CN111715720B

CN111715720B - Rotary extrusion forming die for aluminum-magnesium alloy cup-shaped piece

Info

Publication number: CN111715720B
Application number: CN202010622836.0A
Authority: CN
Inventors: 郑杰; 薛勇; 张治民; 王强; 徐健; 孟模; 张宝红; 李国俊
Original assignee: North University of China
Current assignee: North University of China
Priority date: 2020-06-29
Filing date: 2020-07-01
Publication date: 2022-05-03
Anticipated expiration: 2040-07-01
Also published as: CN111715720A

Abstract

The invention discloses a rotary extrusion forming die for an aluminum-magnesium alloy cup-shaped piece, which comprises an upper die assembly, a male die, a female die and a core die, the core mould is fixed in the forming cavity, the part between the core mould and the female mould is the forming cavity, the forming cavity comprises an extrusion section cavity, a deformation section cavity and an extrusion section cavity, by changing the cross section area and the inclination angle of the forming channel at the joint of the extrusion section cavity and the deformation section cavity and the forming channel at the joint of the deformation section cavity and the extrusion section cavity, and the female die and the core die rotate ceaselessly in the extrusion process, so that the metal undergoes twice shear deformation, twice reducing extrusion deformation and torsion deformation in the deformation process, the plastic deformation of the cup-shaped member is greatly improved, the grain refining effect is enhanced, the anisotropy of mechanical properties is reduced, and the comprehensive mechanical properties of the cup-shaped member are improved. In addition, the cup-shaped members with different specifications can be prepared by replacing the core mold, so that the production cost is reduced.

Description

Rotary extrusion forming die for aluminum-magnesium alloy cup-shaped piece

Technical Field

The invention belongs to the technical field of metal plastic processing technology and forming, and particularly relates to a rotary extrusion forming die for an aluminum-magnesium alloy cup-shaped piece.

Background

With the rapid development of the fields of aerospace, national defense and military industry, automobile industry and the like, the structural parts of the automobile have the problems of low performance and light weight. The cup-shaped member, one of the most representative structural forms in these fields, also faces a bottleneck of light weight and high performance. Magnesium alloys have received increasing attention from researchers as the lightest and potentially large metal at present, but this greatly limits the widespread use of aluminum/magnesium alloys due to their poor performance as cast aluminum/magnesium alloys (especially magnesium alloys). The cup-shaped part is a typical part of the traditional backward extrusion technology, but the performance of the cup-shaped part cannot meet the requirements of the current industrial field due to small deformation amount of the traditional backward extrusion; although the grain size of the cup-shaped piece can be effectively achieved by carrying out the backward extrusion process after the early-stage multi-pass blank making, the ideal fine grain strengthening effect is achieved, the working procedure is complex, and the production efficiency is low; in addition, in the process of forming the cup-shaped piece by the traditional extrusion process, the flow of metal is uneven, the cup wall has strong basal plane texture, the anisotropy of the component is obvious, and the tensile strength of the component in the circumferential direction and the axial direction is greatly different. Therefore, it is of practical significance to research and develop the cup-shaped member of aluminum/magnesium alloy with high performance and no anisotropy.

Disclosure of Invention

The invention mainly aims to provide a rotary extrusion forming die for an aluminum-magnesium alloy cup-shaped piece, which combines multiple deformation modes, can effectively increase the strain capacity and improve the comprehensive mechanical property of a component; and cup-shaped components with different sizes can be processed under the condition of only replacing the core die of the die, so that the processing cost is effectively saved.

