CN104927689A - Three-protection outdoor wooden door dedicated pasting film - Google Patents
Three-protection outdoor wooden door dedicated pasting film Download PDFInfo
- Publication number
- CN104927689A CN104927689A CN201410100433.4A CN201410100433A CN104927689A CN 104927689 A CN104927689 A CN 104927689A CN 201410100433 A CN201410100433 A CN 201410100433A CN 104927689 A CN104927689 A CN 104927689A
- Authority
- CN
- China
- Prior art keywords
- agent
- weight
- proofing
- outdoor
- wooden door
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a three-protection outdoor wooden door dedicated pasting film, specifically relates to the outdoor wooden door dedicated pasting film having water-proofing, sun-proofing and acid-proofing functions and composed of a base layer, a glue layer and a film layer, and is characterized in that the base layer comprises the following components by weight: 70-85% of polyolefin resin, and 15-30% of a filler; the glue layer comprises the following components by weight: 20-25% of aluminum phosphate, 15-20% of magnesium silicate, 15-20% of sodium silicate, 10-15% of an inorganic high-molecular polymerization agent, 5-8% of a fire-proofing agent, and 3-5% of rutile type titanium dioxide; the film layer is composed of the following components by weight: 60-75% of waste PVC plastics, 5-10% of fluorosilane, 5-8% of a PVC toughening agent, 5-8% of an acid proofing agent, 5-8% of aryl phosphate, and 5-8% of an antioxidant 1010. The wooden door dedicated pasting film has the advantages of low cost, no damage to doors, no influence on door appearance beauty, and good mechanical properties and chemical properties, and can be applicable to protection of the outdoor wooden doors.
Description
Technical field
The present invention relates to the special pad pasting of outdoor timber of a kind of waterproof, sun-proof, acid-proof, belong to building materials technology field, specifically the special pad pasting of a kind of three anti-outdoor timber.
Background technology
In recent years, along with the continuous propelling of China's reform and opening-up, living standards of the people significantly improve, and especially the development in rural area presents quick, flourishing scene, thus has driven the high speed development of rustic home construction industry.At present, China's rustic home floor area of building constantly expands, and rural area is assumed an entirely new aspect.But, the house of major part Rural areas, still based on traditional style building, adopts the wooden door and window in old times but without any safeguard procedures, makes door and window because of wind, Exposure to Sunlight in the course of time, drench with rain and cause deformed damaged, not only have impact on house attractive in appearance, and cause unnecessary financial loss.In order to address this problem, some areas adopt paint brushing in case door and window deformed damaged, but high-quality paint is expensive, can not be adopted by most of peasant household.
For the problems referred to above, present inventors have proposed a kind of special pad pasting of timber possessing waterproof, sun-proof, anti-acid function, price comparative good-quality paint is lower, pad pasting is simple, and the common paint of the shop front can not be damaged, not only serve the object of protecting outdoor timber, and can be most of user and accepted, also can not affect the shop front attractive in appearance, even reach the effect of beautifying the shop front.Find through retrieval, there is no relevant report at present.
Summary of the invention
The object of the invention is to: the special pad pasting of outdoor timber that a kind of waterproof, sun-proof, acid-proof are provided, adopt glue-line, basic unit and rete three-layer protection means, reach the deformation that the outdoor timber of protection causes because of wind, Exposure to Sunlight, the climatic factor such as to drench with rain to damage, have and do not hinder door, beautify the shop front, operate easy, simple and quick, that cost is low advantage.
To achieve these goals, the present invention adopts following technique means:
The special pad pasting of a kind of three anti-outdoor timber, is made up of basic unit, glue-line, rete, it is characterized in that: described basic unit comprises following component (in weight fraction):
Polyolefin resin 70 ~ 85%
Weighting agent 15 ~ 30%;
Described glue-line comprises following component (with parts by weight):
Described rete is made up of (with parts by weight) following component:
Further, described weighting agent is by Nano-meter CaCO3
3, nano-TiO
2, talcum powder composition.
Described three anti-outdoor timber special-purpose plaster film thicknesses are 2 ~ 3mm.
