CN111286770A - 一种高结合力的复合材料 - Google Patents
一种高结合力的复合材料 Download PDFInfo
- Publication number
- CN111286770A CN111286770A CN202010193556.2A CN202010193556A CN111286770A CN 111286770 A CN111286770 A CN 111286770A CN 202010193556 A CN202010193556 A CN 202010193556A CN 111286770 A CN111286770 A CN 111286770A
- Authority
- CN
- China
- Prior art keywords
- aluminum
- layer
- composite material
- electroplating
- nickel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供了一种高结合力的复合材料,通过除去阳极氧化膜底部的屏蔽层,露出铝金属基材,然后进行电镀单金属处理,最终有效提高阳极氧化基材与镀层的结合。
Description
技术领域
本发明涉及一种高结合力的复合材料,属于电化学方法制备无屏蔽层的阳极氧化膜铝材领域,尤其适用于提高铝材和电镀金属的结合力。
技术背景
随着科技和工业的迅速发展,人们对金属性能要求越来越苛刻,轻质高硬度的金属合金材料在相关领域中应用广泛,由于铝在全球的产量仅次于铁因此轻质金属铝合金材料备受关注。铝及铝合金材料硬度低、耐磨性差、易产生晶间腐蚀,而且铝在自然条件下表面易形成一层很薄的氧化膜,该膜易破损,特别在酸(碱) 性条件下,迅速溶解,极大地降低其耐腐蚀能力,铝及铝合金基材应用受到极大地限制,需要在其表面覆盖一层强耐蚀性膜,以达到防护的目的,通常可以用氧化处理、外加涂层、电镀等方式实现。镍的标准电位是-0.25V,具有很强耐腐蚀性能,也是用量最多最广的金属,因此,用镍作为铝合金材料的防护及装饰镀层备受人们关注,成为一种良好金属防护镀层。
现有技术中,关于在铝材表面电镀的方法有很多,如湖南大学CN1793436 A一种铝或铝合金表面直接电镀的方法,按如下步骤操作:
1)前处理:包括机械预处理和化学抛光;
2)电镀镍:在镀液中采用直流或脉冲电流法,对铝合金进行直接电镀;在电镀液中加入络合除膜剂,其浓度控制在20~40g/L。
所述在铝材表面电镀Ni,虽然方法简单,但存在较为明显的技术问题,即镀层与铝材的剥离强度不高,难于满足工业需求。
此外,本田技研工业株式会社US577589A(同族CN1144852A)公开了一种硅阳极氧化方法,方法包括对所述含硅铝合金进行阳极氧化处理,在阳极化膜上镀镍以形成镀镍膜;以及在镀镍的表面上再镀铬,其中通过在铝材表面阳极氧化中间层,可有效提高基材与镀层的结合力,但所述现有技术中严重忽视了阳极氧化膜导电性差的问题,更忽视了阳极氧化膜对镀层与基材结合力的不利影响。
此外,深圳富泰宏精密工业有限公司US2013164555A(同族CN103173834 A)公开了一种铝或铝合金表面处理方法及制品,所述阳极氧化膜包括依次形成于铝或铝合金基体表面的阻挡层及多孔层,所述阳极氧化膜还形成有若干第二氧化孔,所述第二氧化孔贯穿所述阻挡层与多孔层,该制品还包括形成于所述阳极氧化膜上的电镀层,所述现有技术中明确记载了“该第二氧化孔40的形成使电镀层15与铝或铝合金基体11之间结合产生卡扣效应,电镀层15与铝或铝合金基体11之间的结合力被增强。”,即明确提到了在阳极氧化膜电镀过程中应当除去阳极氧化膜中的屏蔽层,但是除去屏蔽层的原理和方法明显的违背电化学原则,具体而言,如说明书中所记载“在所述阳极氧化处理过程中,首先,在所述铝或铝合金基体11表面形成阳极氧化膜13,该阳极氧化膜13包括依次形成于铝或铝合金基体11表面的阻挡层131及多孔层133,所述多孔层133形成有若干第一氧化孔20。由于电解液的酸性适中,EDTA与铝离子络合形成的络合物易于发生离解,该络合物的形成不会阻碍所述阻挡层131的生长;随着反应时间的增加,所述第一氧化孔20底端靠近阻挡层131的区域的析氧反应加剧,生产的氢离子增多,使该区域的电解液呈强酸性,在强酸性环境下EDTA与铝离子的络合物稳定性较强,可阻碍阻挡层131的生长;且由于阳极氧化过程电化学反应的平衡,所述阻挡层131在生长的同时也会溶解,因此,当阻挡层131的生长受到阻碍时,最终,所述第一氧化孔20底部的阻挡层131被逐渐溶解形成第二氧化孔40。所述第二氧化孔40贯穿所述阻挡层131与多孔层133。”,即所述现有技术直接通过控制阳极氧化过程中的参数,就可以避免在阳极氧化膜孔道底部形成屏蔽层,这严重违背了阳极氧化膜形成的原理。
