂12份，二氧化钛具有无毒、最佳的不透明性、最佳白度和光亮度的特性，是制备液体钛白粉的重要成份，碳酸钙是一种无机化合物，无有害成份，活化剂能够对碳酸钙粉体进行表面活化的处理，活化剂具有助磨作用，促进碳酸钙粉体表面产生活化离子，进而提升二氧化钛粉体对碳酸钙纳米粉体的包覆率，加入的耐磨耐酸粉末，使得制备后的纳米级液体钛白粉在使用后，具有良好的耐磨效果，同时，加入的阻燃剂，使得纳米级液体钛白粉在使用后，具有阻燃性，进而制备出具有品质优良的液体钛白粉。
具体的，耐磨耐酸粉末为铸石粉与白刚玉的混合物，且混合比例为铸石粉：白刚玉＝3：1。
具体的，活化剂为磷酸丙二胺、聚乙烯亚胺、磷酸乙二胺中的一种或者多种按任意比例混合。
具体的，阻燃剂为正丁醇、醋酸丁酯、珍珠岩中的一种或者多种按任意比例混合。
一种新型涂料用纳米级液体钛白粉的制备方法，包括以下步骤：
步骤一、将二氧化钛颗粒、碳酸钙粉体、耐磨耐酸粉末分别通过纳米级研磨机进行研磨，得到纳米粉末备用，使用的碳酸钙粉体和二氧化钛粉体均研磨呈纳米级，可以进一步的保障后续包裹效果。
步骤二、将获得的碳酸钙纳米粉末与活化剂通过搅拌机进行充分混合，得到表面活化后的碳酸钙纳米粉末，混合碳酸钙纳米粉末与活化剂时，温度保持在90-112℃，搅拌机的转速为500-600r/min，搅拌时间为5-10min，在混合过程中对物料施加的机械能和活化剂的双重作用，可以使碳酸钙纳米粉末的表面被高度活化。
步骤三、将表面活化后的碳酸钙纳米粉末与去离子水通过搅拌机混合均匀，然后加入纳米耐磨耐酸粉末和阻燃剂继续搅拌至完全充分混合，得到混合溶液，制备合溶液时，温度保持在90-120℃，搅拌机的转速为800-1200r/min，搅拌时间为5-8min，使得溶液能够充分的混合均匀。
步骤四、向混合溶液内加入纳米级二氧化钛粉末，充分搅拌，制备得到纳米级液体钛白粉，制备的纳米级液体钛白粉具有优良的品质。
实施例6：
一种新型涂料用纳米级液体钛白粉，包括如下重量份的原料：二氧化钛颗粒76份、碳酸钙粉体116份、耐磨耐酸粉末66份、去离子水876份、活化剂12份、阻燃剂16份，二氧化钛具有无毒、最佳的不透明性、最佳白度和光亮度的特性，是制备液体钛白粉的重要成份，碳酸钙是一种无机化合物，无有害成份，活化剂能够对碳酸钙粉体进行表面活化的处理，活化剂具有助磨作用，促进碳酸钙粉体表面产生活化离子，进而提升二氧化钛粉体对碳酸钙纳米粉体的包覆率，加入的耐磨耐酸粉末，使得制备后的纳米级液体钛白粉在使用后，具有良好的耐磨效果，同时，加入的阻燃剂，使得纳米级液体钛白粉在使用后，具有阻燃性，进而制备出具有品质优良的液体钛白粉。
具体的，耐磨耐酸粉末为铸石粉与白刚玉的混合物，且混合比例为铸石粉：白刚玉＝3：1。
具体的，活化剂为磷酸丙二胺、聚乙烯亚胺、磷酸乙二胺中的一种或者多种按任意比例混合。
具体的，阻燃剂为正丁醇、醋酸丁酯、珍珠岩中的一种或者多种按任意比例混合。
一种新型涂料用纳米级液体钛白粉的制备方法，包括以下步骤：
步骤一、将二氧化钛颗粒、碳酸钙粉体、耐磨耐酸粉末分别通过纳米级研磨机进行研磨，得到纳米粉末备用，使用的碳酸钙粉体和二氧化钛粉体均研磨呈纳米级，可以进一步的保障后续包裹效果。
