CN111321419A - 一种用于马口铁工艺中的脱脂剂及使用方法 - Google Patents
一种用于马口铁工艺中的脱脂剂及使用方法 Download PDFInfo
- Publication number
- CN111321419A CN111321419A CN202010285235.5A CN202010285235A CN111321419A CN 111321419 A CN111321419 A CN 111321419A CN 202010285235 A CN202010285235 A CN 202010285235A CN 111321419 A CN111321419 A CN 111321419A
- Authority
- CN
- China
- Prior art keywords
- tinplate
- degreasing agent
- polyoxyethylene ether
- agent
- surfactant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种用于马口铁工艺中的脱脂剂及使用方法,包含表面活性剂、防锈剂和助剂等。采用的表面活性剂为非离子表面活性剂如烷基聚萄糖苷、壬基酚聚氧乙烯醚和脂肪醇聚氧乙烯醚,以及阴离子表面活性剂如仲烷基磺酸钠、脂肪醇聚氧乙烯醚硫酸钠和脂肪醇聚氧乙烯醚磷酸酯。本发明的配方质量组成为非离子表面活性剂0.3%~2%,阴离子表面活性剂0.3%~2%,防锈剂为三乙醇胺0.1%‑2%、乌洛托品0.1%‑2%,防腐剂为丙酸钙1%‑5%、助剂为乙醇1%‑5%、余量为去离子水。本发明的脱酯剂能够迅速有效地清除马口铁金属表面的油脂及污染物,并对金属表面具有良好的防锈作用。
Description
技术领域
本发明涉及一种用于马口铁工艺中的脱脂剂及使用方法,特别是用于清洗钢带加工过程中金属表面脱脂剂及其使用方法。
背景技术
马口铁等金属零件的加工过程中,大多数都使用油性润滑剂和类似物质,在金属零件表面会留下油渍。金属零件在表面处理之前或最终使用前,需要将这些油渍除去。去除油渍的金属表面脱脂剂包括二氯甲烷、汽油、氢氧化钠等,在油渍较难处理时,通常采用蒸汽脱脂法。蒸汽脱脂法是将金属零件暴露在不断回流的脱脂剂气化物中。该 方法虽然脱脂效果较好,但工业中常用的碱性脱脂剂中含有大量的碱性物质如40~50%NaOH、20~40%Na2CO3,并且含磷,如磷酸三丁酯、磷酸三钠等等,含价格昂贵且对工件腐蚀大,脱脂时间长(对重污垢零件清理需要更长时间 ),并且需要加热至 85℃~95℃,能耗大,溶剂挥发和含磷都会严重污染环境。因此,设计出一种便于清理马口铁表面油渍,进行脱脂处理的表面脱脂剂则显得非常有必要。
发明内容
本发明的旨在提供一种用于马口铁工艺中的脱脂剂及使用方法,它解决上述现有技术所存在的技术问题,能够快速、有效、彻底地清除马口铁上的油脂和污染物,并对具有保护金属表面免受腐蚀。
技术方案如下所示:
一种用于马口铁工艺中的脱脂剂及使用方法,包含表面活性剂、防锈剂和助剂等。采用的表面活性剂为非离子表面活性剂如烷基聚萄糖苷、壬基酚聚氧乙烯醚和脂肪醇聚氧乙烯醚,以及阴离子表面活性剂如仲烷基磺酸钠、脂肪醇聚氧乙烯醚硫酸钠和脂肪醇聚氧乙烯醚磷酸酯。本发明的配方质量组成为非离子表面活性剂0.3%~2%,阴离子表面活性剂0.3%~2%,防锈剂为三乙醇胺0.1%-2%、乌洛托品0.1%-2%,防腐剂为丙酸钙1%-5%、助剂为乙醇1%-5%、余量为去离子水。本发明的脱酯剂能够迅速有效地清除马口铁金属表面的油脂及污染物,并对金属表面具有良好的防锈作用。
进一步的,所述表面脱脂剂的使用方法如下:
(1)将加工完成的马口铁工件在室温下没入表面脱脂剂溶液内,浸渍5-10min;
(2)取出马口铁工件,观察表面能否形成连续水膜,若能形成,表示马口铁工件清理完成,反之。
