CN111114186A - 一种刺绣墙画及其制备方法 - Google Patents
一种刺绣墙画及其制备方法 Download PDFInfo
- Publication number
- CN111114186A CN111114186A CN202010031160.8A CN202010031160A CN111114186A CN 111114186 A CN111114186 A CN 111114186A CN 202010031160 A CN202010031160 A CN 202010031160A CN 111114186 A CN111114186 A CN 111114186A
- Authority
- CN
- China
- Prior art keywords
- layer
- parts
- embroidery
- area
- image
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种刺绣墙画及其制备方法，所述刺绣墙画包括：基材层；所述基材层由图像区、刺绣区和底色区组成；设置在所述图像区的图像层；所述图像层由复合在所述图像区表面的发泡层和复合在所述发泡层表面的油墨层组成，或为数码图像层；设置在所述刺绣区的绣花层；设置在所述底色区的底色层；所述绣花层、图像层和底色层整体形成图案效果面；复合在图案效果面上的保护层。与现有技术相比，本发明提供的刺绣墙画远看是画，近看是工艺品，并通过不同图案组合，实现虚实结合，相得益彰，色彩丰富，立体感强的效果，且成本低；同时本发明提供的刺绣墙画采用特定保护层，增强产品的耐摩擦性，减缓油墨的变色，增强防水性能以及方便刺绣墙画的清洁。
Description
技术领域
本发明涉及室内装饰材料技术领域，更具体地说，是涉及一种刺绣墙画及其制备方法。
背景技术
墙画是一种室内的装饰材料，被广泛的应用在住宅、办公室等地方的室内装修中。墙画在制造时，主要是通过普通的印刷方式将图案印刷在基材上。随着人们生活的质量的不断提高，对墙画的要求也越来越高，由于直接将图案印刷在基材上立体感较差，现有的做法是在墙布上进行刺绣以增强墙画的立体感。
但是，当对墙布进行低档刺绣时，墙画的色彩较为单一，当对墙布进行高档刺绣时，其成本较高。
发明内容
有鉴于此，本发明的目的在于提供一种刺绣墙画及其制备方法，该刺绣墙画具有幅宽不受限制，图案虚实结合、色彩丰富、立体感强的效果，且成本低，同时具有耐摩擦、减缓油墨的变色、防水及易清洁的优点。
本发明提供了一种刺绣墙画，包括：
基材层；所述基材层由图像区、刺绣区和底色区组成；
设置在所述图像区的图像层；所述图像层由复合在所述图像区表面的发泡层和复合在所述发泡层表面的油墨层组成，或为数码图像层；
设置在所述刺绣区的绣花层；
设置在所述底色区的底色层；所述绣花层、图像层和底色层整体形成图案效果面；
复合在所述图案效果面上的保护层。
优选的，所述基材层为无纺纸、平织布、无纺布、油画布、星光布、宣绒布、仿真丝、麻布或染色布。
优选的，所述发泡层由发泡浆料形成；所述发泡浆料包括以下组分：
树脂100重量份～150重量份；
流平剂0.5重量份～1.5重量份；
稳定剂1重量份～2重量份；
发泡剂5重量份～10重量份；
碳酸钙10重量份～20重量份；
钛白粉25重量份～35重量份；
增稠剂2.5重量份～3.5重量份；