具体而言:铝或铝合金阳极氧化是指将铝或铝合金浸入合适的电解液中作为阳极进行通电处理,在铝或铝合金的表面生成一层氧化膜(Al2O层)的过程。这层氧化膜的存在能够提高铝合金的耐腐蚀性能,同时,借助于氧化膜的特殊结构,加上后期的处理工艺,比如阳极氧化膜也可以配合表面涂漆等进一步处理使得基体在较为苛刻的环境中达到更好的保护作用,或通过染色对铝及铝合金制件进行装饰,使膜层具备了装饰性以及其他防护性能。常用的阳极氧化工艺有硫酸阳极氧化、铬酸阳极氧化等。
从化学反应的热力学条件上看,铝可以在相当大的pH值范围(pH=4.45-8.38)内生成稳定的氧化膜层。而从电化学反应的机理来看,阳极氧化膜的形成实际上是由膜的生长和膜的溶解两个过程共同作用的结果。
(1)膜的生长:
阴极,析氢反应:2H++2e→H2
阳极,氧化反应:H2O-2e→O+2H+
阳极反应中产生的氧,既可以形成氧分子以气态形式析出,又可以在阳极表面形成氧化铝膜层:
2Al+3O→Al2O3+Q。
此反应为放热反应,Q=1669J/mol,阳极氧化过程速度很快,通电几秒钟就可以生成一层很薄的、无孔、致密、附着力强、高绝缘性的氧化膜,膜不断生长,厚度不断增加,电阻也随之增大,生成膜的反应速度就会不断降低,直至停止。
(2)膜的溶解。正是有了膜的溶解,才使得膜可以不断生长。在反应过程中,铝和生成的氧化铝膜层在酸性电解质溶液中都可以发生溶解。
2Al+6H+→2Al3++3H2
Al2O3+6H+→2Al3++3H2O
溶解反应会使铝的表面生成大量的小孔。膜的溶解过程是与膜的生成过程同步进行的,由于初生的膜层并不均匀,膜层较薄的地方就容易溶解而产生小孔,电解质溶液可以穿过小孔进入膜内,在铝的基体上不断生成氧化膜,同时不断溶解,最终形成氧化膜的小孔(针孔)由表及里形成锥形结构,膜的溶解与电解质的性质、反应生成物的结构、电流、电压、溶液温度及通电的时间等因素有关。
铝及铝合金阳极氧化膜的多孔蜂窝结构,在其膜层上,微孔垂直于表面,其结构单元的尺寸、孔径、壁厚和阻挡层厚等参数均可由电解液成分和工艺参数控,即铝的阳极氧化膜有两大类:壁垒型阳极氧化膜和多孔型阳极氧化膜。壁垒型阳极氧化膜是一层紧靠金属表面的致密无孔的薄阳极氧化膜,简称壁垒膜,其厚度取决于外加的阳极氧化电压一般非常薄,不会超过0.1μm主要用于制作电解电容器。壁垒型阳极氧化膜也叫屏蔽层阳极氧化膜,简单而言,多孔阳极氧化膜包括有屏蔽层和多孔层,两者在具体的结构和组成方面具有显著不同,其中屏蔽层为致密无孔的非晶态氧化物,通常为γ-Al2O3,而多孔层由非晶态的氧化铝组成,其主要成分为α-AlOOH氧化铝形态存在。
通常而言,上述的位于阳极氧化膜孔道底部的屏蔽层对于阳极氧化膜的耐腐蚀性和硬度具有积极贡献,如硬度较高,能阻挡外界侵蚀,即所述在使用铝材阳极氧化膜的屏蔽层的过程中通常不需要关注,也不需要对所述屏蔽层做任何处理,但是在特定领域时,所述阳极氧化膜中的屏蔽层则必须除去,否则对后续的产品生产带来不利影响,如在阳极氧化膜表面电镀金属层,以提高或完全改变阳极氧化膜铝材表面的物理化学性质,具体而言:
(Ⅰ)CN201710570978,申请人傅敏杰公开了一种一种铝基复合材料的制备方法,包括如下步骤:
A、铝材质的基体准备;
B、AAO模板的形成,至少包括通过阳极氧化法在基体表面形成AAO模板;
C、高分子纳米线的生成,其为通过AAO模板聚合得到纳米线后,再经过去除部分AAO模板,以使模板厚度减少,使高分子纳米线至少部分露出AAO模板;
D、外包层的形成,其包覆于高分子纳米线,并且露出AAO模板的高分子纳米线被包裹在外包层内。
所述步骤B还包括将AAO模板的部分纳米孔的底部氧化铝层腐蚀形成空洞。
即所述现有技术中为了提高金属镀层与阳极氧化膜的结合力,提出了对阳极氧化膜底部的屏蔽层进行除去处理的方案,具体参见说明书中记载除去屏蔽层的方法为“采用微针管探入相应纳米孔内输送适量强酸或者强碱腐蚀液,在经去离子水抽吸冲洗后得到”,并“通过底部的空洞,在结合形态下可以对界面结合力进行增强调控,从而有利于改善复合材料的机械性能,满足强机械性能需求”,即所述现有技术中除去屏蔽层的方法记载含糊,且使用微针碳管的技术难度大,对设备要求高,此外,当阳极氧化膜的孔道通常少则4-8个/μm2,多则成千上万,完全没有能力去单个一一腐蚀屏蔽层。
