CN106830749B - A kind of color liquid sliver and its application - Google Patents
A kind of color liquid sliver and its application Download PDFInfo
- Publication number
- CN106830749B CN106830749B CN201611247670.9A CN201611247670A CN106830749B CN 106830749 B CN106830749 B CN 106830749B CN 201611247670 A CN201611247670 A CN 201611247670A CN 106830749 B CN106830749 B CN 106830749B
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- color liquid
- lotion
- sliver
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of color liquid slivers; the color liquid sliver includes 15~70 parts of rubber powder, 3~15 parts of hydroxyethyl cellulose, 40~80 parts of kaolin of protection; 200~420 parts of lotion, sand or 270~600 parts of coarse whiting, 10~35 parts of auxiliary agent and 400~1000 parts of deionized water.The liquid sliver is to be made by the steps: (1) the aqueous solution preparation of protective glue；(2) prepared by base paint；(3) preparation of color liquid sliver.Prepared color liquid sliver has high rigidity, and excellent weatherability and resistance to ag(e)ing, sliver color stable is uniform, and storage stability is good；Sliver size in lacquer coating is added to stablize, liquid sliver not drop, not bleeding, while coating can obtain the marmorean texture effect of hair side, more close to true marble, preferably provides the dicoration of sand textured coating.
Description
Technical field
The invention belongs to the field of building materials, and in particular to a kind of color liquid sliver and its application.
Background technique
With the continuous development of decoration industry, the continuous renewal of ornament materials, water burnt-in sand of new generation and the colorful painting of water-water
Expect the favor by customers.But there are complex manufacturing technologies for water burnt-in sand and water-in-water multicolor coating, and in operating process
It is easy to appear colour mixture, drop, particle size is difficult to control, while coating color is also difficult to control, while the water resistance of coating, resistance to
Time property is bad.In addition, water burnt-in sand and water-in-water multicolor coating transportation stability are poor, it is easy to appear coating finished product during transportation
Viscosity constantly increases, and finally brings difficulty to construction.
Summary of the invention
The object of the invention is that the shortcomings that overcoming the prior art and deficiency, provide a kind of color liquid sliver, by liquid
Sliver is added in lacquer, by adjusting the ratio of lacquer and can get marmorean effect, and completely instead of water packet
The continuous phase of sand and water-in-water multicolor coating keeps production technology simpler, and coating finished product is not in thick thickening, significantly improves
The water resistance and weatherability of coating.
Another object of the present invention is to provide the preparation methods of above-mentioned color liquid sliver.
Above-mentioned purpose of the present invention is achieved by the following technical programs:
A kind of color liquid sliver includes 15~70 parts of rubber powder of protection, hydroxyethyl cellulose 3~15 by weight calculating
Part, 40~80 parts of kaolin, 220~420 parts of lotion, sand or 270~600 parts of coarse whiting, 10~35 parts of auxiliary agent and deionized water 400
~1000 parts.
Preferably, by weight calculate, comprising protection rubber powder 20-60 parts, 5-11 parts of hydroxyethyl cellulose, kaolin 50~
70 parts, 200~400 parts of lotion, sand or 300~580 parts of coarse whiting, 15~29 parts of auxiliary agent and 480~930 parts of deionized water.
Preferably, the protection rubber powder is HG-1 powder, GTS powder or RDS powder；The sand is natural colour sand, dyeing coloured silk
Sand or artificial burning colorful sand.
Preferably, the auxiliary agent is wetting agent, dispersing agent, defoaming agent, fungicide, coalescing agent, antifreezing agent and pH tune
Save agent.
It is further preferable that the wetting agent is that alkyl phenol polyoxyethylene ether, polyether silicones or non-ionic fluorine carbon poly are closed
Object, the dispersing agent are polycarboxylate sodium, ammonium polyacrylate salt or ammonium polyacrylate salt, and the defoaming agent is mineral oil or poly- has
Organic siloxane, the fungicide are isothiazolinone derivatives or benzimidazole compound, and the coalescing agent is 2,2,4- tri-
Methyl-1,3- pentanediol mono isobutyrate, propandiol butyl ether or butyl glycol ether, the antifreezing agent are ethylene glycol or propylene glycol；
The pH adjusting agent is 2-amino-2-methyl-1-propanol or dimethylethanolamine.
Preferably, the lotion is elastic acrylate lotion or organosilicon-modified acrylate emulsion.
