CN111058573A - Waterproof roof and construction method thereof - Google Patents
Waterproof roof and construction method thereof Download PDFInfo
- Publication number
- CN111058573A CN111058573A CN201911261763.0A CN201911261763A CN111058573A CN 111058573 A CN111058573 A CN 111058573A CN 201911261763 A CN201911261763 A CN 201911261763A CN 111058573 A CN111058573 A CN 111058573A
- Authority
- CN
- China
- Prior art keywords
- parts
- waterproof
- roof
- layer
- waterproofing membrane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a waterproof roof and a construction method of the waterproof roof, and relates to the technical field of building roofs. This waterproof roof, including the roof covering, the upper surface of roof covering is provided with the enhancement layer, the upper surface of enhancement layer is provided with the waterproof glue, the upper surface of waterproof glue is provided with a plurality of waterproofing membrane, one side fixedly connected with laminating strip of waterproofing membrane, the laminating groove has been seted up to waterproofing membrane's opposite side, and one of them waterproofing membrane's laminating strip is located another adjacent waterproofing membrane's laminating inslot portion. According to the invention, two waterproof rolls can be stably and seamlessly connected together, and meanwhile, the adhesive force of the waterproof adhesive is improved by carrying out sand blasting treatment on the surface of the reinforcing layer, so that the waterproof rolls can be adhered to the surface of the reinforcing layer for a long time, the situation that the waterproof rolls are wrinkled is avoided, the service life of the waterproof rolls is prolonged, and the waterproof capability of a roof is further improved.
Description
Technical Field
The invention relates to the technical field of building roofs, in particular to a waterproof roof and a construction method of the waterproof roof.
Background
The roof is an external protection component on the uppermost layer of the building, is used for resisting the influence of adverse factors such as rain, snow, wind, frost, solar radiation, temperature change and the like in the nature, ensures that a good use environment exists in the building, and can meet the functional requirements of firmness, durability, water resistance, heat preservation, heat insulation, fire prevention and resistance to various adverse effects, the roof can be divided into a flat roof and a sloping roof, the flat roof refers to a roof with the roof gradient less than or equal to 5 percent, the common gradient is 2 to 3 percent, and the roof can be divided into a manned roof and a non-manned roof, the gradient of the manned roof is 1 to 2 percent, and the plane roof is provided with cornice, parapet and cornice parapet and the like in the common form; the sloping roof refers to a roof with the slope of more than 10 percent; the sloping roof is formed by connecting inclined planes with the same gradient, and the common forms of the sloping roof comprise a single-slope type, a hard-hill type, a suspended-hill type, a four-slope type, a rolling shed type and the like; other roofs are more in types, such as hyperbolic arch type, masonry arch type, cylindrical shell type, spherical net shell type, V-shaped net shell type flat shell type, wheel-shaped suspension cable type, saddle-shaped suspension cable type and the like.
The traditional waterproof roof is generally only paved with a layer of waterproof coiled material simply on the roof of a building, although the method can also have a certain waterproof effect on the roof, the time is long, the joint of the waterproof coiled material is easy to enter water, so that the roof can have a certain amount of water more or less, and the existing waterproof coiled material is easy to wrinkle, thereby losing the waterproof capability.
Disclosure of Invention
Technical problem to be solved
Aiming at the defects of the prior art, the invention provides a waterproof roof and a construction method of the waterproof roof, and solves the problems that the joint of a waterproof coiled material is easy to enter water, so that the roof is more or less provided with certain water, and the existing waterproof coiled material is easy to wrinkle, so that the waterproof capability is lost.
(II) technical scheme
In order to achieve the purpose, the invention is realized by the following technical scheme: the utility model provides a waterproof roof, includes the roof covering, the upper surface of roof covering is provided with the enhancement layer, the upper surface of enhancement layer is provided with the waterproof glue, the upper surface of waterproof glue is provided with a plurality of waterproofing membrane, one side fixedly connected with laminating strip of waterproofing membrane, the laminating groove has been seted up to waterproofing membrane's opposite side, and one of them waterproofing membrane's laminating strip is located another adjacent waterproofing membrane's laminating inslot portion.
