CN111593457A - 一种高强超低收缩型涤纶长丝接经工艺 - Google Patents
一种高强超低收缩型涤纶长丝接经工艺 Download PDFInfo
- Publication number
- CN111593457A CN111593457A CN202010482459.5A CN202010482459A CN111593457A CN 111593457 A CN111593457 A CN 111593457A CN 202010482459 A CN202010482459 A CN 202010482459A CN 111593457 A CN111593457 A CN 111593457A
- Authority
- CN
- China
- Prior art keywords
- warp
- polyester filament
- shrinkage polyester
- yarns
- low shrinkage
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明的高强超低收缩型涤纶长丝接经工艺,此制备工艺不仅省时省力,提高了生产效率,同时,接经工艺的高效对高强超低收缩型涤纶长丝的生产效率的提升有极大的帮助,经纱组数量控制在200组到300组之间能有效的提升接经的效率,每组经纱组的距离在2mm能使得每组经纱组之间的排布更合理,能够提升能够接经的速度。
Description
技术领域
本发明属于新型纤维及复合材料制备技术,特别涉及一种高强超低收缩型涤纶长丝接经工艺。
背景技术
随着人们生活水平的提高,人们对产品功能及质量的意识不断提高,特别是在涤纶丝的选择方面,越来越注重涤纶丝的各项性能。高强超低收缩型涤纶长丝,具有耐磨性、阻燃性、抗芯吸性等特点,在市场上有很大的占有率。
发明内容
发明目的为更好的生产高强超低收缩型涤纶长丝,是的生产高强超低收缩型涤纶长丝的接经工艺更高效。
技术方案:一种高强超低收缩型涤纶长丝接经工艺:制备工艺包括如下步骤:
(1)将旧经纱和经纱组上新经纱放入接经机内;
(2)通过接经机内的夹持部件对旧经纱和新经纱进行固定;
(3)启动接经机,将在接经机内完成旧经纱和新经纱的接经;
(4)清理余留的废丝,并将继续整经的工作。
进一步,上述的高强超低收缩型涤纶长丝接经工艺,其特征在于:经纱组数量为200到300组。作为本发明的一种优选,经纱组数量在200到300组之间,能更好的提升工作效率,合理的经纱组数量在实际操作中不容易产生错乱和能够减少失误。
进一步,上述的高强超低收缩型涤纶长丝接经工艺,其特征在于:每组经纱组之间的距离为2mm。作为本发明的一种优选,每个经纱组之间的距离相等,使得排布更合理,在使用及操作方面能够更好的提升效率。
进一步,上述的高强超低收缩型涤纶长丝接经工艺,其特征在于:单个经纱的粗细为150D到200D。作为本发明的一种优选,单个经纱的粗细对最后接经会产生一定的影响,将当个经纱的粗细程度控制在一个合理的范围内,150D到200D的粗细能够通过满足在接经时候单个经纱之间的连贯性。
进一步,上述的高强超低收缩型涤纶长丝接经工艺,其特征在于:接经机型号为groz-beckert AS/3型接经机。作为本发明的一种优选,接经机的性能对接经能够产生直接的影响,稳定可靠的接经机能更好的满足接经的需要。
上述技术方案可以看出,本发明具有如下有益效果:本发明的高强超低收缩型涤纶长丝接经工艺,此制备工艺不仅省时省力,提高了生产效率,同时,接经工艺的高效对高强超低收缩型涤纶长丝的生产效率的提升有极大的帮助,经纱组数量控制在200组到300组之间能有效的提升接经的效率,每组经纱组的距离在2mm能使得每组经纱组之间的排布更合理,能够提升能够接经的速度。
具体实施方式
下面结合具体实施例,进一步阐明本发明。
实施例1
一种高强超低收缩型涤纶长丝接经工艺:制备工艺包括如下步骤:
(1)将旧经纱和经纱组上新经纱放入接经机内;
(2)通过接经机内的夹持部件对旧经纱和新经纱进行固定;
(3)启动接经机,将在接经机内完成旧经纱和新经纱的接经;
(4)清理余留的废丝,并将继续整经的工作。
同时,经纱组数量为200到300组。
此外,每组经纱组之间的距离为2mm。
另外,单个经纱的粗细为150D到200D。
其中,接经机型号为groz-beckert AS/3型接经机。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明原理的前提下,还可以做出若干改进,这些改进也应视为本发明的保护范围。
Claims (5)
1.一种高强超低收缩型涤纶长丝接经工艺:其特征在于:所述制备工艺包括如下步骤:
将旧经纱和经纱组上新经纱放入接经机内;
通过接经机内的夹持部件对旧经纱和新经纱进行固定;
启动接经机,将在接经机内完成旧经纱和新经纱的接经;
清理余留的废丝,并将继续整经的工作。
2.根据权利要求1所述的高强超低收缩型涤纶长丝接经工艺,其特征在于:所述经纱组数量为200到300组。
3.根据权利要求2所述的高强超低收缩型涤纶长丝接经工艺,其特征在于:所述每组经纱组之间的距离为2mm。
4.根据权利要求1所述的高强超低收缩型涤纶长丝接经工艺,其特征在于:单个经纱的粗细为150D到200D。
5.根据权利要求1所述的高强超低收缩型涤纶长丝接经工艺,其特征在于:所述接经机型号为groz-beckert AS/3型接经机。