In order to achieve the above purpose, the solution of the invention is as follows: a rotary extrusion forming die for an aluminum-magnesium alloy cup-shaped piece comprises an upper die assembly, a male die, a female die and a core die, wherein the upper die assembly is connected with a press workbench; the core mould is a variable cross-section cylinder, the female mould is provided with a forming cavity, the male mould is fixed on the upper mould assembly and coaxially arranged above the forming cavity, and the core mould is fixed in the forming cavity; the forming cavity comprises an extrusion section cavity positioned above the core mold, an extrusion section cavity positioned between the core mold and the forming cavity, and a deformation section cavity obliquely connected between the extrusion section cavity and the extrusion section cavity, wherein the inclined angle of the connection part of the deformation section cavity and the extrusion section cavity is a first differential angle, the inclined angle of the connection part of the deformation section cavity and the extrusion section cavity is a second differential angle, the cross-sectional area of the deformation section cavity is smaller than that of the extrusion section cavity, and the cross-sectional area of the extrusion section cavity is smaller than that of the deformation section.

As a further improvement of the invention, a lower template is arranged below the female die, and the core die is fixed on the lower template through a core die pin and a core die screw.

As a further improvement of the invention, the female die is a split female die, the split female die comprises an upper female die and a lower female die, a countersunk hole is formed in the lower die plate at the position corresponding to the mounting hole, an annular flange is formed at the lower end of the upper female die, four mounting holes are uniformly distributed in the annular flange, and the mounting holes and the countersunk hole are connected through a connecting piece, so that the upper female die and the lower female die are combined together and fixed on the lower die plate.

As a further improvement of the invention, the upper die assembly comprises an upper die plate connected with the press workbench and an upper die holder sleeve connected with the upper die plate, and a male die is fixed in the upper die holder sleeve.

The extrusion principle of the invention is as follows: during the deformation process, the blank metal undergoes twice shearing deformation similar to equal channel angular extrusion, twice reducing extrusion deformation and twisting deformation. First shearing deformation and reducing extrusion deformation: the cross section area of the cavity of the deformation section is smaller than that of the cavity of the extrusion section, and the metal is subjected to reducing deformation in the extrusion process; the existence of the first differential angle at the joint of the extrusion section cavity and the deformation section cavity causes that when metal flows from the extrusion section cavity to the deformation section cavity, the flowing speeds of all parts of metal are different, so that the stress gradient is formed in the cross section direction, and the shearing deformation is generated. And (3) second shearing deformation and reducing extrusion deformation: the cross section area of the die cavity of the extrusion section is smaller than that of the die cavity of the deformation section, and the metal is subjected to reducing extrusion deformation in the extrusion process; the existence of the second differential angle at the joint of the deformation section cavity and the extrusion section cavity causes shearing deformation when metal flows from the deformation section cavity to the extrusion section cavity. And (3) torsional deformation: in the whole deformation process, the female die rotates in the circumferential direction while the male die extrudes downwards in the axial direction, so that the metal is deformed in a circumferential torsion mode.

After the scheme is adopted, compared with the traditional backward extrusion technology, the invention has the following beneficial effects:

(1) the deformation is increased, the grain refining effect of the deformed blank is enhanced, and the comprehensive mechanical property of the cup-shaped member is improved. The traditional backward extrusion technology has small strain and poor effect of grain refinement degree; in the invention, the blank undergoes twice shear deformation, twice hole shrinkage extrusion deformation and torsion deformation in the deformation process, so that the strain capacity of the blank is effectively improved, the grain refining effect is enhanced, and the comprehensive mechanical property of the cup-shaped member is improved.

(2) The deformation is more uniform, and the anisotropy of the mechanical property of the cup-shaped component is improved. The cup wall of the cup-shaped component can form strong base texture in the deformation process of the traditional backward extrusion technology, so that the anisotropy of the mechanical property of the cup-shaped component is caused, and the component is easy to generate defects and even break in secondary processing; the cup-shaped component effectively combines the torsional deformation, the shearing deformation and the reducing extrusion deformation, so that the blank undergoes the shearing deformation and the torsional deformation twice in the deformation process, the anisotropy of the mechanical property of the cup wall of the cup-shaped component is effectively improved, and the comprehensive mechanical property of the cup-shaped component is improved.

