CN111234703A - Marble-like paint and preparation method thereof - Google Patents
Marble-like paint and preparation method thereof Download PDFInfo
- Publication number
- CN111234703A CN111234703A CN202010217429.1A CN202010217429A CN111234703A CN 111234703 A CN111234703 A CN 111234703A CN 202010217429 A CN202010217429 A CN 202010217429A CN 111234703 A CN111234703 A CN 111234703A
- Authority
- CN
- China
- Prior art keywords
- parts
- marble
- raw materials
- preparation
- alcohol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a marble-imitated paint and a preparation method thereof, wherein the marble-imitated paint comprises the following raw materials in parts by weight: 25-30 parts of deionized water, 15-25 parts of alcohol, 5-10 parts of volatile essential oil, 2-5 parts of kerosene, 0.4-0.6 part of liquid paraffin, 0.1-0.2 part of glycerol, 0.3-0.4 part of defoaming agent, 0.1-0.2 part of bactericide, 1-2 parts of rutile titanium dioxide, 7.5-8 parts of calcined kaolin, 1-2 parts of cellulose, 0.1-0.2 part of multifunctional auxiliary agent, 1-2 parts of ethylene glycol, 25-30 parts of emulsion, 0.1-0.2 part of long-acting preservative and 5-6 parts of protective adhesive solution. According to the invention, by adding the additives with good volatilization effects after meeting air, such as alcohol, volatile essential oil, kerosene and the like, the raw materials are not dried quickly and are too sticky during the preparation of the raw materials, the preparation of the raw materials is facilitated, the drying speed can be increased by quickly volatilizing the raw materials of the alcohol lamp after the raw materials are sprayed, the quality of the stone-like paint is improved by filtering the raw materials before the preparation, and the stone-like paint is more practical and is suitable for wide popularization and use.
Description
Technical Field
The invention relates to the technical field of stone-like paint, in particular to marble-like paint and a preparation method thereof.
Background
At present, the stone-like paint is a thick exterior wall decorative coating with decorative effect exactly like marble and granite, and is mainly prepared by natural stone powder with various colors, and the stone-like paint has the advantages of fire resistance, water resistance, acid and alkali resistance and pollution resistance. The natural stone paint has the characteristics of no toxicity, no odor, strong bonding force, fastness and the like, can effectively prevent the corrosion of the external severe environment to the building, prolongs the service life of the building, is particularly suitable for being used in cold areas because the natural stone paint has good adhesive force and freeze-thaw resistance, and has the advantages of simple and convenient construction, easy drying and time saving, convenient construction and the like.
The patent No. CN201910285875.3 discloses an imitation marble paint, which comprises the following raw materials in parts by weight: 52-55 parts of deionized water, 0.4-0.6 part of dispersant, 0.1-0.2 part of wetting agent, 0.3-0.4 part of defoaming agent, 0.1-0.2 part of bactericide, 1-2 parts of rutile titanium dioxide, 7.5-8 parts of calcined kaolin, 1-2 parts of cellulose, 0.1-0.2 part of multifunctional additive, 1-2 parts of propylene glycol, 0.5-0.8 part of film-forming additive, 30-35 parts of emulsion, 0.1-0.2 part of long-acting preservative, 5-6 parts of protective adhesive solution and 1-2 parts of thickening agent.
However, the following problems still exist in the practical use process of the invention: 1. the drying speed of the stone-like paint in the construction process is too low, if the components of the film-forming assistant are selected to be increased, the phenomenon of drying and solidification can be caused in the process of brushing the stone-like paint, and the brushing, molding and drying of the stone-like paint are not facilitated; 2. the raw materials are not filtered in advance in the step one, and the quality of the stone-like paint can be influenced by large impurity raw materials. Therefore, the marble-imitated paint and the preparation method thereof are provided.
Disclosure of Invention
The invention aims to provide a marble-imitated paint and a preparation method thereof, wherein additives with good volatilization effects after meeting air, such as alcohol, volatile essential oil, kerosene and the like, are added, so that the raw materials are not dried quickly and are too sticky during preparation, the raw materials are blended conveniently, the drying speed can be increased by quickly volatilizing the raw materials of an alcohol lamp after the raw materials are sprayed, the quality of the marble-imitated paint is improved by filtering the raw materials before preparation, and the marble-imitated paint is practical, is suitable for wide popularization and use and solves the problems in the background art.
