CN111978911A - Production process of plastic glue - Google Patents
Production process of plastic glue Download PDFInfo
- Publication number
- CN111978911A CN111978911A CN202010792041.4A CN202010792041A CN111978911A CN 111978911 A CN111978911 A CN 111978911A CN 202010792041 A CN202010792041 A CN 202010792041A CN 111978911 A CN111978911 A CN 111978911A
- Authority
- CN
- China
- Prior art keywords
- plastic
- glue
- production
- finished
- rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production process of plastic cement, which comprises the following steps: s1: the production preparation of the plastic A glue is reserved, and the raw materials of the plastic A glue comprise polyether polyol, paraffin and MDI; s2: preparing plastic B glue for later use, wherein the raw materials of the plastic B glue comprise polyether polyol, paraffin and a filler; s3: particle production: mixing raw materials of stone powder and colloidal particles, mixing the materials by an internal mixer, extruding and molding semi-finished rubber by an extruder, vulcanizing the semi-finished rubber in a steaming cylinder respectively to heat the rubber material and crosslink rubber molecules, and crushing the rubber material in a crusher to obtain finished particles. The invention adopts simple preparation principle and production process flow, the required equipment is conventional equipment, the production and preparation of the plastic glue are convenient, the plastic glue, color paste, silicon PU and particles are used for paving plastic runways and basketball courts, the plastic glue, the color paste, the silicon PU and the particles can be qualified through GB36246-2018 detection, and the plastic glue is an environment-friendly product.
Description
Technical Field
The invention belongs to the technical field of plastic cement, and particularly relates to a production process of plastic cement.
Background
The plastic cement is mainly used for various plastics, can be used for paving plastic runways and basketball courts together with color paste, silicon PU and particles, but the basic reaction principle of the existing plastic cement preparation is complex, production equipment is not conventional equipment, the production process is complex, and the environmental protection performance is not good.
Disclosure of Invention
The invention aims to provide a production process of plastic cement to solve the problems in the background technology.
In order to achieve the purpose, the invention provides the following technical scheme: a production process of plastic cement comprises the following steps:
s1: the production preparation of the plastic A glue is reserved, and the raw materials of the plastic A glue comprise polyether polyol, paraffin and MDI;
s2: preparing plastic B glue for later use, wherein the raw materials of the plastic B glue comprise polyether polyol, paraffin and a filler;
s3: particle production:
mixing raw materials of stone powder and colloidal particles, mixing the materials by an internal mixer, extruding and molding semi-finished rubber by an extruder, vulcanizing the semi-finished rubber in a steaming cylinder respectively to heat the rubber material and cross-link rubber molecules, changing the structure of the rubber molecules from a linear structure into a net-shaped structure to obtain a product with certain physical and mechanical properties, and crushing the product into finished particles by a crusher respectively.
Preferably, the production and preparation of the plastic A glue comprises the following specific steps: and (3) putting a certain amount of polyether polyol, paraffin and MDI into a reaction kettle, heating the reaction kettle I to 80 ℃, stirring and synthesizing, and discharging the materials after keeping the temperature for 4 hours to obtain the plastic A glue.
Preferably, the temperature of the reaction kettle I is increased to 80 ℃ by adopting a steam heating mode.
Preferably, the production and preparation of the plastic cement B glue comprises the following specific steps: and (3) putting a certain amount of polyether polyol, paraffin and filler into a reaction kettle, heating the reaction kettle II to 80 ℃ for dehydration, preserving the heat for 6 hours, transferring into a stirring kettle for stirring after the dehydration is finished, transferring into a grinding kettle for grinding after the stirring is finished, and discharging the materials after the grinding is finished to obtain the plastic B glue.
Preferably, the temperature of the reaction kettle II is increased to 80 ℃ by adopting a steam heating mode.
Compared with the prior art, the invention has the beneficial effects that: the production process of the plastic cement provided by the invention adopts a simple preparation principle and a production process flow, required equipment is conventional equipment, the production and preparation of the plastic cement are convenient, the plastic cement, color paste, silicon PU and particles are used for paving plastic runways and basketball courts, the plastic cement, the color paste, the silicon PU and the particles can be qualified through GB36246-2018 detection, and the plastic cement is an environment-friendly product.