艾草粉1重量份～3重量份；
抗菌剂1重量份～5重量份；
溶剂50重量份～100重量份；
CT触媒1重量份～5重量份。
优选的，所述图像层的厚度为0.05mm～1.5mm。
优选的，所述绣花层的厚度为0.1mm～3mm。
优选的，所述保护层由树脂组合物形成；所述树脂组合物包括以下组分：
丙烯酸酯乳液20重量份～40重量份；
聚氨酯乳液30重量份～45重量份；
水10重量份～20重量份；
乳化剂0.5重量份～1重量份；
十二碳醇酯5重量份～7重量份；
葡萄糖酸钠0.05重量份～0.3重量份；
纳米二氧化硅20重量份～30重量份；
功能助剂0重量份～5重量份。
优选的，所述保护层的厚度为0.3mm～0.8mm。
本发明还提供了一种上述技术方案所述的刺绣墙画的制备方法，包括以下步骤：
a)将所述基材层分为图像区、刺绣区和底色区；
b)在所述图像区印刷发泡浆料；
在所述发泡浆料及底色区上印刷油墨，分别形成油墨层和底色层，再将涂刷有发泡浆料的基材加热形成发泡层；
或在所述图像区通过数码打印得到数码图像层；
c)在所述刺绣区进行绣花，得到绣花层；
d)在所述绣花层、图像层和底色层整体涂刷树脂组合物，形成保护层，得到刺绣墙画。
优选的，步骤b)中所述加热为分段加热；所述分段加热包括第一阶段加热、第二阶段加热和第三阶段加热；所述第一阶段加热的温度为180℃～200℃，所述第二阶段加热的温度为190℃～220℃，所述第三阶段加热的温度为140℃～180℃。
优选的，步骤d)中所述整体涂刷树脂组合物前，还包括：
采用感光墨水在所述绣花层和图像层周围勾勒轮廓，形成感光线条。
本发明提供了一种刺绣墙画及其制备方法，所述刺绣墙画包括：基材层；所述基材层由图像区、刺绣区和底色区组成；设置在所述图像区的图像层；所述图像层由复合在所述图像区表面的发泡层和复合在所述发泡层表面的油墨层组成，或为数码图像层；设置在所述刺绣区的绣花层；设置在所述底色区的底色层；所述绣花层、图像层和底色层整体形成图案效果面；复合在所述图案效果面上的保护层。与现有技术相比，本发明提供的刺绣墙画通过绣花层和图像层结合，绣花层使图案惟妙惟肖，图像层使图案颜色极其丰富，从而实现该刺绣墙画远看是画，近看是工艺品，并通过不同图案组合，实现虚实结合，相得益彰，色彩丰富，立体感强的效果，且成本低；同时本发明提供的刺绣墙画采用特定保护层，增强产品的耐摩擦性，减缓油墨的变色，增强防水性能以及方便刺绣墙画的清洁。
另外，本发明提供的刺绣墙画能够通过对发泡层、保护层的组分改进，使刺绣墙画在美观的同时又有更多、更强的功能性，丰富其应用领域，具有广阔的发展前景。
附图说明
图1为本发明提供的刺绣墙画的结构示意图；
图2为本发明提供的刺绣墙画的表面示意图；
图3为本发明实施例1提供的刺绣墙画的结构示意图。
具体实施方式
下面将结合本发明实施例，对本发明的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
本发明提供了一种刺绣墙画，包括：
基材层；所述基材层由图像区、刺绣区和底色区组成；
设置在所述图像区的图像层；所述图像层由复合在所述图像区表面的发泡层和复合在所述发泡层表面的油墨层组成，或为数码图像层；
设置在所述刺绣区的绣花层；
设置在所述底色区的底色层；所述绣花层、图像层和底色层整体形成图案效果面；
复合在所述图案效果面上的保护层。