Described three anti-outdoor timber special-purpose plaster membrane preparation methods are as follows:
(1) by described polyolefin resin, Nano-meter CaCO3
3, nano-TiO
2, talcum powder adds in mixing tank simultaneously and mixes, mixing temperature is 130 ~ 150 DEG C, and rotating speed controls 20 ~ 50 turns/min, after mixing terminates, extrudes the thin slice that thickness is 1mm, is cooled to room temperature;
(2) described waste PVC plastics, silicon fluoride, PVC toughner, acid proofing agent, aryl phosphate ester, antioxidant 1010 are added in mixing tank and mix, mixing temperature 150 ~ 180 DEG C, rotating speed controls 30 ~ 50 turns/min, is cooled to 130 DEG C gradually after mixing terminates;
(3) described aluminum phosphate, Magnesium Silicate q-agent, water glass, inorganic polymer polymerizing agent, fireproofing agent, rutile titanium dioxide are added in mixing tank simultaneously and mix, mixing temperature is 120 ~ 150 DEG C, it is 50 ~ 80 turns/min that rotating speed controls, substrate surface is coated, coating thickness 0.5mm after mixing terminates;
(4) basic unit and rete that are coated with glue-line are fitted, the special pad pasting of the anti-outdoor timber of the present invention three can be obtained.
Know-why of the present invention and beneficial effect:
The present invention adopts super hydrophobic material fluorochemical to fill rete, and making the attachment film surface prepared stablize contact angle is 160 ~ 180 °, and Structure deformation angle is less than 5 ~ 8 °; Adopt three-layer thin-film structure, make the pad pasting obtained have excellent mechanical property and chemical property.
The invention has the advantages that:
(1) rete adopts waste PVC plastics to be main raw material, reduces production cost, increases economic efficiency;
(2) glue-line adopts timber special adhesive to become to be grouped into, and has and does not hinder the shop front, nontoxic, harmless advantage;
(3) pad pasting of the present invention is applicable to the protection of outdoor timber, can realize shutter surface damage, also can not affect the shop front attractive in appearance, has good economic benefit and practicality.
Embodiment
Below in conjunction with specific examples, technical scheme of the present invention is described further.
Embodiment 1
The special pad pasting of a kind of three anti-outdoor timber, be made up of basic unit, glue-line, rete, wherein, described basic unit comprises following component (in weight fraction): polyolefin resin 70%, weighting agent 30%;
Described glue-line comprises following component (with parts by weight): aluminum phosphate 25%, Magnesium Silicate q-agent 20%, water glass 20%, inorganic polymer polymerizing agent 15%, fireproofing agent 5%, rutile titanium dioxide 3%;
Described rete is made up of (with parts by weight) following component: waste PVC plastics 60 ~ 75%, silicon fluoride 5 ~ 10%, PVC toughner 5 ~ 8%, acid proofing agent 5 ~ 8%, aryl phosphate ester 5 ~ 8%, antioxidant 1010 5 ~ 8%.
Further, described weighting agent is by Nano-meter CaCO3
3, nano-TiO
2, talcum powder composition.
Described three anti-outdoor timber special-purpose plaster membrane preparation methods are as follows:
(1) by described polyolefin resin, Nano-meter CaCO3
3, nano-TiO
2, talcum powder adds in mixing tank simultaneously and mixes, mixing temperature is 130 DEG C, and rotating speed controls 20 turns/min, after mixing terminates, extrudes the thin slice that thickness is 1mm, is cooled to room temperature;
(2) described waste PVC plastics, silicon fluoride, PVC toughner, acid proofing agent, aryl phosphate ester, antioxidant 1010 are added in mixing tank and mixed, mixing temperature 150 DEG C, rotating speed controls 30 turns/min, is cooled to 130 DEG C gradually after mixing terminates;
(3) described aluminum phosphate, Magnesium Silicate q-agent, water glass, inorganic polymer polymerizing agent, fireproofing agent, rutile titanium dioxide are added in mixing tank simultaneously and mix, mixing temperature is 120 DEG C, it is 50 turns/min that rotating speed controls, and coats substrate surface, coating thickness 0.5mm after mixing terminates;
(4) basic unit and rete that are coated with glue-line are fitted, the special pad pasting of the anti-outdoor timber of the present invention three can be obtained.
It is 2.5mm that this example makes timber special-purpose plaster film thickness.
Embodiment 2
The special pad pasting of a kind of three anti-outdoor timber, be made up of basic unit, glue-line, rete, wherein, described basic unit comprises following component (in weight fraction): polyolefin resin 75%, weighting agent 25%;
Described glue-line comprises following component (with parts by weight): aluminum phosphate 23%, Magnesium Silicate q-agent 18%, water glass 18%, inorganic polymer polymerizing agent 12%, fireproofing agent 6%, rutile titanium dioxide 4%;
Described rete is made up of (with parts by weight) following component: waste PVC plastics 70%, silicon fluoride 8%, PVC toughner 7%, acid proofing agent 6%, aryl phosphate ester 7%, antioxidant 1010 6%.