Preferably, the thickness of the reinforcing layer is 10-15mm, and the thickness of the waterproof glue is 1-2 mm.
Preferably, the length of the attaching strip is the same as that of the waterproof roll.
A construction method of a waterproof roof comprises the following construction steps:
s1, surface treatment: treating the surface of the roof layer, removing foreign matters on the surface of the roof layer, cleaning oil stains, paint and the like on the surface of the roof layer by using a cleaning agent, then washing the surface of the roof layer by using clear water, and finally drying the surface of the roof layer;
s2, pouring: preparing pouring raw materials, wherein 100-200 parts of concrete, 10-20 parts of rubber particles, 6-10 parts of fine fiber stone, 1-2 parts of air entraining agent, 3-4 parts of rust inhibitor, 2-3 parts of accelerator and 3-5 parts of antifreeze agent, putting the concrete, the rubber particles, the fine fiber stone, the air entraining agent, the rust inhibitor, the accelerator and the antifreeze agent into a stirrer, simultaneously adding a proper amount of water into the stirrer, uniformly stirring and then discharging, pouring the stirred mixture on the surface of a roof layer, wherein the poured thickness is 10-15mm, and drying to obtain a reinforcing layer;
s3, sand blasting: performing sand blasting treatment on the surface of the reinforcing layer to improve the roughness of the surface of the reinforcing layer;
s4, gluing: after the sand blasting treatment is finished, uniformly coating a layer of waterproof glue on the surface of the reinforcing layer, wherein the thickness of the waterproof glue is 1-2 mm;
s5, laying coiled materials: the waterproof roll is laid on the waterproof glue according to specifications, the waterproof roll is bonded on the surface of the reinforcing layer by the waterproof glue, then a layer of glue is coated on the upper surface and the lower surface of each bonding strip, the bonding strips coated with the glue are plugged into the bonding grooves of the adjacent waterproof rolls, the joints of the two adjacent waterproof rolls are compacted by the compression rollers, and the laying of all the waterproof rolls is completed according to the method.
Preferably, the particle size of the rubber particles is 100-200 meshes.
Preferably, the pouring raw material comprises the following components in parts by weight: 100 parts of concrete, 10 parts of rubber particles, 6 parts of fine fiber stone, 1 part of air entraining agent, 3 parts of rust inhibitor, 2 parts of accelerator and 3 parts of antifreeze.
Preferably, the pouring raw material comprises the following components in parts by weight: 150 parts of concrete, 15 parts of rubber particles, 8 parts of fine fiber stone, 1.5 parts of air entraining agent, 3.5 parts of rust inhibitor, 2.5 parts of accelerator and 4 parts of antifreezing agent.
Preferably, the pouring raw material comprises the following components in parts by weight: 200 parts of concrete, 20 parts of rubber particles, 10 parts of fine fiber stone, 2 parts of air entraining agent, 4 parts of rust inhibitor, 3 parts of accelerator and 5 parts of antifreezing agent.
(III) advantageous effects
The invention provides a waterproof roof and a construction method of the waterproof roof. The method has the following beneficial effects:
1. this waterproof roof and waterproof roof's construction method, bond waterproofing membrane on the surface of enhancement layer through the waterproof glue, then one deck glue is all scribbled on the upper and lower surface of laminating strip, the laminating inslot portion of adjacent waterproofing membrane is filled in to the laminating strip that will scribble glue again, make two seamless connection that waterproofing membrane can be stable together, simultaneously through carrying out the sand blasting to the enhancement layer surface and handling, the adhesive force of waterproof glue has been improved, thereby make waterproofing membrane can be long-time bonding on the enhancement layer surface, the condition that waterproofing membrane corrugates has been avoided, waterproofing membrane's life has been prolonged, roofing waterproof ability has further been improved.
