CN111074597A - 一种涤棉织物的多功能后整理工艺 - Google Patents

一种涤棉织物的多功能后整理工艺 Download PDF

Info

Publication number
CN111074597A
CN111074597A CN201811212592.8A CN201811212592A CN111074597A CN 111074597 A CN111074597 A CN 111074597A CN 201811212592 A CN201811212592 A CN 201811212592A CN 111074597 A CN111074597 A CN 111074597A
Authority
CN
China
Prior art keywords
fabric
finishing
agent
multifunctional
company
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201811212592.8A
Other languages
English (en)
Inventor
陶晓华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangyin Chuangjiejia Clothing Co Ltd
Original Assignee
Jiangyin Chuangjiejia Clothing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangyin Chuangjiejia Clothing Co Ltd filed Critical Jiangyin Chuangjiejia Clothing Co Ltd
Priority to CN201811212592.8A priority Critical patent/CN111074597A/zh
Publication of CN111074597A publication Critical patent/CN111074597A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种涤棉织物的多功能后整理工艺，工艺步骤包括：将织物放入整理剂中于8‑16℃浸泡20‑30min，再于40‑50℃进行温热处理30‑40min后进行浸轧处理，轧液率为70‑80％，30‑35℃低温烘至7‑8成干；将烘至7‑8成干的织物放入培烘机中进行培烘处理，培烘温度110‑120℃，机车速为40‑50m/min；将培烘后的织物放入定型机中进行定型处理，定型温度100‑125℃，机车速为50‑65m/min；将定型结束后将织物进行收卷。所述整理剂，包括阻燃整理剂SCJ‑968 60‑80g/L、渗透剂OT 1‑3g/L、交联剂3‑5g/L、纳米银抗菌剂3‑6g/L、柔软剂GS‑550 20‑30g/L、紫外线吸收剂UV‑326 10‑20g/L、三防整理剂RHSF‑1 30‑40g/L。本发明能对织物同时进行抗菌、抗紫外、阻燃及其三防整理，简化了生产工艺，降低了生产成本，提高了生产效率，具有良好的市场推广价值。

Description

一种涤棉织物的多功能后整理工艺
技术领域
本发明涉及纺织技术后整理领域，具体地说，是一种涤棉织物的多功能后整理工艺。
背景技术
随着社会和经济的发展，人们生活水平的提高，单一功能的纺织品已远远不能满足人们的需求，多功能整理的纺织品因其优良的性能越来越得到人们的认可和使用。
织物的多功能后整理是通过化学或物理的方法改善织物的外观和手感、增进服用性能或赋予特殊功能（如抗菌、抗紫外、抗皱、防静电、防水防油防污、阻燃等）的工艺过程，是纺织品“锦上添花”的加工过程。
目前，织物的多功能整理往往是单一功能的整理工艺，要赋予织物多种功能，则需要通过多道整理工序依次对织物进行整理，整理过程繁杂，成本高，效率低下。
发明内容
本发明的目的在于克服上述不足，提供一种涤棉织物的多功能后整理工艺，能对织物同时进行抗菌、抗紫外、阻燃及其三防整理，简化生产工艺，降低生产成本，提高生产效率。
本发明一种涤棉织物的多功能后整理工艺，所采用的工艺步骤包括：将织物放入整理剂中于8-16℃浸泡20-30min，再于40-50℃进行温热处理30-40min后进行浸轧处理，轧液率为70-80％，30-35℃低温烘至7-8成干；将烘至7-8成干的织物放入培烘机中进行培烘处理，培烘温度110-120℃，机车速为40-50m/min；将培烘后的织物放入定型机中进行定型处理，定型温度100-125℃，机车速为50-65m/min；将定型结束后将织物进行收卷；
所述整理剂，包括北京洁尔爽高科技公司的阻燃整理剂SCJ-968 60-80g/L、淄博海杰化工公司的渗透剂OT 1-3g/L、交联剂3-5g/L、纳米银抗菌剂 3-6g/L、宁波市鄞州建国化工助剂厂的柔软剂GS-550 20-30g/L、巴斯夫公司的紫外线吸收剂UV-326 10-20g/L、上海环谷新材料科技公司的三防整理剂RHSF-1 30-40g/L。
优选的，所述整理剂包括北京洁尔爽高科技公司的阻燃整理剂SCJ-968 70g/L、淄博海杰化工公司的渗透剂OT 2g/L 、交联剂4g/L、纳米银抗菌剂 4.5g/L、宁波市鄞州建国化工助剂厂的柔软剂GS-550 25g/L、巴斯夫公司的紫外线吸收剂UV-326 15g/L、上海环谷新材料科技公司的三防整理剂RHSF-1 35g/L。
优选的，所述交联剂，为聚马来酸。
优选的，所述浸轧处理为二浸二轧工艺。
优选的，所述培烘温度115℃，机车速为45m/min。
优选的，所述定型温度110℃，机车速为60m/min。
本发明的有益效果：能对织物同时进行抗菌、抗紫外、阻燃及其三防整理，简化了生产工艺，降低了生产成本，提高了生产效率，具有良好的市场推广价值。
具体实施方式
实施例1
一种涤棉织物的多功能后整理工艺，所采用的工艺步骤包括：将织物放入整理剂中于8℃浸泡30min，再于40℃进行温热处理40min后进行二浸二轧处理，轧液率为70％，30℃低温烘至7成干；将烘至7成干的织物放入培烘机中进行培烘处理，培烘温度110℃，机车速为40m/min；将培烘后的织物放入定型机中进行定型处理，定型温度100℃，机车速为50m/min；将定型结束后将织物进行收卷；所述整理剂，包括北京洁尔爽高科技公司的阻燃整理剂SCJ-968 60g/L、淄博海杰化工公司的渗透剂OT 1g/L、聚马来酸交联剂3g/L、纳米银抗菌剂3g/L、宁波市鄞州建国化工助剂厂的柔软剂GS-550 20g/L、巴斯夫公司的紫外线吸收剂UV-326 10g/L、上海环谷新材料科技公司的三防整理剂RHSF-1 30g/L。
实施例2
一种涤棉织物的多功能后整理工艺，所采用的工艺步骤包括：将织物放入整理剂中于12℃浸泡25min，再于45℃进行温热处理35min后进行二浸二轧处理，轧液率为75％，33℃低温烘至8成干；将烘至8成干的织物放入培烘机中进行培烘处理，培烘温度115℃，机车速为45m/min；将培烘后的织物放入定型机中进行定型处理，定型温度110℃，机车速为60m/min；将定型结束后将织物进行收卷；所述整理剂包括北京洁尔爽高科技公司的阻燃整理剂SCJ-968 70g/L、淄博海杰化工公司的渗透剂OT 2g/L、聚马来酸交联剂4g/L、纳米银抗菌剂4.5g/L、宁波市鄞州建国化工助剂厂的柔软剂GS-550 25g/L、巴斯夫公司的紫外线吸收剂UV-326 15g/L、上海环谷新材料科技公司的三防整理剂RHSF-1 35g/L。
实施例3
一种涤棉织物的多功能后整理工艺，所采用的工艺步骤包括：将织物放入整理剂中于16℃浸泡20min，再于50℃进行温热处理30min后进行二浸二轧处理，轧液率为80％，35℃低温烘至8成干；将烘至8成干的织物放入培烘机中进行培烘处理，培烘温度120℃，机车速为50m/min；将培烘后的织物放入定型机中进行定型处理，定型温度125℃，机车速为65m/min；将定型结束后将织物进行收卷；所述整理剂包括北京洁尔爽高科技公司的阻燃整理剂SCJ-968 70g/L、淄博海杰化工公司的渗透剂OT 2g/L、聚马来酸交联剂4g/L、纳米银抗菌剂 6g/L、宁波市鄞州建国化工助剂厂的柔软剂GS-550 25g/L、巴斯夫公司的紫外线吸收剂UV-32620g/L、上海环谷新材料科技公司的三防整理剂RHSF-1 35g/L。
以上已对本发明创造的较佳实施例进行了具体说明，但本发明创造并不限于所述实施例，熟悉本领域的技术人员在不违背本发明创造精神的前提下还可做出种种的等同的变型或替换，这些等同的变型或替换均包含在本申请权利要求所限定的范围内。

