CN111138946A - Novel epoxy coal tar pitch finish paint and preparation method thereof - Google Patents
Novel epoxy coal tar pitch finish paint and preparation method thereof Download PDFInfo
- Publication number
- CN111138946A CN111138946A CN202010024833.7A CN202010024833A CN111138946A CN 111138946 A CN111138946 A CN 111138946A CN 202010024833 A CN202010024833 A CN 202010024833A CN 111138946 A CN111138946 A CN 111138946A
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- coal tar
- tar pitch
- finish paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a novel epoxy coal tar pitch finish paint and a preparation method thereof, and relates to the technical field of paint preparation. The epoxy coal tar pitch finish paint consists of a component A and a component B, wherein the component A comprises the following components in parts by weight: the component B is approximately equal to 10: 1; wherein the component A comprises the following materials in parts by weight: 350 parts of epoxy resin 250-containing materials, 4-6 parts of 983 dispersing agents, 8-12 parts of bentonite, 1-3 parts of polyamide wax powder, 220 parts of 55 ℃ coal tar pitch finish paint 180-containing materials, 70-90 parts of sericite powder, 40-60 parts of aluminum tripolyphosphate, 90-110 parts of talcum powder and 80-120 parts of a mixture of xylene and isobutanol; wherein, the component B is: 72-97 parts of a curing agent. According to the invention, through reasonably selecting the raw materials, the prepared paint has excellent acid resistance, alkali resistance and salt water resistance, has low VOC content, and simultaneously solves the problem that the paint film discolors when meeting water.
Description
Technical Field
The invention relates to the technical field of coating preparation, in particular to a novel epoxy coal tar pitch finish and a preparation method thereof.
Background
The finish paint is a final coating of coating, is a layer coated finally in building wall decoration, and the overall effect presented after decoration is reflected through the layer, so the finish paint has higher requirements on the used materials, not only has good chroma and brightness, but also has the characteristics of good pollution resistance, aging resistance, moisture resistance, good mildew resistance, no environmental pollution, safety, no toxicity, no fire hazard, convenient construction, fast film drying, good light and color retention, good air permeability and the like. Has decorative and protective functions, such as color, luster, texture, etc., and also requires resistance to harsh environments.
At present, the usage amount of the epoxy coal tar asphalt paint is large, but the epoxy coal tar asphalt paint on the market can change color seriously when meeting water after construction.
Disclosure of Invention
Technical problem to be solved
Aiming at the defects of the prior art, the invention provides a novel epoxy coal tar pitch finish paint and a preparation method thereof, which solve the defects and shortcomings in the prior art.
(II) technical scheme
In order to achieve the purpose, the invention is realized by the following technical scheme: the novel epoxy coal tar pitch finish paint is composed of a component A and a component B, wherein the component A comprises the following components: the component B is approximately equal to 10: 1;
wherein the component A comprises the following materials in parts by weight: 350 parts of epoxy resin 250-containing materials, 4-6 parts of 983 dispersing agents, 8-12 parts of bentonite, 1-3 parts of polyamide wax powder, 220 parts of 55 ℃ coal tar pitch finish paint 180-containing materials, 70-90 parts of sericite powder, 40-60 parts of aluminum tripolyphosphate, 90-110 parts of talcum powder and 80-120 parts of a mixture of xylene and isobutanol;
wherein, the component B is: 72-97 parts of a curing agent.
Preferably, the epoxy coal tar pitch finish paint is prepared from the following raw materials in parts by weight:
wherein the component A comprises the following materials in parts by weight: 300 parts of epoxy resin, 5 parts of 983 dispersant, 10 parts of bentonite, 2 parts of polyamide wax powder, 200 parts of 55 ℃ coal tar pitch finish, 80 parts of sericite powder, 50 parts of aluminum tripolyphosphate, 100 parts of talcum powder and 100 parts of a mixture of xylene and isobutanol;
wherein, the component B is: 85 parts of cardanol epoxy curing agent.
Preferably, the epoxy resin is 6101 epoxy resin with a mass fraction of 80%, the curing agent is cardanol epoxy curing agent with a mass fraction of 80%, and the ratio of xylene to isobutanol is 7: 3.
Preferably, the particle size of the sericite powder is 1240-1260 meshes, and the particle size of the talcum powder is 1200-1300 meshes.