(Ⅱ)CN201110174169,申请人福州大学公开了阳极氧化铝模板来制作场发射阴极阵列材料的方法,主要包括以下步骤:
(1)准备预先做好的带有铝基底的阳极氧化铝模板;
(2)去除未被氧化的铝基底;
(3)去除氧化层底部并扩孔;
(4)向氧化铝空洞中灌注溶液;
(5)去除表面溶胶并凝胶化;
(6)高温碳化;
(7)镀金属导电层;
(8)将样品固定于基板上
(9)腐蚀氧化铝、露出碳纳米线阵列。
所述现有技术为了出去阳极氧化膜的底部的阻挡层,直接反向出去底部铝基材的同时,一起将阻挡层除去,虽然所述方法方便后续的电镀处理,但是获得的阳极氧化膜由于没有铝基材的支持,获得的氧化铝膜置地极软,容易分散,后续电镀过程实际极难操作,并没有能力却保证所有的阳极氧化膜孔道垂直向上,也无法有效的克服毛细管压力,实现在每个孔道中充分电镀。
(Ⅲ)US201113310135A,申请人通用汽车环球科技运作有限责任公司公开了将金属结合到基底的方法,该方法包括:
在该基底表面上形成纳米刷,该纳米刷包括在该基底表面上方延伸的多个纳米线;
将处于熔融态的该金属引入到该基底表面上,该金属包围该多个纳米线;和
通过冷却,使包围该多个纳米线的金属凝固,其中在该凝固过程中,在该金属和该基底之间形成至少机械互锁;
其中该纳米刷的形成包括:
在该基底的表面中形成多个纳米孔;
将材料沉积到该多个纳米孔中;
在该多个纳米孔的每个中由该沉积的材料生长纳米线;和
除去一部分的该基底表面以使生长在其中的该纳米线曝露。
具体参见附图1和说明书的相关内容中记载了“在一些情况中,该氧化物结构18可以蚀刻来除去其在纳米孔16底部的部分(包括阻隔层),由此曝露下面的铝基底12”,即所述现有技术直接放弃对屏蔽层19的处理,或者直接含糊的将其蚀刻除去即可,完全没有公开具体的蚀刻方法。
此外,现有技术中也有记载除去所述屏蔽层的方法,包括使用草酸或者磷酸,或者其他的混合物,但是都存在如下明显的技术问题:(1)使用酸液腐蚀无法有限的区分多孔氧化层和屏蔽层,即酸液无差别腐蚀阳极氧化膜,严重影响阳极氧化膜孔道的阵列结构,造成阳极氧化膜阵列结构的坍塌或发生非均匀腐蚀,不利于后续的电镀过程,严重降低镀层的电镀均匀性和结合力的稳定性;(2)腐蚀过程中,当屏蔽层被贯通后,腐蚀液会明显腐蚀铝材,造成基材的损伤。
发明内容
基于上述现有技术存在的问题,本发明提供了一种高结合力的复合材料。
所述复合材料的基材为铝或铝合金,基材表面电镀镀敷有金属镍层,在金属镍层与基材之间设置有阳极氧化孔道过渡层,所述阳极氧化孔道底部的屏蔽层通过定位腐蚀除去,所述孔道内部填充有镍金属,所述复合材料中金属层与铝基材的剥离强度为7-8N/cm。
进一步的,所述阳极氧化孔道的平均孔径为150-200nm,孔数80-150个/μm2,阳极氧化孔道过渡层厚度为0.5-1μm。
进一步的,所述金属镍层的厚度为5-10μm。
进一步的,所述复合材料经过(1)预处理;(2)阳极氧化;(3)定位标记保护膜:该步骤下使用的溶液为γ-氯丙基三甲基硅烷和无水甲苯混合液;(4)除去阳极氧化膜屏蔽层,该步骤下使用的溶液为NaOH、NaF和乙醇的混合液;(5)电镀镍金属层处理。
进一步的,所述电镀镍金属电镀参数如下:电镀液由硫酸镍200~230g/L,氯化镍30~40g/L,硼酸20~30g/L,硫酸镁45-50g/L,十二烷基硫酸钠1-2g/L, pH为3~6,所述电镀过程采用脉冲电镀:脉冲频率10-20Hz,脉冲占空比50~65%,温度20~40oC,电流密度0.7-0.9A/dm2,电镀时间1~2h,无超声辅助。
进一步的,所述步骤(3)过程中辅助有抽真空处理,真空度为90-100Pa,步骤(4)过程中辅助有氮气保护处理,步骤(4)和(5)之间具有真空冷冻干燥处理。
进一步的,所述真空冷冻干燥后,电镀单金属前进行超声辅助的预泡处理,预泡过程中使用的电解液与电镀单金属层使用的电镀液一致,浸泡温度20~40oC,浸泡时间30s-60min。
进一步的,所述阳极氧化使用的溶液为草酸、磷酸和磺基水杨酸混合液,草酸的浓度为0.25-0.3M,磷酸的浓度为0.2-0.4M,磺基水杨酸的浓度为0.05-0.15M。
进一步的,所述阳极氧化过程的电压为20-30V,温度为30oC,电流密度2-3A/dm2,时间20-30min。
进一步的,所述γ-氯丙基三甲基硅烷的浓度为10-20wt.%,其用量为阳极氧化后铝材重量的3-5%,所述NaOH:NaF:乙醇的质量比例为(2-5):(1-2):7。
