CN111205621A - 一种超高压软管的工艺制造方法 - Google Patents

一种超高压软管的工艺制造方法 Download PDF

Info

Publication number
CN111205621A
CN111205621A CN201911417751.2A CN201911417751A CN111205621A CN 111205621 A CN111205621 A CN 111205621A CN 201911417751 A CN201911417751 A CN 201911417751A CN 111205621 A CN111205621 A CN 111205621A
Authority
CN
China
Prior art keywords
extruder
pressure hose
section
ultrahigh pressure
manufacturing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201911417751.2A
Other languages
English (en)
Inventor
薛道应
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Baolihua Machinery Equipment Co ltd
Original Assignee
Anhui Baolihua Machinery Equipment Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Baolihua Machinery Equipment Co ltd filed Critical Anhui Baolihua Machinery Equipment Co ltd
Priority to CN201911417751.2A priority Critical patent/CN111205621A/zh
Publication of CN111205621A publication Critical patent/CN111205621A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种超高压软管的工艺制造方法，该方法包括如下步骤：原料准备：取氯醚橡胶、炭黑、碳酸钙、氧化铝、塑化剂和硫化剂；制取初始料：将步骤一中的各部分原料混合在一起，充分搅拌混合；设置挤出机：开启挤出机，设置挤出机的各项参数；挤出内胶层：设置挤出机各段温度；挤出增强层：设置针织机牵引速度和针织机转速；挤出外胶层：重新设置挤出机的各段温度；本发明依次通过六个步骤制造出超高压软管的内胶层、增强层和外胶层，制造出的超高压软管韧性高、耐高压、耐酸碱且抗腐蚀。

