CN111849282B - 一种单原子抗菌消毒内墙涂料及其制备方法 - Google Patents
一种单原子抗菌消毒内墙涂料及其制备方法 Download PDFInfo
- Publication number
- CN111849282B CN111849282B CN202010727186.6A CN202010727186A CN111849282B CN 111849282 B CN111849282 B CN 111849282B CN 202010727186 A CN202010727186 A CN 202010727186A CN 111849282 B CN111849282 B CN 111849282B
- Authority
- CN
- China
- Prior art keywords
- antibacterial
- stirring
- disinfectant
- interior wall
- deionized water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及内墙涂料领域，具体公开了一种单原子抗菌消毒内墙涂料及其制备方法。一种单原子抗菌消毒内墙涂料，包括以下比例份的原料：丙烯酸乳液18‑22%，消泡剂1‑2%，分散剂2‑5%，丙二醇5‑10%。成膜助剂1‑2%，增稠剂4‑8%，pH调节剂0.2%，单原子抗菌消毒剂2‑5%，填料粉体30‑40%，去离子水17‑28%；其制备方法为：先加去离子水，搅拌依次加入分散剂、消泡剂、丙二醇，再依次加入填料粉体，然后加入增稠剂，调节pH，依次加入丙烯酸乳液、成膜助剂、消泡剂，搅拌均匀，最后将单原子抗菌消毒剂均匀分散在去离子水中，搅拌加入上述体系中制得成品。本发明应用于内墙涂料，其具有无需其他辅助条件，可广谱杀灭常见细菌、霉菌、病毒等致病微生物，也可杀灭超级细菌的优点。
Description
技术领域
本发明涉及内墙涂料领域，更具体地说，它涉及一种单原子抗菌消毒内墙涂料及其制备方法。
背景技术
内墙涂料与人们的健康生活息息相关，随着经济的发展以及人们消费观念的变化，功能性涂料日益深入人们的生活。目前全球性的污染问题日益严重，新型冠状病毒疫情、非洲猪瘟疫情、细菌、霉菌等各种致病微生物对人类社会和生命健康造成的严重危害，因此开发具有广谱抗菌、高效消毒、长效防霉等功能性的内墙涂料有重大的意义，尤其是针对学校、医院、商场等公共场所开发的特种功能涂料，可以有效提高生物安全防护，降低致病微生物对人们生活的影响。
近年来，单原子催化迅速发展为催化科学领域最热门的前沿领域，广泛地应用在能源、材料、化工、医疗、生物等领域，在科学领域掀起一股热烈地研究热潮。相对于纳米尺度催化剂而言，单原子催化剂以单个原子为活性中心，催化活性材料利用率达到了100％，极大地降低了催化剂成本。单原子催化剂活性位点清晰均匀，具有高活性和高选择性。单原子催化成功入选美国化学会2016年度化学化工领域十大研究成果，今年成功入选2019年中国科协年会发布的20大科学技术难题，是我国和世界科研领域的热门。单原子催化剂无需其他辅助条件，可广谱杀灭金黄色葡萄球菌、大肠杆菌、H1N1病毒、沙门氏菌、白色念珠菌、绿脓杆菌、枯草杆菌、霉菌等常见致病微生物，在抗菌、消毒、防霉等领域表现出巨大的应用潜力。