(3) The metal stress state and the strain amount of the deformed blank can be changed. The invention can change the metal flowing state by changing the revolution number of the female die without changing the die, thereby changing the strain capacity to realize different requirements on the performance of the cup-shaped component; and the invention can process light high-performance cup-shaped members with different sizes under the condition of only replacing the core mould and keeping other deformation processes and operation flows unchanged.

After the scheme is adopted, compared with the existing excellent cup-shaped member forming technology, the invention has the following beneficial effects:

(1) the deformation is more uniform. In the deformation process, two times of shearing deformation, two times of reducing extrusion deformation and twisting deformation are combined, so that the refinement degree of crystal grains is enhanced, and the anisotropy of mechanical properties caused by the traditional extrusion technology is further improved.

(2) The processing cost is reduced. In the existing cup-shaped component forming technology, a mold cavity is complex, and only cup-shaped components of the same specification can be processed; by replacing the core moulds with different sizes, other deformation processes and operation processes are unchanged, the cup-shaped members with different specifications can be prepared, and the production cost is effectively reduced.

Drawings

FIG. 1 is a schematic structural diagram of a mold according to an embodiment of the present invention;

FIG. 2 is a schematic front view of a male mold according to one embodiment of the invention;

FIG. 3 is a schematic bottom view of a punch according to an embodiment of the present invention;

fig. 4 is a schematic front view of a core mold according to an embodiment of the present invention;

fig. 5 is a schematic bottom view of a core mold according to an embodiment of the invention;

FIG. 6 is a schematic view of a forming cavity according to one embodiment of the invention;

FIG. 7 is a schematic structural view of an embodiment of the present invention before extrusion;

FIG. 8 is a schematic view of an extruded structure according to an embodiment of the present invention;

FIG. 9 is a schematic view of the extrusion process according to one embodiment of the present invention;

FIG. 10 is a schematic view of an extruded cup-shaped member according to an embodiment of the present invention;

FIG. 11 is a schematic diagram of a Deform-3D simulation of a conventional backward extrusion process;

FIG. 12 is a 10mm thick wall cup wall and 0.209Rad/sDeform-3D simulation of die rotation for a cup-shaped member according to one embodiment of the present invention;

FIG. 13 is a 10mm thick wall thickness of the cup-shaped member cup at a 0.418Rad/sDeform-3D die rotation speed simulation in accordance with one embodiment of the present invention;

FIG. 14 is a 10mm thick wall thickness of the cup-shaped member and a 0.627Rad/sDeform-3D simulation of die rotation speed for an embodiment of the present invention;

FIG. 15 is a simulated view of a cup-shaped member according to an embodiment of the present invention, wherein the cup wall thickness is 5mm and the die rotation speed is 0.209 Rad/sDeform-3D.

Description of reference numerals:

1-upper template, 2-upper pin, 3-upper die holder sleeve, 4-male die, 5-upper female die, 6-extrusion section cavity, 7-first differential angle, 8-second differential angle, 9-bolt, 10-nut, 11-gasket, 12-lower female die, 13-lower pin, 14-lower template, 15-lower screw, 16-core die, 17-extrusion section cavity, 18-deformation section cavity, 19-upper screw, 20-blank, 21-core die pin and 22-core die screw.

Detailed Description

In order to more clearly illustrate the embodiments of the present invention or the technical solutions in the prior art, the drawings used in the description of the embodiments or the prior art will be briefly described below, it is obvious that the drawings in the following description are only some embodiments of the present invention, and for those skilled in the art, other drawings can be obtained according to the drawings without creative efforts.

The invention provides a rotary extrusion forming die for an aluminum-magnesium alloy cup-shaped piece, which refers to fig. 1 and comprises an upper die assembly connected with a press workbench (not shown in the figure), a male die 4, a lower die plate 14, a female die connected with a rotating mechanism (not shown in the figure) and a core die 16; go up the mould subassembly and include the cope match-plate pattern 1 of being connected with the press workstation and with cope match-plate pattern 1 through last pin 2 and the fixed die holder cover 3 of last screw 19, go up die holder cover 3 internal fixation terrace die 4, the die is the components of a whole that can function independently die, the components of a whole that can function independently die includes die 5 and lower die 12, makes things convenient for the dismouting and gets the material.