Further, described weighting agent is by Nano-meter CaCO3
3, nano-TiO
2, talcum powder composition.
Described three anti-outdoor timber special-purpose plaster membrane preparation methods are as follows:
(1) by described polyolefin resin, Nano-meter CaCO3
3, nano-TiO
2, talcum powder adds in mixing tank simultaneously and mixes, mixing temperature is 140 DEG C, and rotating speed controls 35 turns/min, after mixing terminates, extrudes the thin slice that thickness is 1mm, is cooled to room temperature;
(2) described waste PVC plastics, silicon fluoride, PVC toughner, acid proofing agent, aryl phosphate ester, antioxidant 1010 are added in mixing tank and mixed, mixing temperature 165 DEG C, rotating speed controls 40 turns/min, is cooled to 130 DEG C gradually after mixing terminates;
(3) described aluminum phosphate, Magnesium Silicate q-agent, water glass, inorganic polymer polymerizing agent, fireproofing agent, rutile titanium dioxide are added in mixing tank simultaneously and mix, mixing temperature is 135 DEG C, it is 65 DEG C that rotating speed controls, and coats substrate surface, coating thickness 0.5mm after mixing terminates;
(4) basic unit and rete that are coated with glue-line are fitted, the special pad pasting of the anti-outdoor timber of the present invention three can be obtained.
It is 2mm that this example makes timber special-purpose plaster film thickness.
Embodiment 3
The special pad pasting of a kind of three anti-outdoor timber, be made up of basic unit, glue-line, rete, wherein, described basic unit comprises following component (in weight fraction): polyolefin resin 85%, weighting agent 15%;
Described glue-line comprises following component (with parts by weight): aluminum phosphate 25%, Magnesium Silicate q-agent 20%, water glass 20%, inorganic polymer polymerizing agent 15%, fireproofing agent 8%, rutile titanium dioxide 5%;
Described rete is made up of (with parts by weight) following component: waste PVC plastics 75%, silicon fluoride 10%, PVC toughner 8%, acid proofing agent 8%, aryl phosphate ester 8%, antioxidant 1010 8%.
Further, described weighting agent is by Nano-meter CaCO3
3, nano-TiO
2, talcum powder composition.
Described three anti-outdoor timber special-purpose plaster membrane preparation methods are as follows:
(1) by described polyolefin resin, Nano-meter CaCO3
3, nano-TiO
2, talcum powder adds in mixing tank simultaneously and mixes, mixing temperature is 150 DEG C, and rotating speed controls 50 turns/min, after mixing terminates, extrudes the thin slice that thickness is 1mm, is cooled to room temperature;
(2) described waste PVC plastics, silicon fluoride, PVC toughner, acid proofing agent, aryl phosphate ester, antioxidant 1010 are added in mixing tank and mixed, mixing temperature 180 DEG C, rotating speed controls 50 turns/min, is cooled to 130 DEG C gradually after mixing terminates;
(3) described aluminum phosphate, Magnesium Silicate q-agent, water glass, inorganic polymer polymerizing agent, fireproofing agent, rutile titanium dioxide are added in mixing tank simultaneously and mix, mixing temperature is 150 DEG C, it is 80 turns/min that rotating speed controls, and coats substrate surface, coating thickness 0.5mm after mixing terminates;
(4) basic unit and rete that are coated with glue-line are fitted, the special pad pasting of the anti-outdoor timber of the present invention three can be obtained.
The obtained three anti-outdoor timber special-purpose plaster film thicknesses of this example are 3mm.
Claims (3)
1. the special pad pasting of three anti-outdoor timbers, is made up of basic unit, glue-line, rete, it is characterized in that: described basic unit comprises following component (in weight fraction):
Polyolefin resin 70 ~ 85%
Weighting agent 15 ~ 30%;
Described glue-line comprises following component (with parts by weight):
Described rete is made up of (with parts by weight) following component:
2. the special pad pasting of a kind of three anti-outdoor timber as claimed in claim 1, is characterized in that: described weighting agent is by Nano-meter CaCO3
3, nano-TiO
2, talcum powder composition.
3. the special pad pasting of a kind of three anti-outdoor timber as claimed in claim 1, is characterized in that: described three anti-outdoor timber special-purpose plaster film thicknesses are 2 ~ 3mm.