关于上述复合材料和制备方法所使用的试剂、浓度、以及原理做出如下详细解释:
(1)关于原理,如附图5所示,阳极氧化膜通常包括位于阳极氧化膜孔道底部的屏蔽层和纳米阵列的多孔层,其中屏蔽层的主要成分为γ-Al2O3,即无水,极少羟基,而多孔层通常为α-AlOOH氧化铝,富含结晶水和羟基,基于上述屏蔽层与多孔层的区别,在阳极氧化膜内部抽真空引入γ-氯丙基三甲基硅烷,在75oC下,γ-氯丙基三甲基硅烷中的与羟基反应,形成结合力较强的三足鼎立的硅氧键,具体如下反应式:
进而有效的包覆于阳极氧化膜多孔层表面,由于屏蔽层底部没有或者仅有极少的羟基,因此γ-氯丙基三甲基硅烷不糊吸附于屏蔽层表面,进而实现γ-氯丙基三甲基硅烷的精准包覆,此外,定位标记保护膜过程中辅助有抽真空手段为为了方便γ-氯丙基三甲基硅烷有效克服阳极氧化膜纳米管的毛细管效应,此外,阳极氧化膜的纳米孔道为一端开口,一端铝基密封,抽真空更方便γ-氯丙基三甲基硅烷进入纳米孔道,为本发明不可或缺的辅助手段。
接着,使用腐蚀液对屏蔽层进行腐蚀,这里的腐蚀液为碱性腐蚀液,而不是酸性腐蚀液,时用于酸性腐蚀液中的质子容易解离多孔层表面吸附的硅氧键,而使得γ-氯丙基三甲基硅烷从多孔层表面脱附,最终失去保护层的功能,而碱性氢氧化钠不会对γ-氯丙基三甲基硅烷造成影响,同时能够有效的与屏蔽层接触,发生NaOH+Al2O3→NaAlO2+H2O,进而实现有效除去氧化铝的反应,此外,上述腐蚀反应在常温即可发生,无需加热。
另外,本发明的腐蚀液由NaOH、NaF和乙醇组成,不含有任何水分,主要是由于在水的存在条件下,非常容易发生Al+NaOH+H2O—NaAlO2+3H2造成基材的损失,当在腐蚀过程中没有水分时(腐蚀屏蔽层过程中产生的水较少,可以忽略不计),仅仅发生Al和NaOH的反应较难,此外,该腐蚀过程中,辅助有氮气保护,更不会或者很难发生碱与基材的腐蚀,更加简单容易的定位腐蚀,且不发生基材的损伤,此外,NaF为渗透剂,有利于氢氧化钠与致密无孔屏蔽层的腐蚀反应。
(2)关于制备γ-氯丙基三甲基硅烷的方法,可参阅相关的现有技术,具体如下:γ-氯丙基三氯硅烷的制备:设备包括有温度计、恒压滴液漏斗和回流冷凝管,冷凝管上端设置有冷阱、氯化钙干燥管及石蜡油计泡器,以及1000mL三口烧瓶,将三氯硅烷4.5M和3-氯丙烯3M混合置于恒压滴液漏斗中,向反应瓶先放入料液约25mL,随后加入0.1mol/L氯铂酸-异丙醇溶液0.15mL,助催化剂0.15mL,对苯二酚0.25g,在室温下反应被迅速引发,升温至75℃开始滴加料液,调节滴加速度控制温度在80℃,约2h滴加完毕,再回流3h,反应温度最后升至90℃时结束反应。将反应混合物常压分馏,收集182℃馏分,即为3-氯丙基三氯硅烷,收率85%。
(3)关于预处理:
无论何种表面处理工艺,要获得好效果,表面预处理是首要的条件,主要是由于铝材表面存在有各种磨痕、凹坑、毛刺、划伤等缺陷,带有润滑油迹或不同程度地覆盖着磨料和一些脏物,如不清洗掉,就会在阳极氧化处理后暴露出来,影响阳极氧化膜表面的孔道结构和性能,预处理的简单有如下几点:(1)保证氧化膜与与基体表面的附着力,由于后续处理需要在阳极氧化膜表面镀敷其他金属,氧化膜作为中间层的存在,其附着结合力为基础要求;(2)保证基材与后续镀层结合力的各向均匀性。
(a)机械抛光:包括喷砂、刷光、滚光中的一种或多种,其中喷砂是用压缩空气将磨料喷射到工件表面上,利用高速磨料的动能,除去工件表面的氧化皮、腐蚀及其他缺陷的精饰方法,形成均匀的无光表面,喷砂的效果与喷吹距离、喷吹角度、压力、喷嘴大小和形状、磨料尺寸、磨料与水混合比例等因素有关。简单而言,如磨料粒度细小,可产生柔和无光平滑的表面;磨料粒度粗大,可产生粗糙灰暗的表面,用于消除面积较大,伤痕较深的表面缺陷。小颗粒钢丸可使铝表面产生浅灰色,大颗粒钢丸不改变铝表面的自然色泽。用碳化硅微粒使铝表面产生浅灰色,用粉末二氧化硅可使铝表面产生蓝色。
刷光:刷光是用金属丝、动物毛及其他天然或人造纤维制成的刷子加工金属表面的工艺,可以是干刷也可以是湿刷。刷光的效果取决于刷轮的形状特点和金属丝的材质与粗细。
滚光:滚光是把工件和磨料放在滚筒中进行低速旋转,依靠工件和磨料相对摩擦进行抛光处理。
(b)脱脂:本发明采用碱性溶液脱脂,可以使基材表面的植物性油脂和动物性油脂皂化,生成溶于水的肥皂,将其除去,如下反应:
(C17H35COO)3C3H5+3NaOH→3C17H35COONa+C3H5(OH)3