The split female die is provided with a forming cavity, the male die 4 is coaxially arranged above the forming cavity, and the core die 16 is fixed in the forming cavity; the forming cavity comprises an extruding section cavity 6, a deforming section cavity 18 and an extruding section cavity 17, the extruding section cavity 6 is a space above the core mold 16, the extruding section cavity 17 is a space between the core mold 16 and the forming cavity, the deforming section cavity 18 is a space connected between the extruding section cavity 6 and the extruding section cavity 17, a central axis of the deforming section cavity inclines at a certain angle, an inclination angle of a joint of the deforming section cavity 18 and the extruding section cavity 6 is a first differential angle 7, an inclination angle of a joint of the deforming section cavity 18 and the extruding section cavity 17 is a second differential angle 8, in addition, in combination with the drawing 6, the cross-sectional area of the deforming section cavity is smaller than that of the extruding section cavity, and the cross-sectional area of the extruding section cavity is smaller than that of the deforming section.

A lower template 14 is arranged below the lower female die 12, and the core die 16 is fixed on the lower template through a core die pin 21 and a core die screw 22. The central axis of the core die 16 is coaxial with the central axis of the split female die. The core die 16 and the lower concave die 12 are fixedly connected to the lower template 14 through lower pins 13 and lower screws 15; an annular flange is formed at the lower end of the upper female die 5, four mounting holes are uniformly distributed in the annular flange, namely, the setting interval between the mounting holes is 90 degrees, countersunk holes are formed in the positions, corresponding to the mounting holes, of the lower die plate 14, the countersunk holes are connected with the mounting holes through connecting pieces (specifically bolts 9) and are fixed through nuts 10, and gaskets 11 are arranged between the bolts 9 and the nuts 10, so that the upper female die 5 and the lower female die 12 are combined together and fixed on the lower die plate 14. The split female dies are fixed on the rotating mechanism through the lower die plate 14, and the rotating mechanism drives the split

female dies

5 and 12 to rotate circumferentially while the press workbench drives the male die 4 to extrude downwards in the axial direction.

The core die 16 is a variable cross-section cylinder, and cup-shaped members with different sizes can be prepared by replacing core dies 16 with different sizes. As shown in FIG. 10, which is a schematic view of an extruded cup-shaped member of the present invention. The cup-shaped member has an inner diameter D and an outer diameter D1.

The following description will be made of an embodiment in which a magnesium alloy cup-shaped member having an outer diameter of 200mm and an inner diameter of 180mm is prepared.

An embodiment:

referring to fig. 7-9, in the present embodiment, a cylindrical blank 20 with a diameter of 168mm and a height of 140mm is used, a forming cavity L is 34mm, an L1 is 15mm, an L2 is 10mm (L > L1> L2), a diameter D of a core mold 16 is 180mm, a first differential angle 7 and a second differential angle 8 are 117 °, a pressing speed of a punch 1 is 1mm/s, a rotating speed of a die is 0.21Rad/s, and a lubricant is selected from oil-based graphite.

A rotary extrusion forming method of an aluminum-magnesium alloy cup-shaped piece comprises the following steps:

step one, preparing before forming: blanking, processing the bar stock into a cylindrical blank 20 with the diameter of 168mm and the height of 140mm, and carrying out homogenization and heat preservation on the blank 20 at the temperature T of 300 ℃ for 12 h; assembling the aluminum-magnesium alloy cup-shaped piece rotary extrusion forming die, and putting the aluminum-magnesium alloy cup-shaped piece rotary extrusion forming die into a heat preservation furnace to heat to 300 ℃ for 1 h; and taking out the heat-insulated mold, installing and fixing the male mold component on the workbench of the press machine, and installing and fixing the female mold component on the rotating mechanism.