In order to achieve the purpose, the invention provides the following technical scheme: the marble-imitated paint comprises the following raw materials in parts by weight: 25-30 parts of deionized water, 15-25 parts of alcohol, 5-10 parts of volatile essential oil, 2-5 parts of kerosene, 0.4-0.6 part of liquid paraffin, 0.1-0.2 part of glycerol, 0.3-0.4 part of defoaming agent, 0.1-0.2 part of bactericide, 1-2 parts of rutile titanium dioxide, 7.5-8 parts of calcined kaolin, 1-2 parts of cellulose, 0.1-0.2 part of multifunctional auxiliary agent, 1-2 parts of ethylene glycol, 25-30 parts of emulsion, 0.1-0.2 part of long-acting preservative and 5-6 parts of protective adhesive solution.
As a preferred embodiment of the invention, 30 parts of deionized water, 15 parts of alcohol, 5 parts of volatile essential oil, 3 parts of kerosene, 0.4 part of liquid paraffin, 0.2 part of glycerol, 0.3 part of defoamer, 0.1 part of bactericide, 1.6 parts of rutile titanium dioxide, 8 parts of calcined kaolin, 1 part of cellulose, 0.2 part of multifunctional auxiliary agent, 2 parts of ethylene glycol, 27 parts of emulsion, 0.2 part of long-acting preservative and 6 parts of protective colloid solution.
As a preferred embodiment of the invention, 27 parts of deionized water, 20 parts of alcohol, 6 parts of volatile essential oil, 3 parts of kerosene, 0.5 part of liquid paraffin, 0.1 part of glycerol, 0.4 part of defoaming agent, 0.2 part of bactericide, 2 parts of rutile titanium dioxide, 7.5 parts of calcined kaolin, 1 part of cellulose, 0.1 part of multifunctional auxiliary agent, 1 part of ethylene glycol, 25 parts of emulsion, 0.2 part of long-acting preservative and 5 parts of protective colloid solution.
As a preferred embodiment of the invention, the cleaning agent comprises 25 parts of deionized water, 25 parts of alcohol, 5 parts of volatile essential oil, 2 parts of kerosene, 0.5 part of liquid paraffin, 0.1 part of glycerol, 0.4 part of defoaming agent, 0.2 part of bactericide, 2 parts of rutile titanium dioxide, 7.5 parts of calcined kaolin, 1 part of cellulose, 0.1 part of multifunctional auxiliary agent, 1 part of ethylene glycol, 25 parts of emulsion, 0.2 part of long-acting preservative and 5 parts of protective colloid solution.
As a preferred embodiment of the invention, the preparation steps are as follows:
a. weighing the raw materials in parts by weight;
the method comprises the following steps: filtering rutile titanium dioxide and calcined kaolin by using a filter screen for later use, adding deionized water and alcohol into a stirrer, starting the stirrer, slowly adding liquid paraffin and the filtered rutile titanium dioxide and calcined kaolin during stirring, and then stirring for ten minutes at the rotating speed of 600 revolutions per minute;
step two: continuously adding the cellulose into the stirrer, increasing the speed of the stirrer to 1000-1300 rpm, and dispersing at high speed for 30 minutes until the cellulose is completely dissolved;
step three: adding the multifunctional auxiliary agent and the ethylene glycol into the raw materials stirred in the step two, uniformly stirring the raw materials, then turning off the stirrer, adding the kerosene, and continuing stirring for 3 minutes;
step four: starting a stirrer, slowly adding the emulsion and the defoaming agent, stirring for 10-15 minutes until the mixture is uniform, then slowly adding the volatile essential oil, the glycerol, the bactericide, the long-acting preservative and the protective adhesive solution, and stirring for 15 minutes until the mixture is uniform;
step five: and (5) sealing and packaging the stirred raw materials in a dark place.
In a preferred embodiment of the present invention, the stirrer used in the first to fifth steps is a stirrer having a good sealing effect for preventing evaporation of alcohol and other materials.
In a preferred embodiment of the present invention, the alcohol is 75% industrial alcohol.
In a preferred embodiment of the present invention, the first to fifth steps are performed under normal temperature.
Compared with the prior art, the invention has the following beneficial effects:
1. according to the marble-imitated paint and the preparation method thereof, the additives with good volatilization effects after meeting air, such as alcohol, volatile essential oil, kerosene and the like, are added, so that the raw materials are not dried quickly and are too sticky during preparation, the raw materials are favorably blended, the raw materials of the alcohol lamp are volatilized quickly after the raw materials are sprayed, the drying speed can be increased, the raw materials are filtered before the raw materials are prepared, the quality of the marble-imitated paint is improved, and the marble-imitated paint is practical and suitable for wide popularization and use.
