CN105885690A - Water-borne acrylic resin anticorrosive coating and preparation method thereof - Google Patents
Water-borne acrylic resin anticorrosive coating and preparation method thereof Download PDFInfo
- Publication number
- CN105885690A CN105885690A CN201610401977.3A CN201610401977A CN105885690A CN 105885690 A CN105885690 A CN 105885690A CN 201610401977 A CN201610401977 A CN 201610401977A CN 105885690 A CN105885690 A CN 105885690A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- acrylic resin
- azo
- anticorrosive paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a water-borne acrylic resin anticorrosive coating and a preparation method thereof, and belongs to the technical field of coatings. The water-borne acrylic resin anticorrosive coating is prepared from, by weigh , 30-55 parts of modified acrylic emulsion, 16-25 parts of water-borne epoxy resin, 10-16 parts of silica sol, 4-6 parts of aluminum triphosphate, 5-15 parts of anticorrosive pigment, 20-40 parts of pigment filler, 0.5-5 parts of additive and 10-15 parts of water. The water-borne acrylic coating has the advantage of being long in storage time, and still has the good coating property after being stored for 12 months or longer.
Description
Technical field
The present invention relates to a kind of water-borne acrylic resin anticorrosive paint and preparation method thereof, belong to technical field of coatings.
Background technology
The research of acrylic monomers and resin starts from 1805 the earliest, but owing to condition limits, until nineteen twenty-seven just by
Rohm & Haas company industrialized production, real application on coating is then after nineteen fifty-three.Acrylic resin paint
Today of development.It has been the class synthetic resin coating that type is most, combination property is the most complete, versatility is the strongest, high with other
Molecule resin-phase ratio, acrylic resin paint has many prominent advantages, and such as fast light, the weatherability of its excellence, be exposed to the sun in open air
Durability is strong, and ultraviolet light irradiates and is not easily decomposed and turns yellow, and can keep original gloss and color and luster for a long time, heat-resist;Corrosion resistant
Erosion, has the chemicals such as preferable acid and alkali resistance, salt, oils and fats, detergent to stain and corrosive nature.Acrylic resin paint is existing excellent
Decoration performance more, has again good protective value.Both can be made into solvent based coating, and can be made into again water paint, may also be fabricated which
No-solvent type coating.Therefore, acrylic resin paint has become a big class coating of greatest concern, that hidden by green grass or young crops.
It addition, along with the development of coatings industry, a new problem is paid close attention to by people day by day, and i.e. organic coating is to environment
Pollution problem.In coatings industry, often containing VOC (VOC) in solvent used and auxiliary agent, they are waved
It is dealt in air and can cause air pollution.In addition, the poisonous and harmful substance such as hazardous air pollutants (HAPs), heavy metal is also
Environmental and human health impacts is worked the mischief.Every coating using water as solvent or making disperse medium, all can be described as water paint.
Water paint includes water soluble paint, water-reducible coating, water-dispersible paint (latex paint) 3 kinds.Water soluble paint be with
Water-soluble resin is film forming matter, with polyvinyl alcohol and various modifier thereof as representative, and the most water-soluble alkyd resin, water
Molten epoxy resin and inorganic polymer resin etc..Its advantage includes: 1. water paint is with water as solvent, saves ample resources;
Fire risk when water paint eliminates construction;Reduce atmospheric pollution;Water paint is only with a small amount of hypotoxicity alcohol ether
Class organic solvent, improves operating environmental condition.General water paint organic solvent (accounting for coating) between 10%~15%,
And present cathode electrophoresis dope is reduced to less than 1.2%, to reducing, pollution saving resource impact is notable.2. water paint is wet
Surface and wet environment can directly coat construction;Water paint is good to material surface adaptability, and coating adhesion is strong.3. water
Property paint spraying instrument can wash by water, and greatly reduces the consumption of cleaning solvent.4. water paint electrophoresis film is uniform, smooth.
Flattening is good;Certain thickness film can be coated in inner chamber, weld seam, corner angle, seamed edge position, have good protective;Electrophoresis is coated with
Film has best corrosion resistance, the salt fog resistance of thick film cathode electrophoresis coating to reach as high as 1200h.
