CN112110676A - 一种基于低密度轻质磁性球的制作方法及脚底按摩器 - Google Patents
一种基于低密度轻质磁性球的制作方法及脚底按摩器 Download PDFInfo
- Publication number
- CN112110676A CN112110676A CN202010581727.9A CN202010581727A CN112110676A CN 112110676 A CN112110676 A CN 112110676A CN 202010581727 A CN202010581727 A CN 202010581727A CN 112110676 A CN112110676 A CN 112110676A
- Authority
- CN
- China
- Prior art keywords
- low
- powder
- density light
- magnetic
- magnetic ball
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种基于低密度轻质磁性球的制作方法，包括准备原材料、原材料加工、吹塑定型，磁性覆盖和烘干冷却等步骤。同时公开了一种基于低密度轻质磁性球的脚底按摩器。本方法获得球体为空心球体，将现有技术中陶瓷浆液与吹塑材料按照比例混合，该混合材料既能获得空心球体，使得陶瓷浆液的原材料均匀分布与空心球体表面。降低了现有技术中内层为聚丙烯空心球体，外层为陶瓷浆液的包覆层的磁性球的密度。本按摩器其能够自动移动，使得磁性球能够在足底自动移动进行按摩，方便客户使用；并且其使用的磁性球质量较轻，使得电机与弹簧更易配合，提升按摩效果。
Description
技术领域
本发明涉及一种低密度轻质磁性球的制作方法及脚底按摩器，属于磁疗保健技术领域。
背景技术
随着磁疗保健理论的普及，消费者也越来越认可磁疗的功效，市场上出现了种类繁多的磁疗保健产品。诸多产品如眼罩、腰带和护膝，其产品的属性，允许用户随身携带。但是，现有技术中其安装的磁性物质均为实心，使得眼罩、腰带和护膝较为沉重，因此，需要一种低密度轻质磁性球的制作方法，以获得较为轻质的磁性球体。
现有技术中的磁疗足底按摩器，一般需要用户自己移动，产生摩擦效果。因此，需要一种能够自动移动的脚底按摩器，所以本申请提供了一个基于低密度轻质磁性球的脚底按摩器。
发明内容
为了解决上述技术问题，本发明提供一种基于低密度轻质磁性球的制作方法，其具体技术方案为：步骤1，准备原材料，所述原材料包括陶瓷粉料、粉料溶剂、吹塑材料和磁性材料，所述陶瓷粉料包括锆英石、煅烧高岭土、凹凸棒土、泗滨砭石粉和赭石，所述粉料溶剂包括聚丙烯酸钠、羧甲基纤维素钠、糊精和水；所述吹塑材料包括聚丙烯；所述磁性材料包括树脂、有机溶液和分散剂；
步骤2，原材料加工，将锆英石、煅烧高岭土、凹凸棒土、泗滨砭石粉和赭石混合并捣碎碾压呈粉末状的陶瓷粉料，将聚丙烯酸钠、羧甲基纤维素钠、糊精和水混合搅拌均匀呈液态的粉料溶剂，将陶瓷粉料加入至液态的粉料溶剂中，搅拌均匀获得陶瓷浆液；将聚丙烯熔融至液态，将陶瓷浆液与液态的聚丙烯溶液混合搅拌均匀得到混合剂；树脂、有机溶液和分散剂融合在一起呈液态待用；
步骤3，使用步骤2中获得混合剂进行吹塑，获得空心球体；
步骤4，将磁性材料灌入螺旋输送器的管道中，将空心球体投入管道中，随着螺旋输送管道内部的转动被输送至管道外；
步骤5，将表面包裹了磁性材料的空心球体冷却、烘干。
进一步的，所述陶瓷粉料的组分为40-50份锆英石、20-30份煅烧高岭土、5-10份凹凸棒土、10-20份泗滨砭石粉和20-30份赭石，所述粉料溶剂的组分为聚丙烯酸钠0.1％、羧甲基纤维素钠0.05％、糊精1.0％和水98.85％；所述陶瓷粉料和粉料溶剂按照体积比7：3混合；所述陶瓷浆料与聚丙烯熔料按照质量比6：4混合。