Description

一种超高压软管的工艺制造方法
技术领域
本发明涉及输送管道技术领域，尤其涉及一种超高压软管的工艺制造方法。
背景技术
随着社会的快速发展，超高压(工作压力≥20MPa)流体输送的运用领域已越来越广泛，例如：工业化工设备清洗和水刀切割等。上述领域所使用的高压软管的位置一般是不固定的，高压软管在进行作业时经常需要被拖拽，有时会因进入车轮或设备底下而受到挤压，造成高压软管的磨损或割伤。
超高压软管在现代社会中的运用越来越广泛，但是关于超高压软管的制作和生产至今没有形成一套完整的方案。
发明内容
基于背景技术存在的技术问题，本发明提出了一种超高压软管的工艺制造方法，制造的方法步骤简单，通过氯醚橡胶为主要的制作原料，氯醚橡胶具有较好的耐热性、耐油性、耐寒性和耐臭氧性，进而提高超高压软管的各方面性能。
本发明提出的一种超高压软管的工艺制造方法，该方法包括如下步骤：
一、准备：取氯醚橡胶、炭黑、碳酸钙、氧化铝、塑化剂和硫化剂；
二、制取初始料：将步骤一中的各部分原料混合在一起，充分搅拌混合；
三、设置挤出机：开启挤出机，设置挤出机的各项参数；
四、挤出内胶层：设置挤出机各段温度；
五、挤出增强层：设置针织机牵引速度和针织机转速；
六、挤出外胶层：重新设置挤出机的各段温度；
所述内胶层和外胶层都采用氯醚橡胶，配方为氯醚橡胶100份、炭黑N55020-30份、硅酸钙4-6份、氧化铝1-3份、塑化剂8-10份和硫化剂1-3份。
所述增强层采用芳纶纤维制成。
所述挤出机和针织机的工作环境温度为20-22摄氏度。
所述步骤四中挤出机各段温度为螺杆40～50℃，喂料段40～50℃，塑化段50～60℃，机头60～70℃。
所述步骤五中针织机牵引速度3～6m/min，针织机转速100～140转/min。
所述步骤六中挤出机各段温度为螺杆45～55℃，喂料段45～55℃，塑化段55～65℃，机头65～75℃。
所述塑化剂为邻苯二甲酸二酯和邻苯二甲酸二丁酯中的一种。
所述硫化剂为硫磺、金属氧化物和树脂类硫化剂的一种。
本发明提供的一种超高压软管的工艺制造方法的优点在于：选用氯醚橡胶为主要的制作原料，氯醚橡胶具有较好的耐热性、耐油性、耐寒性和耐臭氧性，进而提高超高压软管的各方面性能；本发明通过采用芳纶纤维制成增强层，芳纶纤维具有良好的抗冲击和耐疲劳性能，有良好的介电性和化学稳定性，耐有机溶剂、燃料、有机酸及稀浓度的强酸、强碱，耐屈折性和加工性能好，从提高增强层的性能，进而提高超高压软管的使用性能；本发明通过向原料中加入塑化剂，使原料的柔韧性增强，容易加工；本发明通过向原料中加入硫化剂，硫化剂能使橡胶分子链起交联反应，使线形分子形成立体网状结构，可塑性降低，弹性剂强度增加，进而促进超高压软管的制成。
说明书附图
图1为本发明的方法流程图。
具体实施方式
实施例一
一种超高压软管的工艺制造方法，该方法包括如下步骤：
一、准备：取氯醚橡胶、炭黑、碳酸钙、氧化铝、塑化剂和硫化剂；
二、制取初始料：将步骤一中的各部分原料混合在一起，充分搅拌混合；三、设置挤出机：开启挤出机，设置挤出机的各项参数；
四、挤出内胶层：设置挤出机各段温度；
五、挤出增强层：设置针织机牵引速度和针织机转速；
六、挤出外胶层：重新设置挤出机的各段温度。
所述内胶层和外胶层都采用氯醚橡胶，配方为氯醚橡胶100份、炭黑N55020份、硅酸钙4份、氧化铝1份、塑化剂8份和硫化剂1份。氯醚橡胶具有良好的耐热性、耐寒性和耐臭氧性，从而提高内胶层和外胶层的结构强度，进而提高超高压软管的使用效率；芳纶纤维耐疲劳性，耐磨性好且在高温环境下能保持高强度，具有耐酸耐碱、重量轻、绝缘、抗老化、生命周期长等优良性能，有利于提高超高压软管的结构性能。
所述增强层采用芳纶纤维制成。芳纶纤维具有良好的抗冲击和耐疲劳性能，有良好的介电性和化学稳定性，耐有机溶剂、燃料、有机酸及稀浓度的强酸、强碱，耐屈折性和加工性能好，从提高增强层的性能，进而提高超高压软管的使用性能。
所述挤出机和针织机的工作环境温度为20摄氏度。低温恒定的环境能保证原料的特性，进而提高挤出机和针织机的工作效率。
所述步骤四中挤出机各段温度为螺杆40℃，喂料段40℃，塑化段50℃，机头60℃。
所述步骤五中针织机牵引速度3/min，针织机转速100转/min。
所述步骤六中挤出机各段温度为螺杆45℃，喂料段45℃，塑化段55℃，机头65℃。
所述塑化剂为邻苯二甲酸二酯。邻苯二甲酸二酯是常用的塑化剂，在原料中加入塑化剂，可以使原料的柔韧性增强，容易加工。
所述硫化剂为硫磺。硫磺被广泛应用于橡胶中，硫化剂能使橡胶分子链起交联反应，使线形分子形成立体网状结构，可塑性降低，弹性剂强度增加，进而促进超高压软管的制成。
实施例二
一种超高压软管的工艺制造方法，该方法包括如下步骤：
一、准备：取氯醚橡胶、炭黑、碳酸钙、氧化铝、塑化剂和硫化剂；
二、制取初始料：将步骤一中的各部分原料混合在一起，充分搅拌混合；三、设置挤出机：开启挤出机，设置挤出机的各项参数；
四、挤出内胶层：设置挤出机各段温度；
五、挤出增强层：设置针织机牵引速度和针织机转速；
六、挤出外胶层：重新设置挤出机的各段温度。
所述内胶层和外胶层都采用氯醚橡胶，配方为氯醚橡胶100份、炭黑N55025硅酸钙4-6份、氧化铝2份、塑化剂9份和硫化剂2份。氯醚橡胶具有良好的耐热性、耐寒性和耐臭氧性，从而提高内胶层和外胶层的结构强度，进而提高超高压软管的使用效率；芳纶纤维耐疲劳性，耐磨性好且在高温环境下能保持高强度，具有耐酸耐碱、重量轻、绝缘、抗老化、生命周期长等优良性能，有利于提高超高压软管的结构性能。
所述增强层采用芳纶纤维制成。芳纶纤维具有良好的抗冲击和耐疲劳性能，有良好的介电性和化学稳定性，耐有机溶剂、燃料、有机酸及稀浓度的强酸、强碱，耐屈折性和加工性能好，从提高增强层的性能，进而提高超高压软管的使用性能。
所述挤出机和针织机的工作环境温度为21摄氏度。低温恒定的环境能保证原料的特性，进而提高挤出机和针织机的工作效率。
所述步骤四中挤出机各段温度为螺杆45℃，喂料段45℃，塑化段55℃，机头65℃。
所述步骤五中针织机牵引速度5m/min，针织机转速120转/min。
所述步骤六中挤出机各段温度为螺杆50℃，喂料段50℃，塑化段60℃，机头70℃。
所述塑化剂为邻苯二甲酸二丁酯中。邻苯二甲酸二丁酯是常用的塑化剂，在原料中加入塑化剂，可以使原料的柔韧性增强，容易加工。
所述硫化剂为金属氧化物。金属氧化物被广泛应用于橡胶中，硫化剂能使橡胶分子链起交联反应，使线形分子形成立体网状结构，可塑性降低，弹性剂强度增加，进而促进超高压软管的制成。
实施例三
一种超高压软管的工艺制造方法，该方法包括如下步骤：
一、准备：取氯醚橡胶、炭黑、碳酸钙、氧化铝、塑化剂和硫化剂；
二、制取初始料：将步骤一中的各部分原料混合在一起，充分搅拌混合；三、设置挤出机：开启挤出机，设置挤出机的各项参数；
四、挤出内胶层：设置挤出机各段温度；
五、挤出增强层：设置针织机牵引速度和针织机转速；
六、挤出外胶层：重新设置挤出机的各段温度。
所述内胶层和外胶层都采用氯醚橡胶，配方为氯醚橡胶100份、炭黑N55030份、硅酸钙6份、氧化铝3份、塑化剂10份和硫化剂3份。氯醚橡胶具有良好的耐热性、耐寒性和耐臭氧性，从而提高内胶层和外胶层的结构强度，进而提高超高压软管的使用效率；芳纶纤维耐疲劳性，耐磨性好且在高温环境下能保持高强度，具有耐酸耐碱、重量轻、绝缘、抗老化、生命周期长等优良性能，有利于提高超高压软管的结构性能。
所述增强层采用芳纶纤维制成。芳纶纤维具有良好的抗冲击和耐疲劳性能，有良好的介电性和化学稳定性，耐有机溶剂、燃料、有机酸及稀浓度的强酸、强碱，耐屈折性和加工性能好，从提高增强层的性能，进而提高超高压软管的使用性能。
所述挤出机和针织机的工作环境温度为22摄氏度。低温恒定的环境能保证原料的特性，进而提高挤出机和针织机的工作效率。
所述步骤四中挤出机各段温度为螺杆50℃，喂料段50℃，塑化段60℃，机头70℃。
所述步骤五中针织机牵引速度6m/min，针织机转速140转/min。
所述步骤六中挤出机各段温度为螺杆55℃，喂料段55℃，塑化段65℃，机头75℃。
所述塑化剂为邻苯二甲酸二酯。邻苯二甲酸二酯是常用的塑化剂，在原料中加入塑化剂，可以使原料的柔韧性增强，容易加工。
所述硫化剂为树脂类硫化剂。树脂类硫化剂被广泛应用于橡胶中，树脂类硫化剂能使橡胶分子链起交联反应，使线形分子形成立体网状结构，可塑性降低，弹性剂强度增加，进而促进超高压软管的制成。
本发明中提供的一种超高压软管的工艺制造方法，选用氯醚橡胶为主要的制作原料，氯醚橡胶具有较好的耐热性、耐油性、耐寒性和耐臭氧性，进而提高超高压软管的各方面性能；本发明通过采用芳纶纤维制成增强层，芳纶纤维具有良好的抗冲击和耐疲劳性能，有良好的介电性和化学稳定性，耐有机溶剂、燃料、有机酸及稀浓度的强酸、强碱，耐屈折性和加工性能好，从提高增强层的性能，进而提高超高压软管的使用性能；本发明通过向原料中加入塑化剂，使原料的柔韧性增强，容易加工；本发明通过向原料中加入硫化剂，硫化剂能使橡胶分子链起交联反应，使线形分子形成立体网状结构，可塑性降低，弹性剂强度增加，进而促进超高压软管的制成。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。