请参阅图1～2，图1为本发明提供的刺绣墙画的结构示意图，图2为本发明提供的刺绣墙画的表面示意图；其中，1为基材层，2为图像层，3为绣花层，4为底色层，5为保护层，6为感光线条。
在本发明中，所述基材层优选为无纺纸、平织布、无纺布、油画布、星光布、宣绒布、仿真丝、麻布或染色布，更优选为无纺布。本发明对所述基材层的来源没有特殊限制，采用本领域技术人员熟知的上述无纺纸、平织布、无纺布、油画布、星光布和宣绒布的市售商品即可。在本发明中，所述基材层的厚度优选为0.1mm～1.5mm，更优选为1mm。
在本发明中，所述基材层由图像区、刺绣区和底色区组成；具体可通过在所述基材层表面印刷图案轮廓线进行划分。
在本发明中，所述图像层设置在所述图像区。在本发明中，所述图像层由复合在所述图像区表面的发泡层和复合在所述发泡层表面的油墨层组成，或为数码图像层。
在本发明中，所述发泡层复合在所述图像区表面；所述发泡层优选为兼具抗菌和净化空气作用的发泡层。在本发明中，所述发泡层优选由发泡浆料形成。在本发明中，所述发泡浆料优选包括以下组分：
树脂100重量份～150重量份；
流平剂0.5重量份～1.5重量份；
稳定剂1重量份～2重量份；
发泡剂5重量份～10重量份；
碳酸钙10重量份～20重量份；
钛白粉25重量份～35重量份；
增稠剂2.5重量份～3.5重量份；
艾草粉1重量份～3重量份；
抗菌剂1重量份～5重量份；
溶剂50重量份～100重量份；
CT触媒1重量份～5重量份。
在本发明中，所述树脂优选包括丙烯酸树脂、PVC树脂和EVA树脂中的一种或多种，更优选为丙烯酸树脂；所述丙烯酸酯树脂优选选自甲基丙烯酸甲酯、甲基丙烯酸丁酯、甲基丙烯酸正丁酯和丙烯酸正丁酯中的一种或多种，更优选为甲基丙烯酸甲酯。本发明对所述丙烯酸酯树脂的来源没有特殊限制，采用本领域技术人员熟知的上述甲基丙烯酸甲酯、甲基丙烯酸丁酯、甲基丙烯酸正丁酯和丙烯酸正丁酯的市售商品即可。在本发明中，所述发泡浆料优选包括100重量份～150重量份的丙烯酸酯树脂，更优选为120重量份。
在本发明中，所述流平剂优选选自硅油、聚二甲基硅氧烷、脉醛树脂和三聚氰胺甲醛树脂中的一种或多种，更优选为聚二甲基硅氧烷。本发明对所述流平剂的来源没有特殊限制，采用本领域技术人员熟知的上述硅油、聚二甲基硅氧烷、脉醛树脂和三聚氰胺甲醛树脂的市售商品即可。在本发明中，所述发泡浆料优选包括0.5重量份～1.5重量份的流平剂，更优选为1重量份。
在本发明中，所述稳定剂优选选自亚磷酸甲酯、亚磷酸乙酯、环氧大豆油、季戊四醇、钾锌稳定剂和钙锌稳定剂中的一种或多种，更优选为钾锌稳定剂。本发明对所述稳定剂的来源没有特殊限制，采用本领域技术人员熟知的上述亚磷酸甲酯、亚磷酸乙酯、环氧大豆油、季戊四醇、钾锌稳定剂和钙锌稳定剂的市售商品即可。在本发明中，所述发泡浆料优选包括1重量份～2重量份的稳定剂，更优选为1.5重量份。
在本发明中，所述发泡剂优选选自偶氮二甲酰胺、对氧化二苯磺酰肼和二亚硝基五次甲基四胺中的一种或多种。本发明对所述发泡剂的来源没有特殊限制，采用本领域技术人员熟知的市售商品即可。在本发明中，所述发泡浆料优选包括5重量份～10重量份的发泡剂，更优选为7重量份。
本发明对所述碳酸钙、钛白粉和艾草粉的来源没有特殊限制，采用本领域技术人员熟知的市售商品即可。在本发明中，所述发泡浆料优选包括10重量份～20重量份的碳酸钙，更优选为15重量份；所述发泡浆料优选包括25重量份～35重量份的钛白粉，更优选为30重量份；所述发泡浆料优选包括1重量份～3重量份的艾草粉，更优选为2重量份。
