CN111974933A - 一种建筑钢模脱模剂 - Google Patents
一种建筑钢模脱模剂 Download PDFInfo
- Publication number
- CN111974933A CN111974933A CN202011019536.XA CN202011019536A CN111974933A CN 111974933 A CN111974933 A CN 111974933A CN 202011019536 A CN202011019536 A CN 202011019536A CN 111974933 A CN111974933 A CN 111974933A
- Authority
- CN
- China
- Prior art keywords
- agent
- polyvinyl alcohol
- building steel
- ethanol
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明的目的在于提供一种建筑钢模脱模剂，用以提高建筑钢模的脱模效果。为实现上述目的，本发明提供如下技术方案：一种建筑钢模脱模剂，其特征在于：其组分按质量百分数配比为：聚乙烯醇7‑10%，乙醇24‑58%，水58‑29%，成膜剂5‑7%，防锈剂0.95%，消泡剂0.04‑0.06%，配制方法：按上述比例称取原材料，首先将聚乙烯醇树脂在室温条件下加入到水中浸泡5小时左右，然后升温至95‑1000C，同时不断搅拌，在此温度下保持1个小时左右，待全部溶解后，将其冷却至常温，然后滴加乙醇，并同时加入消泡剂，最后加入成膜剂和防锈剂，搅拌均匀后静置，得到成品。
Description
技术领域
本发明公开了一种建筑钢模脱模剂。
背景技术
目前，建筑钢模脱模剂没有统一、标准的配方产品，使用较多的是普通乳化液，但其成膜性能差、脱模效果不佳。
发明内容
本发明的目的在于提供一种建筑钢模脱模剂，用以提高建筑钢模的脱模效果。
为实现上述目的，本发明提供如下技术方案：一种建筑钢模脱模剂，其特征在于：其组分按质量百分数配比为：聚乙烯醇7-10%，乙醇24-58%，水58-29%，成膜剂5-7%，防锈剂0.95%，消泡剂0.04-0.06%，配制方法：按上述比例称取原材料，首先将聚乙烯醇树脂在室温条件下加入到水中浸泡5小时左右，然后升温至95-1000C，同时不断搅拌，在此温度下保持1个小时左右，待全部溶解后，将其冷却至常温，然后滴加乙醇，并同时加入消泡剂，最后加入成膜剂和防锈剂，搅拌均匀后静置，得到成品。
本发明的进一步改进在于：以聚乙烯醇作为脱模剂主体材料，其具有无毒、无刺激性，具有良好的水溶性、润滑性、保湿性、分散性，且具有优良的粘接性能，是比较理想的钢模脱模剂主材料。
本发明的进一步改进在于：成膜剂为甘油；防锈剂为苯甲酸钠；消泡剂为环氧乙烷、聚丙二醇、硬脂酸锌按质量比3:2:1的混合物。
本发明的进一步改进在于：其组分按质量百分数配比包括：聚乙烯醇7%，乙醇40%，水46%，成膜剂6%，防锈剂0.95%，消泡剂0.05%。
本发明的进一步改进在于：其组分按质量百分数配比包括：聚乙烯醇8%，乙醇36%，水48%，成膜剂7%，防锈剂0.95%，消泡剂0.05%。
本发明的进一步改进在于：其组分按质量百分数配比包括：聚乙烯醇9%，乙醇35%，水50%，成膜剂5%，防锈剂0.95%，消泡剂0.05%。
本发明的进一步改进在于：其组分按质量百分数配比包括：聚乙烯醇10%，乙醇32%，水52%，成膜剂5%，防锈剂0.95%，消泡剂0.05%。
与现有技术相比，本发明的有益效果是：
本发明具有成膜性好、脱模效果佳、性状稳定、无毒无刺激性、环保等优点。
