CN102757704A - Preparation method of universal type interior wall latex paint - Google Patents
Preparation method of universal type interior wall latex paint Download PDFInfo
- Publication number
- CN102757704A CN102757704A CN2011101119512A CN201110111951A CN102757704A CN 102757704 A CN102757704 A CN 102757704A CN 2011101119512 A CN2011101119512 A CN 2011101119512A CN 201110111951 A CN201110111951 A CN 201110111951A CN 102757704 A CN102757704 A CN 102757704A
- Authority
- CN
- China
- Prior art keywords
- latex paint
- preparation
- wall latex
- interior wall
- mins
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of a universal type interior wall latex paint. The product belongs to the field of chemical building materials. The product is prepared by taking deionized water, a sodium polycarboxylate dispersing agent, a defoaming agent, light calcium carbonate (800 meshes), titanium dioxide, anhydrous aluminum silicate, talcum powder, lithopone, hydroxyethyl cellulose, ethanediol, a DC-216 pure acrylic emulsion for interior walls, alcohol ester-12, a thickening agent and ultramarine blue as raw materials and accessorily adopting a specific process. The product has the advantages of smooth paint film, high durability, fast drying, firm adhesion, stable color, excellent water resistance, alkali resistance, aging resistance and contamination resistance, and the like and is mainly used for protecting the surface of the interior wall of a house.
Description
Technical field:
Product of the present invention belongs to the chemical building material field, relates in particular to a kind of preparation method of universal interiro wall latex paint.
Background technology:
Rubber-emulsion paint is called synthetic resin emulsion coating again, and according to the difference of raw materials for production, rubber-emulsion paint mainly contains kinds such as polyvinyl acetate lacquer, vinyl acetate-acrylic latex paint, pure acrylic acid rubber-emulsion paint, styrene-acrylic latex coating; Can be divided into unglazed, mute light, half light, mercerising again and type such as light is arranged according to the luster effect of decorating; Difference according to the product suitable environment; Be divided into two kinds of interiro wall latex paint and exterior wall latex paints, interiro wall latex paint is divided into water-soluble interiro wall latex paint, solvent-borne type interiro wall latex paint, universal interiro wall latex paint, anti-soil interiro wall latex paint, antibacterial interior wall latex paint, tertiary carbon lacquer etc. again.Product of the present invention is a universal interiro wall latex paint of new generation, and these product performance are stable, are widely used; Also more adapt to environmental requirement, effect is white and lackluster, brushes to guarantee that body of wall is clean, clean and tidy and have good opacifying power; Metope is smooth, fine and smooth, comfortable, and side wall can be found out glossiness, but this rubber-emulsion paint requires relatively harshness to body of wall; If the metope ground has injustice slightly, can demonstrate under the light gloss differ to, therefore the constructor is got technical requirements than higher; And metope must be smooth, just can show the effect of its elegance, exquisiteness, exquisiteness fully.Product of the present invention with deionized water as dispersion medium; Use pure acrylic acid emulsion, alcohol ester-12, thickening material, ultramarine as raw material and be aided with specific technology and be made into poly carboxylic acid sodium dispersion agent, skimmer, light calcium carbonate (800 order), white titanium pigment, anhydrous aluminium silicate, talcum powder, zinc sulfide white, Natvosol, terepthaloyl moietie, DC-216 interior wall; This product has advantages such as paint film is smooth, weather resistance strong, drying is rapid, adhere firmly, color stable; Have splendid water-fast, alkaline-resisting, stability to aging and contamination resistance, can be fit to the demand of different hierarchies of consumption.
Summary of the invention:
The problem that the present invention mainly solves provides a kind of compound method of universal interiro wall latex paint; This universal interiro wall latex paint is to prepare for the interior wall in protection house is special; The interiro wall latex paint that belongs to higher class; This product has advantages such as paint film is smooth, weather resistance strong, drying is rapid, adhere firmly, color stable; Have splendid water-fast, alkaline-resisting, stability to aging and contamination resistance; The demand that can be fit to different hierarchies of consumption; And compound method is simple, and the raw material of producing this product use has: deionized water 25%, poly carboxylic acid sodium dispersion agent 0.5%, skimmer 0.5%, light calcium carbonate (800 order) 20%, white titanium pigment 8%-10%, anhydrous aluminium silicate 5%-7%, talcum powder 7%, zinc sulfide white 5%, Natvosol 1%, terepthaloyl moietie 4%, alcohol ester-120.5%, DC-216 interior wall are with pure acrylic acid emulsion 20%, thickening material 0.5%, ultramarine 1%.
The present invention can realize through following technical scheme:
The method of the universal interiro wall latex paint of a kind of batch preparations is characterized in that being made up of following steps:
1. deionized water is sent into vertical grinding machine; Agitator; Rotating speed is adjusted to 1900 rev/mins, and the temperature remains within the normal range, adds poly carboxylic acid sodium dispersion agent, skimmer successively; After stirring, added light calcium carbonate, white titanium pigment, anhydrous aluminium silicate, talcum powder, zinc sulfide white, Natvosol restir 40 minutes.
2. rotating speed is adjusted to 900 rev/mins, adds terepthaloyl moietie, alcohol ester-12 successively, stirred 20 minutes, reach even no particle.