CN104673059A discloses a kind of water-based epoxy acrylic resin anticorrosive paint and preparation method thereof, according to weight
Percentages, including following raw material components: epoxy acrylic resin 27~37%;White carbon black 2~3%;Blanc fixe 17~
27%;Rust resisting pigment 5~13%;Function additive 0.6~1.4%;Dimethylethanolamine 1~2.2%;Cosolvent 5~6%;Increase
Thick dose 0.2~0.6%;Deionized water 22~30%.CN104072657A discloses a kind of water-borne acrylic resin and packaging is held
Device coating, the preparation process of water-borne acrylic resin is for adjusting monomer ratio, and by 1,1-dimethyl-1-heptyl carboxyl shrinks sweet
Grease is modified, and is neutralized through 2-amino-2-methyl-1-propanol, becomes salt, it is achieved Water-borne modification, and preparation viscosity is low, to pigment
The water-borne acrylic resin of good dispersion.Open a kind of hydrophilic acrylic's coating of CN104212287A and preparation method thereof, institute
Stating coating and comprise acrylic emulsion, acrylic emulsion is by including that following monomer prepares through emulsion polymerization: alkyl acrylate
60-110 weight portion, cross-linking monomer 5-65 weight portion, acrylic acid and methacrylic acid 5-40 weight portion altogether, and polyhydric alcohol (first
Base) acrylate 0-65 weight portion, and acrylic acid: the mass ratio of methacrylic acid is 2:(1-2), cross-linking monomer, acrylic acid, first
Base acrylic acid is 70-150 part with the gross weight number of polyhydric alcohol (methyl) acrylate, the glass transition temperature of acrylic emulsion
Degree is for 20-30 DEG C.
But above-mentioned water-borne acrylic coatings is after longer-term storage, it may occur that after use, paint film property declines
Problem.
Summary of the invention
It is an object of the invention to: the water-borne acrylic resin coating of a kind of storage life limit for length, favorable anti-corrosion effect is provided.
Technical scheme is:
A kind of water-borne acrylic resin anticorrosive paint, includes following component by weight: 30~55 parts of modified propylene
Yogurt liquid, 16~25 parts of aqueous epoxy resins, the Ludox of 10~16 parts, 4~6 parts of aluminium triphosphates, anticorrosion face of 5~15 parts
Material, the color stuffing of 20~40 parts, the auxiliary agent of 0.5~5 part and the water of 10~15 parts.
Above-mentioned anti-corrosion paint is one or more the arbitrary proportion mixture in zinc phosphate, modified zinc phosphate, zinc molybdate.
Above-mentioned auxiliary agent be wetting agent, dispersant, coalescents, pH adjusting agent, defoamer, auxiliary rheological agents in any proportion
Mixture.
Above-mentioned color stuffing can be one or more in iron oxide red, titanium dioxide, barium sulfate, Pulvis Talci, mica powder
The mixture of arbitrary proportion.
The preparation method of above-mentioned modified acrylic emulsion is:
S1, by weight, by 50~60 parts of hydroxy silicon oils, 10~15 parts of Silane coupling reagent KH-570s, 3~5 parts of KOH, acetic acid
Ethyl ester 6~10 parts of mix homogeneously, in a nitrogen atmosphere, keep reaction 3h, obtain modified polyorganosiloxane pre-polymerization after being warming up to 90 DEG C
Body;
S2, by weight, takes butyl acrylate 12~15 parts, acrylic acid methyl ester. 5~10 parts, emulsifying agent 1~2 parts and deionization
Water 60~70 parts, high-speed stirred 0.5~1h, add initiator 2~4 parts, at 70~80 DEG C, react 0.5~2h, then drip 6
~10 parts of modified polyorganosiloxane performed polymers and initiator 1~2 parts, at 70~80 DEG C, react 2~3h, then with ammonia regulation pH extremely
7, obtain the acrylic emulsion of modification.