本发明的除油液为20~25g/L碳酸钠和2-3g/L磷酸钠的混合水溶液,温度65-70oC,浸泡时间5-6min,碳酸钠碱性比氢氧化钠弱,有一定的皂化能力,对溶液的pH值有缓冲作用,对金属的腐蚀性和对皮肤的刺激性都比氢氧化钠低,价格低,常作为铝合金脱脂液中的主盐,磷酸钠呈弱碱性,有一定的皂化能力和对pH值有缓冲作用,能络合水中的金属离子,使水质变软,又是一种乳化剂,溶解度大,洗去性好。碱性除油后包括有一次水洗和二次水洗,如其中一次水洗可用60-70℃的热水冲洗,这样能有效除去经脱脂后残留在工件表面的污染物。
(c)碱洗:铝合金工件,经过脱脂工艺后,还不能进行转化膜处理,表面一般存在自然氧化膜,加工条纹等缺陷,需要进行腐蚀处理去除自然氧化膜,活化表面。碱性腐蚀是最常用的腐蚀工艺,主要成分是NaOH溶液,本申请碱洗液为20-30g/LNaOH、3-5g/L的柠檬酸钠水溶液,温度为10-20oC,浸泡时间15-20min,其中天然氧化铝膜与氢氧化钠反应形成偏铝酸钠,铝的腐蚀速度与溶液中氢氧化钠的总含量成正比,并随温度的升高而升高。其中柠檬酸钠的主要作用为络合剂,可以有效的铝离子掩蔽起来,避免制氢氧化铝沉淀的产生。
(d)酸洗:经过碱性脱脂和碱性腐蚀的铝合金工件,表面一般都有一层黑灰。为了取得光亮的金属表面,必须用酸性溶液出光处理。即使是很纯的铝工件,表面的碱液,也很难用水完全洗净,需要用酸性溶液中和处理,本发明的酸洗除灰液为50-70g/L HNO3和4-8g/LNaF的混合水溶液,常温,时间为2-3min。
(e)水洗:任何经化学溶液处理的铝工件,移出处理液后,都应立即水洗,而且越快越好。因为工件离开处理液暴露在空气中,表面处在不均匀的状态下,需要立即用水将化学药剂冲洗掉,使化学反应终止。同时防止将化学药剂带入下一处理液中,污染下一化学处理槽。
(4)关于阳极氧化:阻挡层的厚度取决于阳极氧化的电压,多孔层的孔穴和孔体的尺寸与电解液的组成、浓度和操作条件有关,本发明使用草酸作为主酸,复配有磷酸和磺基水杨酸,其中草酸对铝的溶解能力比硫酸小,所以容易得到比硫酸阳极氧化更稳定的膜层,如本申请的阳极氧化膜的厚度为0.5-1μm;通常使用磷酸进行阳极氧化时,可以有效提高阳极氧化膜的孔隙率,且孔径较大,如本申请的孔数80-150个/μm2,磺基水杨酸有机酸的加入可有效降低草酸和磷酸的使用量,对阳极氧化膜的屏蔽层厚度的降低有轻微提升作用。
电压:在草酸氧化过程中,电压的增加应该缓慢,如上升太快,会造成新生成氧化膜的不均匀处电流集中,导致该处出现严重的电击穿,引起金属铝的腐蚀,电压优选为20-30V。
电流密度:电流密度与氧化铝的生成速度成正比,电流密度愈高,氧化铝的生成速度愈快。但氧化膜的生成速度并不完全与电流密度成正比。氧化膜的生成速度等于化铝的生成速度减去氧化铝在电解液中的溶解速度,氧化铝的溶解是一个化学过程,与电解电流密度无关,它取决于电解液的浓度和溶液的局部温度。电解液的浓度愈高,溶液的局部温度愈高,氧化铝的溶解速度愈快。因此,在相同的电解液浓度和温度的条件下,即氧化铝的溶解速度不变。提高电流密度,氧化膜的生成速度增加,氧化膜的孔隙率下降,因此本发明的电流密度2-3A/dm2。
温度:温度升高,膜层减薄,如果在较高温度时,增加电解液的pH值,膜的厚度可增加,最佳的温度在25-40℃之间,优选30oC。
(4)关于电镀:在电镀单金属前,预先使用镍电解液对除去屏蔽层的阳极氧化铝合金进行浸泡处理,并伴有超声过程,其目的在于使得电解液与阳极氧化膜孔道底部的铝材充分接触,并通过超声,有效除去纳米孔道中多余的气体,实现镀液与基材的充分接触。
本发明的电镀电镀液由硫酸镍200~230g/L,氯化镍30~40g/L,硼酸20~30g/L,硫酸镁45-50g/L,十二烷基硫酸钠1-2g/L组成, pH为3~6,所述电镀过程采用脉冲电镀:脉冲频率10-20Hz,脉冲占空比50~65%,温度20~40oC,电流密度0.7-0.9A/dm2,电镀时间1~2h,无超声辅助。
其中以硫酸镍作为主盐,浓度范围一般在200~230g/L,用作产生镍离子的主盐;
使用氯化镍作为活化剂,其中Ni+可以有效降低硫酸镍的使用量,而Cl-能够提高镀液电导率和阴极分散能力,且所述活化剂不会向镀液中引入其他额外的金属离子;
使用硫酸镁作为导电盐,导电盐非必须添加试剂,但硫酸镁可以改善镀层的光滑和柔软性;
使用硼酸作为缓冲剂,为防止生产中镀液酸度的急剧变化,常加入硼酸作缓冲剂,控制pH=3~6,硼酸具有缓冲作用的同时,还能提高阴极极化和镀液的导电性,使烧焦电流密度提高;