Drawings
Other features, objects and advantages of the invention will become more apparent upon reading of the detailed description of non-limiting embodiments with reference to the following drawings:
FIG. 1 is a flow chart of the marble-imitated paint and the preparation method thereof.
Detailed Description
In order to make the technical means, the creation characteristics, the achievement purposes and the effects of the invention easy to understand, the invention is further described with the specific embodiments.
In the description of the present invention, it is to be understood that the terms "upper", "lower", "front", "rear", "left", "right", "top", "bottom", "inner", "outer", and the like, indicate orientations or positional relationships based on the orientations or positional relationships shown in the drawings, are merely for convenience in describing the present invention and simplifying the description, and do not indicate or imply that the device or element being referred to must have a particular orientation, be constructed and operated in a particular orientation, and thus, should not be construed as limiting the present invention.
In the description of the present invention, it should be noted that unless otherwise explicitly stated or limited, the terms "mounted," "connected," and "disposed" are to be construed broadly, e.g., as meaning fixedly connected, disposed, detachably connected, disposed, or integrally connected and disposed; the type of the electrical appliance provided by the invention is only used for reference. For those skilled in the art, different types of electrical appliances with the same function can be replaced according to actual use conditions, and for those skilled in the art, the specific meaning of the above terms in the present invention can be understood in specific situations.
Referring to fig. 1, the present invention provides a technical solution: the marble-imitated paint comprises the following raw materials in parts by weight: 25-30 parts of deionized water, 15-25 parts of alcohol, 5-10 parts of volatile essential oil, 2-5 parts of kerosene, 0.4-0.6 part of liquid paraffin, 0.1-0.2 part of glycerol, 0.3-0.4 part of defoaming agent, 0.1-0.2 part of bactericide, 1-2 parts of rutile titanium dioxide, 7.5-8 parts of calcined kaolin, 1-2 parts of cellulose, 0.1-0.2 part of multifunctional auxiliary agent, 1-2 parts of ethylene glycol, 25-30 parts of emulsion, 0.1-0.2 part of long-acting preservative and 5-6 parts of protective adhesive solution.
Further, 30 parts of deionized water, 15 parts of alcohol, 5 parts of volatile essential oil, 3 parts of kerosene, 0.4 part of liquid paraffin, 0.2 part of glycerol, 0.3 part of defoaming agent, 0.1 part of bactericide, 1.6 parts of rutile titanium dioxide, 8 parts of calcined kaolin, 1 part of cellulose, 0.2 part of multifunctional auxiliary agent, 2 parts of ethylene glycol, 27 parts of emulsion, 0.2 part of long-acting preservative and 6 parts of protective glue solution.
Further, 27 parts of deionized water, 20 parts of alcohol, 6 parts of volatile essential oil, 3 parts of kerosene, 0.5 part of liquid paraffin, 0.1 part of glycerol, 0.4 part of defoaming agent, 0.2 part of bactericide, 2 parts of rutile titanium dioxide, 7.5 parts of calcined kaolin, 1 part of cellulose, 0.1 part of multifunctional additive, 1 part of ethylene glycol, 25 parts of emulsion, 0.2 part of long-acting preservative and 5 parts of protective glue solution.
Furthermore, 25 parts of deionized water, 25 parts of alcohol, 5 parts of volatile essential oil, 2 parts of kerosene, 0.5 part of liquid paraffin, 0.1 part of glycerol, 0.4 part of defoaming agent, 0.2 part of bactericide, 2 parts of rutile titanium dioxide, 7.5 parts of calcined kaolin, 1 part of cellulose, 0.1 part of multifunctional auxiliary agent, 1 part of ethylene glycol, 25 parts of emulsion, 0.2 part of long-acting preservative and 5 parts of protective glue solution.