步骤二、将获得的碳酸钙纳米粉末与活化剂通过搅拌机进行充分混合，得到表面活化后的碳酸钙纳米粉末，混合碳酸钙纳米粉末与活化剂时，温度保持在90-112℃，搅拌机的转速为500-600r/min，搅拌时间为5-10min，在混合过程中对物料施加的机械能和活化剂的双重作用，可以使碳酸钙纳米粉末的表面被高度活化。
步骤三、将表面活化后的碳酸钙纳米粉末与去离子水通过搅拌机混合均匀，然后加入纳米耐磨耐酸粉末和阻燃剂继续搅拌至完全充分混合，得到混合溶液，制备合溶液时，温度保持在90-120℃，搅拌机的转速为800-1200r/min，搅拌时间为5-8min，使得溶液能够充分的混合均匀。
步骤四、向混合溶液内加入纳米级二氧化钛粉末，充分搅拌，制备得到纳米级液体钛白粉，制备的纳米级液体钛白粉具有优良的品质。
实施例7：
一种新型涂料用纳米级液体钛白粉，包括如下重量份的原料：二氧化钛颗粒70份、碳酸钙粉体110份、耐磨耐酸粉末60份、去离子水770份、活化剂11份、阻燃剂14份，二氧化钛具有无毒、最佳的不透明性、最佳白度和光亮度的特性，是制备液体钛白粉的重要成份，碳酸钙是一种无机化合物，无有害成份，活化剂能够对碳酸钙粉体进行表面活化的处理，活化剂具有助磨作用，促进碳酸钙粉体表面产生活化离子，进而提升二氧化钛粉体对碳酸钙纳米粉体的包覆率，加入的耐磨耐酸粉末，使得制备后的纳米级液体钛白粉在使用后，具有良好的耐磨效果，同时，加入的阻燃剂，使得纳米级液体钛白粉在使用后，具有阻燃性，进而制备出具有品质优良的液体钛白粉。
具体的，耐磨耐酸粉末为铸石粉与白刚玉的混合物，且混合比例为铸石粉：白刚玉＝3：1。
具体的，活化剂为磷酸丙二胺、聚乙烯亚胺、磷酸乙二胺中的一种或者多种按任意比例混合。
具体的，阻燃剂为正丁醇、醋酸丁酯、珍珠岩中的一种或者多种按任意比例混合。
一种新型涂料用纳米级液体钛白粉的制备方法，包括以下步骤：
步骤一、将二氧化钛颗粒、碳酸钙粉体、耐磨耐酸粉末分别通过纳米级研磨机进行研磨，得到纳米粉末备用，使用的碳酸钙粉体和二氧化钛粉体均研磨呈纳米级，可以进一步的保障后续包裹效果。
步骤二、将获得的碳酸钙纳米粉末与活化剂通过搅拌机进行充分混合，得到表面活化后的碳酸钙纳米粉末，混合碳酸钙纳米粉末与活化剂时，温度保持在90-112℃，搅拌机的转速为500-600r/min，搅拌时间为5-10min，在混合过程中对物料施加的机械能和活化剂的双重作用，可以使碳酸钙纳米粉末的表面被高度活化。
步骤三、将表面活化后的碳酸钙纳米粉末与去离子水通过搅拌机混合均匀，然后加入纳米耐磨耐酸粉末和阻燃剂继续搅拌至完全充分混合，得到混合溶液，制备合溶液时，温度保持在90-120℃，搅拌机的转速为800-1200r/min，搅拌时间为5-8min，使得溶液能够充分的混合均匀。
步骤四、向混合溶液内加入纳米级二氧化钛粉末，充分搅拌，制备得到纳米级液体钛白粉，制备的纳米级液体钛白粉具有优良的品质。
为了进一步说明本发明的有益效果，本发明人选取两种液体钛白粉，选取了货名为金红石型钛白粉，货号：R-706，下面简述为第一钛白粉。
同时选择了货名为NTR-606钛白粉，货号：R606，下面简述为第二钛白粉。
同时选择本发明制得液体钛白粉，针对钛白粉的包裹率、耐磨性、阻燃性及使用时间作了对比，得到了以下数据，详见表1：
表1实验数据表
Figure BDA0002702809840000161
Figure BDA0002702809840000171