A preparation method of a novel epoxy coal tar pitch finish paint comprises the following preparation steps:
s1, preparing raw materials which are divided into a component A and a component B;
wherein, the component A comprises the following materials: epoxy resin, 983 dispersant, bentonite, polyamide wax powder, 55 ℃ coal tar pitch finish, sericite powder, aluminum tripolyphosphate, talcum powder, xylene and isobutanol mixture;
wherein, the component B is: a curing agent;
s2, placing epoxy resin, 983 dispersant, bentonite, polyamide wax powder, 55 ℃ coal tar pitch finish, sericite powder, aluminum tripolyphosphate and talcum powder in the component A into a stirring kettle, raising the temperature of the stirring kettle to 60-80 ℃, stirring for a period of time, raising the temperature of the stirring kettle to 100-110 ℃, adding a mixture of xylene and isobutanol, continuing stirring for a period of time, and then reducing the temperature of the stirring kettle to 60-70 ℃ for heat preservation;
s3, after the heat preservation is finished, reducing the temperature of the stirring kettle to be below 40 ℃, then adding a curing agent into the stirring kettle, stirring uniformly and then putting into a plastic barrel;
and S4, performing performance test on the face paint.
Preferably, in the step 2, the stirring kettle is stirred for 5-10min at 60-80 ℃, the stirring speed is 3000r/min, the stirring kettle is stirred for 30-60min at 100-.
Preferably, the stirring time in the step 3 is 10-30min, and the stirring speed is 2000-4000 r/min.
(III) advantageous effects
The invention provides a novel epoxy coal tar pitch finish paint and a preparation method thereof. The method has the following beneficial effects:
according to the invention, through reasonably selecting the raw materials, the prepared paint has excellent acid resistance, alkali resistance and salt water resistance, has low VOC content, and simultaneously solves the problem that the paint film discolors when meeting water.
Detailed Description
The following will clearly and completely describe the technical solutions in the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
The first embodiment is as follows:
the embodiment of the invention provides a novel epoxy coal tar pitch finish paint, which consists of a component A and a component B, wherein the component A comprises the following components in parts by weight: the component B is approximately equal to 10: 1;
wherein the component A comprises the following materials in parts by weight: 250 parts of epoxy resin, 4 parts of 983 dispersant, 8 parts of bentonite, 1 part of polyamide wax powder, 180 parts of 55 ℃ coal tar pitch finish, 70 parts of sericite powder, 40 parts of aluminum tripolyphosphate, 90 parts of talcum powder and 80 parts of a mixture of xylene and isobutanol;
wherein, the component B is: 72 parts of curing agent.
The epoxy resin is 6101 epoxy resin with the mass fraction of 80 percent, the curing agent is cardanol epoxy curing agent with the mass fraction of 80 percent, and the ratio of dimethylbenzene to isobutanol is 7: 3; the granularity of the sericite powder is 1240-1260 meshes, and the granularity of the talcum powder is 1200-1300 meshes.
A preparation method of a novel epoxy coal tar pitch finish paint comprises the following preparation steps:
s1, preparing raw materials which are divided into a component A and a component B;
wherein, the component A comprises the following materials: epoxy resin, 983 dispersant, bentonite, polyamide wax powder, 55 ℃ coal tar pitch finish, sericite powder, aluminum tripolyphosphate, talcum powder, xylene and isobutanol mixture;
wherein, the component B is: a curing agent;
s2, placing epoxy resin, 983 dispersant, bentonite, polyamide wax powder, 55 ℃ coal tar pitch finish, sericite powder, aluminum tripolyphosphate and talcum powder in the component A into a stirring kettle, raising the temperature of the stirring kettle to 60-80 ℃, stirring the stirring kettle for 5-10min at the temperature of 60-80 ℃, wherein the stirring speed is 3000r/min for 2000 plus materials, raising the temperature of the stirring kettle to 110 ℃ for 100 plus materials, adding a mixture of xylene and isobutanol, stirring the stirring kettle for 30-60min at 110 ℃ for 100 plus materials, wherein the stirring speed is 4000r/min for 3000 plus materials, lowering the temperature of the stirring kettle to 60-70 ℃, and preserving the heat for 20-60 min;
s3, after the heat preservation is finished, reducing the temperature of the stirring kettle to be below 40 ℃, then adding a curing agent into the stirring kettle, uniformly stirring, and then putting into a plastic barrel, wherein the stirring time is 10-30min, and the stirring speed is 2000-4000 r/min;
and S4, performing performance test on the face paint.
The finish paint performance test comprises the following specific contents:
1) preparation of a template:
taking a standard plate with the specification of 7.5 multiplied by 12.5cm, preparing a paint film according to a general preparation method of a GB1727 paint film, treating a substrate according to the GB9271 specification, and controlling the thickness of the paint film to be 60-70 mu m;
2) and (3) drying mode: the performance of the paint film is measured after the paint film is dried for 48 hours;
3) performance indexes are as follows:
drying at ① 25 deg.C for 10h, soaking in tap water for 5h without discoloration;
② saline tolerance (3% NaCl) for 30 days;
③ alkali resistance (5% H2SO4) for 30 days;
④ salt spray resistance for 200 h;
⑤ solids content 83%;
⑥ impact strength 50.