Further, the preparation steps are as follows:
a. weighing the raw materials in parts by weight;
the method comprises the following steps: filtering rutile titanium dioxide and calcined kaolin by using a filter screen for later use, adding deionized water and alcohol into a stirrer, starting the stirrer, slowly adding liquid paraffin and the filtered rutile titanium dioxide and calcined kaolin during stirring, and then stirring for ten minutes at the rotating speed of 600 revolutions per minute;
step two: continuously adding the cellulose into the stirrer, increasing the speed of the stirrer to 1000-1300 rpm, and dispersing at high speed for 30 minutes until the cellulose is completely dissolved;
step three: adding the multifunctional auxiliary agent and the ethylene glycol into the raw materials stirred in the step two, uniformly stirring the raw materials, then turning off the stirrer, adding the kerosene, and continuing stirring for 3 minutes;
step four: starting a stirrer, slowly adding the emulsion and the defoaming agent, stirring for 10-15 minutes until the mixture is uniform, then slowly adding the volatile essential oil, the glycerol, the bactericide, the long-acting preservative and the protective adhesive solution, and stirring for 15 minutes until the mixture is uniform;
step five: and (5) sealing and packaging the stirred raw materials in a dark place.
Further, the stirrer used in the first step to the fifth step is a stirrer with good sealing effect and capable of avoiding volatilization of alcohol and other raw materials.
Further, the alcohol is 75% of industrial alcohol.
Further, the first step, the second step and the fifth step are all operated under the normal temperature environment.
Example one
The marble-imitated paint comprises the following raw materials in parts by weight: 30 parts of deionized water, 15 parts of alcohol, 5 parts of volatile essential oil, 3 parts of kerosene, 0.4 part of liquid paraffin, 0.2 part of glycerol, 0.3 part of defoaming agent, 0.1 part of bactericide, 1.6 parts of rutile titanium dioxide, 8 parts of calcined kaolin, 1 part of cellulose, 0.2 part of multifunctional auxiliary agent, 2 parts of ethylene glycol, 27 parts of emulsion, 0.2 part of long-acting preservative and 6 parts of protective glue solution.
The preparation steps are as follows:
a. weighing the raw materials in parts by weight;
the method comprises the following steps: filtering rutile titanium dioxide and calcined kaolin by using a filter screen for later use, adding deionized water and alcohol into a stirrer, starting the stirrer, slowly adding liquid paraffin and the filtered rutile titanium dioxide and calcined kaolin during stirring, and then stirring for ten minutes at the rotating speed of 600 revolutions per minute;
step two: continuously adding the cellulose into the stirrer, increasing the speed of the stirrer to 1000-1300 rpm, and dispersing at high speed for 30 minutes until the cellulose is completely dissolved;
step three: adding the multifunctional auxiliary agent and the ethylene glycol into the raw materials stirred in the step two, uniformly stirring the raw materials, then turning off the stirrer, adding the kerosene, and continuing stirring for 3 minutes;
step four: starting a stirrer, slowly adding the emulsion and the defoaming agent, stirring for 10-15 minutes until the mixture is uniform, then slowly adding the volatile essential oil, the glycerol, the bactericide, the long-acting preservative and the protective adhesive solution, and stirring for 15 minutes until the mixture is uniform;
step five: and (5) sealing and packaging the stirred raw materials in a dark place.
Example two
The marble-imitated paint comprises the following raw materials in parts by weight: 27 parts of deionized water, 20 parts of alcohol, 6 parts of volatile essential oil, 3 parts of kerosene, 0.5 part of liquid paraffin, 0.1 part of glycerol, 0.4 part of defoaming agent, 0.2 part of bactericide, 2 parts of rutile titanium dioxide, 7.5 parts of calcined kaolin, 1 part of cellulose, 0.1 part of multifunctional auxiliary agent, 1 part of ethylene glycol, 25 parts of emulsion, 0.2 part of long-acting preservative and 5 parts of protective glue solution.
The preparation steps are as follows:
a. weighing the raw materials in parts by weight;
the method comprises the following steps: filtering rutile titanium dioxide and calcined kaolin by using a filter screen for later use, adding deionized water and alcohol into a stirrer, starting the stirrer, slowly adding liquid paraffin and the filtered rutile titanium dioxide and calcined kaolin during stirring, and then stirring for ten minutes at the rotating speed of 600 revolutions per minute;
step two: continuously adding the cellulose into the stirrer, increasing the speed of the stirrer to 1000-1300 rpm, and dispersing at high speed for 30 minutes until the cellulose is completely dissolved;
step three: adding the multifunctional auxiliary agent and the ethylene glycol into the raw materials stirred in the step two, uniformly stirring the raw materials, then turning off the stirrer, adding the kerosene, and continuing stirring for 3 minutes;
step four: starting a stirrer, slowly adding the emulsion and the defoaming agent, stirring for 10-15 minutes until the mixture is uniform, then slowly adding the volatile essential oil, the glycerol, the bactericide, the long-acting preservative and the protective adhesive solution, and stirring for 15 minutes until the mixture is uniform;
step five: and (5) sealing and packaging the stirred raw materials in a dark place.