在本发明中，所述增稠剂优选选自甲基纤维素、淀粉、明胶、聚乙烯醇和聚氧化乙烯中的一种或多种，更优选为聚乙烯醇。本发明对所述增稠剂的来源没有特殊限制，采用本领域技术人员熟知的上述能够实现增稠作用的甲基纤维素、淀粉、明胶、聚乙烯醇和聚氧化乙烯的市售商品即可。在本发明中，所述发泡浆料优选包括2.5重量份～3.5重量份的增稠剂，更优选为3重量份。
在本发明中，所述抗菌剂优选选自氧化锌、氧化铜、磷酸二氢铵、碳酸锂、香草醛、壳聚糖、山梨酸、黄姜根醇、孟宗竹提取物、日柏醇、乙基香草醛类、酰基苯胺类、异噻唑酮衍生物、双呱类、季铵盐类、噻唑类、咪唑类和酚类中的一种或多种，更优选为孟宗竹提取物。本发明对所述抗菌剂的来源没有特殊限制，采用本领域技术人员熟知的上述能够实现抗菌作用的氧化锌、氧化铜、磷酸二氢铵、碳酸锂、香草醛、壳聚糖、山梨酸、黄姜根醇、孟宗竹提取物、日柏醇、乙基香草醛类、酰基苯胺类、异噻唑酮衍生物、双呱类、季铵盐类、噻唑类、咪唑类和酚类的市售商品即可。在本发明中，所述发泡浆料优选包括1重量份～5重量份的抗菌剂，更优选为1.5重量份。
在本发明中，所述溶剂优选选自乙酸乙酯、乙酸丁酯、甲酸乙酯和乙酸异丙酯中的一种或多种，更优选为乙酸丁酯。本发明对所述溶剂的来源没有特殊限制，采用本领域技术人员熟知的上述乙酸乙酯、乙酸丁酯、甲酸乙酯和乙酸异丙酯的市售商品即可。在本发明中，所述发泡浆料优选包括50重量份～100重量份的溶剂，更优选为75重量份。
在本发明中，所述CT触媒(C＝Charge(电荷)，T＝Transfer(移动)，触媒＝能催化和速进化学反应的物质)原理是：以CT粒子利用大气温度引发本身分子结构与污染粒子透过电荷移动，最后产生氧化及还原反应，将污染粒子结构分解，在不需要水及紫外光运作下等同每天24小时运作，大气中释放的热能会令CT触媒里的结晶震动，从而引致电荷移动；这电荷移动导致氧化和还原反应，能提供连续式的分解功能。CT触媒有别于光触媒，不需要光便可24小时运作并达到分解VOC的理想效能，同时可提供防霉、防菌、除臭等功能。同时CT触媒已取得国际，中国，日本专利号，并已于国际权威认可机构测试，如日本纺织协会、香港标准及检定中心及广州分析测试中心等作严格检定，得出结果无论在除甲醛、VOC等有毒气体外、防菌、防霉、安全及使用等效能都均比市面上所有空气净化产品更为优胜。在室温下，CT触媒的流动电荷会对周围的分子进行重复不断的氧化还原反应：
ACID–COOH+O2(+e)→CO2+H2O；
ALKALINE–(OH)+H→2H2O(+e)。
在本发明中，所述发泡浆料优选包括1重量份～5重量份的CT触媒，更优选为1.5重量份。
在本发明中，所述复合发泡层的过程优选具体为：
在所述图像区印刷发泡浆料，加热后形成发泡层。在本发明中，所述印刷发泡浆料的方式优选为圆网印刷、凹版印刷、凸版印刷或胶印，更优选为圆网印刷。
在本发明中，所述发泡层的厚度优选为0.5mm～1.5mm，更优选为1mm。
在本发明中，所述油墨层复合在所述发泡层表面，由油墨形成。在本发明中，所述油墨优选为水性油墨或溶剂型油墨，更优选为水性油墨。本发明对所述油墨的来源没有特殊限制，采用本领域技术人员熟知的上述水性油墨和溶剂型油墨的市售商品即可。
在本发明中，所述复合油墨层的过程优选具体为：