发明内容
针对现有技术存在的多种致病微生物对人类社会和生命健康造成的严重危害的问题，本发明的第一个目的在于提供一种单原子抗菌消毒内墙涂料，具有无需其他辅助条件，可广谱杀灭常见致病微生物，也可杀灭超级细菌的优点。
本发明的第二个目的在于提供一种单原子抗菌消毒内墙涂料的制备方法，所述制备方法具有操作简单，可进行大规模工业化生产的优点。
为实现上述第一个目的，本发明提供了如下技术方案：一种单原子抗菌消毒内墙涂料，产品包含以下重量百分比的组分：丙烯酸乳液15-25％，消泡剂1-2％，分散剂1-5％，丙二醇5-10％，成膜助剂1-2％，增稠剂2-8％，pH调节剂0.1-0.5％，单原子抗菌消毒剂1-10％，填料粉体30-40％，去离子水15-30％。
通过采用上述技术方案，由于采用自主研发的单原子抗菌消毒剂，该单原子抗菌消毒剂无需其他辅助条件，可广谱杀灭常见致病微生物，也可消灭超级细菌，用单原子抗菌消毒剂改性涂料，使得涂料在抗菌、消毒具有巨大潜能，生产的内墙涂料无需其他辅助条件，可广谱杀灭常见致病微生物，也可杀灭超级细菌的效果。
进一步地，产品包含以下重量百分比的组分：丙烯酸乳液18-22％，消泡剂1-2％，分散剂2-5％，丙二醇5-10％，成膜助剂1-2％，增稠剂4-8％，pH调节剂0.2％，单原子抗菌消毒剂2-5％，填料粉体30-40％，去离子水17-28％。
通过采用上述技术方案，由于采用自主研发的单原子抗菌消毒剂对涂料进行改性，该单原子抗菌消毒剂的质量百分比大于5％以上时，随着单原子抗菌消毒剂的质量百分比的提升，抗菌消毒性能增加不明显，单原子抗菌消毒剂2-5％可保证抗菌消毒性能同时降低工艺生产成本。
进一步地，消泡剂为非硅酮矿物油消泡剂；所述分散剂为20％的聚羧酸铵盐；所述成膜助剂为醇酯十二；所述增稠剂为纤维素；所述pH调节剂为二甲基乙醇胺。
通过采用上述技术方案，由于采用聚羧酸铵盐，因此，获得对填料粉体有良好的分散效果好；由于采用纤维素，因此，获得了可调节粘度同时辅助提升涂料的抗菌能力的效果；采用二甲基乙醇胺可调节pH同时作水溶性涂料助溶剂；醇酯十二可有效降低其最低成膜温度，便于涂料使用。
进一步地，单原子抗菌消毒剂由载体和过渡金属组成，其中载体为钛白粉、硅藻土、碳酸钙、高岭土、氧化铝、沸石分子筛中的一种或多种，过渡金属选自铁、钴、镍、铜、锌、银、锰中的一种或多种。
通过采用上述技术方案，由于载体为钛白粉、硅藻土、碳酸钙、高岭土、氧化铝、沸石分子筛中的一种或多种，该载体与涂料中的填料组分相同，能被很好的分散，起到良好的抗菌杀毒作用。
进一步地，单原子抗菌消毒剂过渡金属以单原子形式锚定在载体表面的缺陷位点中；所述单原子抗菌消毒剂中过渡金属和载体的质量比为1:20-1:200。
通过采用上述技术方案，对起到抗菌消毒的过渡金属有效成分进行控制，当过渡金属和载体的质量比为1:20-1:200时，运用到本申请的内墙涂料中，不仅可以与填料均匀混合，使其在长时间使用过程中，单原子抗菌消毒剂析出释放，保证生产的单原子抗菌消毒剂的质量，还可降低单原子抗菌消毒剂在涂料配方中的质量百分比，降低工业生产成本。
进一步地，填料粉体包括占原料质量的7-10％钛白粉，7-10％高岭土，6-8％滑石粉，8-14％重质碳酸钙。