EXAMPLE III
The marble-imitated paint comprises the following raw materials in parts by weight: 25 parts of deionized water, 25 parts of alcohol, 5 parts of volatile essential oil, 2 parts of kerosene, 0.5 part of liquid paraffin, 0.1 part of glycerol, 0.4 part of defoaming agent, 0.2 part of bactericide, 2 parts of rutile titanium dioxide, 7.5 parts of calcined kaolin, 1 part of cellulose, 0.1 part of multifunctional auxiliary agent, 1 part of ethylene glycol, 25 parts of emulsion, 0.2 part of long-acting preservative and 5 parts of protective glue solution.
The preparation steps are as follows:
a. weighing the raw materials in parts by weight;
the method comprises the following steps: filtering rutile titanium dioxide and calcined kaolin by using a filter screen for later use, adding deionized water and alcohol into a stirrer, starting the stirrer, slowly adding liquid paraffin and the filtered rutile titanium dioxide and calcined kaolin during stirring, and then stirring for ten minutes at the rotating speed of 600 revolutions per minute;
step two: continuously adding the cellulose into the stirrer, increasing the speed of the stirrer to 1000-1300 rpm, and dispersing at high speed for 30 minutes until the cellulose is completely dissolved;
step three: adding the multifunctional auxiliary agent and the ethylene glycol into the raw materials stirred in the step two, uniformly stirring the raw materials, then turning off the stirrer, adding the kerosene, and continuing stirring for 3 minutes;
step four: starting a stirrer, slowly adding the emulsion and the defoaming agent, stirring for 10-15 minutes until the mixture is uniform, then slowly adding the volatile essential oil, the glycerol, the bactericide, the long-acting preservative and the protective adhesive solution, and stirring for 15 minutes until the mixture is uniform;
step five: and (5) sealing and packaging the stirred raw materials in a dark place.
The traditional marble-like paint data parameters are as follows in table 1:
| test items | The stirring is difficult and easy | Drying speed | Hardness in drying | Content of impurities |
| Parameter index | Difficulty in | Slow | Good effect | Chinese character shao (a Chinese character of 'shao') |
Example a marble-like paint data parameters table 2 is as follows:
| test items | The stirring is difficult and easy | Drying speed | Hardness in drying | Content of impurities |
| Parameter index | Is easy to use | In general | Good effect | Is free of |
Example two marble-imitated lacquer data parameters table 3 is as follows:
| test items | The stirring is difficult and easy | Drying speed | Hardness in drying | Content of impurities |
| Parameter index | Is easy to use | Is quicker | Good effect | Is free of |
Example three marble-imitated lacquer data parameters table 4 is as follows:
| test items | The stirring is difficult and easy | Drying speed | Hardness in drying | Content of impurities |
| Parameter index | Is easy to use | Very fast | Good effect | Is free of |
In summary, the data are compared with the data in tables 1, 2, 3 and 4 to obtain: when the stone-like paint is prepared under the conditions of the third embodiment, the raw materials of the paint are easy to stir, the drying speed is extremely high, the dried hardness is good, and no impurity is contained, so that the conclusion is that the paint prepared in the third embodiment has the fastest drying speed and the best performance.
While there have been shown and described what are at present considered the fundamental principles and essential features of the invention and its advantages, it will be apparent to those skilled in the art that the invention is not limited to the details of the foregoing exemplary embodiments, but is capable of other specific forms without departing from the spirit or essential characteristics thereof. The present embodiments are therefore to be considered in all respects as illustrative and not restrictive, the scope of the invention being indicated by the appended claims rather than by the foregoing description, and all changes which come within the meaning and range of equivalency of the claims are therefore intended to be embraced therein. Any reference sign in a claim should not be construed as limiting the claim concerned.
Furthermore, it should be understood that although the present description refers to embodiments, not every embodiment may contain only a single embodiment, and such description is for clarity only, and those skilled in the art should integrate the description, and the embodiments may be combined as appropriate to form other embodiments understood by those skilled in the art.
