CN111040543A - Water-based ready-mixed paint with good adhesive force to various types of materials and preparation method thereof - Google Patents

Water-based ready-mixed paint with good adhesive force to various types of materials and preparation method thereof Download PDF

Info

Publication number
CN111040543A
CN111040543A CN201911356662.1A CN201911356662A CN111040543A CN 111040543 A CN111040543 A CN 111040543A CN 201911356662 A CN201911356662 A CN 201911356662A CN 111040543 A CN111040543 A CN 111040543A
Authority
CN
China
Prior art keywords
water
various types
materials
mixed paint
mixing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201911356662.1A
Other languages
Chinese (zh)
Inventor
江世奇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chengdu Dabao Chemical Products Co Ltd
Dongguan Taiho Chemical Industry Products Co ltd
Original Assignee
Chengdu Dabao Chemical Products Co Ltd
Dongguan Taiho Chemical Industry Products Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chengdu Dabao Chemical Products Co Ltd, Dongguan Taiho Chemical Industry Products Co ltd filed Critical Chengdu Dabao Chemical Products Co Ltd
Priority to CN201911356662.1A priority Critical patent/CN111040543A/en
Publication of CN111040543A publication Critical patent/CN111040543A/en
Pending legal-status Critical Current

Abstract

The invention relates to the technical field of coatings, in particular to a water-based ready mixed paint with good adhesive force to various types of materials and a preparation method thereof. Because the self-drying water-based acrylic emulsion is used for replacing the traditional solvent-based alkyd resin, the self-drying property of the water-based acrylic emulsion is utilized without adding a metal drier and a solvent, and the characteristics of reducing smell, reducing VOC and not containing heavy metal are achieved. The self-drying water-based acrylic emulsion has good adhesive force to various materials, and the water-based ready mixed paint has the advantages of low smell, low voc, no heavy metal and good rust prevention effect by adding the anti-flash rust agent. The preparation method has the characteristics of simple process, low production cost and suitability for large-scale production.