通过采用上述技术方案，钛白粉的使用可使本内墙涂料在日光照射下,耐日晒,不开裂、不变色，伸展率大、耐酸碱；高岭土良好的结合性，可使得钛白粉、滑石粉、重质碳酸钙更好混合在一起，保证填料混合均匀度；滑石粉起到良好遮盖力和润滑作用；重质碳酸钙可使涂料不沉降,使得体系易分散,制备的涂料层光泽好、耐寒耐热。
进一步地，填料粉体还包括占原料质量的1-5％纳米二氧化钛，0.1-2％的氧化锌晶须，纳米二氧化钛和氧化锌晶须质量比为5-10:1；填料粉体的粒径为1-50μm。
通过采用上述技术方案，纳米二氧化钛良好的分散性可与填料中的钛白粉、高岭土、滑石粉、重质碳酸钙结合分散涂料体系中，起到辅助增强抗菌性和耐候性的作用；氧化锌晶须高度形态规整和尺寸均一性，可有效改善涂料墙面的耐老化性能和耐热性，同时因氧化锌晶须高密度的特性，涂了本申请的墙面的吸波减振性能良好，起到良好的隔音效果，可营造良好的居住环境；氧化锌晶须呈四脚三维空间结构，可有效与单原子抗菌消毒剂的结合，降低单原子抗菌消毒剂在使用过程中，从涂料层中脱离的概率，起到辅助强度抗菌消毒作用。
为实现上述第二个目的，本发明提供了如下技术方案：一种单原子抗菌消毒内墙涂料的制备方法，包括以下步骤：
步骤1：取一容器，加入去离子水，在搅拌状态下，依次加入分散剂、消泡剂、丙二醇，搅拌3-5分钟。
步骤2：调节搅拌转速，依次加入填料粉体，搅拌10-15分钟。
步骤3：缓慢加入增稠剂，持续搅拌30分钟，加入pH调节剂，调节pH值为6.5-7。
步骤4：依次加入丙烯酸乳液、成膜助剂，持续搅拌10分钟，调节搅拌转速并加入消泡剂，继续搅拌30分钟，最后将单原子抗菌消毒剂均匀分散在去离子水中，搅拌加入上述体系中制得涂料成品。
通过采用上述技术方案，涂料配制操作简单，可进行大规模工业化生产。
进一步地，步骤1中，搅拌状态下转速200-400转/分钟；步骤2中，搅拌转速调到400-600转/分钟；步骤3中，搅拌转速控制在1000-1100转/分钟。
通过采用上述技术方案，可使步骤1中的去离子水、分散剂、消泡剂、丙二醇混合均匀；可使步骤2中填料粉体混合均匀；可使增稠剂与步骤2中体系充分混合。
进一步地，步骤4中，依次加入丙烯酸乳液、成膜助剂，持续高速分散10分钟，搅拌转速1200-1500转/分钟，以每分钟降低150转的速度，调节搅拌转速至300转/分钟并加入消泡剂，继续搅拌30分钟，最后将单原子抗菌消毒剂均匀分散在去离子水中，300转/分钟搅拌加入上述体系中制得涂料成品。
通过采用上述技术方案，进一步使步骤4中的丙烯酸乳液、成膜助剂、消泡剂、抗菌消毒剂均匀混合均匀，保证制备得到的内墙涂料的质量。
综上所述，本发明具有以下有益效果：
1、本发明的单原子抗菌消毒内墙涂料使用无机单原子抗菌消毒剂，采用全新的原子灭菌技术，无需其他辅助条件，可广谱杀灭金黄色葡萄球菌、大肠杆菌、H1N1病毒、沙门氏菌、白色念珠菌、绿脓杆菌、枯草杆菌、霉菌，这些常见致病微生物，也可以快速持续杀灭危害性较大的超级细菌。
2、本发明的单原子抗菌消毒内墙涂料的持续杀菌消毒作用时间较长且自身不产生任何耐药性，赋予了涂料广谱抗菌、高效消毒、长效防霉、无味无毒、绿色环保的优势功效。