具体实施方式：
下面将结合本发明实的施例，对本发明实施例中的技术方案进行较为完整的描述，但所描述的实施例仅是本发明的一部分，即本发明包括但不限于这些实施例。
本实施例提供一种技术方案：一种建筑钢模脱模剂，其特征在于：其组分按质量百分数配比为：聚乙烯醇7-10%，乙醇24-58%，水58-29%，成膜剂5-7%，防锈剂0.95%，消泡剂0.04-0.06%，配制方法：按上述比例称取原材料，首先将聚乙烯醇树脂在室温条件下加入到水中浸泡5小时左右，然后升温至95-1000C,同时不断搅拌，在此温度下保持1个小时左右，待全部溶解后，将其冷却至常温，然后滴加乙醇，并同时加入消泡剂，最后加入成膜剂和防锈剂，搅拌均匀后静置，得到成品。
所述成膜剂为甘油；所述防锈剂为苯甲酸钠；所述消泡剂为环氧乙烷、聚丙二醇、硬脂酸锌按质量比3:2:1的混合物。
实施例1
一种建筑钢模脱模剂，其组分按质量百分数配比包括：聚乙烯醇7%，乙醇40%，水46%，成膜剂6%，防锈剂0.95%，消泡剂0.05%，配制方法：按上述比例称取原材料，首先将聚乙烯醇树脂在室温条件下加入到水中浸泡5小时左右，然后升温至95-1000C,同时不断搅拌，在此温度下保持1个小时左右，待全部溶解后，将其冷却至常温，然后滴加乙醇，并同时加入消泡剂，最后加入成膜剂和防锈剂，搅拌均匀后静置，得到成品。
实施例2
一种建筑钢模脱模剂，其组分按质量百分数配比包括：聚乙烯醇8%，乙醇36%，水48%，成膜剂7%，防锈剂0.95%，消泡剂0.05%，配制方法：按上述比例称取原材料，首先将聚乙烯醇树脂在室温条件下加入到水中浸泡5小时左右，然后升温至95-1000C,同时不断搅拌，在此温度下保持1个小时左右，待全部溶解后，将其冷却至常温，然后滴加乙醇，并同时加入消泡剂，最后加入成膜剂和防锈剂，搅拌均匀后静置，得到成品。
实施例3
一种建筑钢模脱模剂，其组分按质量百分数配比包括：聚乙烯醇9%，乙醇35%，水50%，成膜剂5%，防锈剂0.95%，消泡剂0.05%，配制方法：按上述比例称取原材料，首先将聚乙烯醇树脂在室温条件下加入到水中浸泡5小时左右，然后升温至95-1000C,同时不断搅拌，在此温度下保持1个小时左右，待全部溶解后，将其冷却至常温，然后滴加乙醇，并同时加入消泡剂，最后加入成膜剂和防锈剂，搅拌均匀后静置，得到成品。
实施例4
一种建筑钢模脱模剂，其组分按质量百分数配比包括：聚乙烯醇10%，乙醇32%，水52%，成膜剂5%，防锈剂0.95%，消泡剂0.05%，配制方法：按上述比例称取原材料，首先将聚乙烯醇树脂在室温条件下加入到水中浸泡5小时左右，然后升温至95-1000C,同时不断搅拌，在此温度下保持1个小时左右，待全部溶解后，将其冷却至常温，然后滴加乙醇，并同时加入消泡剂，最后加入成膜剂和防锈剂，搅拌均匀后静置，得到成品。
本发明具有成膜性好、脱模效果佳、性状稳定、无毒无刺激性、环保等优点。
Claims (2)
1.一种建筑钢模脱模剂，其特征在于：其组分按质量百分数配比为：聚乙烯醇7-10%，乙醇24-58%，水58-29%，成膜剂5-7%，防锈剂0.95%，消泡剂0.04-0.06%，配制方法：按上述比例称取原材料，首先将聚乙烯醇树脂在室温条件下加入到水中浸泡5小时左右，然后升温至95-1000C，同时不断搅拌，在此温度下保持1个小时左右，待全部溶解后，将其冷却至常温，然后滴加乙醇，并同时加入消泡剂，最后加入成膜剂和防锈剂，搅拌均匀后静置，得到成品。
2.根据权利要求1所述的一种建筑钢模脱模剂，其特征在于：所述成膜剂为甘油；所述防锈剂为苯甲酸钠；所述消泡剂为环氧乙烷、聚丙二醇、硬脂酸锌按质量比3:2:1的混合物。