Described azo-initiator is selected from azo-bis-iso-dimethyl, azo-bis-isobutyrate hydrochloride, azo two formyl
Amine, azo diisopropyl imidazoline hydrochloride, azo isobutyl cyano group Methanamide, azo dicyclohexyl formonitrile HCN, azo dicyano penta
One or more in acid, azo diisopropyl imidazoline, azodiisobutyronitrile, AMBN and 2,2'-Azobis(2,4-dimethylvaleronitrile).
Hydroxy radical content in hydroxy silicon oil is 8wt%.
High-speed stirred in step S2 refers to rotating speed 2000rpm.
Above-mentioned water-borne acrylic resin preparation method of anticorrosion paint is: by modified acrylic emulsion, water-base epoxy tree
Fat, Ludox, aluminium triphosphate, auxiliary agent and water mixing and stirring;Add anti-corrosion paint and color stuffing the most while stirring, stir
Mix uniformly, obtain water-based anticorrosive paint.
Aqueous epoxy resins employed in following example is the OudraSperse WB 6001 of DOW Chemical.
Ludox employed in following example is the PA30 of Shandong Bai Te new material company limited.
Auxiliary agent employed in following example: wetting agent (FLASH-X 330, Halox company of the U.S.), dispersant
(Byk191, Germany Bi Ke), coalescents (Texanol, Eastman Chemical Company), pH adjusting agent (AMP-95, DOW Chemical),
Defoamer (river 8225, sea, Hai Chuan new material Science and Technology Ltd.), auxiliary rheological agents (attapulgite, Nanjing unity active hargil
Factory).
Beneficial effect
The water-borne acrylic coatings provided in the present invention has the advantage of storage time length, through the storages of more than 12 months still
Can have preferable film performance.
Detailed description of the invention
Embodiment 1
It is on the waiting list following raw material: 30 parts of modified acrylic emulsions, 16 parts of aqueous epoxy resins, the Ludox of 10 parts, 4 parts of trimerization phosphorus
Acid aluminum, the anti-corrosion paint zinc phosphate of 5 parts, the color stuffing iron oxide red of 20 parts, the auxiliary agent of 0.5 part and the water of 10 parts.Auxiliary agent is profit
Humectant, dispersant, coalescents, pH adjusting agent, defoamer, auxiliary rheological agents are by the mixing of equal proportion.
Wherein, the preparation method of modified acrylic emulsion is:
S1, by weight, by 50 parts of hydroxy silicon oils, 10 parts of Silane coupling reagent KH-570s, 3 parts of KOH, ethyl acetate 6 parts mixing
Uniformly, in a nitrogen atmosphere, keep reaction 3h after being warming up to 90 DEG C, obtain modified polyorganosiloxane performed polymer;In hydroxy silicon oil
Hydroxy radical content is 8wt%;
S2, by weight, takes butyl acrylate 12 parts, acrylic acid methyl ester. 5 parts, emulsifying agent 1 part and deionized water 60 parts,
2000rpm high-speed stirred 0.5h, adds initiator azo dicyclohexyl formonitrile HCN 2 parts, reacts 0.5h, then drip 6 at 70 DEG C
Part modified polyorganosiloxane performed polymer and initiator azo dicyclohexyl formonitrile HCN 1 part, react 2h at 70 DEG C, then regulate pH with ammonia
To 7, obtain the acrylic emulsion of modification.
Above-mentioned water-borne acrylic resin preparation method of anticorrosion paint is: by modified acrylic emulsion, water-base epoxy tree
Fat, Ludox, aluminium triphosphate, auxiliary agent and water mixing and stirring;Add anti-corrosion paint and color stuffing the most while stirring, stir
Mix uniformly, obtain water-based anticorrosive paint.
Embodiment 2
It is on the waiting list following raw material:
55 parts of modified acrylic emulsions, 25 parts of aqueous epoxy resins, the Ludox of 16 parts, 6 parts of aluminium triphosphates, 15 parts anti-
Rotten pigment zinc phosphate, the color stuffing iron oxide red of 40 parts, the auxiliary agent of 5 parts and the water of 15 parts.Auxiliary agent is wetting agent, dispersant, one-tenth
Film auxiliary agent, pH adjusting agent, defoamer, auxiliary rheological agents are by the mixing of equal proportion.