Description

Water-based ready-mixed paint with good adhesive force to various types of materials and preparation method thereof
Technical Field
The invention relates to the technical field of coatings, in particular to a water-based ready mixed paint with good adhesive force to various types of materials and a preparation method thereof.
Background
The traditional mixed paint is composed of alkyd resin, pigment, No. 200 solvent gasoline, drier and the like, and is ground and mixed to produce the paint with good adhesive force and antirust effect on metal surfaces. The traditional type of ready mixed paint has the defects of strong smell, high VOC, heavy metal content and the like due to the characteristics of raw materials.
However, with the continuous improvement of environmental protection requirements and market requirements, the mixed paint has the advantages of low odor, low voc and no heavy metal, has an antirust effect, and meanwhile, the mixed paint no longer only needs to meet the requirement of good adhesion to metal, and is often applied to mixed construction sites made of different materials such as wood, PVC, cement, ceramic tiles and the like during construction of users, or original old facilities are renovated. However, the ready-mixed paint in the prior art cannot be widely applied to type materials, and is mainly characterized by having the defect of poor adhesion.
Disclosure of Invention
One of the purposes of the invention is to provide the water-based ready-mixed paint with good adhesion to various types of materials, aiming at the defects of the prior art, and the water-based ready-mixed paint with good adhesion to various types of materials has the advantages of low smell, low voc, no heavy metal and good rust prevention effect.
The second purpose of the invention is to provide a preparation method of the water-based ready-mixed paint with good adhesive force to various types of materials aiming at the defects of the prior art.
In order to achieve one of the purposes, the invention adopts the following technical scheme:
the water-based ready-mixed paint with good adhesive force to various types of materials is provided, and comprises the following raw materials in parts by weight:
Figure BDA0002336116160000011
Figure BDA0002336116160000021
preferably, the water-based ready-mixed paint with good adhesive force to various types of materials comprises the following raw materials in parts by weight:
Figure BDA0002336116160000022
more preferably, the water-based ready-mixed paint with good adhesive force to various types of materials comprises the following raw materials in parts by weight:
Figure BDA0002336116160000023
Figure BDA0002336116160000031
the self-drying water-based acrylic emulsion is an acrylic emulsion which is commonly known as Coxcen 8196.
The dispersant is SN-DISPERSANT 5029 dispersant of Santonopodaceae;
the defoaming agent is a common DF-226 defoaming agent;
the flash rust inhibitor is an FR-355 flash rust inhibitor.
The pH regulator is a Dow AMP-95pH regulator;
the wetting agent is a coyen Genapol x 080 wetting agent;
the film-forming aid is a composition of dipropylene glycol butyl ether, alcohol ester dodecafilm-forming aid and propylene glycol;
the shake change assistant is a composition of Acrysol RM-3030 shake change assistant, Acrysol RM-8W shake change assistant and Acrysol RM-12W shake change assistant.
In order to achieve the second purpose, the invention adopts the following technical scheme:
the preparation method of the water-based ready-mixed paint with good adhesive force to various types of materials is provided, and comprises the following steps:
step one, color paste preparation: mixing the pigment, barium sulfate, mica powder, a dispersing agent, a defoaming agent and a part of water according to the formula ratio, stirring and mixing for a certain time at a certain rotating speed, and grinding to a certain fineness to obtain a color paste;
step two, preparing a second mixture: adding the formula amounts of the self-drying water-based acrylic emulsion, the flash rust inhibitor, the pH regulator and the wetting agent into the color paste obtained in the step one, and then stirring and mixing for a certain time at a certain rotating speed to obtain a second mixture;
step three, preparing a third mixture: adding the film-forming aid and the rest water in the formula amount into the second mixture obtained in the step two, and stirring and mixing for a certain time at a certain rotating speed to obtain a third mixture;
step four, preparing a product: and (4) adding a formula amount of shaking auxiliary agent into the third mixture obtained in the step three, and stirring and mixing for a certain time at a certain rotating speed to obtain the water-based ready mixed paint with good adhesive force to various types of materials.
In the technical scheme, in the first step, the mixture is stirred and mixed for 10min to 15min at the rotating speed of 950rpm to 1050rpm, and then the mixture is ground until the fineness is less than or equal to 15 microns, so that the color paste is obtained.
In the technical scheme, in the second step, stirring and mixing are carried out at the rotating speed of 550-650 rpm for 10-15 min to obtain a second mixture;
in the technical scheme, in the third step, the mixture is stirred and mixed for 10-15 min at the rotating speed of 750-850 rpm to prepare a third mixture.
In the technical scheme, in the fourth step, stirring and mixing are carried out at the rotating speed of 750-850 rpm for 10-15 min, and the water-based ready-mixed paint with good adhesive force to various types of materials is prepared.
In the technical scheme, the mass ratio of part of water in the first step to the rest of water in the third step is 0.8-1.2: 1.
Compared with the prior art, the invention has the beneficial effects that:
(1) the invention provides water-based ready-mixed paint with good adhesive force to various types of materials, which comprises self-drying water-based acrylic emulsion, pigment, barium sulfate, mica powder, a dispersing agent, a defoaming agent, water, an anti-flash rust agent, a pH regulator, a wetting agent, a film-forming aid and a shaking change aid. Because the self-drying water-based acrylic emulsion is used for replacing the traditional solvent-based alkyd resin, the self-drying property of the water-based acrylic emulsion is utilized without adding a metal drier and a solvent, and the characteristics of reducing smell, reducing VOC and not containing heavy metal are achieved. In addition, the self-drying water-based acrylic emulsion has good adhesive force to various types of materials, and the water-based ready mixed paint with good adhesive force to various types of materials has the advantages of low smell, low voc, no heavy metal and good antirust effect by adding the flash rust inhibitor.
(2) The preparation method of the water-based ready-mixed paint with good adhesive force to various types of materials provided by the invention has the characteristics of simple process, low production cost and suitability for large-scale production.