Step two, a forming process: after oil-based graphite is coated on the outer surface of the male die 1 and the inner surface of the female die forming cavity, the homogenized blank 20 is taken out of the heat preservation furnace, and the outer surface of the blank 20 is uniformly and quickly coated with the oil-based graphite and then is placed into the extrusion section cavity 6; the pressure mechanism and the rotating mechanism are started, the axial feeding of the male die 4 and the circumferential rotation of the split female dies 5 and 12 are controlled, so that metal flows uniformly, and due to the existence of the first differential angle 7 and the second differential angle 8, when the metal flows from the extrusion section cavity 6 to the extrusion section cavity 17 through the deformation section cavity 18, the flow rate of each part of the metal is different, a stress gradient is formed at the connection position of each cavity, and two times of shearing deformation is generated; meanwhile, when the metal flows from the extrusion section cavity 6 to the deformation section cavity 18, the cross section area of the cavity is reduced from L to L1, so that the metal is subjected to reducing extrusion deformation; when the metal flows from the deformation section cavity 18 to the extrusion section cavity 17, the cross section area of the cavity is reduced from L1 to L2, so that the metal is subjected to secondary diameter reduction extrusion deformation until the forming cavity is filled. In summary, during the deformation process, when the metal flows from the extrusion section cavity 6 to the extrusion section cavity 17, the metal undergoes two times of shearing deformation and two times of reducing extrusion deformation.

Step three, forming is completed: after the cavity is filled with metal, the nut 10 is removed, the upper die 5 is removed, the lower pin 13 and the lower screw 15 are removed, the lower die 12 is removed, and the formed cup-shaped member is taken out.

In the whole deformation process, the lower female die assembly and the core die 16 are driven by the rotating mechanism to rotate in the circumferential direction, so that the metal also generates circumferential torsional deformation in the deformation process.

(3) The metal stress state and the strain amount of the deformed blank can be changed. The invention can change the metal flowing state by changing the revolution number of the female die without changing the die, thereby changing the strain capacity to realize different requirements on the performance of the cup-shaped component; and the invention can process light high-performance cup-shaped members with different sizes under the condition of only replacing the core mould and keeping other deformation processes and operation processes unchanged.

The specific dimension is substituted into Deform-3D finite element simulation software to carry out the traditional backward extrusion process and the rotary extrusion simulation analysis of the cup-shaped component, and further verification is made that the invention can obtain larger plastic deformation. In terms of simulation parameter setting, the mold material was introduced as a 45 steel mold, and the blank material was introduced as AZ 80. The temperatures of the die and the blank are both 300 ℃, the grid division is 50000, the pressing speed of the male die is 1mm/s, the friction coefficient is 0.3, and the rotary extrusion speed is 0.209439Rad/s, 0.418878Rad/s and 0.628317 Rad/s. Adopting blanks with the same size, and preparing a cup-shaped member with the height of 200mm, the inner diameter of 180mm and the outer diameter of 200mm by using a traditional backward extrusion process; the inventive die produces cup-shaped members 200mm high, 180mm inner diameter and 200mm outer diameter, as well as 200mm high, 90mm inner diameter and 200mm outer diameter. As shown in fig. 11, which is a diagram of a conventional back-extrusion process, for a form-3D simulation, it can be seen that the average equivalent strain is 1.45. As shown in FIGS. 12-14, the above is a simulation of the cup wall thickness of the cup-shaped member of the present invention with a die rotation speed of 0.209Rad/s, 0.418Rad/s and 0.627Rad/s Deform-3D, and it can be seen that when the rotation speed is 0.209Rad/s, the average equivalent strain is 3.79, the maximum folding angle is 328 degrees, the average folding angle is 115 degrees, and the average damage value is 0.098; at a rotation speed of 0.418Rad/s, the average equivalent strain was 3.78, the maximum fold angle was 284 °, the average fold angle was 116 °, and the average damage value was 0.0931; at a rotational speed of 0.627Rad/s, the average equivalent strain was 3.34, the maximum fold angle was 265 °, the average fold angle was 113 °, and the average damage value was 0.0805. Through the simulation of the traditional backward extrusion process and the process disclosed by the invention on the blanks with the same size under the same processing conditions, the average equivalent strain of the process disclosed by the invention is far greater than that of the traditional backward extrusion process, and the technical advantages of the process disclosed by the invention are further verified. In addition, from comparison of fig. 12 to 14, it is found that the average equivalent strain is gradually reduced with the increase of the rotation speed, but the maximum folding angle and the average damage value are both greatly reduced, which indicates that the increase of the rotation speed is helpful for improving the blank forming performance and avoiding cracking and folding defects. FIG. 15 is a Deform-3D simulation of a mold according to the present invention for making cup-shaped members with an outer diameter of 200mm and an inner diameter of 190mm at a rotation speed of 0.209Rad/s, demonstrating that cup-shaped members of different specifications can be made by changing the size of the core mold, and that the increase in the amount of reduction extrusion deformation results in an average equivalent strain of 6.40. In summary, the above experimental data show that the advantages of the present invention are: the strain capacity is large; deformation is uniform; the deformation state is controllable; cup-shaped components with different specifications can be prepared only by replacing the core mould, so that the processing cost is reduced.