Wherein, the preparation method of modified acrylic emulsion is:
S1, by weight, by 60 parts of hydroxy silicon oils, 15 parts of Silane coupling reagent KH-570s, 5 parts of KOH, ethyl acetate 10 parts mixing
Uniformly, in a nitrogen atmosphere, keep reaction 3h after being warming up to 90 DEG C, obtain modified polyorganosiloxane performed polymer;In hydroxy silicon oil
Hydroxy radical content is 8wt%;
S2, by weight, takes butyl acrylate 15 parts, acrylic acid methyl ester. 10 parts, emulsifying agent 2 parts and deionized water 70 parts,
2000rpm high-speed stirred 1h, adds initiator azo dicyclohexyl formonitrile HCN 4 parts, reacts 2h, then drip 10 parts and change at 80 DEG C
Property polysiloxane pre polymers body and initiator azo dicyclohexyl formonitrile HCN 2 parts, at 80 DEG C, react 3h, then regulate pH to 7 with ammonia,
Obtain the acrylic emulsion of modification.
Above-mentioned water-borne acrylic resin preparation method of anticorrosion paint is: by modified acrylic emulsion, water-base epoxy tree
Fat, Ludox, aluminium triphosphate, auxiliary agent and water mixing and stirring;Add anti-corrosion paint and color stuffing the most while stirring, stir
Mix uniformly, obtain water-based anticorrosive paint.
Embodiment 3
It is on the waiting list following raw material:
40 parts of modified acrylic emulsions, 20 parts of aqueous epoxy resins, the Ludox of 12 parts, 5 parts of aluminium triphosphates, 12 parts anti-
Rotten pigment zinc phosphate, the color stuffing iron oxide red of 30 parts, the auxiliary agent of 3 parts and the water of 12 parts.Auxiliary agent is wetting agent, dispersant, one-tenth
Film auxiliary agent, pH adjusting agent, defoamer, auxiliary rheological agents are by the mixing of equal proportion.
Wherein, the preparation method of modified acrylic emulsion is:
S1, by weight, by 55 parts of hydroxy silicon oils, 12 parts of Silane coupling reagent KH-570s, 4 parts of KOH, ethyl acetate 8 parts mixing
Uniformly, in a nitrogen atmosphere, keep reaction 3h after being warming up to 90 DEG C, obtain modified polyorganosiloxane performed polymer;In hydroxy silicon oil
Hydroxy radical content is 8wt%;
S2, by weight, takes butyl acrylate 13 parts, acrylic acid methyl ester. 8 parts, emulsifying agent 2 parts and deionized water 5 parts,
2000rpm high-speed stirred 0.8h, adds initiator azo dicyclohexyl formonitrile HCN 3 parts, reacts 1h, then drip 7 parts at 75 DEG C
Modified polyorganosiloxane performed polymer and initiator azo dicyclohexyl formonitrile HCN 2 parts, react 3h at 75 DEG C, then regulate pH extremely with ammonia
7, obtain the acrylic emulsion of modification.
Above-mentioned water-borne acrylic resin preparation method of anticorrosion paint is: by modified acrylic emulsion, water-base epoxy tree
Fat, Ludox, aluminium triphosphate, auxiliary agent and water mixing and stirring;Add anti-corrosion paint and color stuffing the most while stirring, stir
Mix uniformly, obtain water-based anticorrosive paint.
Reference examples 1
Difference with embodiment 3 is: modified without poly-silica in acrylic emulsion.
It is on the waiting list following raw material:
40 parts of acrylic emulsions, 20 parts of aqueous epoxy resins, the Ludox of 12 parts, 5 parts of aluminium triphosphates, anti-corrosion paints of 12 parts
Zinc phosphate, the color stuffing iron oxide red of 30 parts, the auxiliary agent of 3 parts and the water of 12 parts.Auxiliary agent be wetting agent, dispersant, coalescents,
PH adjusting agent, defoamer, auxiliary rheological agents are by the mixing of equal proportion.
