CN108250867A - A kind of aqueous silver color process paint and preparation method thereof - Google Patents
A kind of aqueous silver color process paint and preparation method thereof Download PDFInfo
- Publication number
- CN108250867A CN108250867A CN201810010818.XA CN201810010818A CN108250867A CN 108250867 A CN108250867 A CN 108250867A CN 201810010818 A CN201810010818 A CN 201810010818A CN 108250867 A CN108250867 A CN 108250867A
- Authority
- CN
- China
- Prior art keywords
- silver color
- agent
- color process
- water
- aqueous silver
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of aqueous silver color process paint, it is characterised in that the raw material matched by following weight is made：Water-based acrylic resin 70 80%；Water 5 10%；Polycarbodiimide 1 2%；Dispersant 0.20 0.80%；Wetting agent 0.20 0.80%；Levelling agent 0.10 0.60%；Antifoaming agent 0.20 0.80%；Aqueous aluminum powder slurry 5 10%；Fungicide 0.10 0.50%；Thickener 0.50 3%；Coalescents 2 6%；PH adjusting agent 0.10 0.50%.The present invention also provides a kind of preparation methods of above-mentioned aqueous silver color process paint.The aqueous silver color process paint of the present invention pre-processes water-based acrylic resin as a result of polycarbodiimide, carboxylic acid reaction micro in water-based acrylic resin is fallen, so that the stability of the water paint added in after aqueous aluminum powder slurry is obviously improved, and do not have any harmful effect to the performance and storage characteristics of whole water paint；This aqueous silver color process paint can be dried at normal temperatures, be a kind of aqueous product having compared with high storage stability, can solve the problems, such as that product rises tank in the flatulence of storage process.
Description
Technical field
The present invention relates to paint fields, and in particular to a kind of aqueous silver color process paint and preparation method thereof.
Background technology
In craftwork polychromy, golden silver color is liked deeply with the metal effect of its unique and beautiful always, big in the past
Use solvent type nitro or acrylic compounds metallic paint more, it is easy because containing in solvent based product with the reinforcement of environmental consciousness
Toxic organic solvent is fired, is increasingly used limitation.Government has promulgated a series of pressure of limitation solvent based coatings successively
Standard, part municipal government shopping list clear stipulaties can only select environmentally friendly aqueous product, and water paint replaces molten
The paces of dosage form coating have been getting faster.
So the release of water-based metal effect paint has great significance, at present because can not have in golden aqueous effect paint
Cu-Zn alloy powder and using being produced to the highly stable Pearlied gold pigment of water and water-base resin, so difficulty is little.But silver color
Pigment used in metal effect paint will usually use aluminium powder, and the activity of aluminium is higher, although raw material producer carries out coating to it
In the case that processing, makes it avoid reacting with water, but water-base resin in formula contains a small amount of carboxylic acid, still have micro anti-
It should occur, product is made easily to generate flatulence during storage and is risen tank phenomenon, product quality can be also influenced when serious and is imitated with construction
Fruit.
Invention content
The technical problems to be solved by the invention are to provide a kind of aqueous silver color process paint and preparation method thereof, this aqueous
Silver color process paint storage stability is high, solves the problems, such as that product rises tank in the flatulence of storage process.The technical solution of use is as follows：
A kind of aqueous silver color process paint, it is characterised in that the raw material matched by following weight is made：Water-based acrylic resin 70-
80%；Water 5-10%；Polycarbodiimide 1-2%；Dispersant 0.20-0.80%；Wetting agent 0.20-0.80%；Levelling agent 0.10-
0.60%；Antifoaming agent 0.20-0.80%；Aqueous aluminum powder starches 5-10%；Fungicide 0.10-0.50%；Thickener 0.50-3%；Film forming helps
Agent 2-6%；PH adjusting agent 0.10-0.50%.
Above-mentioned water-based acrylic resin is film forming matter, provides paint film.
Diluent of the above-mentioned water as aqueous silver color process paint plays diluting effect.
Above-mentioned polycarbodiimide plays the role of reacting with the carboxyl in water-based acrylic resin as inorganic agent；Profit
Water-based acrylic resin is pre-processed with polycarbodiimide, carboxylic acid reaction micro in resin is fallen.