使用十二烷基硫酸钠作为防针孔剂,所述防针孔剂能够降低或消除阴极上析出的氢量,从而消除针孔,提高镀敷效果。
酸度(pH值),范围为pH为3~6,pH值低时,阴极上大量析出氢气,电流效率降低,当pH值低于3时,会猛烈放出氢气,甚至电流效率为0,但当pH值超过6或者接近于中性时,又会生成氢氧化镍沉淀,夹杂于镍层中使镀层剥落、发脆、深孔难于沉积等,pH值高时,用3wt.%硫酸溶液调整,pH值低时,可加入3%氢氧化钠调整;添加氢氧化钠时,易产生沉淀,应在不断搅拌下缓慢加入,用碳酸镍代替氢氧化钠效果更好;
温度,对镀层内应力影响很大,当温度由10℃升至35℃时,镍层内应力迅速降低,而温度由35℃升到60℃内应力降低较慢。当温度进一步升高,内应力则几乎不变。加温还可以使电镀液中各成分的溶解度增大,进而可以采用浓镀镍液;同时,温度升高,镀液的电导率增加,电流效率提高。
脉冲电镀,脉冲电镀技术与普通电镀相比,显著的优点是它可以控制电镀过程中的传质过程,可以产生高于平均电流的峰值电流,从而影响电镀过程中的瞬时电流大小、反应速度以及电镀过程中晶粒的形核与长大,因此选用电流密度0.7-0.9A/dm2,占空比50~65%,电镀效果最好。
本发明所述方案具有以下有益效果:
(1)通过γ-氯丙基三甲基硅烷对多孔层和屏蔽的层选择性吸附反应,以及后续碱性腐蚀反应能够有效的腐蚀位于阳极氧化膜孔道底部的屏蔽层;
(2)通过预处理和阳极氧化处理可以获得纳米氧化膜孔道阵列,孔道结构完整,均匀。
(3)γ氧化铝屏蔽层的除去可以有效提高阳极氧化基材的导电性;
(4)屏蔽层的腐蚀去除能够有效提高后续镀层与铝基材的结合力,金属层与铝基材的剥离强度为7-8N/cm;
(5)镀层与基材的结合力的波动系数小,即镀层的稳定性优秀。
附图说明
图1为本发明的阳极氧化膜孔道阵列俯视SEM图。
图2为本发明的阳极氧化膜孔道切面SEM图。
图3为本发明的阳极氧化膜孔道阵列切面SEM图。
图4为本发明的阳极氧化膜孔道阵列选择性腐蚀后切面SEM图。
图5为本发明的除去阳极氧化铝孔道内屏蔽层的过程示意图。
图6为本发明的镍金属填充纳米孔道的俯视SEM高倍图。
图7为本发明的镍金属填充纳米孔道的切面SEM图。
图8为本发明的镍金属填充纳米孔道的俯视SEM低倍图。
图9为本发明的阳极氧化铝合金与镀层的切面SEM图。
具体实施方式
实施例1
实施例1-3所使用的预处理步骤和溶液一致,均包括机械抛光-除油-热水洗-碱洗-热水洗-冷水洗-酸洗-水洗:
所述机械抛光为喷砂,
所述除油为碱性除油,除油液为23g/L碳酸钠和2.5g/L磷酸钠的混合水溶液,温度67oC,浸泡时间5.5min;
所述碱洗液为25g/LNaOH、4g/L的柠檬酸钠水溶液,温度为15oC,浸泡时间17.5min;
所述酸洗除灰液为60g/L HNO3和6g/LNaF的混合水溶液,常温,时间为2.5min。
(2)阳极氧化:以经过步骤(1)处理过的铝材为阳极,石墨作为阴极,浸入电解液,通过导线分别连接电源,所述电解液为草酸、磷酸和磺基水杨酸混合液,草酸的浓度为0.2M,磷酸的浓度为0.2M,磺基水杨酸的浓度为0.05M,电解参数如下,电压为20V,温度为30oC,电流密度2A/dm2,时间20min;阳极氧化后,乙醇浸泡清洗,并使用真空干燥,除去氧化膜内电解液,整个过程严格避免阳极氧化后的铝材接触空气或水,避免发生封孔。
(3)定位标记保护膜:将经过步骤(2)处理的铝材浸泡于γ-氯丙基三甲基硅烷的甲苯溶液中,浓度为10wt.%,其用量为阳极氧化后铝材重量的4%;浸泡过程中辅助有抽真空处理,真空度为100Pa,见孔道内无气泡溢出后,静置7min,充分反应。
(4)除去阳极氧化膜屏蔽层:将经过步骤(3)处理的铝材浸泡于NaOH、NaF和乙醇的混合液中,于氮气保护下,充分反应5min,所述NaOH:NaF:乙醇的质量比例为2:1:7。
(5)真空冷冻干燥。
(6)预泡处理。
(7)电镀镍:电镀液由硫酸镍200g/L,氯化镍30g/L,硼酸20g/L,硫酸镁45g/L,十二烷基硫酸钠1g/L,所述电镀过程采用脉冲电镀:脉冲频率10Hz,脉冲占空比50%,温度20oC,电流密度0.7A/dm2,电镀时间1h。
(8)镀后清洗干燥,获得的样品命名为S-1。
实施例2
