CN1117898A - 连铸结晶器用保护渣 - Google Patents

连铸结晶器用保护渣 Download PDF

Info

Publication number
CN1117898A
CN1117898A CN 95106296 CN95106296A CN1117898A CN 1117898 A CN1117898 A CN 1117898A CN 95106296 CN95106296 CN 95106296 CN 95106296 A CN95106296 A CN 95106296A CN 1117898 A CN1117898 A CN 1117898A
Authority
CN
China
Prior art keywords
casting
continuously
powder
steel
graphite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 95106296
Other languages
English (en)
Inventor
翟光源
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
YICHUAN COUNTY CASTING POWDER FACTORY
Original Assignee
YICHUAN COUNTY CASTING POWDER FACTORY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by YICHUAN COUNTY CASTING POWDER FACTORY filed Critical YICHUAN COUNTY CASTING POWDER FACTORY
Priority to CN 95106296 priority Critical patent/CN1117898A/zh
Publication of CN1117898A publication Critical patent/CN1117898A/zh
Pending legal-status Critical Current

Abstract

本发明属于钢铁连铸用保护渣，它由水泥熟料、石英粉、荧石粉、纯碱等组成，通过加入一定量价格便宜、来源丰富的农作物淀粉和石墨来取替价格昂贵，供应紧张的炭黑，控制其适当含量以达到不同钢种和钢坯的连铸要求。该保护渣具有保温性能好，。熔化均匀，熔速均匀，润滑效果好，成本低等特点。

Description

连铸结晶器用保护渣
本发明属于冶金连铸领域，是钢坯连铸结晶器用保护渣技术。
随着连铸技术的发展，钢铁连铸比增长较快，相应连铸用保护渣的需求量增大。目前武钢二炼厂，河南伊川保护渣厂等生产厂家制造的保护渣，都是以水泥熟料、石英粉、萤石粉、纯碱为基础材料，配入2.5-6％的炭黑来实现其保护渣在高温下调整熔化速度的作用。又如北京钢铁研究总院的发明(CN1060050A)专利申请(91108426.6)，该项技术中除加炭黑外，还加有B2O3。来改善保护渣性能。目前炭黑生产因天燃气缺乏而限产、炭黑供应十分紧张，其价格较为昂贵，进厂价为4800元/吨。B2O3的价格则更贵。
本发明目的在于，寻求一种成本低、材料来源容易的材料取代炭黑。
本发明所提供的连铸结晶器用保护渣，亦是采用已有技术中保温渣的基础材料。其特征在于加入一定量价格低廉、来源丰富的农作物淀粉(入厂价1000元/吨)和石墨(入厂价1800元/吨)来取代炭黑。本发明的保护渣组成(重量百分比)为：水泥熟料42-46％，石英粉26-30％，萤石粉10-14％，纯碱10-14％，石墨1-17％，农作物淀粉0.5-6％。
  实施例的组成(重量比)：    1       2
  水泥熟料                  44      46
  石英粉                    27      28
  萤石粉                    12      11
  纯碱                      12      11
  石墨                      1       2
  农作物淀粉                4       2
本发明的保护渣经生产实践证明，该保护渣的熔化速度、熔化均匀性、润滑效果和保温性能都完全适应现代连铸技术的要求。加入的淀粉不仅能起到炭黑作骨架粒子调整保护渣在高温下熔化速度的作用，而且在保护渣制作过程中还起到粘合剂的作用。加入石墨提高了保温性能。石墨和淀粉同时加入，通过调整其配比，使保护渣适应不同连铸条件的需要，由于石墨和农作物淀粉的成本低，来源丰富，使保护渣成本降低178元/吨左右。在制作过程中它们又不污染环境，定会受生产厂家和使用厂家青睐。

Claims (2)

1、一种连铸结晶器用保护渣，它含有水泥熟料、石英粉、萤石粉、纯碱，其特征在于配入有农作物淀粉和石墨。
2、根据权利要求1所述的保护渣，其特征在于农作物淀粉的加入量为0.5-6％，石墨的加入量为1-17％。
CN 95106296 1995-06-03 1995-06-03 连铸结晶器用保护渣 Pending CN1117898A (zh)