进一步的，所述空心球体的直径为1cm。
进一步的，所述步骤5中，将空心球体使用热风机烘干持续10分钟，随后冷却至室温。
一种基于低密度轻质磁性球的脚底按摩器，包括基座，所述基座的内部设有移动板，所述移动板上设有若干个半圆槽，每个半圆槽内放置一个低密度轻质磁性球，所述基座的上表面设有一层布，所述布张紧并将低密度轻质磁性球覆盖；所述移动板的一端使用弹簧与基座的内壁连接，另一端与凸轮连接，所述凸轮由电机控制。
进一步的，所述布为棉织布。
进一步的，所述若干个半圆槽分布呈椭圆形。
本发明的有益效果是：本发明的基于低密度轻质磁性球的制作方法，获得球体为空心球体，将现有技术中陶瓷浆液与吹塑材料按照比例混合，该混合材料既能获得空心球体，使得陶瓷浆液的原材料均匀分布与空心球体表面。降低了现有技术中内层为聚丙烯空心球体，外层为陶瓷浆液的包覆层的磁性球的密度。本发明的基于低密度轻质磁性球的脚底按摩器，其能够自动移动，使得磁性球能够在足底自动移动进行按摩，方便客户使用；并且其使用的磁性球质量较轻，使得电机与弹簧更易配合，提升按摩效果。
附图说明
图1是本发明的基于低密度轻质磁性球的制作方法的流程图，
图2是本发明的螺栓输送管道的结构示意图，
图3是本发明的基于低密度轻质磁性球的脚底按摩器的结构示意图，
图中：1-基座，2-移动板，3-低密度轻质磁性球，4-布，5-弹簧，6-凸轮。
具体实施方式
现在结合附图对本发明作进一步详细的说明。这些附图均为简化的示意图，仅以示意方式说明本发明的基本结构，因此其仅显示与本发明有关的构成。
实施例1
本基于低密度轻质磁性球的制作方法，其具体技术方案为：
步骤1，准备原材料，所述原材料包括陶瓷粉料、粉料溶剂、吹塑材料和磁性材料，
所述陶瓷粉料包括40份锆英石、煅20份烧高岭土、5份凹凸棒土、10份泗滨砭石粉和20份赭石，所述粉料溶剂包括聚丙烯酸钠0.1％、羧甲基纤维素钠0.05％、糊精1.0％和水98.85％；所述吹塑材料包括聚丙烯；所述磁性材料包括树脂45份、20份有机溶液和10份分散剂。分散剂可以为聚丙烯酸钠、聚乙烯亚胺或亚甲基丙烯酸胺。
步骤2，原材料加工，将锆英石、煅烧高岭土、凹凸棒土、泗滨砭石粉和赭石混合并捣碎碾压呈粉末状的陶瓷粉料，将聚丙烯酸钠、羧甲基纤维素钠、糊精和水混合搅拌均匀呈液态的粉料溶剂，将陶瓷粉料加入至液态的粉料溶剂中，搅拌均匀获得陶瓷浆液；将聚丙烯熔融至液态，将陶瓷浆液与液态的聚丙烯溶液混合搅拌均匀得到混合剂；树脂、有机溶液和分散剂融合在一起呈液态待用。所述陶瓷粉料和粉料溶剂按照体积比7：3混合；所述陶瓷浆料与聚丙烯熔料按照质量比6：4混合。
步骤3，使用步骤2中获得混合剂进行吹塑，获得直径空心球体；
步骤4，将磁性材料灌入螺旋输送器的管道中，将空心球体投入管道中，随着螺旋输送管道内部的转动被输送至管道外。本实施例中，螺旋输送管道水平放置。该结构，既保证了空心球体在螺旋输送器的管道中全方位旋转，空心球体外壁与磁性材料溶液充分融合，保证空心球体外壁每一处都涂抹磁性材料。又保证了空心球体在磁性材料中的放置时间相同，保证了磁性材料在空心球体外壁的厚度一致。
步骤5，将表面包裹了磁性材料的空心球体冷却、烘干。将空心球体使用热风机烘干持续10分钟，随后冷却至室温。
赭石具有平肝降逆，加入该组分，使得制得的磁性球增加护肝疗效。并且，赭石可作为X线胃肠造影剂，当无法判断孩童是否误吞时，进行X光拍摄，即可判断是否吞食，免受开腹之苦。泗滨砭石粉具有远红外效应，作用于人体经络穴位，可促进血流速度，改善微循环。
进一步的，所述陶瓷粉料的组分为40-50份锆英石、20-30份煅烧高岭土、5-10份凹凸棒土、10-20份泗滨砭石粉和20-30份赭石，所述粉料溶剂的组分为聚丙烯酸钠0.1％、羧甲基纤维素钠0.05％、糊精1.0％和水98.85％；进一步的，所述空心球体的直径为1cm。
