CN111807710A - 一种冰箱用正面触摸层玻璃及其生产工艺 - Google Patents
一种冰箱用正面触摸层玻璃及其生产工艺 Download PDFInfo
- Publication number
- CN111807710A CN111807710A CN202010718512.7A CN202010718512A CN111807710A CN 111807710 A CN111807710 A CN 111807710A CN 202010718512 A CN202010718512 A CN 202010718512A CN 111807710 A CN111807710 A CN 111807710A
- Authority
- CN
- China
- Prior art keywords
- glass
- touch layer
- front touch
- antibacterial
- refrigerator
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种冰箱用正面触摸层玻璃及其生产工艺，涉及家用电器技术领域。本发明包括正面触摸层和玻璃原片、背面印刷层；玻璃原片的背面印刷有背面印刷层；玻璃原片的正面设置有正面触摸层；正面触摸层采用抗菌除臭材料和液体透明油墨制成。本发明可有效防止污染物在玻璃表面积累，解决玻璃表面防指纹效果不佳的缺点；通过玻璃正面添加抗菌除臭材料，对其表面起到抗菌作用；同时使用本发明的工艺方法制得的正面触摸层的玻璃，提高视觉触觉效果,工艺操作简单,容易实现工业化。
Description
技术领域
本发明属于家用电器技术领域，特别是涉及一种冰箱用正面触摸层玻璃及其生产工艺。
背景技术
在冰箱行业中,玻璃门冰箱因其外观精致和花色品类繁多而受到市场的青睐。随着人们生活水平的提高，对家电的功能要求的基础上，大家希望更冰箱的看的漂亮，摸着舒服，平光的玻璃外观已经满足不了人们对视觉触觉的体验了。
抗菌功能已经成为冰箱的核心功能之一。目前抗菌剂主要可以分为无机、有机和天然三种。早期抗菌剂基本都属于有机系列，大多是含氮、硫、氯等元素的各类复杂化合物，其主要品种有:季铵盐类、双胍类、醇类、酚类、醛类、有机金属类、砒啶类、噻吩类等。该类抗菌剂短期杀菌效果好，但大多都有耐热稳定性差、寿命短等缺点，不适用于冰箱门。
在冰箱使用过程中，人们不可避免的接触到各种各样的细菌、真菌等微生物，并将这些微生物经过触碰传播，在开关门的同时，会带入冰箱内部，并迅速滋生和繁衍，从而影响到人们的饮食健康。因此，随着生活水平的提高；在消费者经常触碰的冰箱门表面增加抗菌功能，成为高端冰箱进一步深化抗菌功能急需解决的问题。
发明内容
本发明的目的在于提供一种冰箱用正面触摸层玻璃及其生产工艺，可有效防止污染物在玻璃表面积累，解决玻璃表面防指纹效果不佳的缺点；通过玻璃正面添加抗菌除臭材料，对其表面起到抗菌作用；同时使用本发明的工艺方法制得的正面触摸层的玻璃，提高视觉触觉效果,工艺操作简单,容易实现工业化。
为解决上述技术问题，本发明是通过以下技术方案实现的：
本发明为一种冰箱用正面触摸层玻璃，包括所述正面触摸层玻璃包括正面触摸层和玻璃原片、背面印刷层；所述玻璃原片的背面印刷有背面印刷层；所述玻璃原片的正面设置有正面触摸层。
进一步地，所述正面触摸层采用抗菌除臭材料和液体透明油墨制成。
进一步地，所述正面触摸层中的抗菌除臭材料的含量为0.5％-10％。
进一步地，所述抗菌除臭材料选自纳米银或二氧化钛或二氧化锌或沸石中的至少一种或多种。
进一步地，所述抗菌除臭材料中的二氧化钛的制备方法有水热法或溶胶凝胶法或气相沉积法或电化学法。
一种冰箱用正面触摸层玻璃的生产工艺，包括如下步骤：
SS01、玻璃原片裁剪：将玻璃原片进行切片，磨边，清洗吹干；
SS02、抗菌除臭材料的制备：将抗菌除臭材料与透明高温油墨，稳定分散剂混配，进行充分搅拌均匀得到混合物；
SS03、正面触摸层的制备：将SS02中的混合物通过丝网印刷到玻璃原片上；
SS04、正面触摸层玻璃的制备：将SS03中印刷有抗菌除臭材料的玻璃原片进行高温烧结后，在背面进行印刷，即可得到正面触摸层玻璃。
本发明具有以下有益效果：
1、本发明通过正面触摸层和玻璃原片、背面印刷层的作用，可有效防止污染物在玻璃表面积累，解决玻璃表面防指纹效果不佳的缺点；通过玻璃正面添加抗菌除臭材料，对其表面起到抗菌作用；同时使用本发明的工艺方法制得的正面触摸层的玻璃，提高视觉触觉效果,工艺操作简单,容易实现工业化。
2、本发明采用多层印刷,结合高温透明油墨，通过高温烧结抗菌除臭材料覆盖在玻璃表面，具有玻璃耐脏，抗菌，耐划痕、防手印等优点。
