CN1114042A - 一体成型防弹头盔的制造方法 - Google Patents

一体成型防弹头盔的制造方法 Download PDF

Info

Publication number
CN1114042A
CN1114042A CN 94105876 CN94105876A CN1114042A CN 1114042 A CN1114042 A CN 1114042A CN 94105876 CN94105876 CN 94105876 CN 94105876 A CN94105876 A CN 94105876A CN 1114042 A CN1114042 A CN 1114042A
Authority
CN
China
Prior art keywords
fiber cloth
cloth
bulletproof halmet
resin
proof
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 94105876
Other languages
English (en)
Inventor
周胜贤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TONGGUO INDUSTRY Co Ltd
Original Assignee
TONGGUO INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TONGGUO INDUSTRY Co Ltd filed Critical TONGGUO INDUSTRY Co Ltd
Priority to CN 94105876 priority Critical patent/CN1114042A/zh
Publication of CN1114042A publication Critical patent/CN1114042A/zh
Pending legal-status Critical Current

Abstract

一体成型防弹头盔制造方法，采用3000丹尼纤 维丝编织成强力纤维布，用树脂调制挤压成薄膜，令 纤维布与树脂薄膜辗压一复合纤维层，再将此复合纤 维布裁切旋叶片状而折弯成碗状，令其层层交错叠 置，且于上侧数层圆心顶点处置入补强纤维布，以利 挤压拉伸成型，再于高温高压下用膜具对叠置的碗状 复合纤维布加压。令其紧密结合，而成一组织细密的 高密度纤维壳体，同时自动截断其成品毛边废料，再 喷以耐高温的防火涂料，即可成为强度高，防弹能力 好，重量轻的一体成型防弹头盔。

