CN104927631A - Efficient anticorrosion paint special for mechanical equipment - Google Patents
Efficient anticorrosion paint special for mechanical equipment Download PDFInfo
- Publication number
- CN104927631A CN104927631A CN201510361621.7A CN201510361621A CN104927631A CN 104927631 A CN104927631 A CN 104927631A CN 201510361621 A CN201510361621 A CN 201510361621A CN 104927631 A CN104927631 A CN 104927631A
- Authority
- CN
- China
- Prior art keywords
- parts
- epoxy resin
- anticorrosion paint
- good
- mechanical equipment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
An efficient anticorrosion paint special for mechanical equipment is made from, by weight, 8 to 12 parts of iron oxide, 2 to 4 parts of styrene butadiene rubber, 6 to 12 parts of silane coupling agent, 10 to 18 parts of aromatic polyurethane acrylate, 5 to 8 parts of silica sol, 1 to 4 parts of isopropanol, 12 o 24 parts of polyurethane acrylate, 10 to 15 parts of E-12 epoxy resin, 20 to 40 parts of methyl malonate, 12 to 18 parts of brominated epoxy resin, 10 to 17 parts of aliphatic polyurethane acrylic resin, 0.5 to 1.4 parts of nano ferroferric oxide, 4 to 6 parts of aluminum triphosphate, 3 to 5 parts of vinyl triamine, 4 to 6 parts of leveling agent, 4 to 7 parts of adhesion accelerant, 2 to 6 parts of initiator, and 5 to 8 parts of xylene. The efficient anticorrosion paint is high in corrosion resistance, good in mold tolerance, low in seepage rate, good in rot resistance, simple to construct, excellent in water tolerance and rust resistance, and pollution free.
Description
Technical field
The present invention relates to a kind of mechanical means specialized paint with high-efficiency anticorrosive effect.
Background technology
Paint is that one firmly can cover body surface, plays protection, decoration, mark and the chemical mixture coating of other special purposes.Under mechanical means is often exposed to physical environment, subject the erosion of wind, rain, salt fog and topsoil, therefore protection against corrosion is an important topic during machinery uses.Corrosion makes normal production to carry out, and the work-ing life of equipment is shortened greatly.Mechanical means is ubiquity phenomenon in the corrosion of life-time service kind, and after mechanical means is corroded, all will change in profile, color and luster and mechanical properties, cause equipment to be destroyed and the serious waste of resource and the energy, enterprise is subject to massive losses.So machinery outside varnishes with lacquer machinery played a very good protection, can slowing down corrosion, and avoid causing hidden danger and financial loss.But current paint on the market comes with some shortcomings, and performance is single, and water tolerance, rust-preventing characteristic and corrosion resistance are not good, can not meet current user demand, need to improve further meet the need of market.
Summary of the invention
For the deficiencies in the prior art, the problem to be solved in the present invention is, provide a kind of mechanical means specialized paint with high-efficiency anticorrosive effect, anti-corrosion capability is strong, resistance to fungi is good, and rate of permeation is low, and antiseptic property is good, construction technology is simple, water-fast splendid with rustless property, and pollution-free.
For solving prior art problem, technical scheme provided by the invention is, a kind of mechanical means specialized paint with high-efficiency anticorrosive effect, and it is made up of the raw material of following parts by weight:
Ferric oxide 8-12 part; styrene-butadiene rubber(SBR) 2-4 part; silane coupling agent 6-12 part; aromatic urethane acrylate 10-18 part, silicon sol 5-8 part, Virahol 1-4 part; urethane acrylate 12-24 part; E-12 epoxy resin 10-15 part, methylmalonate 20-40 part, brominated epoxy resin 12-18 part; aliphatic polyurethane acrylic resin 10-17 part; nano ferriferrous oxide 0.5-1.4 part, aluminium triphosphate 4-6 part, vinyl triamine 3-5 part; flow agent 4-6 part; adhesion promoter 4-7 part, initiator 2-6 part, dimethylbenzene 5-8 part.
The invention has the beneficial effects as follows: the mechanical means specialized paint with high-efficiency anticorrosive effect of the present invention, anti-corrosion capability is strong, and resistance to fungi is good, and rate of permeation is low, and antiseptic property is good, and construction technology is simple, water-fast splendid with rustless property, and pollution-free.
Embodiment
embodiment 1
Have a mechanical means specialized paint for high-efficiency anticorrosive effect, it is made up of the raw material of following parts by weight:
Ferric oxide 8 parts, 2 parts, styrene-butadiene rubber(SBR), silane coupling agent 6 parts, aromatic urethane acrylate 10 parts, silicon sol 5 parts, Virahol 1 part, urethane acrylate 12 parts, E-12 epoxy resin 10 parts, methylmalonate 20 parts, brominated epoxy resin 12 parts, aliphatic polyurethane acrylic resin 10 parts, nano ferriferrous oxide 0.5 part, aluminium triphosphate 4 parts, vinyl triamine 3 parts, flow agent 4 parts, adhesion promoter 4 parts, initiator 2 parts, dimethylbenzene 5 parts.
embodiment 2
Have a mechanical means specialized paint for high-efficiency anticorrosive effect, it is made up of the raw material of following parts by weight:
Ferric oxide 12 parts, 4 parts, styrene-butadiene rubber(SBR), silane coupling agent 12 parts, aromatic urethane acrylate 18 parts, silicon sol 8 parts, Virahol 4 parts, urethane acrylate 24 parts, E-12 epoxy resin 15 parts, methylmalonate 40 parts, brominated epoxy resin 18 parts, aliphatic polyurethane acrylic resin 17 parts, nano ferriferrous oxide 1.4 parts, aluminium triphosphate 6 parts, vinyl triamine 5 parts, flow agent 6 parts, adhesion promoter 7 parts, initiator 6 parts, dimethylbenzene 8 parts.
Claims (1)
1. there is a mechanical means specialized paint for high-efficiency anticorrosive effect, it is characterized in that: it is made up of the raw material of following parts by weight:
Ferric oxide 8-12 part; styrene-butadiene rubber(SBR) 2-4 part; silane coupling agent 6-12 part; aromatic urethane acrylate 10-18 part, silicon sol 5-8 part, Virahol 1-4 part; urethane acrylate 12-24 part; E-12 epoxy resin 10-15 part, methylmalonate 20-40 part, brominated epoxy resin 12-18 part; aliphatic polyurethane acrylic resin 10-17 part; nano ferriferrous oxide 0.5-1.4 part, aluminium triphosphate 4-6 part, vinyl triamine 3-5 part; flow agent 4-6 part; adhesion promoter 4-7 part, initiator 2-6 part, dimethylbenzene 5-8 part.