当然，实施本发明的任一产品并不一定需要同时达到以上所述的所有优点。
附图说明
为了更清楚地说明本发明实施例的技术方案，下面将对实施例描述所需要使用的附图作简单地介绍，显而易见地，下面描述中的附图仅仅是本发明的一些实施例，对于本领域普通技术人员来讲，在不付出创造性劳动的前提下，还可以根据这些附图获得其他的附图。
图1为本发明一种冰箱用正面触摸层玻璃与冰箱的结构示意图；
图2为本发明一种冰箱用正面触摸层玻璃的结构示意图；
图3为本发明一种冰箱用正面触摸层玻璃的生产工艺的流程示意图；
附图中，各标号所代表的部件列表如下：
1-正面触摸层玻璃，2-正面触摸层，3-玻璃原片，4-背面印刷层。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
实施例一
请参阅图1-2所示，本发明为一种冰箱用正面触摸层玻璃，包括正面触摸层玻璃1包括正面触摸层2和玻璃原片3、背面印刷层4；玻璃原片3的背面印刷有背面印刷层4；玻璃原片3的正面设置有正面触摸层2。
进一步地，正面触摸层2采用抗菌除臭材料和液体透明油墨制成。
进一步地，正面触摸层2中的抗菌除臭材料的含量为0.5％-10％。
进一步地，抗菌除臭材料选自纳米银或二氧化钛或二氧化锌或沸石中的至少一种或多种。
进一步地，抗菌除臭材料中的二氧化钛的制备方法有水热法或溶胶凝胶法或气相沉积法或电化学法。
请参阅图3所示，一种冰箱用正面触摸层玻璃的生产工艺，包括如下步骤：
SS01、玻璃原片裁剪：将玻璃原片进行切片，磨边，清洗吹干；
SS02、抗菌除臭材料的制备：将抗菌除臭材料与透明高温油墨，稳定分散剂混配，进行充分搅拌均匀得到混合物；
SS03、正面触摸层的制备：将SS02中的混合物通过丝网印刷到玻璃原片上；
SS04、正面触摸层玻璃的制备：将SS03中印刷有抗菌除臭材料的玻璃原片进行高温烧结后，在背面进行印刷，即可得到正面触摸层玻璃。
实施例二
制备方法同实施例1，所不同的是称取0.5质量的纳米TiO2，0.5纳米银，99质量的透明油墨，经过超声处理，将纳米TiO2粉末和纳米银充分与透明油墨混合，将制成的混合油墨并通过丝网印刷到玻璃原片上，经过600℃高温烧结，即可得到正面触摸层玻璃。玻璃表面的纳米银离子抗菌层为绿色环保型抗菌剂，属于无机纳米系抗菌剂领域，具有耐热性高、抗菌性强、安全可靠等特点；纳米TiO2材料可以对其附着在玻璃表面物质氧化分解，得到抗菌的作用。
在本说明书的描述中，参考术语“一个实施例”、“示例”、“具体示例”等的描述意指结合该实施例或示例描述的具体特征、结构、材料或者特点包含于本发明的至少一个实施例或示例中。在本说明书中，对上述术语的示意性表述不一定指的是相同的实施例或示例。而且，描述的具体特征、结构、材料或者特点可以在任何的一个或多个实施例或示例中以合适的方式结合。
以上公开的本发明优选实施例只是用于帮助阐述本发明。优选实施例并没有详尽叙述所有的细节，也不限制该发明仅为所述的具体实施方式。显然，根据本说明书的内容，可作很多的修改和变化。本说明书选取并具体描述这些实施例，是为了更好地解释本发明的原理和实际应用，从而使所属技术领域技术人员能很好地理解和利用本发明。本发明仅受权利要求书及其全部范围和等效物的限制。
Claims (6)
1.一种冰箱用正面触摸层玻璃，其特征在于：所述正面触摸层玻璃(1)包括正面触摸层(2)和玻璃原片(3)、背面印刷层(4)；
所述玻璃原片(3)的背面印刷有背面印刷层(4)；所述玻璃原片(3)的正面设置有正面触摸层(2)。
2.根据权利要求1所述的一种冰箱用正面触摸层玻璃，其特征在于，所述正面触摸层(2)采用抗菌除臭材料和液体透明油墨制成。
3.根据权利要求2所述的一种冰箱用正面触摸层玻璃，其特征在于，所述正面触摸层(2)中的抗菌除臭材料的含量为0.5％-10％。
4.根据权利要求2所述的一种冰箱用正面触摸层玻璃，其特征在于，所述抗菌除臭材料选自纳米银或二氧化钛或二氧化锌或沸石中的一种或多种。
5.根据权利要求4所述的一种冰箱用正面触摸层玻璃，其特征在于，所述抗菌除臭材料中的二氧化钛的制备方法有水热法或溶胶凝胶法或气相沉积法或电化学法。
6.根据权利要求1所述的一种冰箱用正面触摸层玻璃的生产工艺，其特征在于，包括如下步骤：
SS01、将玻璃原片进行切片，磨边，清洗吹干；
SS02、将抗菌除臭材料与透明高温油墨，稳定分散剂混配，进行充分搅拌均匀得到混合物；
SS03、将SS02中的混合物通过丝网印刷到玻璃原片上；
SS04、将SS03中印刷有抗菌除臭材料的玻璃原片进行高温烧结后，在背面进行印刷，即可得到正面触感玻璃。