Description

本发明涉及一种一体成型防弹头盔的制造，特别涉及一种成型迅速且结构组织细密的防弹头盔制造方法。
现有的头盔一种为钢制的，其本身重量非常重，防弹效果也不好。另一种以合成强化纤维布涂覆树脂，待干后层层叠置以模具加压成型，成型后需另予以修整毛边废料，方成一完整半成品，然而在加工过程中，纤维布的制作非常费时，而且成型后的盔体裁修工作繁杂，使整个制作过程费时费工，很不经济。
本发明的目的在于提供一种一体成型的防弹头盔制造方法，其工艺简单，头盔流线性好。
为了实现上述目的，本发明采用纤维丝编织成强力纤维布，用树脂调制挤压成薄膜，令纤维布与树脂薄膜在20℃～30℃温度下辗压成复合纤维布，再将此复合纤维布裁切成旋叶片状后折弯成碗状，令其层层交错叠置，且于上侧数层圆心顶点处置入补强纤维布，以利挤压拉伸成型，再于高温高压下用膜具对叠置的碗状复合纤维布加压。令其紧密结合，而成一组织细密的高密度纤维壳体，同时自动截断其成品毛边废料，再喷以耐高温的防火涂料。
采用本方法生产出的防弹头盔，具有强度高，防弹能力好，重量轻的特点。而且由于采用一次成型的生产方法，具有如下优点：
1.强力纤维布与混合树脂以披覆法结合制成复合纤维布，其制作时间短，强度佳;
2.复合纤维布交错叠置，令组织细密，弹头不易贯穿;
3.复合纤维布预折成碗状，于高温加压时，不易因挤压拉伸而过度变形，故无盔体厚度不均匀而致头盔之防弹能力减低的缺点;
4.盔体以上下模具直接一体成形，且同时藉下模具的切断口连带切断毛边废料，制造迅速，省时省工;
5.盔体约重1.2～1.3kg，比目前世界各国所使用的防弹头盔重量轻。
下面结合附图详细说明本发明的实施例。
附图说明：
图1.为本发明的工艺流程图
图2.为复合纤维布辗制示意图
图3.为本发明裁切的旋叶片体形状图
图4.为本发明模具加压成型示意图
图5.为本发明实例成品外观图
图中标号说明：
（1）强力纤维布  （2）薄膜
（3）滚轮  （A）复合纤维布
（A1）缺口  （A2）片体
（B）补强纤维布  （C）上模具
（D）下模具  （D1）切断口
三、实施例1
图1所示本发明的流程分为复合纤维布的制作，裁切成型及叠置加压成型三部分。
其中，复合纤维布的制作分为：
（1）将含3000丹尼纤维丝的纤维，以单股交织编成一强力纤维布，即为3000丹尼1×1组织之强力纤维布（1）;
（2）强化树脂为45%之酚醛树脂及聚乙烯醇缩丁醛树脂混合调制挤压成一披覆薄膜（2）;
（3）将混合树脂制成的薄膜（2）披覆于强力纤维布（1）上，在温度为20℃下以滚轮（3）辗压，令两者紧密结合，即成一组织细密的复合纤维布（A）、（如图2所示）。
复合纤维布的裁切成形如图3所示：
将辗压成型的复合纤维布（A）先裁切成圆形，再于圆周外缘裁出三角缺口（A1），令圆形的复合纤维布（A）形成一具八叶片体（A2）的旋叶状，且于缺口（A1）尖端向圆心点制作切口（A3），以利弯曲接合成型。
叠置加压成型，如图4所示：
将裁切后的旋叶状复合纤维布（A）由切开处折弯片体（A2），使其互相连接而成一碗体，用15层交笋叠置，且于上侧，如图4所示的位置处在圆心顶点夹层内置入略呈三角状的补强纤维布（B），以适应顶点处受挤压时较大的拉伸变形度，再将层层叠置之复合纤维布料（A）置于一组上下模具（C）（D）中，于高温170℃，高压7kg/cm2对该复合纤维布料加压（A）并维持10分钟，令其压挤成一组织紧密且为一体之壳体，同时上模具（C）以周缘配合下模具（D）之切断口（D1）自动截断毛边废料，再涂以耐高温的防火涂料，从而制成本发明涉及的防弹头盔成品（如图五所示）。
实施例2：
复合纤维布的制作部分，采用50%之酚醛树脂及聚乙烯醇缩丁醛树脂混合调制挤压成一披覆薄膜（2），选用25℃温度下辗压，其它与实施例1相同，裁切成型部分与实施例1相同，而叠置加压成型部分中将层层叠置的复合纤维布料（A）置于一组上下模具（C）（D）中时，于高温175℃高压7.5kg/cm2下对复合纤维布料（A）加压并维持12.5分钟，令其压成一组织紧密且为一体的壳体，同时上模具（C）以周缘配合下模具（D）之切断口（D1）自动截断毛边废料，再涂以耐高温的防火涂料，即制成本发明涉及的防弹头盔成品（如图五所示）。
实施例3：
复合纤维布的制作部分，以55%之酚醛树脂及聚乙烯醇缩丁醛树脂混合调制挤压成一披覆薄膜（2），选用30℃温度下辗压，其它与实施例1相同，裁切成型部分与实施例1相同，而叠置加压成型部分中将层层叠置的复合纤维布料（A）置于一组上下模具（C）（D）中时，于高温180℃高压8kg/cm2下对复合纤维布料（A）加压并维持15分钟，令其压成一组织紧密且为一体的壳体，同时上模具（C）以周缘配合下模具（D）之切断口（D1）自动截断毛边废料，再涂以耐高温的防火涂料，即制成本发明涉及的防弹头盔成品（如图五所示）。

Claims (4)

1、一种一体成型防弹头盔的制造方法，其特征在于：用树脂调和挤压预制成的薄膜披覆于3000丹尼纤维丝单股纺织成的强力纤维布上，辗压制成复合纤维布；再将此复合纤维布裁切成旋叶状，并折弯成碗状，令其层层交错叠置，且于上侧多层的圆心顶点间置入补强纤维布，而于高压高温下在成型模具中对叠置的碗状复合纤维布加压，使其压缩紧密，而成一组织细密的高密度纤维壳体，同时以上下模具相配合自动裁断毛边废料，再喷上耐高温的防火涂料，制成防弹头盔。
2、根据权利要求1所述的一体成型防弹头盔的制造方法，其特征在于：所述树脂为浓度45%至55%之酚醛树脂与聚乙烯醇缩丁醛树脂混合成而成。
3、根据权利要求1所述的一体成型防弹头盔的制造方法，其特征在于：所述加压温度为170～180℃;压力为7～8kg/cm2。
4、根据权利要求1所述的一体成型防弹头盔的制造方法，其特征在于：该叠置复合纤维布于成型模具中加压的时间可为10～15分钟。
CN 94105876 1994-05-31 1994-05-31 一体成型防弹头盔的制造方法 Pending CN1114042A (zh)