It is further preferable that the elastic acrylate lotion is in the acrylic acid containing emulsifier alkylbenzene polyethers sodium sulfonate
In ester monomer aqueous solution, under the conditions of existing for the initiator ammonium persulfate, reaction temperature is 80~90 DEG C, the elastomeric propylene of formation
Acid esters lotion；The organosilicon-modified acrylate emulsion is in the acrylic monomers containing emulsifier neopelex
Under the conditions of vinyltriethoxysilane is added in aqueous solution existing for the initiator ammonium persulfate, reaction temperature is 60~70
DEG C, react the organosilicon-modified acrylate emulsion of formation.
The solid content of the elastic acrylate lotion is 47~50%, and the partial size of elastic acrylate lotion is 0.1
~0.2 μm, the pH value of elastic acrylate lotion is 7~9；The solid content of the organosilicon-modified acrylate emulsion is 47
~50%, the partial size of organosilicon-modified acrylate emulsion is 0.1~0.2 μm, the pH value of organosilicon-modified acrylate emulsion
It is 7~9.
A kind of preparation method of above-mentioned color liquid sliver, comprises the following specific steps that:
S1. protection rubber powder is added in deionized water, makes that rubber powder is protected to be completely dissolved, obtains the aqueous solution of protective glue；
S2. by hydroxyethyl cellulose, auxiliary agent, kaolin is add to deionized water, is stirred with 1500~2500r/min speed
30~45min is mixed, lotion is added and the aqueous solution of protective glue that part steps S1 is obtained is uniformly mixed, obtain base paint；
S3. sand or coarse whiting are added in the base paint of step S2 preparation and are uniformly mixed, is then added remaining in step S1
It protects in glue solution, is granulated to get color liquid sliver is arrived.
Preferably, the matter of the aqueous solution of protective glue described in the aqueous solution of protective glue described in step S2 and step S3
Amount is than being 1:(4.5~7.5), the mode of the granulation is shearing disk, sieve or negative pressure of vacuum.
Application of the above-mentioned color liquid sliver in building coating field.
Compared with prior art, the invention has the following advantages:
1. color liquid sliver prepared by the present invention has high rigidity, excellent weatherability and resistance to ag(e)ing, sliver color
Stable homogeneous, storage stability are good；Sliver size in lacquer coating is added to stablize, liquid sliver not drop, not bleeding, simultaneously
Coating can obtain the marmorean texture effect of hair side, more close to true marble.
2. partial size can be made more compared with the prior art in the simple production process of color liquid sliver prepared by the present invention
Add homogeneous liquid sliver color liquid sliver, particle size uniform, controllable, partial size is respectively in 1~3mm and 3~5mm, with market
On the compound sliver that uses be entirely different two kinds of product, can alternative composite sliver completely, make water packet obtained
The color of sand and lacquer coating is uniform, obtains better marbling effect.
Specific embodiment
The contents of the present invention are further illustrated combined with specific embodiments below, but should not be construed as limiting the invention.
Unless otherwise specified, the conventional means that technological means used in embodiment is well known to those skilled in the art.Except non-specifically
Illustrate, reagent that the present invention uses, method and apparatus is the art conventional reagents, method and apparatus.
In embodiment in 1-5:
The wetting agent alkyl phenol polyoxyethylene ether is the NP-100 of Akzo Nobel N.V., NP-400, Kening Co., Ltd
PE-100；
The dispersing agent polycarboxylate sodium is the SN-5040 or SN-5027 of Nuo Puke company；Kening Co., Ltd
Hydropalat-5040 or Hydropalat-5041；
The defoaming agent polysiloxane is the Foamaster-111, the AM-1512 of Ya Shilan company of Kening Co., Ltd；
The bactericide of iso-thiazolinone class is the Kathon LXE of DOW Chemical；
The coalescing agent 2,2,4- trimethyl -1,3- pentanediol mono isobutyrate is the TexanolOE- of Eastman company
300, the UCAR Filmer IBT of DOW Chemical；
The antifreezing agent is commercially available ethylene glycol or propylene glycol；
The pH adjusting agent 2-amino-2-methyl-1-propanol is the AMP-95 and AMP-90 of DOW Chemical.
The protection rubber powder is HG-1 powder, GTS powder or RDS powder；
The lotion is RS-2788, RS-6733, RS-996AD or the RS-3788 of Ahmedabad richness company.
Embodiment 1
1. fetching protection 20 parts of rubber powder HG-1 powder by mass fraction, 380 parts of deionized water, protection rubber powder HG-1 powder addition is gone
In ionized water, make that rubber powder is protected to be completely dissolved.