It is preferred that above-mentioned dispersant is the polyacrylic hydrosol of the affinity groups containing pigment.Above-mentioned dispersant plays dispersion and makees
With.
It is preferred that above-mentioned wetting agent is non-ionic polysiloxane surfactant.Above-mentioned wetting agent plays wetting and dispersing and makees
With.
It is preferred that above-mentioned levelling agent is the copolymer of siloxanes and polyethers.Above-mentioned levelling agent plays levelling, can promote coating
A smooth, smooth, uniform film is formed during drying and forming-film.
It is preferred that above-mentioned antifoaming agent is Siloxane-Oxyalkylene Copolymers solution.Above-mentioned antifoaming agent plays defoaming.
Above-mentioned aqueous aluminum powder slurry is metallic pigments, plays pigmentation.Aqueous aluminum powder slurry is also known as water aluminum-silver slurry, can be in market
On buy.
It is preferred that above-mentioned fungicide is isothiazolinone.Above-mentioned fungicide plays sterilization and anticorrosion.
It is preferred that above-mentioned thickener is polyurethane-modified polyethers thickener.Above-mentioned thickener plays thickening power.
It is preferred that above-mentioned coalescents are the mixtures of dipropylene glycol methyl ether (DPM) and dipropylene (DPNB).It is more excellent
It is 1 to select the weight ratio of dipropylene glycol methyl ether and dipropylene:(0.8-1.2).Even more preferably dipropylene glycol methyl ether and two
The weight ratio of propandiol butyl ether is 1:1.This coalescents, which rise, helps water-based acrylic resin filming function.
It is preferred that above-mentioned pH adjusting agent is 2- amino-2-methyl propyl alcohol.This pH adjusting agent rises and stablizes for adjusting acid-base value
System acts on.
The present invention also provides a kind of preparation methods of above-mentioned aqueous silver color process paint, it is characterised in that includes the following steps：
（1）Following raw materials are equipped with according to the weight percent of setting：Water-based acrylic resin 70-80%, water 5-10%, poly- carbonization two
Imines 1-2%, dispersant 0.20-0.80%, wetting agent 0.20-0.80%, levelling agent 0.10-0.60%, antifoaming agent 0.20-0.80%,
Aqueous aluminum powder slurry 5-10%, fungicide 0.10-0.50%, thickener 0.50-3%, coalescents 2-6%, pH adjusting agent 0.10-
0.50%；
（2）Water-based acrylic resin and water are added in stirring container, polycarbodiimide is added in while stirring, is stirred
24-48 hours are stood after uniformly, it is spare；
（3）By step（2）The spare material stood is added in a mixing bowl equipped with blender, then by dispersant, profit
Humectant, levelling agent and antifoaming agent are added in a mixing bowl, are mixed slowly 5-10 minutes, after stirring evenly, when stirring by aqueous aluminium
Slurry is added in a mixing bowl, and then moderate-speed mixer disperses 10-20 minutes, then by fungicide, thickener, coalescents and pH
Conditioning agent is added in a mixing bowl, and the pH value for stirring evenly and adjusting mixture obtains aqueous silver color process paint to 8-9.
It is preferred that above-mentioned steps（3）In, the rotating speed of blender is 300~400 turns per minute when mixing slowly, during moderate-speed mixer
The rotating speed of blender is 600~800 turns per minute.
Above-mentioned steps（3）In, after moderate-speed mixer disperses 10-20 minutes, paint film, eye can be prepared with 150 microns of thick broaching tools
After eyeball observation is without apparent coarse grain, then will be in fungicide, thickener, coalescents and pH adjusting agent addition a mixing bowl.
The advantageous effect of the present invention against existing technologies is, as a result of polycarbodiimide to water-based acrylic resin
It is pre-processed, carboxylic acid reaction micro in water-based acrylic resin is fallen so that add in the water paint after aqueous aluminum powder slurry
Stability be obviously improved, and there is no any harmful effect to the performance and storage characteristics of whole water paint；It is this
Aqueous silver color process paint can be dried at normal temperatures, be a kind of aqueous product having compared with high storage stability, can solve to produce
Product rise tank problem in the flatulence of storage process.The aqueous silver color process paint of the present invention can be used for the techniques such as woodwork, ceramics, plastic cement
The incrustation of product.
