CN112012046A - 一种啤酒标签贴瓶后不变黑镀铝纸的制作方法 - Google Patents
一种啤酒标签贴瓶后不变黑镀铝纸的制作方法 Download PDFInfo
- Publication number
- CN112012046A CN112012046A CN202010830712.1A CN202010830712A CN112012046A CN 112012046 A CN112012046 A CN 112012046A CN 202010830712 A CN202010830712 A CN 202010830712A CN 112012046 A CN112012046 A CN 112012046A
- Authority
- CN
- China
- Prior art keywords
- coating
- paper
- base paper
- glue
- treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种啤酒标签贴瓶后不变黑镀铝纸的制作方法，具体包括以下步骤：S1、将原纸送入涂布机中，由涂布机采用酸性的底涂胶水对该原纸表面进行底涂处理，在原纸表面形成底涂层；S2、将步骤S1中底涂处理后的原纸送入真空镀铝机中，由真空镀铝机将铝加热熔融气化对该原纸进行真空镀铝处理，在原纸正面形成镀铝层；S3、将步骤S2中经过镀铝处理的原纸送入涂布机中，在原纸正面形成面涂层；S4、对面涂处理后形成的镀铝纸再次进行回湿处理；本发明的镀铝纸在于碱性的胶水接触时，可以很好的抑制发黑的现象，同时不需要客户对胶水进行更换，可提高产品的市场竞争力。
Description
技术领域
本发明涉及一种标签和包装领域，具体是一种啤酒标签贴瓶后不变黑镀铝纸的制作方法。
背景技术
如今中国的印刷市场已经趋于饱和，产品已经从单一化向多元化发展，企业没有多元化的产品，则跟随不上消费者的审美观，达不到客户的满意度。在这种情况下中国印刷企业要立足、要发展，必须遵循环保责任、成本节约、质量至上的三大生存原则。在多彩的印刷行业中，利用传统工艺生产的厂家目前还占有一定的数量，而大部分的传统印刷方法是费时间费力、费钱，有时还达不到用户的满意度和政府的环保要求，同时客户对产品的品质要求越来越高，部分客户为了节约自己的成本，不得不使用成本低的原材料，如贴啤酒标的胶水，客户换了成本低的胶水，贴上标签后发现标签表面会发黑的现象，好像发霉了一样，如果在市场上出现这样的产品，肯定不行。
发明内容
本发明的目的在于提供一种啤酒标签贴瓶后不变黑镀铝纸的制作方法，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：
一种啤酒标签贴瓶后不变黑镀铝纸的制作方法，具体包括以下步骤：
S1、将原纸送入涂布机中，由涂布机采用酸性的底涂胶水对该原纸表面进行底涂处理，在原纸表面形成底涂层；
S2、将步骤S1中底涂处理后的原纸送入真空镀铝机中，由真空镀铝机将铝加热熔融气化对该原纸进行真空镀铝处理，在原纸正面形成镀铝层；
S3、将步骤S2中经过镀铝处理的原纸送入涂布机中，由涂布机采用酸性的面涂胶水对该原纸正面进行面涂处理，在原纸正面形成面涂层；面涂层对镀铝层起阻止氧化、增加表面光泽度、对表面镀铝层擦伤起保护的作用；
S4、对面涂处理后形成的镀铝纸再次进行回湿处理，使之达到预定4.0-6.0％的含水量，并保持平整。
进一步的，所述步骤S1中原纸选择用65G湿强纸。
进一步的，所述步骤S1中底涂胶水采用丙烯酸808D树脂,用水稀释到25±2％的固含量，施胶量干重1.7-2.0G/m2
进一步的，所述步骤S2中真空镀铝处理过程形成的镀铝层厚度为1.5-2.5Ω。
再进一步的，所述步骤S2中真空镀铝处理过程形成的镀铝层厚度为1.5Ω。
进一步的，所述步骤S3中的面涂胶水采用丙烯酸808M树脂，用水稀释到20±2％的固含量，施胶量干重0.8-1.0G/m2。
与现有技术相比，本发明的有益效果是：在与PH值偏碱性的胶水接触时，胶水会渗透进原纸，然后先与底涂层的酸性的丙烯酸808D树脂中和，丧失碱性，即使中和过后的碱性还有剩余，而偏厚的镀铝层也会使得，部分的镀铝层与碱反应过后，还可以存留背离胶水一侧表面的镀铝层，从而保持标签不会发黑，而胶水干燥过后，即使胶水还是碱性的由于缺少水，反应也会终止。
本发明的镀铝纸在于碱性的胶水接触时，可以很好的抑制发黑的现象，同时不需要客户对胶水进行更换，可提高产品的市场竞争力。
附图说明
图1为一种啤酒标签贴瓶后不变黑镀铝纸的的示意图。
具体实施方式
下面结合具体实施方式对本专利的技术方案作进一步详细地说明。
针对贴标的胶水研究发现，PH值偏碱性，发黑是由于贴标胶水渗透到镀铝层和铝反应，标签上有油墨看上去就发黑。
实际上单纯的反应物并不是黑色的，铝本来常温下很难和水反应,但在大量OH-存在下,还原性增强,就较易和水反应生成Al(OH)3,