由上述实验数据得出，实施例1-7的制备的液体钛白粉，能够提升二氧化钛粉体对碳酸钙纳米粉体的包覆率，具有良好的耐磨效果和阻燃性，本发明制备得液体钛白粉具有品质优良的效果。
以上所述的仅是本发明的优选实施方式，应当指出，对于本领域的普通技术人员来说，在不脱离本发明创造构思的前提下，还可以做出若干变形和改进，这些都属于本发明的保护范围。

Claims (10)

1.一种新型涂料用纳米级液体钛白粉，其特征在于，包括如下重量份的原料：二氧化钛颗粒60-80份、碳酸钙粉体100-120份、耐磨耐酸粉末50-70份、去离子水660-880份、活化剂6-16份、阻燃剂8-20份。
2.根据权利要求1所述的一种新型涂料用纳米级液体钛白粉，其特征在于，包括如下重量份的原料：二氧化钛颗粒58-78份、碳酸钙粉体98-118份、耐磨耐酸粉末48-68份、去离子水658-878份、活化剂8-14份、阻燃剂10-18份。
3.根据权利要求2所述的一种新型涂料用纳米级液体钛白粉，其特征在于，包括如下重量份的原料：二氧化钛颗粒56-76份、碳酸钙粉体96-116份、耐磨耐酸粉末46-66份、去离子水656-876份、活化剂10-12份、阻燃剂12-16份。
4.根据权利要求3所述的一种新型涂料用纳米级液体钛白粉，其特征在于，包括如下重量份的原料：二氧化钛颗粒70份、碳酸钙粉体110份、耐磨耐酸粉末60份、去离子水770份、活化剂11份、阻燃剂14份。
5.根据权利要求1-4任意一项所述的一种新型涂料用纳米级液体钛白粉，其特征在于，所述耐磨耐酸粉末为铸石粉与白刚玉的混合物，且混合比例为铸石粉：白刚玉=3：1。
6.根据权利要求1-4任意一项所述的一种新型涂料用纳米级液体钛白粉，其特征在于，所述活化剂为磷酸丙二胺、聚乙烯亚胺、磷酸乙二胺中的一种或者多种按任意比例混合。
7.根据权利要求1-4任意一项所述的一种新型涂料用纳米级液体钛白粉，其特征在于，所述阻燃剂为正丁醇、醋酸丁酯、珍珠岩中的一种或者多种按任意比例混合。
8.一种新型涂料用纳米级液体钛白粉的制备方法，其特征在于，包括以下步骤：
S1、将二氧化钛颗粒、碳酸钙粉体、耐磨耐酸粉末分别通过纳米级研磨机进行研磨，得到纳米粉末备用；
S2、将获得的碳酸钙纳米粉末与活化剂通过搅拌机进行充分混合，得到表面活化后的碳酸钙纳米粉末；
S3、将表面活化后的碳酸钙纳米粉末与去离子水通过搅拌机混合均匀，然后加入纳米耐磨耐酸粉末和阻燃剂继续搅拌至完全充分混合，得到混合溶液；
S4、向混合溶液内加入纳米级二氧化钛粉末，充分搅拌，制备得到纳米级液体钛白粉。
9.根据权利要求8所述的一种新型涂料用纳米级液体钛白粉的制备方法，其特征在于，将根据S2中的操作步骤，混合碳酸钙纳米粉末与活化剂时，温度保持在90-1120C，搅拌机的转速为500-600r/min，搅拌时间为5-10min。
10.根据权利要求8所述的一种新型涂料用纳米级液体钛白粉的制备方法，其特征在于，将根据S3中的操作步骤，制备合溶液时，温度保持在90-1200C，搅拌机的转速为800-1200r/min，搅拌时间为5-8min。
CN202011028245.7A 2020-09-26 2020-09-26 一种新型涂料用纳米级液体钛白粉 Pending CN112175417A (zh)