CN107141773A - A kind of environment-friendly polyurethane plastic cement race track and preparation method thereof - Google Patents
A kind of environment-friendly polyurethane plastic cement race track and preparation method thereof Download PDFInfo
- Publication number
- CN107141773A CN107141773A CN201710479845.7A CN201710479845A CN107141773A CN 107141773 A CN107141773 A CN 107141773A CN 201710479845 A CN201710479845 A CN 201710479845A CN 107141773 A CN107141773 A CN 107141773A
- Authority
- CN
- China
- Prior art keywords
- parts
- plastic cement
- race track
- cement race
- environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of environment-friendly polyurethane plastic cement race track and preparation method thereof, it is prepared from by the raw material of following parts by weight：130 150 parts of polyisocyanates, 100 120 parts of PPG, 10 20 parts of chlorobenzoyl chloride, 30 50 parts of paraffin oil, 40 60 parts of inorganic filler, 60 80 parts of toluene, 30 40 parts of hydrogen peroxide, 20 35 parts of plasticizer, 5 10 parts of curing agent, 10 20 parts of antioxidant, 36 parts of pigment.Plastic cement race track surface particles produced by the present invention are difficult for drop-off, surfacing, the quality and its service life for improving plastic cement race track, greatly improve the qualification rate of plastic cement race track, more than 95% is brought up to by current 82%, therefore current plastic cement race track service life is substantially improved short, anti-skid slip limiting performance is reduced, the problem of maintenance rate is high, reduce manufacturing cost and use cost, and, raw material used in the present invention is ep-type material, belong to environmentally friendly material, it is to avoid environmental pollution, for the health and safety of sporter provide guarantee.
Description
Technical field
The present invention relates to plastic material field, more particularly, to a kind of environment-friendly polyurethane plastic cement race track and preparation method thereof.
Background technology
Polyurethane full name is polyurethanes, is containing the macromolecular compound for repeating carbamate groups on main chain
General designation.Polyurethane has the superiority such as remarkable wearability, high intensity, high elongation rate, high resiliency, oil resistant, the radiation of resistance to ray
Energy.Polyurethane, which is applied to pavement, has that flatness is good, compression strength is high, the elastic appropriate, spy of stable physical property of hardness
Property, and with certain elasticity and color, with certain anti-uv-ray and ageing-resistant ability.
Traditional polyurethane pavement product is all toluene di-isocyanate(TDI) (TDI) type, due to TDI polyurethane runways
The heavy metal substance inside contained, understands oxidation stain environment in use.In addition, also containing a variety of in TDI polyurethane components
Catalyst (leaded, mercury, tin), binary amine chain extender, organic molecule plasticizer, solvent, rubber chemicals and double benzene solvents etc.
Toxic and harmful substance, has undesirable effect to human body and equal environment.And environment-friendly type '-diphenylmethane diisocyanate (MDI)
Have the advantages that small toxicity, influence small to human health damage, to environment are smaller, the need for more meeting current environmental protection.
The content of the invention
Meet environmental requirement and the superior environment-friendly polyurethane plastic cement race of combination property it is an object of the invention to provide a kind of
Road and preparation method thereof.
In order to achieve the above object, the present invention is achieved through the following technical solutions：
A kind of environment-friendly polyurethane plastic cement race track, it is prepared from by the raw material of following parts by weight：Polyisocyanates 130-150
Part, 100-120 parts of PPG, 10-20 parts of chlorobenzoyl chloride, 30-50 parts of paraffin oil, 40-60 parts of inorganic filler, toluene 60-
80 parts, 30-40 parts of hydrogen peroxide, 20-35 parts of plasticizer, 5-10 parts of curing agent, 10-20 parts of antioxidant, 3-6 parts of pigment.
Further, 130 parts of the polyisocyanates, 100 parts of PPG, 10 parts of chlorobenzoyl chloride, paraffin oil 30
Part, 40 parts of inorganic filler, 80 parts of toluene, 30 parts of hydrogen peroxide, 20 parts of plasticizer, 5 parts of curing agent, 10 parts of antioxidant, pigment 3
Part.
Further, 140 parts of the polyisocyanates, 110 parts of PPG, 15 parts of chlorobenzoyl chloride, 40 parts of paraffin oil,
50 parts of inorganic filler, 70 parts of toluene, 35 parts of hydrogen peroxide, 28 parts of plasticizer, 8 parts of curing agent, 15 parts of antioxidant, 4.5 parts of pigment.
Further, 150 parts of the polyisocyanates, 120 parts of PPG, 20 parts of chlorobenzoyl chloride, paraffin oil 50
Part, 60 parts of inorganic filler, 80 parts of toluene, 40 parts of hydrogen peroxide, 35 parts of plasticizer, 10 parts of curing agent, 20 parts of antioxidant, pigment 6
Part.