3、本发明所使用的无机单原子抗菌消毒剂彻底取代了毒性大、不稳定、有效期短、作用范围局限、易产生耐药性的有机杀菌剂、天然抗菌剂、防腐剂等传统添加剂，是新型长效绿色环保的多功能涂料添加剂。
4、本发明的方法具有涂料配制操作简单，可进行大规模工业化生产的效果。
具体实施方式
以下结合实施例对本发明作进一步详细说明。
原料
原料的制备例
制备例1：
单原子抗菌消毒剂的制备，步骤1，将5g/L硝酸银的水溶液加入硅藻土中，其中过渡金属盐与载体的质量比为1:20，所得溶液100kHz的条件下超声30min分散均匀，然后再将混合溶液100r/min搅拌12h；
步骤2，将步骤1得到的混合溶液升温至水的沸点，高温挥发，蒸干溶剂，并用球磨机于50r/min转速下充分研磨0.5小时，得到固体粉末；
步骤3，将步骤2得到的固体粉末在空气气氛和800℃的温度条件下加热处理2h，冷却到室温，球磨机于50r/min转速下研磨20min，即得所需的催化剂。
实施例
实施例1
一种单原子抗菌消毒内墙涂料，包含以下重量百分比的组分：丙烯酸乳液19％，消泡剂1％，分散剂2％，丙二醇5％。成膜助剂1％，增稠剂4％，pH调节剂0.2％，单原子抗菌消毒剂为1％，填料粉体40％，去离子水26.8％，填料粉体由占原料总质量10％的钛白粉、10％高岭土、6％滑石粉，14％重质碳酸钙组成。
一种单原子抗菌消毒内墙涂料的制备方法，包含以下步骤：
1)不锈钢配料桶中加入20.8kg去离子水，采用机械搅拌，搅拌转速300转/分钟，在搅拌状态下依次加入2kg聚羧酸铵盐、0.5kg消泡剂、5kg丙二醇搅拌5分钟，使加入不锈钢配料桶中的物料混合均匀。
2)将搅拌转速调到500转/分钟，依次缓慢加入10kg钛白粉、10kg高岭土、6kg滑石粉、14kg重质碳酸钙，充分搅拌15分钟。
3)缓慢加入4kg纤维素，调转速到1000转/分钟，持续搅拌30分钟，随后加入0.2kg二甲基乙醇胺，调节pH至6.5-7范围内。
4)在保持1000转/分钟，依次加入19kg丙烯酸乳液、1kg醇酯十二，调转速到1200转/分钟，持续分散10分钟，使所有物料完全混合均匀，以每分钟降低150转的速度，逐渐降低转速至300转/分钟并加入0.5kg消泡剂，继续搅拌30分钟，最后将1kg单原子抗菌消毒剂均匀分散在6kg去离子水中，在300转/分钟搅拌速度下，加入上述体系中，搅拌10分钟，制得涂料成品。
实施例二
实施例二与实施例一的区别在于：单原子抗菌消毒内墙涂料配方中的丙烯酸乳液18％和单原子抗菌消毒剂为2％，其他组分均相同。
实施例三
实施例三与实施例一的区别在于：单原子抗菌消毒内墙涂料配方中的丙烯酸乳液18％、单原子抗菌消毒剂为5％，填料粉体36％，其他组分均相同；填料粉体由钛白粉9％，高岭土9％。滑石粉5％，重质碳酸钙13％组成。
实施例四
实施例四与实施例一的区别在于：单原子抗菌消毒内墙涂料配方中的丙烯酸乳液18％、单原子抗菌消毒剂为8％，填料粉体33％，其他组分均相同；填料粉体由钛白粉8％，高岭土8％。滑石粉5％，重质碳酸钙12％组成。
实施例五
一种单原子抗菌消毒内墙涂料，包含以下重量百分比的组分：丙烯酸乳液20％，消泡剂1.3％，分散剂3％，丙二醇6.5％。成膜助剂1.3％，增稠剂5.5％，pH调节剂0.2％，单原子抗菌消毒剂3％，填料粉体36％，去离子水23.2％；填料粉体由钛白粉10％，高岭土9％，滑石粉7％，重质碳酸钙14％组成。