Claims (6)

1.一种涤棉织物的多功能后整理工艺，其特征在于，所采用的工艺步骤包括：将织物放入整理剂中于8-16℃浸泡20-30min，再于40-50℃进行温热处理30-40min后进行浸轧处理，轧液率为70-80％，30-35℃低温烘至7-8成干；将烘至7-8成干的织物放入培烘机中进行培烘处理，培烘温度110-120℃，机车速为40-50m/min；将培烘后的织物放入定型机中进行定型处理，定型温度100-125℃，机车速为50-65m/min；将定型结束后将织物进行收卷；
所述整理剂，包括北京洁尔爽高科技公司的阻燃整理剂SCJ-968 60-80g/L、淄博海杰化工公司的渗透剂OT 1-3g/L、交联剂3-5g/L、纳米银抗菌剂 3-6g/L、宁波市鄞州建国化工助剂厂的柔软剂GS-550 20-30g/L、巴斯夫公司的紫外线吸收剂UV-326 10-20g/L、上海环谷新材料科技公司的三防整理剂RHSF-1 30-40g/L。
2.如权利要求1所述的一种涤棉织物的多功能后整理工艺，其特征在于，所述整理剂包括北京洁尔爽高科技公司的阻燃整理剂SCJ-968 70g/L、淄博海杰化工公司的渗透剂OT2g/L、交联剂4g/L、纳米银抗菌剂 4.5g/L、宁波市鄞州建国化工助剂厂的柔软剂GS-55025g/L、巴斯夫公司的紫外线吸收剂UV-326 15g/L、上海环谷新材料科技公司的三防整理剂RHSF-1 35g/L。
3.如权利要求1和2所述的一种涤棉织物的多功能后整理工艺，其特征在于，所述交联剂，为聚马来酸。
4.如权利要求1-3所述的一种涤棉织物的多功能后整理工艺，其特征在于，所述浸轧的方式为二浸二轧。
5.如权利要求1-4所述的一种涤棉织物的多功能后整理工艺，其特征在于，所述培烘温度115℃，机车速为45m/min。
6.如权利要求1-5所述的一种涤棉织物的多功能后整理工艺，其特征在于，所述定型温度110℃，机车速为60m/min。
CN201811212592.8A 2018-10-18 2018-10-18 一种涤棉织物的多功能后整理工艺 Withdrawn CN111074597A (zh)