CN1117985A - 一种合成粘着胶 - Google Patents
一种合成粘着胶 Download PDFInfo
- Publication number
- CN1117985A CN1117985A CN 94115953 CN94115953A CN1117985A CN 1117985 A CN1117985 A CN 1117985A CN 94115953 CN94115953 CN 94115953 CN 94115953 A CN94115953 A CN 94115953A CN 1117985 A CN1117985 A CN 1117985A
- Authority
- CN
- China
- Prior art keywords
- weight ratio
- adhesive glue
- agent
- synthesized adhesive
- synthesized
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种合成粘着胶,它包含重量比在25~90%之间的热固性丙烯酸酯树脂及重量比在45%以下的颗粒状热塑性树脂两大组成要素,利用重量比为0.5~1%的交联剂及重量比为0.1%的增稠剂联结该热固性丙烯酸酯树脂及该热塑性树脂成一体,同时还于其中导入对热极敏感而重量比为0.5-1%的膨润剂。
Description
本发明与合贴物的贴合胶液有关,特别是关于一种同时兼具防水、耐水及透气性好的合成粘着胶。
习用的合贴物贴合胶液种类甚多,但各贴合胶液的组成成分单纯,属单一物性,并受限于外在环境的温度变化,因而使用一段时间后,贴合胶液容易老化或活化,不具粘着力,进而使合贴物发生分离,不耐使用的现象;此外,习用的贴合胶即使拉着性良好,也都属于一种透气性不佳的贴合胶而无法得到极佳的透气性。
兹列举以下数种贴合胶液实例,以说明上述情况:
1.热塑性丙烯酸酯树脂,其特色为具有极佳的防水性;但如遇热水仍极易使合贴物分离,故而耐水性不佳,同时经成膜后合贴物会呈现坚硬现象。
2.天然橡胶液(Latex),其特色为具有极佳的防水性,但被合贴物经长时间储存或在高温的情况下,此种胶液容易老化而使被合贴物产生分离现象。
3.乙烯乙酸乙烯酯、热塑性橡胶、聚酰胺、聚酯等类型的热塑性胶液,其特色为具有良好的防水性,但在高温的情况下,仍会再活化而不具粘着力。
4.强力胶、油性胶或丁苯橡胶型的贴合胶:该等类型胶属于天然或合成橡胶系统,在工业界广为使用,但其中掺入有溶剂,而有碍环保。
有鉴于此,本发明的主要目的在于提供一种合成粘着胶,它同时兼具有防水、耐水及透气性好等功效。
以下列举一较佳实施例说明于后,以使审查员对本发明的目的、特征及功效有更进一步的了解与认同。
本发明的合成粘着胶大体融合热固性丙烯酸酯树脂及颗粒状热塑性树脂两大组成要素,而使该合成粘着胶兼具有防水、耐水的特性,此外,还于其中导入一种对热极敏感的膨润剂,而使合成粘着胶贴覆于合贴物时,因烘干受热挥发产生许多气孔,而使合贴物增加透气性。
以下介绍本发明合成粘着胶的详细组成,它包含有:
1.一种热固性丙烯酸酯树脂,其固体成分(Solid Content)占35~55%之间,重量比则在25~90%之间。
2.一种颗粒状热塑性树脂(Thermoplastic Resin Powder),例如聚酯树脂,其粒度在350微米以下,熔点在50℃~230℃间,重量比在45%以下,来源是由回收的保特瓶或聚酯塑胶或纤维,经分级、熔融、定型、造粒后于冷冻设备中磨成粒度极细(350微米以下)的粉体。
3.一种颗粒状天然橡胶:其粒度在350微米以下,重量比在3~5%之间,用以增进合贴物合贴后的后期接着强度。
4.一种交联剂:重量比在0.5~1%之间,用以联结热固性树脂与热塑性树脂两种不同物性的材质。
5.一种膨润剂(Swelling Agent):重量比在0.5~1%间,使用日本触媒化学的S-70表面活性剂,用以让热固性丙烯酸酯树脂与热塑性树脂的混合更为均匀,而当其涂布于合贴物上并受热时,将促使合成粘着胶产生微细小孔,从而增加合贴物合贴后的透气性。
6.一种增稠剂:重量比为0.1%,特别适用于热固性丙烯酸酯树脂与热塑性树脂的结合,用以降低合成后胶液的流动性。
7.一种抑菌剂(Biocide):含量为200ppm,用以抑制合贴物因温度或温度升高而滋生的霉菌及细菌。
8.适量的水,用以平衡上述要剂,且于其中渗入重量比2~3%的水质处理剂(EDTA,即乙二胺四乙酸),用以控制水中的矿物质,以达成稳定品质的功效。
依据上述要剂的组成,本发明在操作时将适量的水与重量比45%以下的颗粒状热塑性树脂混合后,加入重量比0.5~1%的交联剂及重量比0.5%~1%的膨润剂,再加入重量比3~5%的橡胶粉粒,以及重量比25~90%的热固性丙烯酸酯树脂以及200ppm抑菌剂,在控制操作压力于latm,而操作温度在80~85℃之间,经过24小时搅混后再加入重量比为0.1%的增稠剂,即完成合成粘着胶的成品。
完成后的合成粘着胶涂布于合贴物上后,当经过加热烘干的步骤时,该膨润剂将促使合成粘着胶产生微细小孔,从而增进合贴物合贴后的透气性。
综上所述,本发明巧妙地结合了热固性丙烯酸酯树脂与颗粒状热塑性树脂,使其成为一防水、耐水的合成胶,同时还于其中添加膨润剂,使合成胶涂布于合贴物上经加热烘干步骤时,会产生许多极微细透气孔,而使合贴物又具有极佳的透气效果。
Claims (6)
1.一种合成粘着胶,它包含:
重量比在25~90%之间的热固性丙烯酸酯树脂,该丙烯酸酯树脂的固体成分(Solid Content)占35~55%;
重量比在45%以下的粉粒状热塑性树脂(Thermoplastic ResinPowder),其粒度在350微米以下,而熔点则在50℃~230℃间;
重量比为0.5~1%的交联剂;及
重量比在0.5~1%之间的膨润剂(Swelling Agent);以及
适量的水,用以平衡上述要剂,使整体重量比达到100%。
2.权利要求1的合成粘着胶,其组成成分还包含重量比为0.1%的增稠剂。
3.权利要求1的合成粘着胶,其组成成分还包含有重量比在3~5%间的颗粒状天然橡胶,其粒度在350微米以下。
4.权利要求1的合成粘着胶,其中膨润剂(Swelling Agent)使用日本触媒化学的S-70表面活性剂。
5.权利要求1的合成粘着胶,其中组成成分还掺入有含量为200ppm的抑菌剂(Biocide)。
6.权利要求1的合成粘着胶,其中适量的水中还掺入有重量比在2~3%间的水质处理剂EDTA。