CN111808458A - Method for manufacturing nano wall film - Google Patents
Method for manufacturing nano wall film Download PDFInfo
- Publication number
- CN111808458A CN111808458A CN202010743466.6A CN202010743466A CN111808458A CN 111808458 A CN111808458 A CN 111808458A CN 202010743466 A CN202010743466 A CN 202010743466A CN 111808458 A CN111808458 A CN 111808458A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- wall film
- nano
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for manufacturing a nano wall film, which comprises the following steps: the production method of the nano wall film can meet the requirements of people on healthy and environment-friendly wall materials at present, and solves the problem that the requirements of people on the healthy and environment-friendly characteristics of wall products are further enhanced on the basis of ensuring the characteristics of general texture wall film products in the market.
Description
Technical Field
The invention belongs to the technical field of wall paint correlation, and particularly relates to a method for manufacturing a nano wall film.
Background
Wall paper is generally adhered or emulsion paint is brushed on the wall decoration during the decoration of a new house, although the wall paper has multiple styles, gaps are left at the splicing position, the wall paper is easy to mildew and warp edges, the wall paper needs to be replaced regularly, and the cost performance is low; compared with wallpaper, the latex paint is simple in construction and low in cost, but the latex paint is single in decorative effect, poor in covering power and easy to crack.
The texture wall film product is a novel environment-friendly wall surface coating, special raw materials are used for creating decoration effects with different styles and vivid textures on the wall surface through a unique construction process, the texture wall film product integrates the high and new technology and elegant art, the texture wall film decoration effect formed by wall film slurry and the special process is exactly like wallpaper, but the texture wall film product is more environment-friendly and more considerable in cost performance compared with the wallpaper, can overcome various general defects of general coatings and wallpaper, and has the characteristics of environmental protection, water resistance, mildew resistance, wear resistance, strong decoration property, simple and convenient construction and the like.
However, the product is not better, people pay more attention to health and environmental protection in addition to the basic quality aspect of the product, and the characteristic requirements of people on health and environmental protection are also required to be strengthened on the aspect of ensuring the general characteristic of the texture wall film.
Disclosure of Invention
The invention aims to provide a method for manufacturing a nano wall film, which aims to solve the problem of higher characteristic requirements of people on wall materials in the aspects of health and environmental protection in the background technology.
In order to achieve the purpose, the invention provides the following technical scheme: the invention relates to a method for preparing a nano-wall film, which comprises the following materials in parts by weight: defoaming agent, multifunctional assistant, dispersant, wetting agent, titanium dioxide, kaolin, diatomite, nano Tio2, anion powder, odorless emulsion, film forming assistant, preservative, mildew preventive, flatting agent and water;
the manufacturing method of the nano-wall film comprises the following steps:
the method comprises the following steps: all preparation materials were prepared according to the above formulation.
Step two: and (3) putting the water, the defoaming agent, the multifunctional assistant, the dispersing agent and the wetting agent in the formula into a stirring dispersion machine for dispersion, wherein the rotating speed is 1000-1200 r/m, and the dispersion time is 60-70 minutes.
Step three: firstly, sequentially adding the titanium dioxide, kaolin, diatomite, nano Tio2 and anion powder in the formula into a stirring dispersion machine in the second step for dispersion, wherein the rotating speed is 2800-3200 revolutions per minute, and the dispersion time is 100-120 minutes; and then putting the dispersed materials into a sand mill, circularly sanding until the fineness of the materials is less than or equal to 40 micrometers, and finally transferring the materials into a stirring dispersion machine.
Step four: and (3) sequentially putting the odor-free emulsion, the film-forming assistant, the preservative, the mildew preventive and the flatting agent in the formula into a stirring dispersion machine after the third step is completed, and stirring at the rotating speed of 700-900 rpm for 45-60 minutes.
Step five: and (4) filtering the stirred material after the fourth step by using a 130-150 mesh filter screen to prepare the texture wall film, and then filling the texture wall film into a canned finished product.
Preferably, the water used in the formula is clean water or deionized water.