Specific embodiment
Embodiment 1
In the present embodiment, the preparation method of aqueous silver color process paint includes the following steps：
（1）Following raw materials are equipped with according to the weight percent of setting：Water-based acrylic resin 78%, water 8.8%, polycarbodiimide
1.5%th, dispersant 0.30%, wetting agent 0.30%, levelling agent 0.20%, antifoaming agent 0.50%, aqueous aluminum powder slurry 6%, fungicide 0.30%
（It is isothiazolinone）, thickener 1%, coalescents 3%（Wherein dipropylene glycol methyl ether 1.5%, dipropylene 1.5%）、
PH adjusting agent 0.10%（It is 2- amino-2-methyl propyl alcohol）；
（2）Water-based acrylic resin and water are added in stirring container, polycarbodiimide is added in while stirring, is stirred
24 hours are stood after uniformly, it is spare；
（3）By step（2）The spare material stood is added in a mixing bowl equipped with blender, then by dispersant, profit
Humectant, levelling agent and antifoaming agent are added in a mixing bowl, are mixed slowly 5 minutes, after stirring evenly, are starched aqueous aluminum powder when stirring
It is added in a mixing bowl, then moderate-speed mixer disperses 10 minutes, then by fungicide, thickener, coalescents and pH adjusting agent
It is added in a mixing bowl, the pH value for stirring evenly and adjusting mixture obtains aqueous silver color process paint to 8.
Above-mentioned steps（3）, the rotating speed of blender is 300 turns per minute when mixing slowly, and blender turns during moderate-speed mixer
Speed is 600 turns per minute.
Above-mentioned steps（3）In, moderate-speed mixer disperses after ten minutes, paint film can be prepared with 150 microns of thick broaching tools, and eyes are seen
It examines without after apparent coarse grain, then fungicide, thickener, coalescents and pH adjusting agent is added in a mixing bowl.
Above-mentioned water-based acrylic resin uses the product of Ahmedabad richness company, model 3230D.
Above-mentioned polycarbodiimide uses the product of golden brother company.
Above-mentioned dispersant, levelling agent, wetting agent, antifoaming agent use the product of Di Gao companies of Germany.
Above-mentioned aqueous aluminum powder slurry is using the product of Jun Chi companies, model JCS220.
Above-mentioned fungicide uses the product of Sol company, model EGCT.
Above-mentioned thickener uses the product in Aksu.
Above-mentioned coalescents are using the 1 of the DPM and DPNB of Tao Shi:1 mixed liquor.
Above-mentioned pH adjusting agent uses the product of Tao Shi, model AMP-95.
Embodiment 2
In the present embodiment, the preparation method of aqueous silver color process paint includes the following steps：
（1）Following raw materials are equipped with according to the weight percent of setting：Water-based acrylic resin 75%, water 7%, polycarbodiimide
2%th, dispersant 0.50%, wetting agent 0.50%, levelling agent 0.40%, antifoaming agent 0.70%, aqueous aluminum powder slurry 8%, fungicide 0.50%
（It is isothiazolinone）, thickener 3%, coalescents 4%（Wherein dipropylene glycol methyl ether 2%, dipropylene 2%）, pH tune
Save agent 0.30%（It is 2- amino-2-methyl propyl alcohol）；
（2）Water-based acrylic resin and water are added in stirring container, polycarbodiimide is added in while stirring, is stirred
36 hours are stood after uniformly, it is spare；
（3）By step（2）The spare material stood is added in a mixing bowl equipped with blender, then by dispersant, profit
Humectant, levelling agent and antifoaming agent are added in a mixing bowl, are mixed slowly 7 minutes, after stirring evenly, are starched aqueous aluminum powder when stirring
It is added in a mixing bowl, then moderate-speed mixer disperses 15 minutes, then by fungicide, thickener, coalescents and pH adjusting agent
It is added in a mixing bowl, the pH value for stirring evenly and adjusting mixture obtains aqueous silver color process paint to 8.5.
Above-mentioned steps（3）In, the rotating speed of blender is 350 turns per minute when mixing slowly, blender during moderate-speed mixer
Rotating speed is 700 turns per minute.
