CN111204759A - 一种利用花椒树枝制备活性炭的方法 - Google Patents

一种利用花椒树枝制备活性炭的方法 Download PDF

Info

Publication number
CN111204759A
CN111204759A CN202010210899.5A CN202010210899A CN111204759A CN 111204759 A CN111204759 A CN 111204759A CN 202010210899 A CN202010210899 A CN 202010210899A CN 111204759 A CN111204759 A CN 111204759A
Authority
CN
China
Prior art keywords
activated carbon
pepper
branches
liquid
acid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202010210899.5A
Other languages
English (en)
Inventor
刘必衍
曾惜
陈柏蓉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chongqing Feiyang Environmental Protection Technology Co ltd
Original Assignee
Chongqing Feiyang Environmental Protection Technology Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chongqing Feiyang Environmental Protection Technology Co ltd filed Critical Chongqing Feiyang Environmental Protection Technology Co ltd
Priority to CN202010210899.5A priority Critical patent/CN111204759A/zh
Publication of CN111204759A publication Critical patent/CN111204759A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种利用花椒树枝制备活性炭的方法，解决了花椒修剪的枝条处理处置等问题。本发明包括以下步骤：将收集得到的花椒枝条粉碎、与酸‑氯化锌溶液混合后，高温高压条件下水热碳化，将碳化液固混合物添加导热剂后搅拌均匀，过滤液固分离，微波活化，得到活性炭。本发明实现花椒修剪废弃物资源化利用，所制备活性炭产品比表面积大吸附性能好，强度高，尤其适用于高温吸附VOCs，具有良好的环境效益和经济价值。

Description

一种利用花椒树枝制备活性炭的方法
技术领域
本发明属农业工程技术领域，涉及农业废弃物处理与高值化利用技术领域，具体地说是一种利用花椒树枝制备活性炭的方法。
背景技术
花椒是芸香科、花椒属落叶小乔木，果皮晒干后呈酱红色，且具浓郁的麻香味，是人们日常生活中的一种色香味俱全的重要调味品。花椒在生长过程中需要进行定期修剪以维持果实产量。由于花椒枝条生有短刺，每年花椒修剪的大量枝条处理起来非常麻烦，就地焚烧还会造成严重的大气污染。
发明内容
本发明的目的是提供一种利用花椒树枝制备活性炭的方法，为了实现上述目的，本发明采用的技术方案为：
（a）将收集得到的花椒枝条粉碎、与酸-氯化锌溶液混合后，高温高压条件下水热碳化，酸-氯化锌溶液中酸为盐酸、硫酸，酸的质量浓度为0.2%-1.5%；氯化锌的浓度为40-75%，液固比为7:1-9:1，水热碳化温度为250-500°C，碳化时间为0.5-2小时；
（b）将碳化液固混合物添加导热剂后搅拌均匀，过滤液固分离，微波活化，得到活性炭，导热剂为碳化硅-二氧化钛的混合物，碳化硅与二氧化钛的质量比为0.2:1-6:1，导热剂的添加量为碳化固体产物质量的1.5%-5%，液固分离后，液固比为5:1-7:1，微波活化温度为750-1050°C，活化时间为0.5-2小时。
本发明的有益效果是：
1. 所制备的活性炭材料，比表面积大、强度高。
2. 实现花椒枝条的高质化利用：利用花椒修剪废弃物制备缓释肥，不仅解决了农业废弃物处理处置问题，而且还能变废为宝，产生高附加值产品。
总之，本发明涉及的花椒枝条制备活性炭的方法，可用于农业废弃物处理与高质化转化，有良好的环境效益、经济效益和社会效益。
具体实施方式
以下是对本发明的技术方案的进一步说明，而不是对本发明的限制。除非特别说明，本发明采用的试剂、设备和方法为本技术领域常规市购的试剂、设备和常规使用的方法。
实施例1
将收集得到的花椒枝条粉碎、与酸-氯化锌溶液混合，盐酸-氯化锌溶液中酸的质量浓度为0.8%；氯化锌的浓度为64%，液固比为8:1，380°C条件下水热碳化1小时；将碳化液固混合物添加导热剂后搅拌均匀，导热剂为碳化硅-二氧化钛的混合物，碳化硅与二氧化钛的质量比为1:1，热剂的添加量为碳化固体产物质量的2.3%，过滤液固分离，分离后液固比为7:1，920°C微波活化1小时，得到活性炭制品。经测试，所制备的活性炭比表面积为945平方米/克。

Claims (3)

1.一种利用花椒树枝制备活性炭的方法，其特征在于该方法包括如下步骤：
（a）将收集得到的花椒枝条粉碎、与酸-氯化锌溶液混合后，高温高压条件下水热碳化；
（b）将碳化液固混合物添加导热剂后搅拌均匀，过滤液固分离，微波活化，得到活性炭。
2.根据权利要求1所述的一种利用花椒树枝制备活性炭的方法，其特征在于，步骤（a）中所述的酸-氯化锌溶液中酸为盐酸、硫酸，酸的质量浓度为0.2%-1.5%；氯化锌的浓度为40-75%，液固比为7:1-9:1，水热碳化温度为250-500°C，碳化时间为0.5-2小时。
3.根据权利要求1所述的一种利用花椒树枝制备活性炭的方法，其特征在于，步骤（b）中所述的导热剂为碳化硅-二氧化钛的混合物，碳化硅与二氧化钛的质量比为0.2:1-6:1，导热剂的添加量为碳化固体产物质量的1.5%-5%，液固分离后，液固比为5:1-7:1，微波活化温度为750-1050°C，活化时间为0.5-2小时。
CN202010210899.5A 2020-03-24 2020-03-24 一种利用花椒树枝制备活性炭的方法 Pending CN111204759A (zh)