In the description herein, references to the description of the term "one embodiment," "some embodiments," "an example," "a specific example," or "some examples," etc., mean that a particular feature, structure, material, or characteristic described in connection with the embodiment or example is included in at least one embodiment or example of the invention. In this specification, the schematic representations of the terms used above should not be understood to necessarily refer to the same embodiment or example. Furthermore, the particular features, structures, materials, or characteristics described may be combined in any suitable manner in any one or more embodiments or examples. Furthermore, various embodiments or examples described in this specification can be combined and combined by those skilled in the art.

The information in this background section is only for enhancement of understanding of the general background of the invention and is not necessarily to be construed as an admission or any form of suggestion that this information forms the prior art that is already known to a person of ordinary skill in the art.

The above description is only a preferred embodiment of the present invention, and is not intended to limit the design of the present invention, and all equivalent changes made in the design key point of the present invention fall within the protection scope of the present invention.

Claims

1. The utility model provides an almag cup piece rotary extrusion forming die which characterized in that: comprises an upper die component connected with a press workbench, a male die, a female die connected with a rotating mechanism and a core die; the core die is a variable cross-section cylinder, the female die is provided with a forming cavity, the male die is fixed on the upper die assembly and coaxially arranged above the forming cavity, and the core die is fixed in the forming cavity; the forming cavity comprises an extrusion section cavity positioned above the core mold, an extrusion section cavity positioned between the core mold and the forming cavity, and a deformation section cavity obliquely connected between the extrusion section cavity and the extrusion section cavity, wherein the inclined angle of the connection part of the deformation section cavity and the extrusion section cavity is a first differential angle, the inclined angle of the connection part of the deformation section cavity and the extrusion section cavity is a second differential angle, the cross-sectional area of the deformation section cavity is smaller than that of the extrusion section cavity, and the cross-sectional area of the extrusion section cavity is smaller than that of the deformation section;

the die is the components of a whole that can function independently die, the components of a whole that can function independently die includes last die and lower die, and the position that the lower bolster corresponds the mounting hole is equipped with the counter sink, go up the die lower extreme and form annular flange, four mounting holes of equipartition on the annular flange, mounting hole and counter sink pass through the connecting piece and connect to go up the die and close together and fix on the lower bolster with lower die.

2. The rotary extrusion forming die for the aluminum-magnesium alloy cup-shaped piece according to claim 1, wherein: and a lower template is arranged below the female die, and the core die is fixed on the lower template through a core die pin and a core die screw.

3. The rotary extrusion forming die for the aluminum-magnesium alloy cup-shaped piece according to claim 1, wherein: the upper die assembly comprises an upper die plate connected with the press workbench and an upper die base sleeve connected with the upper die plate, and a male die is fixed in the upper die base sleeve.