Further, described polyisocyanates is Toluene-2,4-diisocyanate, 4- diisocyanate or methyl diphenylene diisocyanate.
Further, described PPG is polyethers 330N or polyethers 3050.
Further, described inorganic filler is one kind or many in calcium carbonate, kaolin, clay, barite, white carbon
Plant mixture.
Further, described plasticizer is diethyl phthalate, ATBC or chlorocosanes.
Further, the preparation method of environment-friendly polyurethane plastic cement race track of the invention, comprises the following steps：
(1) take each raw material to put into after mixing in closed white silk glue machine by the weight proportion to be kneaded, melting temperature is
110-120 DEG C, mixing time is 14-16 minutes；Put into conche and refined again after mixing, the mixed degree of refining is 85-90
DEG C, refining time be 7-10 minutes, obtain refining mixture；
(2) it is 120-140 DEG C refining mixture input agent to be gone out into temperature control in machine continuous sheeting, extruder；So
Decorative pattern is extruded by calender again afterwards, calender temperature controls at 95-100 DEG C, enters back into hot-air channel and vulcanized, and heat is empty
The temperature of gas passage is 140-160 DEG C, and finished product can be obtained after cooling.
The present invention compared with prior art, with following beneficial effect：
(1) plastic cement race track surface particles produced by the present invention are difficult for drop-off, surfacing, the quality for improving plastic cement race track
And its service life, the qualification rate of plastic cement race track is greatly improved, more than 95% is brought up to by current 82%, therefore change significantly
Current plastic cement race track service life has been apt to it short, anti-skid slip limiting performance reduction, the problem of maintenance rate is high reduces manufacturing cost and made
With cost, moreover, the raw material used in the present invention is ep-type material, belong to environmentally friendly material, it is to avoid environmental pollution,
Guarantee is provided for the health and safety of sporter；
(2) chlorobenzoyl chloride, paraffin oil and inorganic filler that the present invention is accordingly matched by addition etc., then can by proportioning mixing
Obtained optimization plastic material, improves the weatherability of plastic material, the problems such as the easy aging of plastic material is solved, while also protecting
Demonstrate,prove surface layer particle difficult for drop-off, and improve antiskid performance；
(3) the polyethers 330N or polyethers 3050 that the present invention is used, can improve 3-5 by the NCO% of Isocyanate prepolymers body
Point, can be such that it reacts completely, it is ensured that the stability of material, and improve the physical and mechanical properties of material.
Embodiment
Concrete technical scheme of the invention described further below, in order to which those skilled in the art is further understood that
The present invention, without constituting the limitation to its right.
Embodiment 1：
A kind of environment-friendly polyurethane plastic cement race track, it is prepared from by the raw material of following parts by weight：130 parts of polyisocyanates,
100 parts of PPG, 10 parts of chlorobenzoyl chloride, 30 parts of paraffin oil, 40 parts of inorganic filler, 80 parts of toluene, 30 parts of hydrogen peroxide, plasticising
20 parts of agent, 5 parts of curing agent, 10 parts of antioxidant, 3 parts of pigment.
The preparation method step of the environment-friendly polyurethane plastic cement race track is as follows：
(1) take each raw material to put into after mixing in closed white silk glue machine by the weight proportion to be kneaded, melting temperature is 1
10 DEG C, mixing time is 14 minutes；Put into conche and refined again after mixing, the mixed degree of refining is 85 DEG C, refining time is 7
Minute, obtain refining mixture；
(2) it is 120 DEG C refining mixture input agent to be gone out into temperature control in machine continuous sheeting, extruder, extrusion speed
Spend for 3 ms/min；Then again by calender extrude decorative pattern, calender temperature control at 95-100 DEG C, embossing speed be 2 meters/
Minute, enter back into hot-air channel and vulcanized, the temperature of hot-air channel is 140 DEG C, and finished product can be obtained after cooling.
Embodiment 2：
A kind of environment-friendly polyurethane plastic cement race track, it is prepared from by the raw material of following parts by weight：140 parts of polyisocyanates,
110 parts of PPG, 15 parts of chlorobenzoyl chloride, 40 parts of paraffin oil, 50 parts of inorganic filler, 70 parts of toluene, 35 parts of hydrogen peroxide, plasticising
28 parts of agent, 8 parts of curing agent, 15 parts of antioxidant, 4.5 parts of pigment.
The preparation method step of the environment-friendly polyurethane plastic cement race track is as follows：
(1) take each raw material to put into after mixing in closed white silk glue machine by the weight proportion to be kneaded, melting temperature is 1
15 DEG C, mixing time is 15 minutes；Put into conche and refined again after mixing, the mixed degree of refining is 88 DEG C, refining time is 9
Minute, obtain refining mixture；
(2) it is 130 DEG C refining mixture input agent to be gone out into temperature control in machine continuous sheeting, extruder, extrusion speed
Spend for 3 ms/min；Then decorative pattern is extruded by calender again, calender temperature is controlled at 98 DEG C, embossing speed is 2 ms/min
Clock, enters back into hot-air channel and is vulcanized, and the temperature of hot-air channel is 150 DEG C, and finished product can be obtained after cooling.
