CN104559514A - Efficient anticorrosive coating - Google Patents
Efficient anticorrosive coating Download PDFInfo
- Publication number
- CN104559514A CN104559514A CN201310497895.XA CN201310497895A CN104559514A CN 104559514 A CN104559514 A CN 104559514A CN 201310497895 A CN201310497895 A CN 201310497895A CN 104559514 A CN104559514 A CN 104559514A
- Authority
- CN
- China
- Prior art keywords
- parts
- anticorrosive coating
- good
- efficient anticorrosive
- amino resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an efficient anticorrosive coating. The efficient anticorrosive coating is prepared from the following raw materials in parts by weight: 25-35 parts of vinyl chloride-vinyl acetate resin, 10-15 parts of flaky graphite, 5-10 parts of chlorinated paraffin, 10-15 parts of amino resin, 12-20 parts of butylated amino resin, 5-8 parts of a silane coupling agent, 7-11 parts of cellulose acetate, and 3-8 parts of a diluent. The efficient anticorrosive coating provided by the invention is high in salt water resistance, good in weather resistance, good in corrosion resistance, high in adhesive force, and good in wear-resisting property and the like.
Description
Technical field
The present invention relates to paint field, specifically relate to a kind of high-efficency anticorrosive paint.
Background technology
Protective system has become the important fresh combatants of paint field, and protective system plays increasing effect, and development prospect is considerable.Protective system, is generally divided into conventional protective system and heavy-duty coating, is requisite a kind of coating in paint.Conventional protective system is under general condition, plays etch-proof effect to metal etc., the life-span that protection non-ferrous metal uses.But traditional product is improved perfect gradually, new product constantly researches and develops appearance, adapt to new standard and requirement in anticorrosion market and environmental regulation development, still need proactive, Continuous Innovation.
Summary of the invention
The object of the invention is to provide a kind of high-efficency anticorrosive paint with resistance to salt water is strong, good weatherability, antiseptic property are good, stronger sticking power and wear resisting property.
For achieving the above object, the technical solution used in the present invention is: a kind of high-efficency anticorrosive paint, is made up of the raw material of following parts by weight: vinyl chloride-vinyl acetate resin 25-35 part; Flaky graphite 10-15 part; Clorafin 5-10 part; Aminoresin 10-15 part; Butylated amino resin 12-20 part; Silane coupling agent 5-8 part; Cellulose acetate 7-11 part; Thinner 3-8 part.
The thinner of described protective system be diacetone alcohol, pimelinketone, ethanol, methyl alcohol, ethylene glycol or ether one or more.
The invention has the beneficial effects as follows: high-efficency anticorrosive paint provided by the invention that there is the advantages such as resistance to salt water is strong, good weatherability, antiseptic property are good, stronger sticking power and wear resisting property.
Embodiment
Below in conjunction with specific embodiment, the invention will be further described:
Embodiment 1, a kind of high-efficency anticorrosive paint, is made up of the raw material of following parts by weight: vinyl chloride-vinyl acetate resin 25 parts; Flaky graphite 10 parts; Clorafin 5 parts; 10 parts, aminoresin; Butylated amino resin 12 parts; Silane coupling agent 5 parts; Cellulose acetate 7 parts; Thinner 3 parts.
Embodiment 2, a kind of high-efficency anticorrosive paint, is made up of the raw material of following parts by weight: vinyl chloride-vinyl acetate resin 30 parts; Flaky graphite 12 parts; Clorafin 8 parts; 12 parts, aminoresin; Butylated amino resin 16 parts; Silane coupling agent 6 parts; Cellulose acetate 10 parts; Thinner 6 parts.
Embodiment 3, a kind of high-efficency anticorrosive paint, is made up of the raw material of following parts by weight: vinyl chloride-vinyl acetate resin 35 parts; Flaky graphite 15 parts; Clorafin 10 parts; 15 parts, aminoresin; Butylated amino resin 20 parts; Silane coupling agent 8 parts; Cellulose acetate 11 parts; Thinner 8 parts.
Claims (2)
1. a high-efficency anticorrosive paint, is characterized in that: be made up of the raw material of following parts by weight: vinyl chloride-vinyl acetate resin 25-35 part; Flaky graphite 10-15 part; Clorafin 5-10 part; Aminoresin 10-15 part; Butylated amino resin 12-20 part; Silane coupling agent 5-8 part; Cellulose acetate 7-11 part; Thinner 3-8 part.
2. high-efficency anticorrosive paint as claimed in claim 1, is characterized in that: thinner be diacetone alcohol, pimelinketone, ethanol, methyl alcohol, ethylene glycol or ether one or more.