(2)阳极氧化:以经过步骤(1)处理过的铝材为阳极,石墨作为阴极,浸入电解液,通过导线分别连接电源,所述电解液为草酸、磷酸和磺基水杨酸混合液,草酸的浓度为0.275M,磷酸的浓度为0.3M,磺基水杨酸的浓度为0.1M,电解参数如下,电压为25V,温度为30oC,电流密度2.5A/dm2,时间25min;阳极氧化后,乙醇浸泡清洗,并使用真空干燥,除去氧化膜内电解液,整个过程严格避免阳极氧化后的铝材接触空气或水,避免发生封孔。
(3)定位标记保护膜:将经过步骤(2)处理的铝材浸泡于γ-氯丙基三甲基硅烷的甲苯溶液中,浓度为15wt.%,其用量为阳极氧化后铝材重量的4%;浸泡过程中辅助有抽真空处理,真空度为100Pa,见孔道内无气泡溢出后,静置7min,充分反应。
(4)除去阳极氧化膜屏蔽层:将经过步骤(3)处理的铝材浸泡于NaOH、NaF和乙醇的混合液中,于氮气保护下,充分反应5min,所述NaOH:NaF:乙醇的质量比例为3.5:1.5:7。
(5)真空冷冻干燥。
(6)预泡处理。
(7)电镀镍:电镀液由硫酸镍225g/L,氯化镍35g/L,硼酸25g/L,硫酸镁47.5g/L,十二烷基硫酸钠1.5g/L,所述电镀过程采用脉冲电镀:脉冲频率15Hz,脉冲占空比60%,温度30oC,电流密度0.8A/dm2,电镀时间1.5h。
(8)镀后清洗干燥,获得的样品命名为S-2。
实施例3
(2)阳极氧化:以经过步骤(1)处理过的铝材为阳极,石墨作为阴极,浸入电解液,通过导线分别连接电源,所述电解液为草酸、磷酸和磺基水杨酸混合液,草酸的浓度为0.275M,磷酸的浓度为0.3M,磺基水杨酸的浓度为0.1M,电解参数如下,电压为25V,温度为30oC,电流密度2.5A/dm2,时间25min;阳极氧化后,乙醇浸泡清洗,并使用真空干燥,除去氧化膜内电解液,整个过程严格避免阳极氧化后的铝材接触空气或水,避免发生封孔。
(3)定位标记保护膜:将经过步骤(2)处理的铝材浸泡于γ-氯丙基三甲基硅烷的甲苯溶液中,浓度为15wt.%,其用量为阳极氧化后铝材重量的4%;浸泡过程中辅助有抽真空处理,真空度为100Pa,见孔道内无气泡溢出后,静置7min,充分反应。
(4)除去阳极氧化膜屏蔽层:将经过步骤(3)处理的铝材浸泡于NaOH、NaF和乙醇的混合液中,于氮气保护下,充分反应5min,所述NaOH:NaF:乙醇的质量比例为3.5:1.5:7。
(5)真空冷冻干燥。
(6)预泡处理。
(7)电镀镍:电镀液由硫酸镍230g/L,氯化镍40g/L,硼酸30g/L,硫酸镁50g/L,十二烷基硫酸钠2g/L,所述电镀过程采用脉冲电镀:脉冲频率20Hz,脉冲占空比65%,温度40oC,电流密度0.9A/dm2,电镀时间2h。
(8)镀后清洗干燥,获得的样品命名为S-3。
对比例1
(2)阳极氧化:以经过步骤(1)处理过的铝材为阳极,石墨作为阴极,浸入电解液,通过导线分别连接电源,所述电解液为草酸、磷酸和磺基水杨酸混合液,草酸的浓度为0.275M,磷酸的浓度为0.3M,电解参数如下,电压为25V,温度为30oC,电流密度2.5A/dm2,时间25min;阳极氧化后,乙醇浸泡清洗,并使用真空干燥,除去氧化膜内电解液,整个过程严格避免阳极氧化后的铝材接触空气或水,避免发生封孔。
(3)腐蚀:将经过步骤(2)处理的铝材浸泡于NaOH、NaF和乙醇的混合液中,于氮气保护下,充分反应5min,所述NaOH:NaF:乙醇的质量比例为3.5:1.5:7。
(4)预泡处理。
(5)电镀镍:电镀液由硫酸镍225g/L,氯化镍35g/L,硼酸25g/L,硫酸镁47.5g/L,十二烷基硫酸钠1.5g/L,所述电镀过程采用脉冲电镀:脉冲频率15Hz,脉冲占空比60%,温度30oC,电流密度0.8A/dm2,电镀时间1.5h。
(6)镀后清洗干燥,获得的样品命名为D-1。
对比例2
(2)活化、腐蚀。
(3)预泡处理。
(4)电镀镍:电镀液由硫酸镍225g/L,氯化镍35g/L,硼酸25g/L,硫酸镁47.5g/L,十二烷基硫酸钠1.5g/L,所述电镀过程采用脉冲电镀:脉冲频率15Hz,脉冲占空比60%,温度30oC,电流密度0.8A/dm2,电镀时间1.5h。
(5)镀后清洗干燥,获得的样品命名为D-2。
表1对比例1-2与实施例2结合力数据
如附图1所示,采用本发明的预处理+阳极氧化手段,可以获得均匀且规整的纳米氧化膜孔道阵列,如表1所示,阳极氧化孔道平均孔径为150-200nm,通过控制电解参数,可以获得
孔数80-150个/μm2,阳极氧化膜的厚度为0.5-1μm,屏蔽层的厚度为5-15nm。
如附图2所示,阳极氧化后,在孔道底部可见明显的屏蔽层,屏蔽层的厚度为5-15nm,如如附图3、附图4所示,通过γ-氯丙基三氯硅烷的选择性吸附反应,可是后续的碱性腐蚀液有效腐蚀阳极氧化膜孔道底部的屏蔽层。