2. According to the waterproof roof and the construction method thereof, the roof is poured by mixing the concrete, the rubber particles, the fine fiber stone, the air entraining agent, the rust inhibitor, the accelerator and the antifreeze, so that the pressure resistance and various performances of the roof are greatly improved.
Drawings
FIG. 1 is a schematic structural view of the present invention;
FIG. 2 is a flow chart of the construction process of the present invention.
Wherein, 1, roof layer; 2. a reinforcing layer; 3. waterproof glue; 4. waterproof coiled materials; 5. fitting strips; 6. and fitting the groove.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the drawings in the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
The first embodiment is as follows:
as shown in fig. 1-2, an embodiment of the present invention provides a waterproof roof, including a roof layer 1, wherein a reinforcing layer 2 is disposed on an upper surface of the roof layer 1, a thickness of the reinforcing layer 2 is 10-15mm, a waterproof adhesive 3 is disposed on an upper surface of the reinforcing layer 2, a thickness of the waterproof adhesive 3 is 1-2mm, a plurality of waterproof rolls 4 are disposed on an upper surface of the waterproof adhesive 3, a fitting strip 5 is fixedly connected to one side of each waterproof roll 4, a fitting groove 6 is disposed on the other side of each waterproof roll 4, the fitting strip 5 of one waterproof roll 4 is located inside the fitting groove 6 of another adjacent waterproof roll 4, and a length of the fitting strip 5 is the same as a length of each waterproof roll 4.
A construction method of a waterproof roof comprises the following construction steps:
s1, surface treatment: treating the surface of the roof layer 1, removing foreign matters on the surface of the roof layer 1, cleaning oil stains, paint and the like on the surface of the roof layer 1 by using a cleaning agent, then washing the surface of the roof layer 1 by using clear water, and finally drying the surface of the roof layer 1;
s2, pouring: preparing a pouring raw material, wherein the pouring raw material comprises the following components in parts by weight: 100 parts of concrete, 10 parts of rubber particles, 6 parts of fine fiber stone, 1 part of air entraining agent, 3 parts of rust inhibitor, 2 parts of accelerator and 3 parts of antifreeze, wherein the granularity of the rubber particles is 100-200 meshes, the concrete, the rubber particles, the fine fiber stone, the air entraining agent, the rust inhibitor, the accelerator and the antifreeze are put into a stirrer, simultaneously, a proper amount of water is added into the stirrer, the mixture is discharged after being uniformly stirred, the mixed material after being stirred is poured on the surface of a roof layer 1, the poured thickness is 10-15mm, and the reinforcing layer 2 is obtained after drying;
s3, sand blasting: carrying out sand blasting treatment on the surface of the reinforcing layer 2 to improve the roughness of the surface of the reinforcing layer 2;
s4, gluing: after the sand blasting treatment is finished, uniformly coating a layer of waterproof glue 3 on the surface of the reinforcing layer 2, wherein the thickness of the waterproof glue 3 is 1-2 mm;
s5, laying coiled materials: laying waterproof roll 4 on waterproof glue 3 according to the specification, utilizing waterproof glue 3 to bond waterproof roll 4 on the surface of enhancement layer 2, then all coating a layer of glue on the upper and lower surface of laminating strip 5, again will scribble the laminating strip 5 of glue and fill in into the laminating groove 6 inside of adjacent waterproof roll 4, utilize the compression roller to compact the junction of two adjacent waterproof roll 4, according to above-mentioned method, accomplish laying of all waterproof roll 4 can.