3. rotating speed is transferred to 400 rev/mins, add the DC-216 interior wall successively, stir and promptly obtained finished product in 30 minutes with pure acrylic acid emulsion, thickening material, ultramarine.
The beneficial effect of product of the present invention is: the preparation method that a kind of universal interiro wall latex paint is provided; It is simple, easy to operate that this method has technology; The universal interiro wall latex paint of producing has that paint film is smooth, weather resistance is strong, dry rapidly, advantages such as adhere firmly, color stable, product has splendid water-fast, alkaline-resisting, stability to aging and contamination resistance.
Embodiment:
Embodiment 1
With accounting for total amount is that 25% deionized water is sent into vertical grinding machine; Agitator; Rotating speed is adjusted to 1900 rev/mins, and the temperature remains within the normal range, adds successively that to account for total amount be 0.5% poly carboxylic acid sodium dispersion agent, 0.5% skimmer; After stirring, add that to account for total amount be 20% light calcium carbonate, 8% white titanium pigment, 7% anhydrous aluminium silicate, 7% talcum powder, 5% zinc sulfide white, 1% Natvosol restir 40 minutes; Rotating speed is adjusted to 900 rev/mins, adds successively that to account for total amount be 4% terepthaloyl moietie, 0.5% alcohol ester-12, stirred 20 minutes, reach even no particle; Rotating speed is transferred to 400 rev/mins, add successively account for total amount be 20% DC-216 interior wall with pure acrylic acid emulsion, 0.5% thickening material, 1% ultramarine, stir and promptly obtained finished product in 30 minutes.
Embodiment 2
With accounting for total amount is that 25% deionized water is sent into vertical grinding machine; Agitator; Rotating speed is adjusted to 1900 rev/mins, and the temperature remains within the normal range, adds successively that to account for total amount be 0.5% poly carboxylic acid sodium dispersion agent, 0.5% skimmer; After stirring, add that to account for total amount be 20% light calcium carbonate, 9% white titanium pigment, 6% anhydrous aluminium silicate, 7% talcum powder, 5% zinc sulfide white, 1% Natvosol restir 40 minutes; Rotating speed is adjusted to 900 rev/mins, adds successively that to account for total amount be 4% terepthaloyl moietie, 0.5% alcohol ester-12, stirred 20 minutes, reach even no particle; Rotating speed is transferred to 400 rev/mins, add successively account for total amount be 20% DC-216 interior wall with pure acrylic acid emulsion, 0.5% thickening material, 1% ultramarine, stir and promptly obtained finished product in 30 minutes.
Embodiment 3
With accounting for total amount is that 25% deionized water is sent into vertical grinding machine; Agitator; Rotating speed is adjusted to 1900 rev/mins, and the temperature remains within the normal range, adds successively that to account for total amount be 0.5% poly carboxylic acid sodium dispersion agent, 0.5% skimmer; After stirring, add that to account for total amount be 20% light calcium carbonate, 10% white titanium pigment, 5% anhydrous aluminium silicate, 7% talcum powder, 5% zinc sulfide white, 1% Natvosol restir 40 minutes; Rotating speed is adjusted to 900 rev/mins, adds successively that to account for total amount be 4% terepthaloyl moietie, 0.5% alcohol ester-12, stirred 20 minutes, reach even no particle; Rotating speed is transferred to 400 rev/mins, add successively account for total amount be 20% DC-216 interior wall with pure acrylic acid emulsion, 0.5% thickening material, 1% ultramarine, stir and promptly obtained finished product in 30 minutes.
Claims (4)
1. the preparation method of a universal interiro wall latex paint; It is characterized in that: use pure acrylic acid emulsion 20%, thickening material 0.5%, ultramarine 1% to be raw material with deionized water 25%, poly carboxylic acid sodium dispersion agent 0.5%, skimmer 0.5%, light calcium carbonate (800 order) 20%, white titanium pigment 8%-10%, anhydrous aluminium silicate 5%-7%, talcum powder 7%, zinc sulfide white 5%, Natvosol 1%, terepthaloyl moietie 4%, alcohol ester-120.5%, DC-216 interior wall, obtain finished product through following steps.
2. the preparation method of a kind of high-grade exterior wall latex paint according to claim 1; The characteristic of its first step is: deionized water is sent into vertical grinding machine, and agitator is adjusted to 1900 rev/mins with rotating speed; The temperature remains within the normal range; Add poly carboxylic acid sodium dispersion agent, skimmer successively, after stirring, added light calcium carbonate, white titanium pigment, anhydrous aluminium silicate, talcum powder, zinc sulfide white, Natvosol restir 40 minutes.
3. the preparation method of a kind of high-grade exterior wall latex paint according to claim 1, the characteristic in its second step is: rotating speed is adjusted to 900 rev/mins, adds terepthaloyl moietie, alcohol ester-12 successively, stirred 20 minutes, reach even no particle.
4. the preparation method of a kind of high-grade exterior wall latex paint according to claim 1, the characteristic in its 3rd step is: rotating speed is transferred to 400 rev/mins, add the DC-216 interior wall successively with pure acrylic acid emulsion, thickening material, ultramarine, stir and promptly obtained finished product in 30 minutes.