Example two:
the embodiment of the invention provides a novel epoxy coal tar pitch finish paint, which consists of a component A and a component B, wherein the component A comprises the following components in parts by weight: the component B is approximately equal to 10: 1;
wherein the component A comprises the following materials in parts by weight: 300 parts of epoxy resin, 5 parts of 983 dispersant, 10 parts of bentonite, 2 parts of polyamide wax powder, 200 parts of 55 ℃ coal tar pitch finish, 80 parts of sericite powder, 50 parts of aluminum tripolyphosphate, 100 parts of talcum powder and 100 parts of a mixture of xylene and isobutanol;
wherein, the component B is: 85 parts of cardanol epoxy curing agent.
The epoxy resin is 6101 epoxy resin with the mass fraction of 80 percent, the curing agent is cardanol epoxy curing agent with the mass fraction of 80 percent, and the ratio of dimethylbenzene to isobutanol is 7: 3; the granularity of the sericite powder is 1240-1260 meshes, and the granularity of the talcum powder is 1200-1300 meshes.
A preparation method of a novel epoxy coal tar pitch finish paint comprises the following preparation steps:
s1, preparing raw materials which are divided into a component A and a component B;
wherein, the component A comprises the following materials: epoxy resin, 983 dispersant, bentonite, polyamide wax powder, 55 ℃ coal tar pitch finish, sericite powder, aluminum tripolyphosphate, talcum powder, xylene and isobutanol mixture;
wherein, the component B is: a curing agent;
s2, placing epoxy resin, 983 dispersant, bentonite, polyamide wax powder, 55 ℃ coal tar pitch finish, sericite powder, aluminum tripolyphosphate and talcum powder in the component A into a stirring kettle, raising the temperature of the stirring kettle to 60-80 ℃, stirring the stirring kettle for 5-10min at the temperature of 60-80 ℃, wherein the stirring speed is 3000r/min for 2000 plus materials, raising the temperature of the stirring kettle to 110 ℃ for 100 plus materials, adding a mixture of xylene and isobutanol, stirring the stirring kettle for 30-60min at 110 ℃ for 100 plus materials, wherein the stirring speed is 4000r/min for 3000 plus materials, lowering the temperature of the stirring kettle to 60-70 ℃, and preserving the heat for 20-60 min;
s3, after the heat preservation is finished, reducing the temperature of the stirring kettle to be below 40 ℃, then adding a curing agent into the stirring kettle, uniformly stirring, and then putting into a plastic barrel, wherein the stirring time is 10-30min, and the stirring speed is 2000-4000 r/min;
and S4, performing performance test on the face paint.
Example three:
the embodiment of the invention provides a novel epoxy coal tar pitch finish paint, which consists of a component A and a component B, wherein the component A comprises the following components in parts by weight: the component B is approximately equal to 10: 1;
wherein the component A comprises the following materials in parts by weight: 350 parts of epoxy resin, 6 parts of 983 dispersing agent, 12 parts of bentonite, 3 parts of polyamide wax powder, 220 parts of 55 ℃ coal tar pitch finish, 90 parts of sericite powder, 60 parts of aluminum tripolyphosphate, 110 parts of talcum powder and 120 parts of a mixture of xylene and isobutanol;
wherein, the component B is: and 97 parts of curing agent.
The epoxy resin is 6101 epoxy resin with the mass fraction of 80 percent, the curing agent is cardanol epoxy curing agent with the mass fraction of 80 percent, and the ratio of dimethylbenzene to isobutanol is 7: 3; the granularity of the sericite powder is 1240-1260 meshes, and the granularity of the talcum powder is 1200-1300 meshes.
A preparation method of a novel epoxy coal tar pitch finish paint comprises the following preparation steps:
s1, preparing raw materials which are divided into a component A and a component B;
wherein, the component A comprises the following materials: epoxy resin, 983 dispersant, bentonite, polyamide wax powder, 55 ℃ coal tar pitch finish, sericite powder, aluminum tripolyphosphate, talcum powder, xylene and isobutanol mixture;
wherein, the component B is: a curing agent;
s2, placing epoxy resin, 983 dispersant, bentonite, polyamide wax powder, 55 ℃ coal tar pitch finish, sericite powder, aluminum tripolyphosphate and talcum powder in the component A into a stirring kettle, raising the temperature of the stirring kettle to 60-80 ℃, stirring the stirring kettle for 5-10min at the temperature of 60-80 ℃, wherein the stirring speed is 3000r/min for 2000 plus materials, raising the temperature of the stirring kettle to 110 ℃ for 100 plus materials, adding a mixture of xylene and isobutanol, stirring the stirring kettle for 30-60min at 110 ℃ for 100 plus materials, wherein the stirring speed is 4000r/min for 3000 plus materials, lowering the temperature of the stirring kettle to 60-70 ℃, and preserving the heat for 20-60 min;
s3, after the heat preservation is finished, reducing the temperature of the stirring kettle to be below 40 ℃, then adding a curing agent into the stirring kettle, uniformly stirring, and then putting into a plastic barrel, wherein the stirring time is 10-30min, and the stirring speed is 2000-4000 r/min;
and S4, performing performance test on the face paint.