2. 100 parts of ionized water are removed by mass fraction, 5 parts of hydroxyethyl cellulose, auxiliary agent (wetting agent is NP-400:1 parts,
SN-5040:1 parts of dispersing agent, AM-1512:1 parts of defoaming agent, LXE:1 parts of fungicide Kathon, coalescing agent Texanol OE-
300:8 parts, 1 part of ethylene glycol, AMP-95:2 parts of pH adjusting agent), 50 parts of kaolin, by hydroxyethyl cellulose, auxiliary agent, kaolin adds
Enter into deionized water 1500r/min to stir 45 minutes, then be added made from 200 parts of Ahmedabad richness RS-2788 lotion and step 1
50 parts of glue solution of protection stirs evenly to get base paint.
3. taking 420 parts of the base paint in step 2 by mass fraction, 300 parts of natural colour sand, the protective glue in step 1 is water-soluble
350 parts of liquid.Natural colour sand is added in base paint first and is uniformly mixed, is then added in protection glue solution, using shearing disk
It is granulated to get color liquid sliver is arrived.
Color liquid sliver 5 parts of hydroxyethyl cellulose, is soaked by weight calculating, including 20 parts of rubber powder HG-1 powder of protection
NP-400:1 parts of agent, SN-5040:1 parts of dispersing agent, AM-1512:1 parts of defoaming agent, LXE:1 parts of fungicide Kathon, film forming helps
OE-300:8 parts of agent Texanol, 1 part of ethylene glycol, pH adjusting agent AMP-95,50 parts of kaolin, Ahmedabad richness RS-2788 lotion 200
Part, 300 parts and 480 parts of deionized water of natural colour sand.
Embodiment 2
1. fetch protection 60 parts of rubber powder GTS powder by mass fraction, 690 parts of deionized water, will protection rubber powder GTS powder addition go from
In sub- water, make that rubber powder is protected to be completely dissolved.
2. removing 240 parts of ionized water by mass fraction, 11 parts of hydroxyethyl cellulose, (NP-100:2 parts of wetting agent, divide auxiliary agent
SN-5027:2 parts of powder, Foamaster-111:2.5 parts of defoaming agent, LXE:2.5 parts of fungicide Kathon, coalescing agent
OE-300:25 parts of Texanol, 2.5 parts of ethylene glycol, AMP-90:2.5 parts of pH adjusting agent), 70 parts of kaolin, by hydroxy ethyl fiber
Element, auxiliary agent, kaolin are add to deionized water with 2500r/min stirring 30 minutes, and Ahmedabad richness RS-6733 lotion is then added
400 parts, step 1 90 parts of glue solution of protection obtained stirs evenly to get base paint.
3. 840 parts of the base paint in step 2 are taken by mass fraction, 580 parts of artificial burning colorful sand, the protective glue in step 1
660 parts of aqueous solution.Artificial burning colorful sand is added in base paint first and is uniformly mixed, is then added in protection glue solution, adopts
It is granulated with shearing disk to get color liquid sliver is arrived.
Color liquid sliver by weight calculating, including protects 60 parts of rubber powder GTS, and 11 parts of hydroxyethyl cellulose, auxiliary agent
(NP-100:2 parts of wetting agent, SN-5027:2 parts of dispersing agent, Foamaster-111:2.5 parts of defoaming agent, fungicide Kathon
LXE:2.5 parts, OE-300:25 parts of coalescing agent Texanol, 2.5 parts of ethylene glycol, AMP-90:2.5 parts of pH adjusting agent), kaolinite
70 parts of soil, 400 parts of lotion of Ahmedabad richness RS-6733,580 parts and 930 parts of deionized water of artificial burning colorful sand.
Embodiment 3
1. taking RDS to protect 36.4 parts of rubber powder by mass fraction, 523.6 parts of deionized water, deionization is added in protection rubber powder
In water, make that rubber powder is protected to be completely dissolved.
2. removing 150 parts of ionized water by mass fraction, 6 parts of hydroxyethyl cellulose, (PE-100:1 parts of wetting agent, divide auxiliary agent
Hydropalat-5040:1 parts of powder, Foamaster-111:1 parts of defoaming agent, KathonLXE:1 parts of fungicide, coalescing agent
IBT:12 parts of UCAR Filmer, 1.5 parts of propylene glycol, AMP-95:1.5 parts of pH adjusting agent), 55 parts of kaolin.By ethoxy fibre
Dimension element, auxiliary agent, kaolin are add to deionized water with 2500r/min stirring 30 minutes, and Ahmedabad richness RS-3788 cream is then added
60 parts of protection glue solution in liquid 280 and step 1 stir evenly to get base paint.