在所述发泡层上印刷油墨，形成油墨层。在本发明中，所述印刷油墨的方式优选为凸版印刷、圆网印刷或胶印，更优选为凸版印刷。
在本发明中，所述数码图像层通过数码打印形成，优选为UV图像层、数码直喷图像层或热升华直喷图像层，更优选为UV图像层；所述UV图像层通过UV打印的堆墨打印(白墨堆积)形成，具有较好的立体效果。在本发明中，所述数码图像层的厚度优选为0.05mm～1.5mm，更优选为1mm。
在本发明中，所述绣花层设置在所述刺绣区。本发明对所述设置绣花层的方式没有特殊限制，采用本领域技术人员熟知的人工绣花或电脑绣花的技术方案均可；在本发明优选的实施例中，采用电脑绣花的定位装置，在定位装置的作用下，可在基材层的任意位置上进行刺绣。
在本发明中，所述绣花层的厚度优选为0.1mm～3mm，更优选为1.5mm～2mm。
在本发明中，在印刷油墨层的同时在底色区印刷底色层，一方面，底色层的设置使壁纸的色彩更丰富，另一方面，油墨层与底色层同时印刷有效的节省墙画的生产步骤。
在本发明中，所述绣花层、图像层和底色区整体形成图案效果面。
在本发明中，所述保护层复合在所述图案效果面上；所述保护层优选由树脂组合物形成。在本发明中，所述树脂组合物优选包括以下组分：
丙烯酸酯乳液20重量份～40重量份；
聚氨酯乳液30重量份～45重量份；
水10重量份～20重量份；
乳化剂0.5重量份～1重量份；
十二碳醇酯5重量份～7重量份；
葡萄糖酸钠0.05重量份～0.3重量份；
纳米二氧化硅20重量份～30重量份；
功能助剂0重量份～5重量份。
本发明对所述树脂组合物中各原料的来源没有特殊限制，采用本领域技术人员熟知的市售商品(水为去离子水)即可；其中，所述功能助剂优选选自阻燃剂、哑光剂、耐磨填料、防水剂、除甲醛剂和防霉剂中的一种或多种，从而形成具有相应效果的保护层，使刺绣墙画在美观的同时又有更多、更强的功能性，丰富其应用领域，具有广阔的发展前景。
在本发明中，所述复合保护层的过程优选具体为：
在所述图案效果面上涂刷上述树脂组合物，形成保护层。在本发明中，所述保护层优选为透明保护层。
在本发明中，所述保护层的厚度优选为0.3mm～0.8mm，更优选为0.5mm。
本发明提供的刺绣墙画通过绣花层和图像层结合，绣花层使图案惟妙惟肖，图像层使图案颜色极其丰富，并有3D立体感(图像层为UV图像层时)，从而实现该刺绣墙画远看是画，近看是工艺品，并通过不同图案组合，实现虚实结合，相得益彰，色彩丰富，立体感强的效果，且成本低；同时本发明提供的刺绣墙画采用特定保护层，增强产品的耐摩擦性，减缓油墨的变色，增强防水性能以及方便刺绣墙画的清洁。
在本发明优选的实施例中，所述刺绣墙画具有三种层次的立体：第一是基材本身的立体，第二是UV图像层的立体，第三个是刺绣层的立体。
本发明还提供了一种上述技术方案所述的刺绣墙画的制备方法，包括以下步骤：
a)将所述基材层分为图像区、刺绣区和底色区；
b)在所述图像区印刷发泡浆料；
在所述发泡浆料及底色区上印刷油墨，分别形成油墨层和底色层，再将涂刷有发泡浆料的基材加热形成发泡层；
或在所述图像区通过数码打印得到数码图像层；
c)在所述刺绣区进行绣花，得到绣花层；
d)在所述绣花层、图像层和底色区整体涂刷树脂组合物，形成保护层，得到刺绣墙画。