Example two:
as shown in fig. 1-2, an embodiment of the present invention provides a method for constructing a waterproof roof, including the following steps:
s1, surface treatment: treating the surface of the roof layer 1, removing foreign matters on the surface of the roof layer 1, cleaning oil stains, paint and the like on the surface of the roof layer 1 by using a cleaning agent, then washing the surface of the roof layer 1 by using clear water, and finally drying the surface of the roof layer 1;
s2, pouring: preparing a pouring raw material, wherein the pouring raw material comprises the following components in parts by weight: 150 parts of concrete, 15 parts of rubber particles, 8 parts of fine fiber stone, 1.5 parts of air entraining agent, 3.5 parts of rust inhibitor, 2.5 parts of accelerator and 4 parts of antifreezing agent, wherein the granularity of the rubber particles is 100 meshes, the concrete, the rubber particles, the fine fiber stone, the air entraining agent, the rust inhibitor, the accelerator and the antifreezing agent are put into a stirrer, meanwhile, a proper amount of water is added into the stirrer, the materials are discharged after uniform stirring, the stirred mixture is poured on the surface of the roof layer 1, the poured thickness is 10-15mm, and the reinforcing layer 2 is obtained after drying;
s3, sand blasting: carrying out sand blasting treatment on the surface of the reinforcing layer 2 to improve the roughness of the surface of the reinforcing layer 2;
s4, gluing: after the sand blasting treatment is finished, uniformly coating a layer of waterproof glue 3 on the surface of the reinforcing layer 2, wherein the thickness of the waterproof glue 3 is 1-2 mm;
s5, laying coiled materials: laying waterproof roll 4 on waterproof glue 3 according to the specification, utilizing waterproof glue 3 to bond waterproof roll 4 on the surface of enhancement layer 2, then all coating a layer of glue on the upper and lower surface of laminating strip 5, again will scribble the laminating strip 5 of glue and fill in into the laminating groove 6 inside of adjacent waterproof roll 4, utilize the compression roller to compact the junction of two adjacent waterproof roll 4, according to above-mentioned method, accomplish laying of all waterproof roll 4 can.
Example three:
as shown in fig. 1-2, an embodiment of the present invention provides a method for constructing a waterproof roof, including the following steps:
s1, surface treatment: treating the surface of the roof layer 1, removing foreign matters on the surface of the roof layer 1, cleaning oil stains, paint and the like on the surface of the roof layer 1 by using a cleaning agent, then washing the surface of the roof layer 1 by using clear water, and finally drying the surface of the roof layer 1;
s2, pouring: preparing a pouring raw material, wherein the pouring raw material comprises the following components in parts by weight: 200 parts of concrete, 20 parts of rubber particles, 10 parts of fine fiber stone, 2 parts of air entraining agent, 4 parts of rust inhibitor, 3 parts of accelerator and 5 parts of antifreeze, wherein the granularity of the rubber particles is 100-mesh and 200-mesh, the concrete, the rubber particles, the fine fiber stone, the air entraining agent, the rust inhibitor, the accelerator and the antifreeze are put into a stirrer, simultaneously, a proper amount of water is added into the stirrer, the mixture is discharged after being uniformly stirred, the stirred mixture is poured on the surface of a roof layer 1, the poured thickness is 10-15mm, and the reinforcing layer 2 is obtained after drying;
s3, sand blasting: carrying out sand blasting treatment on the surface of the reinforcing layer 2 to improve the roughness of the surface of the reinforcing layer 2;
s4, gluing: after the sand blasting treatment is finished, uniformly coating a layer of waterproof glue 3 on the surface of the reinforcing layer 2, wherein the thickness of the waterproof glue 3 is 1-2 mm;
s5, laying coiled materials: laying waterproof roll 4 on waterproof glue 3 according to the specification, utilizing waterproof glue 3 to bond waterproof roll 4 on the surface of enhancement layer 2, then all coating a layer of glue on the upper and lower surface of laminating strip 5, again will scribble the laminating strip 5 of glue and fill in into the laminating groove 6 inside of adjacent waterproof roll 4, utilize the compression roller to compact the junction of two adjacent waterproof roll 4, according to above-mentioned method, accomplish laying of all waterproof roll 4 can.
Although embodiments of the present invention have been shown and described, it will be appreciated by those skilled in the art that changes, modifications, substitutions and alterations can be made in these embodiments without departing from the principles and spirit of the invention, the scope of which is defined in the appended claims and their equivalents.