3. taking 600 parts of the base paint in step 2 by mass fraction, 450 parts of color sand are dyed, the protective glue in step 1 is water-soluble
500 parts of liquid.First will dyeing color sand be added base paint in be uniformly mixed, then be added protection glue solution in, using sieve into
Row is granulated to arrive color liquid sliver.
Color liquid sliver 6 parts of hydroxyethyl cellulose, is soaked by weight calculating, including 36.4 parts of rubber powder GTS of protection
PE-100:1 parts of agent, Hydropalat-5040:1 parts of dispersing agent, Foamaster-111:1 parts of defoaming agent, fungicide Kathon
LXE:1 parts, IBT:12 parts of coalescing agent UCAR Filmer, 1.5 parts of propylene glycol, AMP-95:1.5 parts of pH adjusting agent, kaolin
55 parts, 280 parts of lotion of Ahmedabad richness RS-3788,450 parts and 703.6 parts of deionized water of dyeing color sand.
Embodiment 4
1. taking RDS to protect 46.2 parts of rubber powder by mass fraction, 613.8 parts of deionized water, deionization is added in protection rubber powder
In water, make that rubber powder is protected to be completely dissolved.
2. removing 200 parts of ionized water by mass fraction, 8 parts of hydroxyethyl cellulose, (PE-100:1 parts of wetting agent, divide auxiliary agent
Hydropalat-5041:1 parts of powder, AM-1512:1.5 parts of defoaming agent, LXE:1.5 parts of fungicide Kathon, coalescing agent
IBT:13 parts of UCARFilmer, 1.5 parts of propylene glycol, AMP-90:2.5 parts of pH adjusting agent), 65 parts of kaolin.By hydroxy ethyl fiber
Element, auxiliary agent, kaolin are add to deionized water with 1500r/min stirring 45 minutes, and Ahmedabad richness RS-996AD cream is then added
80 parts of glue solution of protection stirs evenly to get base paint in 350 parts of liquid and step 1.
3. 725 parts of the base paint in step 2 are taken using mass fraction, 500 parts of natural colour sand, the protection glue in step 1
580 parts of solution.Natural colour sand is added in base paint first and is uniformly mixed, is then added in protection glue solution, using negative pressure
Vacuum equipment is granulated to arrive color liquid sliver.
Color liquid sliver by weight calculating, including protects 46.3 parts of rubber powder RDS, and 8 parts of hydroxyethyl cellulose, auxiliary agent
(PE-100:1 parts of wetting agent, Hydropalat-5041:1 parts of dispersing agent, AM-1512:1.5 parts of defoaming agent, fungicide Kathon
LXE:1.5 parts, IBT:13 parts of coalescing agent UCAR Filmer, 1.5 parts of propylene glycol, AMP-90:2.5 parts of pH adjusting agent), kaolinite
65 parts of soil, 350 parts of lotion of Ahmedabad richness RS-996AD, 500 parts and 813.8 parts of deionized water of natural colour sand.
Embodiment 5
1. taking RDS to protect 60 parts of rubber powder by mass fraction, 690 parts of deionized water, protection rubber powder is added in deionized water,
Make that rubber powder is protected to be completely dissolved.
2. removing 240 parts of ionized water by mass fraction, 11 parts of hydroxyethyl cellulose, (NP-400:2 parts of wetting agent, divide auxiliary agent
Hydropalat-5040:2 parts of powder, Foamaster-111:2.5 parts of defoaming agent, LXE:2.5 parts of fungicide Kathon, film forming
IBT:15 parts of auxiliary agent UCAR Filmer), 2.5 parts of propylene glycol, AMP-95:2.5 parts of pH adjusting agent), 70 parts of kaolin.By hydroxyl second
Base cellulose, auxiliary agent, kaolin are add to deionized water with 2500r/min stirring 30 minutes, and then Jia Badefu 996AD is newborn
90 parts of protection glue solution in 400 parts of liquid and step 1 stir evenly to get base paint is arrived.
3. 840 parts of the base paint in step 2 are taken by mass fraction, 580 parts of coarse whiting, the protection glue solution 660 in step 1
Part.Coarse whiting is added in base paint first and is uniformly mixed, is then added in protection glue solution, is granulated using shearing disk,
Obtain color liquid sliver.