Although embodiments of the present invention have been shown and described, it will be appreciated by those skilled in the art that changes, modifications, substitutions and alterations can be made in these embodiments without departing from the principles and spirit of the invention, the scope of which is defined in the appended claims and their equivalents.
Claims (7)
1. A novel epoxy coal tar pitch finish paint is characterized in that: the epoxy coal tar pitch finish paint is composed of a component A and a component B, wherein the component A is as follows: the component B is approximately equal to 10: 1;
wherein the component A comprises the following materials in parts by weight: 350 parts of epoxy resin 250-containing materials, 4-6 parts of 983 dispersing agents, 8-12 parts of bentonite, 1-3 parts of polyamide wax powder, 220 parts of 55 ℃ coal tar pitch finish paint 180-containing materials, 70-90 parts of sericite powder, 40-60 parts of aluminum tripolyphosphate, 90-110 parts of talcum powder and 80-120 parts of a mixture of xylene and isobutanol;
wherein, the component B is: 72-97 parts of a curing agent.
2. The novel epoxy coal tar pitch finish paint as claimed in claim 1, characterized in that: the epoxy coal tar pitch finish paint is prepared from the following raw materials in parts by weight:
wherein the component A comprises the following materials in parts by weight: 300 parts of epoxy resin, 5 parts of 983 dispersant, 10 parts of bentonite, 2 parts of polyamide wax powder, 200 parts of 55 ℃ coal tar pitch finish, 80 parts of sericite powder, 50 parts of aluminum tripolyphosphate, 100 parts of talcum powder and 100 parts of a mixture of xylene and isobutanol;
wherein, the component B is: 85 parts of cardanol epoxy curing agent.
3. The novel epoxy coal tar pitch finish paint as claimed in claim 1, characterized in that: the epoxy resin is 6101 epoxy resin with the mass fraction of 80%, the curing agent is cardanol epoxy curing agent with the mass fraction of 80%, and the ratio of the dimethylbenzene to the isobutanol is 7: 3.
4. The novel epoxy coal tar pitch finish paint as claimed in claim 1, characterized in that: the particle size of the sericite powder is 1240-1260 meshes, and the particle size of the talcum powder is 1200-1300 meshes.
5. A preparation method of a novel epoxy coal tar pitch finish paint is characterized by comprising the following steps: the preparation method comprises the following preparation steps:
s1, preparing raw materials which are divided into a component A and a component B;
wherein, the component A comprises the following materials: epoxy resin, 983 dispersant, bentonite, polyamide wax powder, 55 ℃ coal tar pitch finish, sericite powder, aluminum tripolyphosphate, talcum powder, xylene and isobutanol mixture;
wherein, the component B is: a curing agent;
s2, placing epoxy resin, 983 dispersant, bentonite, polyamide wax powder, 55 ℃ coal tar pitch finish, sericite powder, aluminum tripolyphosphate and talcum powder in the component A into a stirring kettle, raising the temperature of the stirring kettle to 60-80 ℃, stirring for a period of time, raising the temperature of the stirring kettle to 100-110 ℃, adding a mixture of xylene and isobutanol, continuing stirring for a period of time, and then reducing the temperature of the stirring kettle to 60-70 ℃ for heat preservation;
s3, after the heat preservation is finished, reducing the temperature of the stirring kettle to be below 40 ℃, then adding a curing agent into the stirring kettle, stirring uniformly and then putting into a plastic barrel;
and S4, performing performance test on the face paint.
6. The novel epoxy coal tar pitch finish paint and the preparation method thereof as claimed in claim 5, wherein the epoxy coal tar pitch finish paint is characterized in that: in the step 2, the stirring kettle is stirred for 5-10min at the temperature of 60-80 ℃, the stirring speed is 3000r/min, the stirring kettle is stirred for 30-60min at the temperature of 100-.
7. The novel epoxy coal tar pitch finish paint and the preparation method thereof as claimed in claim 5, wherein the epoxy coal tar pitch finish paint is characterized in that: the stirring time in the step 3 is 10-30min, and the stirring speed is 2000-4000 r/min.