Preferably, the preservative is prepared from methyl paraben and tetramethrin according to the mass ratio of 1: 1.6.
Preferably, the film forming aid is propylene glycol methyl ether acetate.
Preferably, the dispersant is a polyacrylate.
Preferably, the wetting agent is a polyoxyethylene fatty alcohol ether.
Preferably, the defoamer is a silicone defoamer.
Compared with the prior art, the invention has the beneficial effects that: the nano wall film is a product which has smooth and fine touch feeling, high covering, easy construction, scrubbing resistance, easy cleaning, moisture and mildew resistance, formaldehyde degradation and negative ion dilution, and has the following advantages:
1. the nanometer wall film has excellent physical and chemical properties, avoids the disadvantages of easy edge warping, seam formation, mildew generation, complex secondary construction and the like of the traditional wallpaper, and simultaneously ensures the new characteristics of no toxicity, no pollution, oxidation resistance, aging resistance and the like.
2. The nano wall film is green and environment-friendly, and has good effects on degrading formaldehyde and purifying air by adopting diatomite and anion powder as main raw materials.
3. The construction is simple and convenient, the nano wall film is extremely convenient to decorate, the construction is simple, and people can learn the nano wall film and finish the wall surface of hundreds of square meters in a short time.
4. The nano wall film has compact and waterproof surface, and may be cleaned with wet rag directly in wet weather.
Detailed Description
Through the above detailed description, the technical solutions in the embodiments of the present invention are clearly and completely described, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
According to the above embodiment, the present invention provides a technical solution: the invention relates to a method for preparing a nano-wall film, which comprises the following materials in parts by weight: 3 parts of defoaming agent, 2 parts of multifunctional auxiliary agent, 5 parts of dispersing agent, 2 parts of wetting agent, 200 parts of titanium dioxide, 75 parts of kaolin, 30 parts of diatomite, 220 parts of nano Tio, 30 parts of anion powder, 250 parts of odor-free emulsion, 15 parts of film-forming auxiliary agent, 2 parts of preservative, 3 parts of mildew preventive, 5 parts of flatting agent and 358 water
The above is 1000g of formula proportion;
the manufacturing method of the nano wall film comprises the following steps:
the method comprises the following steps: all preparation materials were prepared according to the above formulation.
Step two: and (3) putting the water, the defoaming agent, the multifunctional assistant, the dispersing agent and the wetting agent in the formula into a stirring dispersion machine for dispersion, wherein the rotating speed is 1000-1200 r/m, and the dispersion time is 60-70 minutes.
Step three: firstly, sequentially adding the titanium dioxide, kaolin, diatomite, nano Tio2 and anion powder in the formula into a stirring dispersion machine in the second step for dispersion, wherein the rotating speed is 2800-3200 revolutions per minute, and the dispersion time is 100-120 minutes; and then putting the dispersed materials into a sand mill, circularly sanding until the fineness of the materials is less than or equal to 40 micrometers, and finally transferring the materials into a stirring dispersion machine.
Step four: and (3) sequentially putting the odor-free emulsion, the film-forming assistant, the preservative, the mildew preventive and the flatting agent in the formula into a stirring dispersion machine after the third step is completed, and stirring at the rotating speed of 700-900 rpm for 45-60 minutes.
Step five: and filtering the stirred material after the fourth step by using a 130-150 mesh filter screen to prepare the texture wall film, and filling the texture wall film into a can to obtain a finished product.
The method needs to take the following points:
1. the water used in the formula is pure water or deionized water.
2. The preservative is prepared from methyl paraben and tetramethrin according to the mass ratio of 1: 1.6.
3. The film-forming assistant is propylene glycol methyl ether acetate.
4. The dispersant is polyacrylate.
5. The wetting agent is polyoxyethylene fatty alcohol ether.
6. The defoaming agent is an organic silicon defoaming agent.
The simple construction process flow of the nano wall film comprises the following steps:
1, coating a full-function base coat (15 percent of water) on the wall surface by a roller;
2. and (3) rolling and coating the nano wall film (added with water by 20%) on the wall surface twice by using a roller.