Wherein, the preparation method of acrylic emulsion is:
By weight, butyl acrylate 13 parts, acrylic acid methyl ester. 8 parts, emulsifying agent 2 parts and deionized water 5 parts, 2000rpm are taken
High-speed stirred 0.8h, adds initiator azo dicyclohexyl formonitrile HCN 3 parts, reacts 1h, then drip initiator azo at 75 DEG C
Dicyclohexyl formonitrile HCN 2 parts, reacts 3h at 75 DEG C, then regulates pH to 7, the acrylic emulsion obtained with ammonia.
Above-mentioned water-borne acrylic resin preparation method of anticorrosion paint is: by molten to acrylic emulsion, aqueous epoxy resins, silicon
Glue, aluminium triphosphate, auxiliary agent and water mixing and stirring;Add anti-corrosion paint and color stuffing the most while stirring, stir,
Obtain water-based anticorrosive paint.
Performance test
1,1000 mesh fine sandpapers are used to carry out grinding process sheet metal (50mm × 120mm × 0.5mm);
2, the water-based anticorrosive paint produced is sprayed on sheet metal respectively, place under 25 DEG C of constant temperatures from dry 24 hours;
Measure.
Project | Embodiment 1 | Embodiment 2 | Embodiment 3 | Reference examples 1 | Method of testing |
Hardness | 2H | 2H | 2H | H | GB/T 6739-2006 |
Pliability/mm | 1 | 1 | 1 | 2 | GB/T1731-1993 |
Impact resistance/Kg.m | 50 | 50 | 50 | 40 | GB/T1732-1993 |
Adhesive force (draws circle method) | 1 grade | 1 grade | 1 grade | 1 grade | GB/T1720-1979 |
Adhesive force (pulls open method) | 6.3MPa | 6.1MPa | 6.7MPa | 6.4MPa | GB/T 5210-2006 |
Resistance to water (23 DEG C) | 240 hours non-foaming, does not falls off non-corrosive | 240 hours non-foaming, does not falls off non-corrosive | 240 hours non-foaming, does not falls off non-corrosive | Within 180 hours, occur bubbling | GB/T1733-1993 |
Alkali resistance (25 DEG C, 0.1N NaOH) | 24 hours non-foaming, wrinkle resistant | 24 hours non-foaming, wrinkle resistant | 24 hours non-foaming, wrinkle resistant | Within 15 hours, occur bubbling and wrinkling | GB/T9274-1998 |
Acid resistance (25 DEG C, 0.1N H2SO4) | 24 hours non-foaming, wrinkle resistant | 24 hours non-foaming, wrinkle resistant | 24 hours non-foaming, wrinkle resistant | Within 15 hours, occur bubbling and wrinkling | GB/T9274-1998 |
Salt spray resistance/hour | 1000 hours | 1000 hours | 1050 hours | 850 hours | GB/T1771-2007 |
After above-mentioned coating being placed in 35 DEG C of lower seals placements 12 months, taking out and carry out above-mentioned test again, result is as follows:
Project | Embodiment 1 | Embodiment 2 | Embodiment 3 | Reference examples 1 | Method of testing |
Hardness | 2H | 2H | 2H | H | GB/T 6739-2006 |
Pliability/mm | 1 | 1 | 1 | 4 | GB/T1731-1993 |
Impact resistance/Kg.m | 50 | 50 | 50 | 35 | GB/T1732-1993 |
Adhesive force (draws circle method) | 1 grade | 1 grade | 1 grade | 2 grades | GB/T1720-1979 |
Adhesive force (pulls open method) | 6.1MPa | 6.0MPa | 6.5MPa | 5.8MPa | GB/T 5210-2006 |
Resistance to water (23 DEG C) | 240 hours non-foaming, does not falls off non-corrosive | 240 hours non-foaming, does not falls off non-corrosive | 240 hours non-foaming, does not falls off non-corrosive | Within 120 hours, occur bubbling | GB/T1733-1993 |
Alkali resistance (25 DEG C, 0.1N NaOH) | 24 hours non-foaming, wrinkle resistant | 24 hours non-foaming, wrinkle resistant | 24 hours non-foaming, wrinkle resistant | Within 12 hours, occur bubbling and wrinkling | GB/T9274-1998 |
Acid resistance (25 DEG C, 0.1N H2SO4) | 24 hours non-foaming, wrinkle resistant | 24 hours non-foaming, wrinkle resistant | 24 hours non-foaming, wrinkle resistant | Within 12 hours, occur bubbling and wrinkling | GB/T9274-1998 |
Salt spray resistance/hour | 970 hours | 980 hours | 1020 hours | 620 hours | GB/T1771-2007 |
As can be seen from the above table, after acrylic resin is modified, the storage time of coating can be extended, through 12
After the storage of individual month, adhesive force, weather resistance are all decreased obviously.