进一步说明的是,表面活性剂为非离子表面活性剂如烷基聚萄糖苷、壬基酚聚氧乙烯醚和脂肪醇聚氧乙烯醚,以及阴离子表面活性剂如仲烷基磺酸钠、脂肪醇聚氧乙烯醚硫酸钠和脂肪醇聚氧乙烯醚磷酸酯,可以强烈地吸附在污垢表面,具有脱脂、乳化、增溶、去污能力和消泡等作用,提高油脂和污垢的脱除能力,同时配方中的缓蚀剂及防腐剂能有效地防止金属腐蚀。
有益效果
本发明提供的马口铁用表面脱脂剂,其组成简单、配制方便,同时可在常温条件下进行使用,且清洗率高。
具体实施方式
实施例1
以10Kg金属表面脱脂剂为例 ( 按重量百分比 ) :非离子表面活性剂烷基聚萄糖苷0.1%+壬基酚聚氧乙烯醚0.1%和脂肪醇聚氧乙烯醚0.1%,阴离子表面活性剂仲烷基磺酸钠1%+脂肪醇聚氧乙烯醚硫酸钠0.1%+脂肪醇聚氧乙烯醚磷酸酯0.1%,防锈剂三乙醇胺0.1%、乌洛托品2%,防腐剂丙酸钙5%、助剂乙醇1%、去离子水90.4%。
按上述方法制备马口铁用表面脱脂剂溶液。将加工完成的马口铁工件在室温下没入上述脱脂剂溶液中,浸泡 5min 后取出,观察工件表面能形成连续水膜,说明已完全清洗干净。
实施例 2 :
以10Kg金属表面脱脂剂为例 ( 按重量百分比 ) :非离子表面活性剂烷基聚萄糖苷1.5%+壬基酚聚氧乙烯醚0.3%+脂肪醇聚氧乙烯醚0.2%,阴离子表面活性剂仲烷基磺酸钠1.8%+脂肪醇聚氧乙烯醚硫酸钠0.1%+脂肪醇聚氧乙烯醚磷酸酯0.1%,防锈剂三乙醇胺1%、乌洛托品0.1%,防腐剂丙酸钙1%、助剂乙醇2%、去离子水91.9%。
按上述方法制备马口铁用表面脱脂剂溶液。将加工完成的马口铁工件在室温下没入上述脱脂剂溶液中,浸泡 8min 后取出,观察工件表面能形成连续水膜,说明已完全清洗干净。
实施例 3 :
以10Kg金属表面脱脂剂为例 ( 按重量百分比 ) :非离子表面活性剂烷基聚萄糖苷0.1%+壬基酚聚氧乙烯醚0.5%+脂肪醇聚氧乙烯醚0.5%,阴离子表面活性剂仲烷基磺酸钠0.1%+脂肪醇聚氧乙烯醚硫酸钠0.1%+脂肪醇聚氧乙烯醚磷酸酯0.1%,防锈剂三乙醇胺2%、乌洛托品0.1%,防腐剂丙酸钙2%、助剂乙醇5%、去离子水89.5%。
按上述方法制备马口铁用表面脱脂剂溶液。将加工完成的马口铁工件在室温下没入上述脱脂剂溶液中,浸泡 10min 后取出,观察工件表面能形成连续水膜,说明已完全清洗干净。
上述事实例仅为优选实施例而已,并不用于限制发明,尽管参照前述事实例对本发明进行详细的说明,对于本领域的技术人员来说,其依然可以对前述实施例所记载的技术方案进行修改,或者对其部分技术特征进行同等替换。凡在发明的精神和原则至内,所做的任何修改、同等替换、改进等,均应包含在本发明的保护范围之内。
Claims (7)
1.一种用于马口铁工艺中的脱脂剂及使用方法,其特征在于,所述表面脱脂剂包含有表面活性剂、防锈剂、防腐剂和助剂。
2.根据权利要求1所述的一种用于马口铁工艺中的脱脂剂及使用方法,其特征在于,所述表面活性剂为非离子表面活性剂和阴离子表面活性剂,所选非离子表面活性剂为非离子表面活性剂如烷基聚萄糖苷、壬基酚聚氧乙烯醚、脂肪醇聚氧乙烯醚等的一种或几种混合;所选阴离子表面活性剂为如仲烷基磺酸钠、脂肪醇聚氧乙烯醚硫酸钠和脂肪醇聚氧乙烯醚磷酸酯的一种或几种混合。
3.根据权利要求1所述的一种用于马口铁工艺中的脱脂剂及使用方法,其特征在于,所述防锈剂为三乙醇胺和乌洛托品。
4.根据权利要求1所述的一种用于马口铁工艺中的脱脂剂及使用方法,其特征在于,所述防腐剂为丙酸钙。
5.根据权利要求1所述的一种用于马口铁工艺中的脱脂剂及使用方法,其特征在于,所述助剂为乙醇。
6.根据权利要求1所述的一种用于马口铁工艺中的脱脂剂及使用方法,其特征在于,所述表面脱脂剂的具体组成为:非离子表面活性剂0.3%~2%,阴离子表面活性剂0.3%~2%,防锈剂为三乙醇胺0.5%-2%、乌洛托品0.5%-2%,防腐剂为丙酸钙1%-2%、助剂为乙醇1%-5%、余量为去离子水。
7.根据权利要求1所述的一种用于马口铁工艺中的脱脂剂及使用方法,其特征在于,所述表面脱脂剂的使用方法如下:
将加工完成的马口铁工件在室温下没入表面脱脂剂溶液内,浸渍5-10min;
取出马口铁工件,观察表面能否形成连续水膜,若能形成,表示马口铁工件清理完成,反之。