Color liquid sliver by weight calculating, including protects rubber powder RDS:60 parts, and 11 parts of hydroxyethyl cellulose, auxiliary agent
(NP-400:2 parts of wetting agent, Hydropalat-5040:2 parts of dispersing agent, Foamaster-111:2.5 parts of defoaming agent, fungicide
LXE:2.5 parts of Kathon, IBT:15 parts of coalescing agent UCAR Filmer, 2.5 parts of propylene glycol, pH adjusting agent AMP-95:2.5
Part), 70 parts of kaolin, 400 parts of lotion of Ahmedabad richness RS-996AD, 580 parts and 930 parts of deionized water of coarse whiting.
Embodiment 6
1. fetching protection 15 parts of rubber powder HG-1 powder by mass fraction, 300 parts of deionized water, protection rubber powder HG-1 powder addition is gone
In ionized water, make that rubber powder is protected to be completely dissolved.
2. 100 parts of ionized water are removed by mass fraction, 3 parts of hydroxyethyl cellulose, auxiliary agent (wetting agent is NP-400:1 parts,
SN-5040:0.5 parts of dispersing agent, AM-1512:0.5 parts of defoaming agent, LXE:0.5 parts of fungicide Kathon, coalescing agent
OE-300:6.5 parts of Texanol, 0.5 part of ethylene glycol, AMP-95:0.5 parts of pH adjusting agent), 40 parts of kaolin, by ethoxy fibre
Dimension element, auxiliary agent, kaolin are add to deionized water 1500r/min and stir 45 minutes, and Ahmedabad richness RS-2788 lotion is then added
220 parts stir evenly with step 1 50 parts of glue solution of protection obtained to get base paint.
3. taking 323 parts of the base paint in step 2 by mass fraction, 270 parts of natural colour sand, the protective glue in step 1 is water-soluble
265 parts of liquid.Natural colour sand is added in base paint first and is uniformly mixed, is then added in protection glue solution, using shearing disk
It is granulated to get color liquid sliver is arrived.
Color liquid sliver 3 parts of hydroxyethyl cellulose, is soaked by weight calculating, including 15 parts of rubber powder HG-1 powder of protection
Agent is NP-400:1 parts, and dispersing agent is SN-5040:0.5 parts, and defoaming agent is AM-1512:0.5 parts, fungicide Kathon
LXE:0.5 parts, coalescing agent is Texanol OE-300:6.5 parts, ethylene glycol: 0.5 part, pH adjusting agent is AMP-95:0.5 parts,
40 parts of kaolin, 220 parts of lotion of Ahmedabad richness RS-2788,270 parts and 400 parts of deionized water of natural colour sand.
Embodiment 7
1. taking RDS to protect 70 parts of rubber powder by mass fraction, 760 parts of deionized water, protection rubber powder is added in deionized water,
Make that rubber powder is protected to be completely dissolved.
2. removing 240 parts of ionized water by mass fraction, 15 parts of hydroxyethyl cellulose, (NP-400:3 parts of wetting agent, divide auxiliary agent
Hydropalat-5040:3 parts of powder, Foamaster-111:3 parts of defoaming agent, LXE:3 parts of fungicide Kathon, coalescing agent
IBT:17 parts of UCAR Filmer), 3 parts of propylene glycol, AMP-95:3 parts of pH adjusting agent), 80 parts of kaolin.By hydroxy ethyl fiber
Element, auxiliary agent, kaolin are add to deionized water with 2500r/min stirring 30 minutes, then Jia Badefu RS-3788 lotion
420 parts stir evenly with 150 parts of protection glue solution in step 1 to get base paint is arrived.
3. 840 parts of the base paint in step 2 are taken by mass fraction, 600 parts of coarse whiting, the protection glue solution 680 in step
Part.Coarse whiting is added in base paint first and is uniformly mixed, is then added in protection glue solution, is granulated using sieve, i.e.,
Obtain color liquid sliver.
Color liquid sliver by weight calculating, including protects rubber powder RDS:70 parts, and 15 parts of hydroxyethyl cellulose, auxiliary agent
(NP-400:3 parts of wetting agent, Hydropalat-5040:3 parts of dispersing agent, Foamaster-111:3 parts of defoaming agent, fungicide
LXE:3 parts of Kathon, IBT:17 parts of coalescing agent UCAR Filmer), 3 parts of propylene glycol, AMP-95:3 parts of pH adjusting agent) and, high
80 parts of ridge soil, 420 parts of lotion of Ahmedabad richness RS-3788,600 parts and 1000 parts of deionized water of coarse whiting.
