CN101838489B - Undersurface syncretic anti-corrosion paint - Google Patents
Undersurface syncretic anti-corrosion paint Download PDFInfo
- Publication number
- CN101838489B CN101838489B CN2010101873026A CN201010187302A CN101838489B CN 101838489 B CN101838489 B CN 101838489B CN 2010101873026 A CN2010101873026 A CN 2010101873026A CN 201010187302 A CN201010187302 A CN 201010187302A CN 101838489 B CN101838489 B CN 101838489B
- Authority
- CN
- China
- Prior art keywords
- parts
- weight parts
- paint
- corrosion
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses an undersurface syncretic anti-corrosion paint, comprising 20-30 parts of high chlorinated polyethylene resin, 10-20 parts of chlorinated rubber resin, 10-20 parts of water loss malic acid resin, 6-10 parts of epoxy resin, 20-40 parts of xylene, 10-15 parts of butyl acetate, 8-15 parts of titanium white, 8-15 parts of aluminium trippolyhosphate, 3-10 parts of plasticizer and 2-7 parts of ultraviolet absorber. The anti-corrosion paint of the invention has excellent weathering aging property, corrosion resistance of salt mist, acid, alkali and salt, chemical atmosphere resistance, water proofness, oil resistance, tough and wear-resistant paint film, strong adhesion and rapid drying, can carry out construction under low temperature, does not need to paint a base paint, can meet the anti-corrosion and antirust requirements by only painting two layers of coating, has convenient construction, and is widely applied.
Description
Technical field
The present invention relates to a kind of protective system, particularly a kind of primer-topcoat integrated anticorrosive lacquer.
Background technology
Existing protective system generally is made up of priming paint and finish paint.Such protective system need be coated with priming earlier, treat the priming paint drying after, brushing finish paint again.This form of construction work is complicated, takes time and effort, and efficient is comparatively low.
In addition, for reaching good preservative effect, require protective system to have excellent hardness, sticking power, anti-various corrosion, and general protective system all can not satisfy these requirements, effective anticorrosion time limit also only has 5～8 years.
Summary of the invention
The objective of the invention is to be to provide a kind of novel protective system.
The technical scheme that the present invention taked is:
A kind of primer-topcoat integrated anticorrosive lacquer comprises HCPE 20～30 weight parts, chlorinated rubber resin 10～20 weight parts, maleficent acid resin 10～20 weight parts, epoxy resin 6～10 weight parts, YLENE 20～40 weight parts, N-BUTYL ACETATE 10～15 weight parts, white titanium pigment 8～15 weight parts, aluminium triphosphate 8～15 weight parts, softening agent 3～10 weight parts, UV light absorber 2～7 weight parts.
Softening agent is preferably Witcizer 300, clorafin.
UV light absorber is preferably UV-9, UV-P.
Protective system of the present invention has the corrodibility of good weatherability, salt spray resistance, acid-and base-resisting, salt; Anti-chemical atmosphere, water-fast, oil resistant, paint film tough and hard wear resistant, strong adhesion; Fast drying, but low-temperature construction need not be coated with priming; Brushing twice coating just can reach antiseptic and rustproof requirement, easy construction.Can be widely used as steelwork equipment such as chemical pipeline, pipeline, support, factory building and facility and acid, alkali, salt basin outer wall anticorrosion of industries such as metallurgy, oil, chemical industry, building, harbour, harbour, the energy, also can be used for concrete facility external coatings such as concrete structure tower body, cement wall surface, sewage lagoon.
Embodiment
A kind of primer-topcoat integrated anticorrosive lacquer comprises HCPE 20～30 weight parts, chlorinated rubber resin 10～20 weight parts, maleficent acid resin 10～20 weight parts, epoxy resin 6～10 weight parts, YLENE 20～40 weight parts, N-BUTYL ACETATE 10～15 weight parts, white titanium pigment 8～15 weight parts, aluminium triphosphate 8～15 weight parts, softening agent 3～10 weight parts, UV light absorber 2～7 weight parts.
Softening agent is preferably Witcizer 300, clorafin.
UV light absorber is preferably UV-9, UV-P.
Below in conjunction with embodiment, further specify the present invention.
Embodiment 1
Protective system of the present invention comprises following weight part:
23 parts of HCPEs, chlorinated rubber are set 17 fat parts, 13 parts of maleficent acid resins, 6 parts of epoxy resin, 27 parts of YLENE, 12 parts of N-BUTYL ACETATEs, 15 parts of white titanium pigments, 13 parts of aluminium triphosphates, 3 parts of Witcizer 300s, 4 parts of clorafins, 5 parts of UV light absorber UV-9.
Embodiment 2
Protective system of the present invention comprises following weight part:
20 parts of HCPEs, 20 parts of chlorinated rubber resins, 17 parts of maleficent acid resins, 8 parts of epoxy resin, 20 parts of YLENE, 14 parts of N-BUTYL ACETATEs, 12 parts of white titanium pigments, 11 parts of aluminium triphosphates, 3 parts of Witcizer 300s, 4 parts of Ultraviolet Absorber UV-P.
Embodiment 3
Protective system of the present invention comprises following weight part:
30 parts of HCPEs, 13 parts of chlorinated rubber resins, 10 parts of maleficent acid resins, 7 parts of epoxy resin, 34 parts of YLENE, 15 parts of N-BUTYL ACETATEs, 13 parts of white titanium pigments, 15 parts of aluminium triphosphates, 6 parts of clorafins, 2 parts of Ultraviolet Absorber UV-P.
Embodiment 4
Protective system of the present invention comprises following weight part:
27 parts of HCPEs, 10 parts of chlorinated rubber resins, 20 parts of maleficent acid resins, 10 parts of epoxy resin, 40 parts of YLENE, 10 parts of N-BUTYL ACETATEs, 10 parts of white titanium pigments, 8 parts of aluminium triphosphates, 4 parts of Witcizer 300s, 6 parts of clorafins, 3 parts of UV light absorber UV-9,4 parts of UV-P.
Adopt ordinary method to detect the performance perameter of above each embodiment, the result is following.
Protective system of the present invention has the corrodibility of good weatherability, salt spray resistance, acid-and base-resisting, salt; Anti-chemical atmosphere, water-fast, oil resistant, paint film tough and hard wear resistant, strong adhesion; Fast drying, but low-temperature construction need not be coated with priming; Brushing twice coating just can reach antiseptic and rustproof requirement, easy construction.Can be widely used as steelwork equipment such as chemical pipeline, pipeline, support, factory building and facility and acid, alkali, salt basin outer wall anticorrosion of industries such as metallurgy, oil, chemical industry, building, harbour, harbour, the energy, also can be used for concrete facility external coatings such as concrete structure tower body, cement wall surface, sewage lagoon.
Claims (3)
1. a primer-topcoat integrated anticorrosive lacquer comprises HCPE 20～30 weight parts, chlorinated rubber resin 10～20 weight parts, maleficent acid resin 10～20 weight parts, epoxy resin 6～10 weight parts, YLENE 20～40 weight parts, N-BUTYL ACETATE 10～15 weight parts, white titanium pigment 8～15 weight parts, aluminium triphosphate 8～15 weight parts, softening agent 3～10 weight parts, UV light absorber 2～7 weight parts.
2. a kind of primer-topcoat integrated anticorrosive lacquer according to claim 1 is characterized in that: softening agent is at least a in Witcizer 300, the clorafin.
3. a kind of primer-topcoat integrated anticorrosive lacquer according to claim 1 is characterized in that: UV light absorber is at least a among UV-9, the UV-P.