实施例2
本基于低密度轻质磁性球的制作方法，其具体技术方案为：
步骤1，准备原材料，所述原材料包括陶瓷粉料、粉料溶剂、吹塑材料和磁性材料，
所述陶瓷粉料包括50份锆英石、30份煅烧高岭土、10份凹凸棒土、20份泗滨砭石粉和30份赭石，所述粉料溶剂包括聚丙烯酸钠0.1％、羧甲基纤维素钠0.05％、糊精1.0％和水98.85％；所述吹塑材料包括聚丙烯；所述磁性材料包括树脂45份、20份有机溶液和10份分散剂；
步骤2，原材料加工，将锆英石、煅烧高岭土、凹凸棒土、泗滨砭石粉和赭石混合并捣碎碾压呈粉末状的陶瓷粉料，将聚丙烯酸钠、羧甲基纤维素钠、糊精和水混合搅拌均匀呈液态的粉料溶剂，将陶瓷粉料加入至液态的粉料溶剂中，搅拌均匀获得陶瓷浆液；将聚丙烯熔融至液态，将陶瓷浆液与液态的聚丙烯溶液混合搅拌均匀得到混合剂；树脂、有机溶液和分散剂融合在一起呈液态待用。所述陶瓷粉料和粉料溶剂按照体积比7：3混合；所述陶瓷浆料与聚丙烯熔料按照质量比6：4混合。
步骤3，使用步骤2中获得混合剂进行吹塑，获得直径空心球体；
步骤4，将磁性材料灌入螺旋输送器的管道中，将空心球体投入管道中，随着螺旋输送管道内部的转动被输送至管道外。本实施例中，螺旋输送管道水平放置。该结构，既保证了空心球体在螺旋输送器的管道中全方位旋转，空心球体外壁与磁性材料溶液充分融合，保证空心球体外壁每一处都涂抹磁性材料。又保证了空心球体在磁性材料中的放置时间相同，保证了磁性材料在空心球体外壁的厚度一致。
步骤5，将表面包裹了磁性材料的空心球体冷却、烘干。将空心球体使用热风机烘干持续10分钟，随后冷却至室温。
实施例3
本基于低密度轻质磁性球的制作方法，其具体技术方案为：
步骤1，准备原材料，所述原材料包括陶瓷粉料、粉料溶剂、吹塑材料和磁性材料，
所述陶瓷粉料包括45份锆英石、25份煅烧高岭土、8份凹凸棒土、25份泗滨砭石粉和25份赭石，所述粉料溶剂包括聚丙烯酸钠0.1％、羧甲基纤维素钠0.05％、糊精1.0％和水98.85％；所述吹塑材料包括聚丙烯；所述磁性材料包括树脂45份、20份有机溶液和10份分散剂；
步骤2，原材料加工，将锆英石、煅烧高岭土、凹凸棒土、泗滨砭石粉和赭石混合并捣碎碾压呈粉末状的陶瓷粉料，将聚丙烯酸钠、羧甲基纤维素钠、糊精和水混合搅拌均匀呈液态的粉料溶剂，将陶瓷粉料加入至液态的粉料溶剂中，搅拌均匀获得陶瓷浆液；将聚丙烯熔融至液态，将陶瓷浆液与液态的聚丙烯溶液混合搅拌均匀得到混合剂；树脂、有机溶液和分散剂融合在一起呈液态待用。所述陶瓷粉料和粉料溶剂按照体积比7：3混合；所述陶瓷浆料与聚丙烯熔料按照质量比6：4混合。
步骤3，使用步骤2中获得混合剂进行吹塑，获得直径空心球体；
步骤4，将磁性材料灌入螺旋输送器的管道中，将空心球体投入管道中，随着螺旋输送管道内部的转动被输送至管道外。本实施例中，螺旋输送管道水平放置。该结构，既保证了空心球体在螺旋输送器的管道中全方位旋转，空心球体外壁与磁性材料溶液充分融合，保证空心球体外壁每一处都涂抹磁性材料。又保证了空心球体在磁性材料中的放置时间相同，保证了磁性材料在空心球体外壁的厚度一致。
步骤5，将表面包裹了磁性材料的空心球体冷却、烘干。将空心球体使用热风机烘干持续10分钟，随后冷却至室温。
本基于低密度轻质磁性球的脚底按摩器，包括基座，所述基座的内部设有移动板，所述移动板上设有若干个半圆槽，每个半圆槽内放置一个低密度轻质磁性球，所述基座的上表面设有一层布，所述布张紧并将低密度轻质磁性球覆盖；所述移动板的一端使用弹簧与基座的内壁连接，另一端与凸轮连接，所述凸轮由电机控制。
所述布为棉织布。所述若干个半圆槽分布呈椭圆形。