Above-mentioned steps（3）In, after moderate-speed mixer disperses 15 minutes, paint film can be prepared with 150 microns of thick broaching tools, eyes are seen
It examines without after apparent coarse grain, then fungicide, thickener, coalescents and pH adjusting agent is added in a mixing bowl.
Above-mentioned water-based acrylic resin uses the product of Ahmedabad richness company, model 3230D.
Above-mentioned polycarbodiimide uses the product of golden brother company.
Above-mentioned dispersant, levelling agent, wetting agent, antifoaming agent use the product of Di Gao companies of Germany.
Above-mentioned aqueous aluminum powder slurry is using the product of Jun Chi companies, model JCS220.
Above-mentioned fungicide uses the product of Sol company, model EGCT.
Above-mentioned thickener uses the product in Aksu.
Above-mentioned coalescents are using the 1 of the DPM and DPNB of Tao Shi:1 mixed liquor.
Above-mentioned pH adjusting agent uses the product of Tao Shi, model AMP-95.
Embodiment 3
In the present embodiment, the preparation method of aqueous silver color process paint includes the following steps：
（1）Following raw materials are equipped with according to the weight percent of setting：Water-based acrylic resin 71%, water 5%, polycarbodiimide
1%th, dispersant 0.70%, wetting agent 0.70%, levelling agent 0.50%, antifoaming agent 0.20%, aqueous aluminum powder slurry 10%, fungicide 0.10%
（It is isothiazolinone）, thickener 2%, coalescents 6%（Wherein dipropylene glycol methyl ether 3%, dipropylene 3%）, pH tune
Save agent 0.50%（It is 2- amino-2-methyl propyl alcohol）；
（2）Water-based acrylic resin and water are added in stirring container, polycarbodiimide is added in while stirring, is stirred
48 hours are stood after uniformly, it is spare；
（3）By step（2）The spare material stood is added in a mixing bowl equipped with blender, then by dispersant, profit
Humectant, levelling agent and antifoaming agent are added in a mixing bowl, are mixed slowly 10 minutes, after stirring evenly, when stirring by aqueous aluminum powder
Slurry is added in a mixing bowl, and then moderate-speed mixer disperses 20 minutes, then adjusts fungicide, thickener, coalescents and pH
Agent is added in a mixing bowl, and the pH value for stirring evenly and adjusting mixture obtains aqueous silver color process paint to 9.
Above-mentioned steps（3）In, the rotating speed of blender is 400 turns per minute when mixing slowly, blender during moderate-speed mixer
Rotating speed is 800 turns per minute.
Above-mentioned steps（3）In, moderate-speed mixer disperses after twenty minutes, paint film can be prepared with 150 microns of thick broaching tools, and eyes are seen
It examines without after apparent coarse grain, then fungicide, thickener, coalescents and pH adjusting agent is added in a mixing bowl.
Above-mentioned water-based acrylic resin uses the product of Ahmedabad richness company, model 3230D.
Above-mentioned polycarbodiimide uses the product of golden brother company.
Above-mentioned dispersant, levelling agent, wetting agent, antifoaming agent use the product of Di Gao companies of Germany.
Above-mentioned aqueous aluminum powder slurry is using the product of Jun Chi companies, model JCS220.
Above-mentioned fungicide uses the product of Sol company, model EGCT.
Above-mentioned thickener uses the product in Aksu.
Above-mentioned coalescents are using the 1 of the DPM and DPNB of Tao Shi:1 mixed liquor.
Above-mentioned pH adjusting agent uses the product of Tao Shi, model AMP-95.
Existing water before storage stability and our company to the obtained aqueous silver color process paints of above-described embodiment 1-3
The storage stability of property silver color process paint is compared, and test result is as follows shown in table 1.
