CN112154224A - 热冲压成形构件、热冲压成形用预涂镀钢板及热冲压成形工艺 - Google Patents
热冲压成形构件、热冲压成形用预涂镀钢板及热冲压成形工艺 Download PDFInfo
- Publication number
- CN112154224A CN112154224A CN201880092265.5A CN201880092265A CN112154224A CN 112154224 A CN112154224 A CN 112154224A CN 201880092265 A CN201880092265 A CN 201880092265A CN 112154224 A CN112154224 A CN 112154224A
- Authority
- CN
- China
- Prior art keywords
- layer
- thickness
- coating
- heating
- hot press
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供一种热冲压成形构件、热冲压成形用预涂镀钢板以及热冲压成形工艺。本发明的热冲压成形构件在基础钢的至少一个表面上设置有铝或铝合金的涂层,所述涂层由所述基础钢与铝或铝合金的预涂层之间的相互扩散产生,所述涂层的厚度为6~26μm。
Description
PCT国内申请,说明书已公开。
Claims (15)
- PCT国内申请,权利要求书已公开。