一种单原子抗菌消毒内墙涂料的制备方法，包含以下步骤：
1)不锈钢配料桶中加入17.2kg去离子水，采用机械搅拌，搅拌转速300转/分钟，在搅拌状态下依次加入3kg聚羧酸铵盐、0.5kg消泡剂、6.5kg丙二醇搅拌5分钟，使所有物料混合均匀。
2)将分散机转速调到500转/分钟，依次缓慢加入10kg钛白粉、9kg高岭土、7kg滑石粉、14kg重质碳酸钙，充分搅拌15分钟。
3)缓慢加入5.5kg纤维素，调转速到1000转/分钟，持续搅拌30分钟，随后加入0.2kg二甲基乙醇胺，调节pH至6.5-7范围内。
4)在保持1000转/分钟，依次加入20kg丙烯酸乳液、1.3kg醇酯十二，调转速到1200转/分钟，持续分散10分钟，使所有物料完全混合均匀，以每分钟降低150转的速度，逐渐降低转速至300转/分钟并加入0.5kg消泡剂，继续搅拌30分钟，最后将3kg单原子抗菌消毒剂均匀分散在6kg去离子水中，300转/分钟搅拌速度下，加入上述体系中制得涂料成品。
实施例六
一种单原子抗菌消毒内墙涂料，包含以下重量百分比的组分：丙烯酸乳液22％，消泡剂1.6％，分散剂4％，丙二醇8％。成膜助剂1.6％，增稠剂7％，pH调节剂0.2％，单原子抗菌消毒剂4％，填料粉体33％，去离子水18.6％；填料粉体由钛白粉8％，高岭土8％。滑石粉7％，重质碳酸钙10％组成。
一种单原子抗菌消毒内墙涂料的制备方法，包含以下步骤：
1)不锈钢配料桶中加入12.6kg去离子水，采用机械搅拌，搅拌转速300转/分钟，在搅拌状态下依次加入4kg聚羧酸铵盐、0.5kg消泡剂、8kg丙二醇搅拌5分钟，使所有物料混合均匀。
2)将分散机转速调到500转/分钟，依次缓慢加入8kg钛白粉、8kg高岭土、7kg滑石粉、10kg重质碳酸钙，充分搅拌15分钟。
3)缓慢加入5.5kg纤维素，调转速到1000转/分钟，持续搅拌30分钟，随后加入0.2kg二甲基乙醇胺，调节pH至6.5-7范围内。
4)在保持1000转/分钟，依次加入22kg丙烯酸乳液、1.6kg醇酯十二，调转速到1200转/分钟，持续分散10分钟，使所有物料完全混合均匀，以每分钟降低150转的速度，逐渐降低转速至300转/分钟并加入0.5kg消泡剂，继续搅拌30分钟，最后将4kg单原子抗菌消毒剂均匀分散在6kg去离子水中，300转/分钟搅拌速度下，加入上述体系中制得涂料成品。
实施例七
一种单原子抗菌消毒内墙涂料，包含以下重量百分比的组分：丙烯酸乳液20％，消泡剂2％，分散剂5％，丙二醇10％。成膜助剂2％，增稠剂8％，pH调节剂0.2％，单原子抗菌消毒剂5％，填料粉体30％，去离子水17.8％；钛白粉7％，高岭土7％。滑石粉8％，重质碳酸钙8％组成。
一种单原子抗菌消毒内墙涂料的制备方法，包含以下步骤：
1)不锈钢配料桶中加入11.8kg去离子水，采用磁力搅拌，搅拌转速300转/分钟，在搅拌状态下依次加入5kg聚羧酸铵盐、0.5kg消泡剂、10kg丙二醇搅拌5分钟，使所有物料混合均匀。
2)将分散机转速调到500转/分钟，依次缓慢加入7kg钛白粉、7kg高岭土、8kg滑石粉、8kg重质碳酸钙，充分搅拌15分钟。