本发明首先将所述基材层分为图像区、刺绣区和底色区；优选通过在基材层表面印刷图案轮廓线进行划分；所述印刷图案轮廓线优选印刷两条以上，并印刷底色，从而能够清晰地划分出图像区、刺绣区和底色区。在本发明中，所述图像区、刺绣区和底色区随机排布或规律排布，具体根据刺绣墙画的图案要求设置。在本发明中，所述基材层与上述技术方案中所述的相同，在此不再赘述。
之后，本发明先在所述图像区印刷发泡浆料；在所述发泡浆料及底色区上印刷油墨，分别形成油墨层和底色层，再将涂刷有发泡浆料的基材加热形成发泡层；或在所述图像区通过数码打印得到数码图像层；然后，在所述刺绣区进行绣花，得到绣花层。通过上述特定工艺步骤，实现印花发泡技术和绣花工艺相结合，进一步形成的绣花层使图案惟妙惟肖，图像层使图案颜色极其丰富，从而实现该刺绣墙画远看是画，近看是工艺品，并通过不同图案组合，实现虚实结合，相得益彰，色彩丰富，立体感强的效果，且成本低。
在本发明中，所述发泡浆料、油墨以及印刷发泡浆料的过程、印刷油墨的过程、数码图像层的形成过程均与上述技术方案中所述的相同，在此不再赘述。
在本发明中，所述加热优选为分段加热；所述分段加热包括第一阶段加热、第二阶段加热和第三阶段加热；所述第一阶段加热的温度优选为180℃～200℃，更优选为190℃；所述第二阶段加热的温度优选为190℃～220℃，更优选为210℃；所述第三阶段加热的温度优选为140℃～180℃，更优选为160℃。本发明采用上述分段加热的工艺，通过第一阶段和第二阶段的加热，可以使发泡浆料能充分的发泡，通过第三阶段的加热，可以使发泡更加均匀。
在本发明中，所述绣花的过程与上述技术方案中所述的相同，在此不再赘述。本发明对所述绣花的线没有特殊限制，如可采用本领域技术人员熟知的市售夜光线。
最后，本发明在所述绣花层、图像层和底色层整体涂刷树脂组合物，形成保护层，得到刺绣墙画。在本发明中，所述整体涂刷树脂组合物前，优选还包括：
采用感光墨水在所述绣花层和图像层周围勾勒轮廓，形成感光线条；从而使绣花层、图像层形成的整体图案效果更佳清晰，进一步增强立体感。
在本发明中，所述树脂组合物、整体涂刷树脂组合物的过程均与上述技术方案所述的相同，在此不再赘述。
本发明通过设置上述保护层，一方面可对发泡层和绣花层进行保护，另一方面增强所述刺绣墙画的耐摩擦性，减缓油墨的变色，增强防水性能以及方便刺绣墙画的清洁。
本发明提供了一种刺绣墙画及其制备方法，所述刺绣墙画包括：基材层；所述基材层由图像区、刺绣区和底色区组成；设置在所述图像区的图像层；所述图像层由复合在所述图像区表面的发泡层和复合在所述发泡层表面的油墨层组成，或为数码图像层；设置在所述刺绣区的绣花层；设置在底色区的底色层，所述绣花层、图像层和底色层整体形成图案效果面；复合在所述图案效果面上的保护层。与现有技术相比，本发明提供的刺绣墙画通过绣花层和图像层结合，绣花层使图案惟妙惟肖，图像层使图案颜色极其丰富，从而实现该刺绣墙画远看是画，近看是工艺品，并通过不同图案组合，实现虚实结合，相得益彰，色彩丰富，立体感强的效果，且成本低；同时本发明提供的刺绣墙画采用特定保护层，增强产品的耐摩擦性，减缓油墨的变色，增强防水性能以及方便刺绣墙画的清洁。
另外，本发明提供的刺绣墙画能够通过对发泡层、保护层的组分改进，使刺绣墙画在美观的同时又有更多、更强的功能性，丰富其应用领域，具有广阔的发展前景。
为了进一步说明本发明，下面通过以下实施例进行详细说明。本发明以下实施例所用的原材料均为市售商品。
实施例1