The above embodiment is a preferred embodiment of the present invention, but embodiments of the present invention are not by above-described embodiment
Limitation, it is other it is any without departing from the spirit and principles of the present invention made by change, modification, substitution, combination and simplify,
It should be equivalent substitute mode, be included within the scope of the present invention.
Claims (7)
1. a kind of color liquid sliver, which is characterized in that by weight calculating, comprising 15~70 parts of rubber powder of protection, ethoxy is fine
3~15 parts of dimension element, 220~420 parts of lotion, sand or 270~600 parts of coarse whiting, 10~35 parts of auxiliary agent and is gone by 40~80 parts of kaolin
400~1000 parts of ionized water；
The color liquid sliver the preparation method is as follows:
S1. protection rubber powder is added in deionized water, makes that rubber powder is protected to be completely dissolved, obtains the aqueous solution of protective glue；
S2. by hydroxyethyl cellulose, auxiliary agent, kaolin is add to deionized water, with 1500~2500r/min speed stirring 30
~45min, adds lotion and the aqueous solution of protective glue that part steps S1 is obtained is uniformly mixed, and obtains base paint；
S3. sand or coarse whiting are added in the base paint of step S2 preparation and are uniformly mixed, remaining protection in step S1 is then added
In glue solution, it is granulated to get color liquid sliver is arrived；
Wherein, the lotion is elastic acrylate lotion or organosilicon-modified acrylate emulsion；The protection rubber powder
For HG-1 powder, GTS powder or RDS powder；The sand is natural colour sand, dyeing color sand or artificial burning colorful sand；The auxiliary agent is
Wetting agent, dispersing agent, defoaming agent, fungicide, coalescing agent, antifreezing agent and pH adjusting agent；
The elastic acrylate lotion be in the acrylate monomer aqueous solution containing emulsifier alkylbenzene polyethers sodium sulfonate,
Under the conditions of existing for the initiator ammonium persulfate, reaction temperature is 80~90 DEG C, the elastic acrylate lotion of formation；It is described to have
Machine acrylate emulsion modified with organosiloxane is that second is added in the acrylic monomers aqueous solution containing emulsifier neopelex
Under the conditions of alkenyl triethoxysilane is existing for the initiator ammonium persulfate, reaction temperature is 60~70 DEG C, and that reacts formation has
Machine acrylate emulsion modified with organosiloxane.
2. color liquid sliver according to claim 1, which is characterized in that by weight calculating, comprising protection rubber powder 20~
60 parts, 5~11 parts of hydroxyethyl cellulose, 50~70 parts of kaolin, 220~400 parts of lotion, 300~580 parts of sand or coarse whiting help
15~29 parts and 480~930 parts of deionized water of agent.
3. color liquid sliver according to claim 1, which is characterized in that the wetting agent be alkyl phenol polyoxyethylene ether,
Polyether silicones or non-ionic fluorocarbon polymer, the dispersing agent are polycarboxylate sodium or ammonium polyacrylate salt, the defoaming
Agent be mineral oil or polysiloxane, the fungicide be isothiazolinone derivatives or benzimidazole compound, it is described at
Film auxiliary agent is 2,2,4- trimethyl -1,3- pentanediol mono isobutyrates, propandiol butyl ether or butyl glycol ether, and the antifreezing agent is
Ethylene glycol or propylene glycol；The pH adjusting agent is 2-amino-2-methyl-1-propanol or dimethylethanolamine.
4. color liquid sliver according to claim 1, which is characterized in that the solid content of the elastic acrylate lotion
It is 47~50%, the partial size of elastic acrylate lotion is 0.1~0.2 μm, and the pH value of elastic acrylate lotion is 7~9；Institute
The solid content for stating organosilicon-modified acrylate emulsion is 47~50%, and the partial size of organosilicon-modified acrylate emulsion is
0.1~0.2 μm, the pH value of organosilicon-modified acrylate emulsion is 7~9.
5. color liquid sliver according to claim 1, which is characterized in that the aqueous solution of protective glue described in step S2 and
The mass ratio of the aqueous solution of protective glue described in step S3 is 1:(4.5~7.5).
6. color liquid sliver according to claim 1, which is characterized in that the mode of granulation described in step S3 is shearing
Disk, sieve or negative pressure of vacuum.
7. application of any one of the claim 1-6 color liquid sliver in building coating field.