铝本来常温下很难和水反应,但在大量OH-存在下,还原性增强,就较易和水反应生成Al(OH)3,两性的Al(OH)3继而和NaOH反应生成偏铝酸钠和水。
在镀铝层与与这种胶水接触时，
首先镀铝层表面的氧化膜先参与反应：
反应方程式为：AL2O3+2OH-+3H2O＝＝2AL(OH)3
然后铝参与反应：
反应方程式为：2Al+6H2O→2Al(OH)3+3H2↑
然后两性的Al(OH)3继而和NaOH反应：
反应方程式为：Al(OH)3+NaOH→Na[Al(OH)4]
其中无论是2AL(OH)3还是Na[Al(OH)4]都不是黑色的而是白色，但是由于镀铝层反应后消失丧失本身的光亮效果，然后加上标签上有油墨，因而看上去就会发黑；
如果要消除这种现象，可以从三方面入手，首先：改变胶水的PH值偏碱性的状况，要求客户改用中性的胶水，但是由于客户因为本身是因为成本问题，换了PH值偏碱性的成本低胶水，所以不现实，所以要从另外的角度入手；
其次：则是增加镀铝层的厚度，使得反应过后，还可以存留背离胶水一侧表面的镀铝层，从而保持标签不会发黑；
最后：减少水含量，先抑制铝第一步与水的反应，胶水采用水作为溶剂成本是最低的，如果采用另外的溶剂成本过高。
因此，啤酒标签贴瓶后不变黑镀铝纸的制作方法，大致就包括：第一，消除胶水的PH值偏碱性的影响；第二，增加镀铝层的厚度。
一种啤酒标签贴瓶后不变黑镀铝纸的制作方法，具体包括以下步骤：
S1、将原纸100送入涂布机中，由涂布机采用底涂胶水对该原纸100表面进行底涂处理，在原纸100表面形成底涂层200，原纸100选择用65G湿强纸；
底涂胶水采用丙烯酸808D树脂,用水稀释到25±2％的固含量，
施胶量干重1.7-2.0G/m2；
S2、将步骤S1中底涂处理后的原纸100送入真空镀铝机中，由真空镀铝机将铝加热熔融气化对该原纸100进行真空镀铝处理，在原纸100正面形成镀铝层300，该真空镀铝处理过程形成的镀铝层300厚度为1.5-2.5Ω(块电阻测量法)，本实施例中优选为，镀铝层300厚度为1.5Ω；
S3、将步骤S2中经过镀铝处理的原纸100送入涂布机中，由涂布机采用面涂胶水对该原纸100正面进行面涂处理，在原纸100正面形成面涂层400；面涂层400对镀铝层300起阻止氧化、增加表面光泽度、对表面镀铝层300擦伤起保护的作用，
面涂胶水采用丙烯酸808M树脂，用水稀释到20±2％的固含量，施胶量干重0.8-1.0G/m2；
S4、对面涂处理后形成的镀铝纸再次进行回湿处理，使之达到预定4.0-6.0％的含水量，并保持平整，然后进行后续的印刷、分切等工序；
本实施例的镀铝纸，在与PH值偏碱性的胶水接触时，胶水会渗透进原纸100，然后先与底涂层200的酸性的丙烯酸808D树脂中和，丧失碱性，即使中和过后的碱性还有剩余，而偏厚的镀铝层300也会使得，部分的镀铝层300与碱反应过后，还可以存留背离胶水一侧表面的镀铝层300，从而保持标签不会发黑，而胶水干燥过后，即使胶水还是碱性的由于缺少水，反应也会终止。
上面对本专利的较佳实施方式作了详细说明，但是本专利并不限于上述实施方式，在本领域的普通技术人员所具备的知识范围内，还可以在不脱离本专利宗旨的前提下做出各种变化。
Claims (6)
1.一种啤酒标签贴瓶后不变黑镀铝纸的制作方法，其特征在于，具体包括以下步骤：
S1、将原纸送入涂布机中，由涂布机采用酸性的底涂胶水对该原纸表面进行底涂处理，在原纸表面形成底涂层；
S2、将步骤S1中底涂处理后的原纸送入真空镀铝机中，由真空镀铝机将铝加热熔融气化对该原纸进行真空镀铝处理，在原纸正面形成镀铝层；
S3、将步骤S2中经过镀铝处理的原纸送入涂布机中，由涂布机采用酸性的面涂胶水对该原纸正面进行面涂处理，在原纸正面形成面涂层；面涂层对镀铝层起阻止氧化、增加表面光泽度、对表面镀铝层擦伤起保护的作用；
S4、对面涂处理后形成的镀铝纸再次进行回湿处理，使之达到预定4.0-6.0％的含水量，并保持平整。
2.根据权利要求1所述的一种啤酒标签贴瓶后不变黑镀铝纸的制作方法，其特征在于，所述步骤S1中原纸选择用65G湿强纸。
3.根据权利要求1所述的一种啤酒标签贴瓶后不变黑镀铝纸的制作方法，其特征在于，所述步骤S1中底涂胶水采用丙烯酸808D树脂,用水稀释到25±2％的固含量，施胶量干重1.7-2.0G/m2。
4.根据权利要求1所述的一种啤酒标签贴瓶后不变黑镀铝纸的制作方法，其特征在于，所述步骤S2中真空镀铝处理过程形成的镀铝层厚度为1.5-2.5Ω。
5.根据权利要求1所述的一种啤酒标签贴瓶后不变黑镀铝纸的制作方法，其特征在于，所述步骤S2中真空镀铝处理过程形成的镀铝层厚度为1.5Ω。
6.根据权利要求1所述的一种啤酒标签贴瓶后不变黑镀铝纸的制作方法，其特征在于，所述步骤S3中的面涂胶水采用丙烯酸808M树脂，用水稀释到20±2％的固含量，施胶量干重0.8-1.0G/m2。