(1)在厚度为1mm的无纺布表面印刷图案轮廓线，划分出图像区、刺绣区和底色区；
(2)在所述图像区圆网印刷发泡浆料(所述发泡浆料包括以下组分：丙烯酸酯树脂120重量份，聚二甲基硅氧烷1重量份，钾锌稳定剂1.5重量份，发泡剂7重量份，碳酸钙15重量份，钛白粉30重量份，聚乙烯醇3重量份，艾草粉2重量份，孟宗竹提取物1.5重量份，乙酸丁酯75重量份，CT触媒1.5重量份)，干燥后形成发泡浆料层，在发泡浆料层及底色区上凸版印刷水性油墨，分别形成油墨层和底色层，加热(分段加热，包括第一阶段加热、第二阶段加热和第三阶段加热；所述第一阶段加热的温度为190℃；所述第二阶段加热的温度为210℃；所述第三阶段加热的温度为160℃)后形成厚度为1mm的发泡层从而在所述图像区得到图像层；
(3)在所述刺绣区用夜光线进行电脑绣花，得到厚度为1.5mm～2mm的绣花层；另外，采用感光墨水在所述绣花层和图像层周围勾勒轮廓，形成感光线条；
(4)在所述绣花层、图像层和底色层整体涂刷树脂组合物(所述树脂组合物包括以下组分：丙烯酸酯乳液30重量份，聚氨酯乳液40重量份，水15重量份，乳化剂0.8重量份，十二碳醇酯6重量份，葡萄糖酸钠0.15重量份，纳米二氧化硅25重量份，耐磨填料2.5重量份)，形成厚度为0.5mm的保护层，得到刺绣墙画。
本发明实施例1提供的刺绣墙画的结构示意图参见图3所示，其中，1为基材层，3为绣花层，5为保护层，7为发泡层，8为油墨层，9为底色层。
实施例2
采用实施例1提供的制备方法得到刺绣墙画；区别在于：所述发泡浆料包括以下组分：丙烯酸酯树脂120重量份，聚二甲基硅氧烷1重量份，钾锌稳定剂1.5重量份，发泡剂7重量份，碳酸钙15重量份，钛白粉30重量份，聚乙烯醇3重量份，艾草粉2重量份，磷酸二氢铵3重量份，乙酸丁酯75重量份，CT触媒2重量份。
实施例3
采用实施例1提供的制备方法得到刺绣墙画；区别在于：所述发泡浆料包括以下组分：丙烯酸酯树脂120重量份，聚二甲基硅氧烷1重量份，钾锌稳定剂1.5重量份，发泡剂7重量份，碳酸钙15重量份，钛白粉30重量份，聚乙烯醇3重量份，艾草粉2重量份，磷酸二氢铵5重量份，乙酸丁酯75重量份，CT触媒5重量份。
对比例
市售普通的刺绣墙纸。
对实施例1～3和对比例所对应的产品进行耐摩擦检测、抗变色检测、防水性和易去污性进行测试。其中，检测方法如下：
1、耐摩擦检测：按照QB/T 4034-2010《壁纸》要求中耐摩擦色牢度中的方法进行测试，干摩擦25次，湿摩擦5次。
2、褪色性检测：按照QB/T 4034-2010《壁纸》要求中褪色性的方法进行测试。
3、防水性测试：按照GB/T 4745-2012《纺织品防水性能的检测和评价沾水法》中的喷淋法进行表面拒水性进行检测，其中，测试用水温为20℃。
4、易去污性的测试：按照FZ/T 01118-2012《防污性能的检测和评价易去污性》中的擦拭法，和使用沾污物酱油进行检测。
测试结果参见表1所示。
表1实施例1～3和对比例所对应的产品各项性能的检测结果
| 耐摩擦/级 | 褪色性/级 | 防水性能/级 | 易去污性能/级 | |
| 实施例1 | >4 | 4-5 | 4-5 | 4 |
| 实施例2 | >4 | 4-5 | 4-5 | 4 |
| 实施例3 | >4 | 4-5 | 4-5 | 4 |
| 对比例 | >4 | 3 | 2 | 2 |