Embodiment 3：
A kind of environment-friendly polyurethane plastic cement race track, it is prepared from by the raw material of following parts by weight：150 parts of polyisocyanates,
120 parts of PPG, 20 parts of chlorobenzoyl chloride, 50 parts of paraffin oil, 60 parts of inorganic filler, 80 parts of toluene, 40 parts of hydrogen peroxide, plasticising
35 parts of agent, 10 parts of curing agent, 20 parts of antioxidant, 6 parts of pigment.
The preparation method step of the environment-friendly polyurethane plastic cement race track is as follows：
(1) take each raw material to put into after mixing in closed white silk glue machine by the weight proportion to be kneaded, melting temperature is 1
20 DEG C, mixing time is 16 minutes；Put into conche and refined again after mixing, the mixed degree of refining is 90 DEG C, refining time is
10 minutes, obtain refining mixture；
(2) it is 140 DEG C refining mixture input agent to be gone out into temperature control in machine continuous sheeting, extruder, extrusion speed
Spend for 3 ms/min；Then decorative pattern is extruded by calender again, calender temperature is controlled at 100 DEG C, embossing speed is 2 ms/min
Clock, enters back into hot-air channel and is vulcanized, and the temperature of hot-air channel is 160 DEG C, and finished product can be obtained after cooling.
Embodiment 4：
A kind of environment-friendly polyurethane plastic cement race track, it is prepared from by the raw material of following parts by weight：135 parts of polyisocyanates,
115 parts of PPG, 13 parts of chlorobenzoyl chloride, 38 parts of paraffin oil, 55 parts of inorganic filler, 65 parts of toluene, 38 parts of hydrogen peroxide, plasticising
30 parts of agent, 6 parts of curing agent, 13 parts of antioxidant, 4 parts of pigment.
The preparation method step of the environment-friendly polyurethane plastic cement race track is as follows：
(1) take each raw material to put into after mixing in closed white silk glue machine by the weight proportion to be kneaded, melting temperature is 1
18 DEG C, mixing time is 15 minutes；Put into conche and refined again after mixing, the mixed degree of refining is 88 DEG C, refining time is 9
Minute, obtain refining mixture；
(2) it is 136 DEG C refining mixture input agent to be gone out into temperature control in machine continuous sheeting, extruder, extrusion speed
Spend for 3 ms/min；Then decorative pattern is extruded by calender again, calender temperature is controlled at 98 DEG C, embossing speed is 2 ms/min
Clock, enters back into hot-air channel and is vulcanized, and the temperature of hot-air channel is 155 DEG C, and finished product can be obtained after cooling.
Embodiment 5：
A kind of environment-friendly polyurethane plastic cement race track, it is prepared from by the raw material of following parts by weight：145 parts of polyisocyanates,
105 parts of PPG, 18 parts of chlorobenzoyl chloride, 48 parts of paraffin oil, 44 parts of inorganic filler, 76 parts of toluene, 32 parts of hydrogen peroxide, plasticising
25 parts of agent, 8 parts of curing agent, 17 parts of antioxidant, 5.5 parts of pigment.
The preparation method step of the environment-friendly polyurethane plastic cement race track is as follows：
(3) take each raw material to put into after mixing in closed white silk glue machine by the weight proportion to be kneaded, melting temperature is 1
12 DEG C, mixing time is 15 minutes；Put into conche and refined again after mixing, the mixed degree of refining is 86 DEG C, refining time is 8
Minute, obtain refining mixture；
(4) it is 125 DEG C refining mixture input agent to be gone out into temperature control in machine continuous sheeting, extruder, extrusion speed
Spend for 3 ms/min；Then decorative pattern is extruded by calender again, calender temperature is controlled at 96 DEG C, embossing speed is 2 ms/min
Clock, enters back into hot-air channel and is vulcanized, and the temperature of hot-air channel is 145 DEG C, and finished product can be obtained after cooling.
Service check is carried out to environment-friendly polyurethane plastic cement race track prepared by above-mentioned 5 embodiments below, wherein being compareed
Group 1 is to use application notification number polyurethane plastic runway made from the preparation method described in CN106700497A；Control group 2
To use Authorization Notice No. plastic cement race track made from the preparation method described in CN106677008A；Specific performance assay is such as
Shown in following table：
Above-mentioned detection project is measured according to the regulation of GB/T14833-1993.
