CN111821988A - 一种加氢脱硫催化剂及其制备方法 - Google Patents
一种加氢脱硫催化剂及其制备方法 Download PDFInfo
- Publication number
- CN111821988A CN111821988A CN201910308416.2A CN201910308416A CN111821988A CN 111821988 A CN111821988 A CN 111821988A CN 201910308416 A CN201910308416 A CN 201910308416A CN 111821988 A CN111821988 A CN 111821988A
- Authority
- CN
- China
- Prior art keywords
- modified alumina
- catalyst
- rod
- pore
- shaped
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
实施例1 | 实施例2 | 实施例3 | 实施例4 | 对比例1 | 对比例2 | 对比例3 | |
催化剂编号 | Cat-1 | Cat-2 | Cat-3 | Cat-4 | Cat-5 | Cat-6 | Cat-7 |
催化剂性质 | |||||||
比表面积,m<sup>2</sup>/g | 220 | 235 | 207 | 213 | 168 | 159 | 173 |
孔容,mL/g | 0.89 | 0.93 | 0.91 | 0.88 | 0.71 | 0.73 | 0.75 |
孔分布*,v% | |||||||
小于10nm | 11 | 13 | 12 | 9 | 13 | 14 | 17 |
10-30nm | 53 | 50 | 49 | 54 | 38 | 36 | 34 |
100-600nm | 18 | 19 | 22 | 21 | 13 | 14 | 11 |
大于1000nm | 4 | 4 | 3 | 2 | - | - | - |
3µm以上 | 无 | 无 | 无 | 无 | 8 | 7 | 8 |
压碎强度,N/mm | 12.0 | 11.7 | 11.5 | 12.4 | 8.9 | 9.1 | 9.9 |
催化剂组成 | |||||||
WO<sub>3</sub>含量,wt% | 2.9 | 2.1 | 1.8 | 2.4 | 2.9 | 2.9 | 2.9 |
MoO<sub>3</sub>含量,wt% | 10.7 | 11.8 | 12.4 | 11.7 | 10.7 | 10.7 | 10.7 |
CoO<sub>3</sub>含量,wt% | 0.8 | 1.2 | 1.7 | 2 | 0.9 | 0.8 | 0.8 |
NiO含量,wt% | 3.2 | 2.6 | 2.1 | 2 | 3.2 | 3.2 | 3.2 |
项目 | |
密度(20℃),g/cm<sup>3</sup> | 0.98 |
S,wt% | 3.8 |
N,wt% | 0.42 |
Ni,µg/g | 57.6 |
V,µg/g | 97.8 |
CCR,wt% | 13.9 |
加氢脱硫催化剂 | Cat-1 | Cat-2 | Cat-3 | Cat-4 | Cat-5 | Cat-6 | Cat-7 |
脱硫率,% | 93.2 | 91.3 | 90.8 | 92.4 | 68.3 | 67.8 | 68.4 |
脱残炭率,% | 73.3 | 72.8 | 71.7 | 72.6 | 49.6 | 48.7 | 48.5 |
Claims (22)