1 storage stability test result of table
| Storage stability | 50 DEG C store 1 month | 50 DEG C store 3 months | Naturally half a year is placed | Naturally it places 1 year |
| Existing aqueous silver process paint sample | There is a small amount of bubble to generate in tank | Bubble is more, micro- to have the tank phenomenon that rises | There is a small amount of bubble to generate in tank | Bubble is more, there is the apparent tank phenomenon that rises |
| Embodiment 1 | Normally, bubble-free, without the tank phenomenon that rises | Normally, bubble-free, without the tank phenomenon that rises | Normally, bubble-free, without the tank phenomenon that rises | Normally, bubble-free, without the tank phenomenon that rises |
| Embodiment 2 | Normally, bubble-free, without the tank phenomenon that rises | Normally, bubble-free, without the tank phenomenon that rises | Normally, bubble-free, without the tank phenomenon that rises | Normally, bubble-free, without the tank phenomenon that rises |
| Embodiment 3 | Normally, bubble-free, without the tank phenomenon that rises | Normally, bubble-free, without the tank phenomenon that rises | Normally, bubble-free, without the tank phenomenon that rises | Normally, bubble-free, without the tank phenomenon that rises |
The storage stability that can be seen that the aqueous silver color process paint of embodiment 1-3 from more than test result is fine, can be normal
The lower drying of temperature, is a kind of aqueous product having compared with high storage stability.
Claims (10)
1. a kind of aqueous silver color process paint, it is characterised in that the raw material matched by following weight is made：Water-based acrylic resin 70-
80%；Water 5-10%；Polycarbodiimide 1-2%；Dispersant 0.20-0.80%；Wetting agent 0.20-0.80%；Levelling agent 0.10-
0.60%；Antifoaming agent 0.20-0.80%；Aqueous aluminum powder starches 5-10%；Fungicide 0.10-0.50%；Thickener 0.50-3%；Film forming helps
Agent 2-6%；PH adjusting agent 0.10-0.50%.
2. aqueous silver color process paint according to claim 1, it is characterised in that：The dispersant is affinity groups containing pigment
Polyacrylic hydrosol.
3. aqueous silver color process paint according to claim 1, it is characterised in that：The wetting agent is non-ionic poly- silicon
Oxygen alkane surfactant.
4. aqueous silver color process paint according to claim 1, it is characterised in that：The levelling agent is siloxanes and polyethers
Copolymer.
5. aqueous silver color process paint according to claim 1, it is characterised in that：The antifoaming agent is polyether-modified poly- silica
Alkane solution.
6. aqueous silver color process paint according to claim 1, it is characterised in that：The fungicide is isothiazolinone；Institute
It is polyurethane-modified polyethers thickener to state thickener；The pH adjusting agent is 2- amino-2-methyl propyl alcohol.
7. aqueous silver color process paint according to claim 1, it is characterised in that：The coalescents are dipropylene glycol methyl ethers
With the mixture of dipropylene；The weight ratio of the dipropylene glycol methyl ether and the dipropylene is 1:(0.8-
1.2)。
8. aqueous silver color process paint according to claim 7, it is characterised in that：The dipropylene glycol methyl ether and the dipropyl
The weight ratio of glycol butyl ether is 1:1.
9. a kind of preparation method of aqueous silver color process paint, it is characterised in that include the following steps：
（1）Following raw materials are equipped with according to the weight percent of setting：Water-based acrylic resin 70-80%, water 5-10%, poly- carbonization two
Imines 1-2%, dispersant 0.20-0.80%, wetting agent 0.20-0.80%, levelling agent 0.10-0.60%, antifoaming agent 0.20-0.80%,
Aqueous aluminum powder slurry 5-10%, fungicide 0.10-0.50%, thickener 0.50-3%, coalescents 2-6%, pH adjusting agent 0.10-
0.50%；
（2）Water-based acrylic resin and water are added in stirring container, polycarbodiimide is added in while stirring, is stirred
24-48 hours are stood after uniformly, it is spare；
（3）By step（2）The spare material stood is added in a mixing bowl equipped with blender, then by dispersant, profit
Humectant, levelling agent and antifoaming agent are added in a mixing bowl, are mixed slowly 5-10 minutes, after stirring evenly, when stirring by aqueous aluminium
Slurry is added in a mixing bowl, and then moderate-speed mixer disperses 10-20 minutes, then by fungicide, thickener, coalescents and pH
Conditioning agent is added in a mixing bowl, and the pH value for stirring evenly and adjusting mixture obtains aqueous silver color process paint to 8-9.
10. the preparation method of aqueous silver color process paint according to claim 9, it is characterised in that：
The step（3）In, the rotating speed of blender is 300~400 turns per minute when mixing slowly, blender during moderate-speed mixer
Rotating speed is 600~800 turns per minute.