本发明的有益效果是：本发明的基于低密度轻质磁性球的制作方法，获得球体为空心球体，将现有技术中陶瓷浆液与吹塑材料按照比例混合，该混合材料既能获得空心球体，使得陶瓷浆液的原材料均匀分布与空心球体表面。降低了现有技术中内层为聚丙烯空心球体，外层为陶瓷浆液的包覆层的磁性球的密度。本发明的基于低密度轻质磁性球的脚底按摩器，其能够自动移动，使得磁性球能够在足底自动移动进行按摩，方便客户使用；并且其使用的磁性球质量较轻，使得电机与弹簧更易配合，提升按摩效果。
本技术领域技术人员可以理解，除非另外定义，这里使用的所有术语(包括技术术语和科学术语)具有与本申请所属领域中的普通技术人员的一般理解相同的意义。还应该理解的是，诸如通用字典中定义的那些术语应该被理解为具有与现有技术的上下文中的意义一致的意义，并且除非像这里一样定义，不会用理想化或过于正式的含义来解释。
本申请中所述的“和/或”的含义指的是各自单独存在或两者同时存在的情况均包括在内。
本申请中所述的“连接”的含义可以是部件之间的直接连接也可以是部件间通过其它部件的间接连接。
以上述依据本发明的理想实施例为启示，通过上述的说明内容，相关工作人员完全可以在不偏离本项发明技术思想的范围内，进行多样的变更以及修改。本项发明的技术性范围并不局限于说明书上的内容，必须要根据权利要求范围来确定其技术性范围。
Claims (7)
1.一种基于低密度轻质磁性球的制作方法，其特征在于：包括
步骤1，准备原材料，所述原材料包括陶瓷粉料、粉料溶剂、吹塑材料和磁性材料，所述陶瓷粉料包括锆英石、煅烧高岭土、凹凸棒土、泗滨砭石粉和赭石，所述粉料溶剂包括聚丙烯酸钠、羧甲基纤维素钠、糊精和水；所述吹塑材料包括聚丙烯；所述磁性材料包括树脂、有机溶液和分散剂；
步骤2，原材料加工，将锆英石、煅烧高岭土、凹凸棒土、泗滨砭石粉和赭石混合并捣碎碾压呈粉末状的陶瓷粉料，将聚丙烯酸钠、羧甲基纤维素钠、糊精和水混合搅拌均匀呈液态的粉料溶剂，将陶瓷粉料加入至液态的粉料溶剂中，搅拌均匀获得陶瓷浆液；将聚丙烯熔融至液态，将陶瓷浆液与液态的聚丙烯溶液混合搅拌均匀得到混合剂；树脂、有机溶液和分散剂融合在一起呈液态待用；
步骤3，吹塑定型，使用步骤2中获得混合剂进行吹塑，获得空心球体；
步骤4，磁性覆盖，将磁性材料灌入螺旋输送器的管道中，将空心球体投入管道中，随着螺旋输送管道内部的转动被输送至管道外；
步骤5，烘干冷却，将表面包裹了磁性材料的空心球体冷却、烘干。
2.根据权利要求1所述的基于低密度轻质磁性球的制作方法，其特征在于：所述陶瓷粉料的组分为40-50份锆英石、20-30份煅烧高岭土、5-10份凹凸棒土、10-20份泗滨砭石粉和20-30份赭石，所述粉料溶剂的组分为聚丙烯酸钠0.1％、羧甲基纤维素钠0.05％、糊精1.0％和水98.85％；所述陶瓷粉料和粉料溶剂按照体积比7：3混合；所述陶瓷浆料与聚丙烯熔料按照质量比6：4混合。
3.根据权利要求1所述的基于低密度轻质磁性球的制作方法，其特征在于：所述空心球体的直径为1cm。
4.根据权利要求1所述的基于低密度轻质磁性球的制作方法，其特征在于：所述步骤5中，将空心球体使用热风机烘干持续10分钟，随后冷却至室温。
5.一种基于低密度轻质磁性球的脚底按摩器，其特征在于：包括基座(1)，所述基座(1)的内部设有移动板(2)，所述移动板(2)上设有若干个半圆槽，每个半圆槽内放置一个低密度轻质磁性球(3)，所述基座(1)的上表面设有一层布(4)，所述布(4)张紧并将低密度轻质磁性球(3)覆盖；所述移动板(2)的一端使用弹簧(5)与基座(1)的内壁连接，另一端与凸轮(6)连接，所述凸轮(6)由电机(7)控制。
6.根据权利5所述的基于低密度轻质磁性球的脚底按摩器，其特征在于：所述布(4)为棉织布。
7.根据权利5所述的基于低密度轻质磁性球的脚底按摩器，其特征在于：所述若干个半圆槽分布呈椭圆形。