Claims (9)

1.一种超高压软管的工艺制造方法，其特征在于，该方法包括如下步骤：
一、原料准备：取氯醚橡胶、炭黑、碳酸钙、氧化铝、塑化剂和硫化剂；
二、制取初始料：将步骤一中的各部分原料混合在一起，充分搅拌混合；
三、设置挤出机：开启挤出机，设置挤出机的各项参数；
四、挤出内胶层：设置挤出机各段温度；
五、挤出增强层：设置针织机牵引速度和针织机转速；
六、挤出外胶层：重新设置挤出机的各段温度。
2.根据权利要求1所述的一种超高压软管的工艺制造方法，其特征在于，所述内胶层和外胶层都采用氯醚橡胶，配方为氯醚橡胶100份、炭黑N550 20-30份、硅酸钙4-6份、氧化铝1-3份、塑化剂8-10份和硫化剂1-3份。
3.根据权利要求1所述的一种超高压软管的工艺制造方法，其特征在于，所述增强层采用芳纶纤维制成。
4.根据权利要求1所述的一种超高压软管的工艺制造方法，其特征在于，所述挤出机和针织机的工作环境温度为20-22摄氏度。
5.根据权利要求1所述的一种超高压软管的工艺制造方法，其特征在于，所述步骤四中挤出机各段温度为螺杆40～50℃，喂料段40～50℃，塑化段50～60℃，机头60～70℃。
6.根据权利要求1所述的一种超高压软管的工艺制造方法，其特征在于，所述步骤五中针织机牵引速度3～6m/min，针织机转速100～140转/min。
7.根据权利要求1所述的一种超高压软管的工艺制造方法，其特征在于，所述步骤六中挤出机各段温度为螺杆45～55℃，喂料段45～55℃，塑化段55～65℃，机头65～75℃。
8.根据权利要求1所述的一种超高压软管的工艺制造方法，其特征在于，所述塑化剂为邻苯二甲酸二酯和邻苯二甲酸二丁酯中的一种。
9.根据权利要求1所述的一种超高压软管的工艺制造方法，其特征在于，所述硫化剂为硫磺、金属氧化物和树脂类硫化剂的一种。
CN201911417751.2A 2019-12-31 2019-12-31 一种超高压软管的工艺制造方法 Pending CN111205621A (zh)