由表1可知，本发明提供的刺绣墙画具有耐摩擦、减缓油墨的变色、防水及易清洁的优点；其中，耐摩擦等级大于4级，褪色性结果均为4-5级，防水性能为4-5级，易去污性能为4级。
所公开的实施例的上述说明，使本领域专业技术人员能够实现或使用本发明。对这些实施例的多种修改对本领域的专业技术人员来说将是显而易见的，本文中所定义的一般原理可以在不脱离本发明的精神或范围的情况下，在其它实施例中实现。因此，本发明将不会被限制于本文所示的这些实施例，而是要符合与本文所公开的原理和新颖特点相一致的最宽的范围。
Claims (10)
1.一种刺绣墙画，包括：
基材层；所述基材层由图像区、刺绣区和底色区组成；
设置在所述图像区的图像层；所述图像层由复合在所述图像区表面的发泡层和复合在所述发泡层表面的油墨层组成，或为数码图像层；
设置在所述刺绣区的绣花层；
设置在所述底色区的底色层；所述绣花层、图像层和底色层整体形成图案效果面；
复合在所述图案效果面上的保护层。
2.根据权利要求1所述的刺绣墙画，其特征在于，所述基材层为无纺纸、平织布、无纺布、油画布、星光布、宣绒布、仿真丝、麻布或染色布。
3.根据权利要求1所述的刺绣墙画，其特征在于，所述发泡层由发泡浆料形成；所述发泡浆料包括以下组分：
树脂100重量份～150重量份；
流平剂0.5重量份～1.5重量份；
稳定剂1重量份～2重量份；
发泡剂5重量份～10重量份；
碳酸钙10重量份～20重量份；
钛白粉25重量份～35重量份；
增稠剂2.5重量份～3.5重量份；
艾草粉1重量份～3重量份；
抗菌剂1重量份～5重量份；
溶剂50重量份～100重量份；
CT触媒1重量份～5重量份。
4.根据权利要求1所述的刺绣墙画，其特征在于，所述图像层的厚度为0.05mm～1.5mm。
5.根据权利要求1所述的刺绣墙画，其特征在于，所述绣花层的厚度为0.1mm～3mm。
6.根据权利要求1所述的刺绣墙画，其特征在于，所述保护层由树脂组合物形成；所述树脂组合物包括以下组分：
丙烯酸酯乳液20重量份～40重量份；
聚氨酯乳液30重量份～45重量份；
水10重量份～20重量份；
乳化剂0.5重量份～1重量份；
十二碳醇酯5重量份～7重量份；
葡萄糖酸钠0.05重量份～0.3重量份；
纳米二氧化硅20重量份～30重量份；
功能助剂0重量份～5重量份。
7.根据权利要求1所述的刺绣墙画，其特征在于，所述保护层的厚度为0.3mm～0.8mm。
8.一种权利要求1～7任一项所述的刺绣墙画的制备方法，包括以下步骤：
a)将所述基材层分为图像区、刺绣区和底色区；
b)在所述图像区印刷发泡浆料；
在所述发泡浆料及底色区上印刷油墨，分别形成油墨层及底色层，再将涂刷有发泡浆料的基材加热形成发泡层；
或在所述图像区通过数码打印得到数码图像层；
c)在所述刺绣区进行绣花，得到绣花层；
d)在所述绣花层、图像层和底色区整体涂刷树脂组合物，形成保护层，得到刺绣墙画。
9.根据权利要求8所述的制备方法，其特征在于，步骤b)中所述加热为分段加热；所述分段加热包括第一阶段加热、第二阶段加热和第三阶段加热；所述第一阶段加热的温度为180℃～200℃，所述第二阶段加热的温度为190℃～220℃，所述第三阶段加热的温度为140℃～180℃。
10.根据权利要求8所述的制备方法，其特征在于，步骤d)中所述整体涂刷树脂组合物前，还包括：
采用感光墨水在所述绣花层和图像层周围勾勒轮廓，形成感光线条。