Claims (8)
1. A marble-imitated paint and a preparation method thereof are characterized in that: the raw materials comprise the following components in parts by weight: 25-30 parts of deionized water, 15-25 parts of alcohol, 5-10 parts of volatile essential oil, 2-5 parts of kerosene, 0.4-0.6 part of liquid paraffin, 0.1-0.2 part of glycerol, 0.3-0.4 part of defoaming agent, 0.1-0.2 part of bactericide, 1-2 parts of rutile titanium dioxide, 7.5-8 parts of calcined kaolin, 1-2 parts of cellulose, 0.1-0.2 part of multifunctional auxiliary agent, 1-2 parts of ethylene glycol, 25-30 parts of emulsion, 0.1-0.2 part of long-acting preservative and 5-6 parts of protective adhesive solution.
2. The marble-imitated paint and the preparation method thereof according to claim 1, wherein the marble-imitated paint comprises the following components: 30 parts of deionized water, 15 parts of alcohol, 5 parts of volatile essential oil, 3 parts of kerosene, 0.4 part of liquid paraffin, 0.2 part of glycerol, 0.3 part of defoaming agent, 0.1 part of bactericide, 1.6 parts of rutile titanium dioxide, 8 parts of calcined kaolin, 1 part of cellulose, 0.2 part of multifunctional auxiliary agent, 2 parts of ethylene glycol, 27 parts of emulsion, 0.2 part of long-acting preservative and 6 parts of protective glue solution.
3. The marble-imitated paint and the preparation method thereof according to claim 1, wherein the marble-imitated paint comprises the following components: 27 parts of deionized water, 20 parts of alcohol, 6 parts of volatile essential oil, 3 parts of kerosene, 0.5 part of liquid paraffin, 0.1 part of glycerol, 0.4 part of defoaming agent, 0.2 part of bactericide, 2 parts of rutile titanium dioxide, 7.5 parts of calcined kaolin, 1 part of cellulose, 0.1 part of multifunctional auxiliary agent, 1 part of ethylene glycol, 25 parts of emulsion, 0.2 part of long-acting preservative and 5 parts of protective glue solution.
4. The marble-imitated paint and the preparation method thereof according to claim 1, wherein the marble-imitated paint comprises the following components: 25 parts of deionized water, 25 parts of alcohol, 5 parts of volatile essential oil, 2 parts of kerosene, 0.5 part of liquid paraffin, 0.1 part of glycerol, 0.4 part of defoaming agent, 0.2 part of bactericide, 2 parts of rutile titanium dioxide, 7.5 parts of calcined kaolin, 1 part of cellulose, 0.1 part of multifunctional auxiliary agent, 1 part of ethylene glycol, 25 parts of emulsion, 0.2 part of long-acting preservative and 5 parts of protective glue solution.
5. The marble-imitated paint and the preparation method thereof according to claim 1, wherein the marble-imitated paint comprises the following components: the preparation steps are as follows:
a. weighing the raw materials in parts by weight;
the method comprises the following steps: filtering rutile titanium dioxide and calcined kaolin by using a filter screen for later use, adding deionized water and alcohol into a stirrer, starting the stirrer, slowly adding liquid paraffin and the filtered rutile titanium dioxide and calcined kaolin during stirring, and then stirring for ten minutes at the rotating speed of 600 revolutions per minute;
step two: continuously adding the cellulose into the stirrer, increasing the speed of the stirrer to 1000-1300 rpm, and dispersing at high speed for 30 minutes until the cellulose is completely dissolved;
step three: adding the multifunctional auxiliary agent and the ethylene glycol into the raw materials stirred in the step two, uniformly stirring the raw materials, then turning off the stirrer, adding the kerosene, and continuing stirring for 3 minutes;
step four: starting a stirrer, slowly adding the emulsion and the defoaming agent, stirring for 10-15 minutes until the mixture is uniform, then slowly adding the volatile essential oil, the glycerol, the bactericide, the long-acting preservative and the protective adhesive solution, and stirring for 15 minutes until the mixture is uniform;
step five: and (5) sealing and packaging the stirred raw materials in a dark place.
6. The marble-imitated paint and the preparation method thereof according to claim 5, wherein the marble-imitated paint comprises the following components: the stirrer used in the first step to the fifth step is a stirrer with good sealing effect and capable of avoiding volatilization of alcohol and other raw materials.
7. The marble-imitated paint and the preparation method thereof according to claim 1, wherein the marble-imitated paint comprises the following components: the alcohol is 75% of industrial alcohol.
8. The marble-imitated paint and the preparation method thereof according to claim 5, wherein the marble-imitated paint comprises the following components: and the first step to the fifth step are operated under the normal temperature environment.