如附图6、附图7、附图8、附图9所示,镍合金能够完全进入阳极氧化膜的孔道,填充效果好,当氧化膜孔道内部的屏蔽层被除去时,如表1所示,金属层与铝基材的剥离强度为7-8N/cm,平均结合强度为7.48 N/cm,标准偏差为0.30,波动系数为0.041,由所述数据可以得出,镀层与基材的结合力较高,且结合力较为稳定。
而对于为除去阳极氧化膜中的屏蔽层D-1所示,且结合强度2.1-3.9 N/cm,平均结合强度为3.04N/cm,标准偏差为0.61,波动系数为0.20,波动系数较大,其主要原因在于阳极氧化膜的中各个孔道的导电系数不同,无法做到均匀沉积金属,相比而言,直接在铝材表面电镀镍层D-2,其平均结合强度为2.24N/cm,标准偏差为0.56,波动系数为0.25,由于没有铝材与镀层之间的卡扣效应,剥离强度不及D-1,此外,由于D-2处理过程中,包括对基材的腐蚀,腐蚀会造成基材表面粗糙不平,波动起伏,因此D-2的剥离强度的波动系数高于S-2和D-1。
综上述:(1)通过预处理和阳极氧化处理可以获得纳米氧化膜孔道阵列,孔道结构完整,均匀,此外γ-氯丙基三甲基硅烷对多孔层和屏蔽的层选择性吸附反应,以及后续碱性腐蚀反应能够有效的腐蚀位于阳极氧化膜孔道底部的屏蔽层,可以有效提高阳极氧化基材的导电性,有利于后续镀层与铝基材的有效结合;(2)通过在除去阳极氧化膜孔道底部的屏蔽层,并在其上电镀Ni单金属,获得了以阳极氧化铝为基材的高结合力镀层材料,所述材料金属层与铝基材的剥离强度为7-8N/cm,平均结合强度为7.48 N/cm,波动系数为0.041,即结合力和稳定性均较优。
以上,虽然通过优选的实施例对本实用发明进行了例示性的说明,但本实用发明并不局限于这种特定的实施例,可以在记载于本发明的保护范围的范畴内实施适当的变更。
Claims (10)
1.一种高结合力的复合材料,其特征在于所述复合材料的基材为铝或铝合金,基材表面电镀镀敷有金属镍层,在金属镍层与基材之间设置有阳极氧化孔道过渡层,所述阳极氧化孔道底部的屏蔽层通过定位腐蚀除去,所述孔道内部填充有镍金属,所述复合材料中金属层与铝基材的剥离强度为7-8N/cm。
2.如权利要求1所述的一种高结合力的复合材料,其特征在于所述阳极氧化孔道的平均孔径为150-200nm,孔数80-150个/μm2,阳极氧化孔道过渡层厚度为0.5-1μm。
3.如权利要求1所述的一种高结合力的复合材料,其特征在于所述金属镍层的厚度为5-10μm。
4.如权利要求1所述的一种高结合力的复合材料,其特征在于所述复合材料经过(1)预处理;(2)阳极氧化;(3)定位标记保护膜:该步骤下使用的溶液为γ-氯丙基三甲基硅烷和无水甲苯混合液;(4)除去阳极氧化膜屏蔽层,该步骤下使用的溶液为NaOH、NaF和乙醇的混合液;(5)电镀镍金属层处理。
5.如权利要求4所述的一种高结合力的复合材料,其特征在于所述电镀镍金属电镀参数如下:电镀液由硫酸镍200~230g/L,氯化镍30~40g/L,硼酸20~30g/L,硫酸镁45-50g/L,十二烷基硫酸钠1-2g/L, pH为3~6,所述电镀过程采用脉冲电镀:脉冲频率10-20Hz,脉冲占空比50~65%,温度20~40oC,电流密度0.7-0.9A/dm2,电镀时间1~2h,无超声辅助。
6.如权利要求4所述的一种高结合力的复合材料,其特征在于所述步骤(3)过程中辅助有抽真空处理,真空度为90-100Pa,步骤(4)过程中辅助有氮气保护处理,步骤(4)和(5)之间具有真空冷冻干燥处理。
7.如权利要求6所述的一种高结合力的复合材料,其特征在于所述真空冷冻干燥后,电镀单金属前进行超声辅助的预泡处理,预泡过程中使用的电解液与电镀单金属层使用的电镀液一致,浸泡温度20~40oC,浸泡时间30s-60min。
8.如权利要求4所述的一种高结合力的复合材料,其特征在于所述阳极氧化使用的溶液为草酸、磷酸和磺基水杨酸混合液,草酸的浓度为0.25-0.3M,磷酸的浓度为0.2-0.4M,磺基水杨酸的浓度为0.05-0.15M。
9.如权利要求4所述的一种高结合力的复合材料,其特征在于所述阳极氧化过程的电压为20-30V,温度为30oC,电流密度2-3A/dm2,时间20-30min。
10.如权利要求4所述的一种高结合力的复合材料,其特征在于所述γ-氯丙基三甲基硅烷的浓度为10-20wt.%,其用量为阳极氧化后铝材重量的3-5%,所述NaOH:NaF:乙醇的质量比例为(2-5):(1-2):7。