The property indices of environment-friendly polyurethane plastic cement race track prepared by the present invention are equal it can be seen from above table data
In the range of national regulations, wherein tensile strength, compression recovery rate, elongation at break and impact elasticity are far above national standard, and
Being compared with other two contrast experiments examples has obvious advantage, thus environment-friendly polyurethane plastic cement race track of the invention have it is excellent
Mechanical property, there is higher intensity, hardness, wearability and anti-aging.
Plastic cement race track surface particles produced by the present invention are difficult for drop-off, surfacing, the quality for improving plastic cement race track and
Its service life, greatly improves the qualification rate of plastic cement race track, brings up to more than 95% by current 82%, therefore substantially improve
Current plastic cement race track service life is short, and anti-skid slip limiting performance reduction, the problem of maintenance rate is high reduces manufacturing cost and used
Cost, moreover, the raw material used in the present invention is ep-type material, belong to environmentally friendly material, it is to avoid environmental pollution, is
The health and safety of sporter, which are provided, to be ensured.
The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention, although with reference to foregoing reality
Apply example the present invention is described in detail, for those skilled in the art, it still can be to foregoing each implementation
Technical scheme described in example is modified, or carries out equivalent substitution to which part technical characteristic.All essences in the present invention
God is with principle, and any modification, equivalent substitution and improvements made etc. should be included in the scope of the protection.
Claims (9)
1. a kind of environment-friendly polyurethane plastic cement race track, it is characterised in that it is prepared from by the raw material of following parts by weight：Polyisocyanic acid
130-150 parts of ester, 100-120 parts of PPG, 10-20 parts of chlorobenzoyl chloride, 30-50 parts of paraffin oil, inorganic filler 40-60
Part, 60-80 parts of toluene, 30-40 parts of hydrogen peroxide, 20-35 parts of plasticizer, 5-10 parts of curing agent, 10-20 parts of antioxidant, pigment
3-6 parts.
2. environment-friendly polyurethane plastic cement race track according to claim 1, it is characterised in that 130 parts of the polyisocyanates, gathers
100 parts of ethoxylated polyhydric alcohol, 10 parts of chlorobenzoyl chloride, 30 parts of paraffin oil, 40 parts of inorganic filler, 80 parts of toluene, 30 parts of hydrogen peroxide, plasticizer
20 parts, 5 parts of curing agent, 10 parts of antioxidant, 3 parts of pigment.
3. environment-friendly polyurethane plastic cement race track according to claim 1, it is characterised in that 140 parts of the polyisocyanates, gathers
110 parts of ethoxylated polyhydric alcohol, 15 parts of chlorobenzoyl chloride, 40 parts of paraffin oil, 50 parts of inorganic filler, 70 parts of toluene, 35 parts of hydrogen peroxide, plasticizer
28 parts, 8 parts of curing agent, 15 parts of antioxidant, 4.5 parts of pigment.
4. environment-friendly polyurethane plastic cement race track according to claim 1, it is characterised in that 150 parts of the polyisocyanates, gathers
120 parts of ethoxylated polyhydric alcohol, 20 parts of chlorobenzoyl chloride, 50 parts of paraffin oil, 60 parts of inorganic filler, 80 parts of toluene, 40 parts of hydrogen peroxide, plasticizer
35 parts, 10 parts of curing agent, 20 parts of antioxidant, 6 parts of pigment.
5. environment-friendly polyurethane plastic cement race track according to claim 1, it is characterised in that described polyisocyanates is first
Benzene -2,4- diisocyanate or methyl diphenylene diisocyanate.
6. environment-friendly polyurethane plastic cement race track according to claim 1, it is characterised in that described PPG is polyethers
330N or polyethers 3050.
7. environment-friendly polyurethane plastic cement race track according to claim 1, it is characterised in that described inorganic filler is carbonic acid
One or more mixtures in calcium, kaolin, clay, barite, white carbon.
8. environment-friendly polyurethane plastic cement race track according to claim 1, it is characterised in that described plasticizer is O-phthalic
Diethyl phthalate, ATBC or chlorocosanes.
9. the preparation method of the environment-friendly polyurethane plastic cement race track according to claim any one of 1-8, it is characterised in that including
Following steps：
Take each raw material to put into after mixing in closed white silk glue machine by the weight proportion to be kneaded, melting temperature is 110-120
DEG C, mixing time is 14-16 minutes；Put into conche and refined again after mixing, when refining mixes degree for 85-90 DEG C, refining
Between be 7-10 minutes, obtain refining mixture；
It is 120-140 DEG C that refining mixture input agent is gone out into temperature control in machine continuous sheeting, extruder；Then pass through again
Calender extrudes decorative pattern, and calender temperature controls at 95-100 DEG C, enters back into hot-air channel and vulcanized, hot-air channel
Temperature is 140-160 DEG C, and finished product can be obtained after cooling.