The dispensing principle and the expected effect of the method are as follows: the nano wall film is a product which has smooth and fine touch feeling, high covering, easy construction, scrubbing resistance, easy cleaning, moisture and mildew resistance, formaldehyde degradation and negative ion dilution, and has the following advantages:
1. the nanometer wall film has excellent physical and chemical properties, avoids the disadvantages of easy edge warping, seam formation, mildew generation, complex secondary construction and the like of the traditional wallpaper, and simultaneously ensures the new characteristics of no toxicity, no pollution, oxidation resistance, aging resistance and the like.
2. The nano wall film is green and environment-friendly, and has good effects on degrading formaldehyde and purifying air by adopting diatomite and anion powder as main raw materials.
3. The construction is simple and convenient, the nano wall film is extremely convenient to decorate, the construction is simple, and people can learn the nano wall film and finish the wall surface of hundreds of square meters in a short time.
4. The nano wall film has compact and waterproof surface, and may be cleaned with wet rag directly in wet weather.
In summary, the manufacturing method of the nano wall film solves the problem of higher characteristic requirements of people on wall materials in the aspects of health and environmental protection.
The working principle and the using process of the invention are as follows: although embodiments of the present invention have been shown and described, it will be appreciated by those skilled in the art that changes, modifications, substitutions and alterations can be made in these embodiments without departing from the principles and spirit of the invention, the scope of which is defined in the appended claims and their equivalents.
Claims (7)
1. The method for manufacturing the nano-wall film is characterized in that the required formula materials are as follows: 3 parts of defoaming agent, 2 parts of multifunctional auxiliary agent, 5 parts of dispersing agent, 2 parts of wetting agent, 200 parts of titanium dioxide, 75 parts of kaolin, 30 parts of diatomite, 220 parts of nano Tio, 30 parts of anion powder, 250 parts of odor-free emulsion, 15 parts of film-forming auxiliary agent, 2 parts of preservative, 3 parts of mildew preventive, 5 parts of flatting agent and 358 water;
the above is 1000g of formula proportion;
the manufacturing method of the nano-wall film comprises the following steps:
the method comprises the following steps: all preparation materials were prepared according to the above formulation.
Step two: and (3) putting the water, the defoaming agent, the multifunctional assistant, the dispersing agent and the wetting agent in the formula into a stirring dispersion machine for dispersion, wherein the rotating speed is 1000-1200 r/m, and the dispersion time is 60-70 minutes.
Step three: firstly, sequentially adding the titanium dioxide, kaolin, diatomite, nano Tio2 and anion powder in the formula into a stirring dispersion machine in the second step for dispersion, wherein the rotating speed is 2800-3200 revolutions per minute, and the dispersion time is 100-120 minutes; and then putting the dispersed materials into a sand mill, circularly sanding until the fineness of the materials is less than or equal to 40 micrometers, and finally transferring the materials into a stirring dispersion machine.
Step four: and (3) sequentially putting the odor-free emulsion, the film-forming assistant, the preservative, the mildew preventive and the flatting agent in the formula into a stirring dispersion machine after the third step is completed, and stirring at the rotating speed of 700-900 rpm for 45-60 minutes.
Step five: and filtering the stirred material after the fourth step by using a 130-150 mesh filter screen to prepare the texture wall film, and filling the texture wall film into a can to obtain a finished product.
2. The method of claim 1, wherein: the water used in the formula is clean water or deionized water.
3. The method of claim 1, wherein: the preservative is prepared from methyl paraben and tetramethrin according to the mass ratio of 1: 1.6.
4. The method of claim 1, wherein: the film-forming assistant is propylene glycol methyl ether acetate.
5. The method of claim 1, wherein: the dispersant is polyacrylate.
6. The method of claim 1, wherein: the wetting agent is polyoxyethylene fatty alcohol ether.
7. The method of claim 1, wherein: the defoaming agent is an organic silicon defoaming agent.