Claims (10)
1. a water-borne acrylic resin anticorrosive paint, it is characterised in that: include following component by weight: 30~
55 parts of modified acrylic emulsions, 16~25 parts of aqueous epoxy resins, the Ludox of 10~16 parts, 4~6 parts of aluminium triphosphates, 5
~the anti-corrosion paint of 15 parts, the color stuffing of 20~40 parts, the auxiliary agent of 0.5~5 part and the water of 10~15 parts.
Water-borne acrylic resin anticorrosive paint the most according to claim 1, it is characterised in that: described anti-corrosion paint is phosphorus
One or more arbitrary proportion mixture in acid zinc, modified zinc phosphate, zinc molybdate.
Water-borne acrylic resin anticorrosive paint the most according to claim 1, it is characterised in that: described auxiliary agent is moistening
Agent, dispersant, coalescents, pH adjusting agent, defoamer, auxiliary rheological agents mixture in any proportion.
Water-borne acrylic resin anticorrosive paint the most according to claim 1, it is characterised in that: described color stuffing can be
The mixture of one or more arbitrary proportions in iron oxide red, titanium dioxide, barium sulfate, Pulvis Talci, mica powder.
Water-borne acrylic resin anticorrosive paint the most according to claim 1, it is characterised in that: modified acrylic emulsion
Preparation method is: S1, by weight, by 50~60 parts of hydroxy silicon oils, 10~15 parts of Silane coupling reagent KH-570s, 3~5 parts
KOH, ethyl acetate 6~10 parts of mix homogeneously, in a nitrogen atmosphere, keep reaction 3h, obtain modified poly-silicon after being warming up to 90 DEG C
Oxygen alkane performed polymer;S2, by weight, takes butyl acrylate 12~15 parts, acrylic acid methyl ester. 5~10 parts, emulsifying agent 1~2 parts
With deionized water 60~70 parts, high-speed stirred 0.5~1h, add initiator 2~4 parts, react at 70~80 DEG C 0.5~
2h, then drip 6~10 parts of modified polyorganosiloxane performed polymers and initiator 1~2 parts, at 70~80 DEG C, react 2~3h, then use ammonia
Water regulation pH to 7, obtains the acrylic emulsion of modification.
Water-borne acrylic resin anticorrosive paint the most according to claim 5, it is characterised in that: described initiator is azo
Class initiator.
Water-borne acrylic resin anticorrosive paint the most according to claim 6, it is characterised in that: described azo-initiator selects
From azo-bis-iso-dimethyl, azo-bis-isobutyrate hydrochloride, azodicarbonamide, azo diisopropyl imidazoline hydrochloric acid
Salt, azo isobutyl cyano group Methanamide, azo dicyclohexyl formonitrile HCN, azo dicyano valeric acid, azo diisopropyl imidazoline, azo
One or more in bis-isobutyronitrile, AMBN and 2,2'-Azobis(2,4-dimethylvaleronitrile).
Water-borne acrylic resin anticorrosive paint the most according to claim 5, it is characterised in that: the hydroxyl in hydroxy silicon oil contains
Amount is 8wt%.
Water-borne acrylic resin anticorrosive paint the most according to claim 5, it is characterised in that: the high-speed stirred in step S2
Refer to rotating speed 2000rpm.
10. the preparation method of the water-borne acrylic resin anticorrosive paint described in any one of claim 1~9, comprises the steps:
By modified acrylic emulsion, aqueous epoxy resins, Ludox, aluminium triphosphate, auxiliary agent and water mixing and stirring;Then limit
Stirring limit adds anti-corrosion paint and color stuffing, stirs, obtains water-based anticorrosive paint.