Drawings
FIG. 1 is a schematic diagram of the basic reaction principle of the production and preparation of the plastic class A glue of the present invention;
FIG. 2 is a schematic view of a production process of the plastic class A glue of the present invention;
FIG. 3 is a schematic diagram of a production process of the plastic glue B of the present invention;
FIG. 4 is a schematic process flow diagram for the production of pellets according to the present invention.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the drawings in the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
Example 1
The invention provides a production process of plastic cement as shown in figures 1-4, which comprises the following steps:
s1: the production preparation of the plastic A glue is reserved, and the raw materials of the plastic A glue comprise polyether polyol, paraffin and MDI;
s2: preparing plastic B glue for later use, wherein the raw materials of the plastic B glue comprise polyether polyol, paraffin and a filler;
s3: particle production:
mixing raw materials of stone powder and colloidal particles, mixing the materials by an internal mixer, extruding and molding semi-finished rubber by an extruder, vulcanizing the semi-finished rubber in a steaming cylinder respectively to heat the rubber material and cross-link rubber molecules, changing the structure of the rubber molecules from a linear structure into a net-shaped structure to obtain a product with certain physical and mechanical properties, and crushing the product into finished particles by a crusher respectively.
Specifically, the production and preparation of the plastic A glue comprises the following specific steps: and (3) putting a certain amount of polyether polyol, paraffin and MDI into a reaction kettle, heating the reaction kettle I to 80 ℃, stirring and synthesizing, and discharging the materials after keeping the temperature for 4 hours to obtain the plastic A glue.
Specifically, the temperature of the reaction kettle I is increased to 80 ℃ by adopting a steam heating mode.
Specifically, the production and preparation of the plastic B-type glue comprises the following specific steps: and (3) putting a certain amount of polyether polyol, paraffin and filler into a reaction kettle, heating the reaction kettle II to 80 ℃ for dehydration, preserving the heat for 6 hours, transferring into a stirring kettle for stirring after the dehydration is finished, transferring into a grinding kettle for grinding after the stirring is finished, and discharging the materials after the grinding is finished to obtain the plastic B glue.
Specifically, the temperature of the reaction kettle II is increased to 80 ℃ by adopting a steam heating mode.
In conclusion, compared with the prior art, the plastic cement adopts a simple preparation principle and a simple production process flow, the required equipment is conventional equipment, the production and the preparation of the plastic cement are convenient, the plastic cement, the color paste, the silicon PU and the particles are used for paving plastic runways and basketball courts, the plastic cement, the color paste, the silicon PU and the particles can be qualified through GB36246-2018 detection, and the plastic cement is an environment-friendly product.
Finally, it should be noted that: although the present invention has been described in detail with reference to the foregoing embodiments, it will be apparent to those skilled in the art that modifications may be made to the embodiments or portions thereof without departing from the spirit and scope of the invention.
Claims (5)
1. A production process of plastic cement is characterized in that: the method comprises the following steps:
s1: the production preparation of the plastic A glue is reserved, and the raw materials of the plastic A glue comprise polyether polyol, paraffin and MDI;
s2: preparing plastic B glue for later use, wherein the raw materials of the plastic B glue comprise polyether polyol, paraffin and a filler;
s3: particle production:
mixing raw materials of stone powder and colloidal particles, mixing the materials by an internal mixer, extruding and molding semi-finished rubber by an extruder, vulcanizing the semi-finished rubber in a steaming cylinder respectively to heat the rubber material and cross-link rubber molecules, changing the structure of the rubber molecules from a linear structure into a net-shaped structure to obtain a product with certain physical and mechanical properties, and crushing the product into finished particles by a crusher respectively.
2. The process for producing plastic cement according to claim 1, wherein: the production and preparation method of the plastic A glue comprises the following specific steps: and (3) putting a certain amount of polyether polyol, paraffin and MDI into a reaction kettle, heating the reaction kettle I to 80 ℃, stirring and synthesizing, and discharging the materials after keeping the temperature for 4 hours to obtain the plastic A glue.
3. The process for producing plastic cement according to claim 2, wherein: and the temperature of the reaction kettle I is increased to 80 ℃ by adopting a steam heating mode.
4. The process for producing plastic cement according to claim 1, wherein: the production and preparation method of the plastic B glue comprises the following specific steps: and (3) putting a certain amount of polyether polyol, paraffin and filler into a reaction kettle, heating the reaction kettle II to 80 ℃ for dehydration, preserving the heat for 6 hours, transferring into a stirring kettle for stirring after the dehydration is finished, transferring into a grinding kettle for grinding after the stirring is finished, and discharging the materials after the grinding is finished to obtain the plastic B glue.
5. The process for producing plastic cement according to claim 4, wherein: and the reaction kettle II is heated to 80 ℃ in a steam heating mode.