3)缓慢加入8kg纤维素，调转速到1000转/分钟，持续搅拌30分钟，随后加入0.2kg二甲基乙醇胺，调节pH至6.5-7范围内。
4)在保持1000转/分钟，依次加入20kg丙烯酸乳液、2kg醇酯十二，调转速到1200转/分钟，持续分散10分钟，使所有物料完全混合均匀，以每分钟降低150转的速度，逐渐降低转速至300转/分钟并加入0.5kg消泡剂，继续搅拌30分钟，最后将5kg单原子抗菌消毒剂均匀分散在6kg去离子水中，300转/分钟搅拌速度下，加入上述体系中制得涂料成品。
实施例8
实施例8与实施例1的区别在于：填料粉体由钛白粉9.8％，高岭土10％。滑石粉6％，重质碳酸钙13％、纳米二氧化钛1％、0.2氧化锌晶须组成。
对比例
对比例1
与实施例一的区别在于：单原子抗菌消毒内墙涂料配方中的丙烯酸乳液20％，不添加单原子抗菌消毒剂，其他组分均相同。
对比例2
与实施例一的区别在于：单原子抗菌消毒内墙涂料配方中的丙烯酸乳液19.5％，单原子抗菌消毒剂0.5％，其他组分均相同。
性能检测试验
1.抗细菌测试：按照GB/T21866-2008标准要求测试。
2.抗霉菌测试：试验菌种：黑曲霉AS3.4463、土曲霉AS3.3935、宛氏拟青霉AS3.4253、绳状青霉AS3.3875、出芽短梗霉AS3.3984、球毛壳霉AS3.4254。试验条件：时间28天，湿度90％RH，温度28℃。
评价标准：0级不长，即显微镜(放大50倍)下观察未见生长；1级痕迹生长，即肉眼可见生长，但生长覆盖面积小于10％；2级生长覆盖面积大于10％。
3.抗病毒测试：按照ISO22196：2011(Measurement of antibacterial activityon plastics and other non-porous surfaces测定塑料和其他无孔表面的抗菌活性，细菌类型为金黄色葡萄球菌，大肠杆菌)。
检测方法/试验方法
表1实施例1-8和对比例1-3的抗细菌测试参数
表2实施例1-8和对比例1-3的抗霉菌测试参数
表3实施例1-8和对比例1-3的抗病毒测试参数
结合实施例1-8和对比例1-2并结合表1可以看出，添加单原子抗菌消毒剂的涂料具有较好的抗细菌性能。
表1可以看出，实施例1、4与实施例2、3、5、6、7对比，当单原子抗菌消毒剂大于5％，抗菌消毒性能提示不明显，可得单原子抗菌消毒剂用量在2-5％抗细菌效果较优且可降低生产成本。
表1可以看出，实施例1和实施例8对比，可知添加了纳米二氧化钛和氧化锌晶须可补强涂料抗细菌性能。
结合实施例1-8和对比例1-2并结合表2可以看出，添加单原子抗菌消毒剂的涂料具有较好的抗霉菌性能。
结合实施例1-8和对比例1-2并结合表3可以看出，添加单原子抗菌消毒剂的涂料具有较好的抗病毒性能，尤其是对H1N1有着良好消灭作用。
表3可以看出，实施例1和实施例8对比，可知添加了纳米二氧化钛和氧化锌晶须可补强涂料抗病毒性能。
综上所述，本发明的单原子抗菌消毒内墙涂料使用无机单原子抗菌消毒剂，采用全新的原子灭菌技术，无需其他辅助条件，可广谱常见致病微生物，也可以快速持续杀灭危害性较大的超级细菌；单原子抗菌消毒剂用量在2-5％抗细菌效果较优且可降低生产成本；添加了纳米二氧化钛和氧化锌晶须可补强涂料抗病毒性能、抗细菌性能和抗霉菌性能。