Claims (8)
1. A waterproof roof, comprising a roof layer (1), characterized in that: the upper surface of roof boarding (1) is provided with enhancement layer (2), the upper surface of enhancement layer (2) is provided with waterproof glue (3), the upper surface of waterproof glue (3) is provided with a plurality of waterproofing membrane (4), one side fixedly connected with laminating strip (5) of waterproofing membrane (4), laminating groove (6) have been seted up to the opposite side of waterproofing membrane (4), and laminating strip (5) of one of them waterproofing membrane (4) are located inside laminating groove (6) of another adjacent waterproofing membrane (4).
2. A water-resistant roof covering as claimed in claim 1, characterised in that: the thickness of the reinforcing layer (2) is 10-15mm, and the thickness of the waterproof glue (3) is 1-2 mm.
3. A water-resistant roof covering as claimed in claim 1, characterised in that: the length of the attaching strip (5) is the same as that of the waterproof roll (4).
4. A construction method of a waterproof roof is characterized in that: the method comprises the following construction steps:
s1, surface treatment: treating the surface of the roof layer (1), removing foreign matters on the surface of the roof layer (1), cleaning oil stains, paint and the like on the surface of the roof layer (1) by using a cleaning agent, then washing the surface of the roof layer (1) by using clear water, and finally drying the surface of the roof layer (1);
s2, pouring: preparing pouring raw materials, wherein 100-200 parts of concrete, 10-20 parts of rubber particles, 6-10 parts of fine fiber stone, 1-2 parts of air entraining agent, 3-4 parts of rust inhibitor, 2-3 parts of accelerator and 3-5 parts of antifreeze agent, putting the concrete, the rubber particles, the fine fiber stone, the air entraining agent, the rust inhibitor, the accelerator and the antifreeze agent into a stirrer, simultaneously adding a proper amount of water into the stirrer, uniformly stirring and discharging, pouring the stirred mixture onto the surface of the roof layer (1), wherein the pouring thickness is 10-15mm, and drying to obtain the reinforcing layer (2);
s3, sand blasting: carrying out sand blasting treatment on the surface of the reinforcing layer (2) to improve the roughness of the surface of the reinforcing layer (2);
s4, gluing: after the sand blasting treatment is finished, uniformly coating a layer of waterproof glue (3) on the surface of the reinforcing layer (2), wherein the thickness of the waterproof glue (3) is 1-2 mm;
s5, laying coiled materials: lay waterproofing membrane (4) on waterproof glue (3) according to the specification, utilize waterproof glue (3) to bond waterproofing membrane (4) on the surface of enhancement layer (2), then all coat one deck glue on the upper and lower surface of laminating strip (5), again with the laminating strip (5) of scribbling glue fill in inside laminating groove (6) of adjacent waterproofing membrane (4), utilize the compression roller with the junction compaction of two adjacent waterproofing membrane (4), according to above-mentioned method, accomplish the laying of all waterproofing membrane (4) can.
5. The construction method of the waterproof roof as claimed in claim 4, wherein: the granularity of the rubber particles is 100-200 meshes.
6. The construction method of the waterproof roof as claimed in claim 4, wherein: the pouring raw material comprises the following components in parts by weight: 100 parts of concrete, 10 parts of rubber particles, 6 parts of fine fiber stone, 1 part of air entraining agent, 3 parts of rust inhibitor, 2 parts of accelerator and 3 parts of antifreeze.
7. The construction method of the waterproof roof as claimed in claim 4, wherein: the pouring raw material comprises the following components in parts by weight: 150 parts of concrete, 15 parts of rubber particles, 8 parts of fine fiber stone, 1.5 parts of air entraining agent, 3.5 parts of rust inhibitor, 2.5 parts of accelerator and 4 parts of antifreezing agent.
8. The construction method of the waterproof roof as claimed in claim 4, wherein: the pouring raw material comprises the following components in parts by weight: 200 parts of concrete, 20 parts of rubber particles, 10 parts of fine fiber stone, 2 parts of air entraining agent, 4 parts of rust inhibitor, 3 parts of accelerator and 5 parts of antifreezing agent.