本具体实施例仅仅是对本发明的解释，其并不是对本发明的限制，本领域技术人员在阅读完本说明书后可以根据需要对本实施例做出没有创造性贡献的修改，但只要在本发明的权利要求范围内都受到专利法的保护。
Claims (5)
1.一种单原子抗菌消毒内墙涂料，其特征在于，所述产品包含以下重量百分比的组分：丙烯酸乳液18-22%，非硅酮矿物油消泡剂1-2%，分散剂2-5%，丙二醇5-10%，醇酯十二1-2%，纤维素4-8%，二甲基乙醇胺0.2%，单原子抗菌消毒剂2-5%，填料粉体30-40%，去离子水17-28%；分散剂为20%的聚羧酸铵盐；所述单原子抗菌消毒剂由载体和过渡金属组成，其中载体为硅藻土，过渡金属选自银；所述单原子抗菌消毒剂过渡金属以单原子形式锚定在载体表面的缺陷位点中；所述单原子抗菌消毒剂中过渡金属和载体的质量比为1:20；所述单原子抗菌消毒剂的制备方法，步骤 1，将 5g/L 硝酸银的水溶液加入硅藻土中，其中硝酸银与硅藻土的质量比为 1:20，所得溶液 100kHz 的条件下超声 30min 分散均匀，然后再将混合溶液 100r/min 搅拌 12h；步骤 2，将步骤 1 得到的混合溶液升温至水的沸点，高温挥发，蒸干溶剂，并用球磨机于 50r/min 转速下充分研磨 0.5 小时，得到固体粉末；步骤 3，将步骤 2 得到的固体粉末在空气气氛和 800℃的温度条件下加热处理 2h，冷却到室温，球磨机于 50r/min 转速下研磨 20min，即得所需的单原子抗菌消毒剂；填料粉体包括占原料质量的7-10%钛白粉，7-10%的高岭土，6-8%的滑石粉，8-14%的重质碳酸钙。
2.根据权利要求1所述的一种单原子抗菌消毒内墙涂料，其特征在于，所述填料粉体还包括占原料质量的1-5%纳米二氧化钛，0.1-2%的氧化锌晶须，纳米二氧化钛和氧化锌晶须质量比为5-10:1；填料粉体的粒径为1-50μm。
3.权利要求1-2任一所述的一种单原子抗菌消毒内墙涂料的制备方法，其特征在于，包括以下步骤：
步骤1：取一容器，加入去离子水，在搅拌状态下，依次加入20%的聚羧酸铵盐、非硅酮矿物油消泡剂、丙二醇，搅拌3-5分钟；
步骤2：调节搅拌转速，依次加入填料粉体，搅拌10-15分钟；
步骤3：缓慢加入纤维素，持续搅拌30分钟，加入二甲基乙醇胺，调节pH值为6.5-7；
步骤4：依次加入丙烯酸乳液、醇酯十二，持续搅拌10分钟，调节搅拌转速并加入剩余的非硅酮矿物油消泡剂，继续搅拌30分钟，最后将单原子抗菌消毒剂均匀分散在去离子水中，搅拌加入上述体系中制得涂料成品。
4.权利要求3所述的一种单原子抗菌消毒内墙涂料的制备方法，其特征在于，步骤1中，搅拌状态下转速200-400转/分钟；步骤2中，搅拌转速调到400-600转/分钟；步骤3中，搅拌转速控制在1000-1100转/分钟。
5.权利要求3所述的一种单原子抗菌消毒内墙涂料的制备方法，其特征在于，步骤4中，依次加入丙烯酸乳液、醇酯十二，持续高速分散10分钟，搅拌转速1200-1500转/分钟，以每分钟降低150转的速度，调节搅拌转速至300转/分钟并加入剩余的非硅酮矿物油消泡剂，继续搅拌30分钟，最后将单原子抗菌消毒剂均匀分散在去离子水中，在300转/分钟搅拌速度下加入上述体系中制得涂料成品。