Detailed Description
In order to make the technical problems, technical solutions and advantageous effects solved by the present invention more apparent, the present invention is further described in detail below with reference to the following embodiments. It should be understood that the specific embodiments described herein are merely illustrative of the invention and are not intended to limit the invention.
Example 1.
A water-based ready-mixed paint with good adhesive force to various types of materials comprises the following raw materials in parts by weight:
Figure BDA0002336116160000041
Figure BDA0002336116160000051
wherein the self-drying water-based acrylic emulsion is an acrylic emulsion which is commonly known as Coxcen 8196.
Wherein the dispersant is SN-DISPERSANT 5029 dispersant of Santanoploaceae.
Wherein the defoaming agent is DF-226 defoaming agent.
Wherein the flash rust inhibitor is FR-355 flash rust inhibitor.
Wherein the pH regulator is Dow AMP-95pH regulator.
Wherein the wetting agent is a coyen Genapol x 080 wetting agent.
Wherein the film forming aid is a composition of dipropylene glycol butyl ether, an alcohol ester dodecafilm forming aid and propylene glycol.
Wherein the swing additive is a composition of Acrysol RM-3030 swing additive, Acrysol RM-8W swing additive and Acrysol RM-12W swing additive.
The preparation method of the water-based ready-mixed paint with good adhesive force to various types of materials comprises the following steps:
step one, color paste preparation: mixing the pigment, barium sulfate, mica powder, a dispersing agent, a defoaming agent and a part of water according to the formula ratio, stirring and mixing for 12min at the rotating speed of 1000rpm, and grinding until the fineness is less than or equal to 15 mu m to obtain color paste;
step two, preparing a second mixture: adding the self-drying water-based acrylic emulsion, the flash rust inhibitor, the pH regulator and the wetting agent in the formula amount into the color paste obtained in the step one, and then stirring and mixing at the rotating speed of 600rpm for 12min to obtain a second mixture;
step three, preparing a third mixture: adding the film-forming aid and the rest water in the formula amount into the second mixture obtained in the step two, and stirring and mixing at the rotating speed of 800rpm for 12min to obtain a third mixture;
step four, preparing a product: and (4) adding a formula amount of shaking auxiliary agent into the third mixture obtained in the step three, and then stirring and mixing at the rotating speed of 800rpm for 12min to obtain the water-based ready-mixed paint with good adhesive force to various types of materials.
In this embodiment, the mass ratio of a part of water in the first step to the rest of water in the third step is 1: 1.
Example 2.
A water-based ready-mixed paint with good adhesive force to various types of materials comprises the following raw materials in parts by weight:
Figure BDA0002336116160000061
wherein the self-drying water-based acrylic emulsion is an acrylic emulsion which is commonly known as Coxcen 8196.
Wherein the dispersant is SN-DISPERSANT 5029 dispersant of Santanoploaceae.
Wherein the defoaming agent is DF-226 defoaming agent.
Wherein the flash rust inhibitor is FR-355 flash rust inhibitor.
Wherein the pH regulator is Dow AMP-95pH regulator.
Wherein the wetting agent is a coyen Genapol x 080 wetting agent.
Wherein the film forming aid is a composition of dipropylene glycol butyl ether, an alcohol ester dodecafilm forming aid and propylene glycol.
Wherein the swing additive is a composition of Acrysol RM-3030 swing additive, Acrysol RM-8W swing additive and Acrysol RM-12W swing additive.
The preparation method of the water-based ready-mixed paint with good adhesive force to various types of materials comprises the following steps:
step one, color paste preparation: mixing the pigment, barium sulfate, mica powder, a dispersing agent, a defoaming agent and a part of water according to the formula ratio, stirring and mixing for 15min at the rotating speed of 950rpm, and grinding until the fineness is less than or equal to 15 mu m to obtain color paste;
step two, preparing a second mixture: adding the self-drying water-based acrylic emulsion, the flash rust inhibitor, the pH regulator and the wetting agent in the formula amount into the color paste obtained in the step one, and stirring and mixing for 15min at the rotating speed of 550rpm to obtain a second mixture;
step three, preparing a third mixture: adding the film-forming aid and the rest water in the formula amount into the second mixture obtained in the step two, and stirring and mixing for 15min at the rotating speed of 750rpm to obtain a third mixture;
step four, preparing a product: and (4) adding a formula amount of shaking auxiliary agent into the third mixture obtained in the step three, and then stirring and mixing at the rotating speed of 750rpm for 15min to obtain the water-based ready-mixed paint with good adhesive force to various types of materials.
In this example, the mass ratio of a part of water in the first step to the rest of water in the third step was 0.8: 1.
Example 3.
A water-based ready-mixed paint with good adhesive force to various types of materials comprises the following raw materials in parts by weight:
Figure BDA0002336116160000071
Figure BDA0002336116160000081
wherein the self-drying water-based acrylic emulsion is an acrylic emulsion which is commonly known as Coxcen 8196.
Wherein the dispersant is SN-DISPERSANT 5029 dispersant of Santanoploaceae.
Wherein the defoaming agent is DF-226 defoaming agent.
Wherein the flash rust inhibitor is FR-355 flash rust inhibitor.
Wherein the pH regulator is Dow AMP-95pH regulator.
Wherein the wetting agent is a coyen Genapol x 080 wetting agent.
Wherein the film forming aid is a composition of dipropylene glycol butyl ether, an alcohol ester dodecafilm forming aid and propylene glycol.
Wherein the swing additive is a composition of Acrysol RM-3030 swing additive, Acrysol RM-8W swing additive and Acrysol RM-12W swing additive.
The preparation method of the water-based ready-mixed paint with good adhesive force to various types of materials comprises the following steps:
step one, color paste preparation: mixing the pigment, barium sulfate, mica powder, a dispersing agent, a defoaming agent and a part of water according to the formula ratio, stirring and mixing for 10min at the rotating speed of 1050rpm, and grinding until the fineness is less than or equal to 15 mu m to obtain color paste;
step two, preparing a second mixture: adding the self-drying water-based acrylic emulsion, the flash rust inhibitor, the pH regulator and the wetting agent in the formula amount into the color paste obtained in the step one, and then stirring and mixing at the rotating speed of 650rpm for 10min to obtain a second mixture;
step three, preparing a third mixture: adding the film-forming aid and the rest water in the formula amount into the second mixture obtained in the step two, and stirring and mixing for 10min at the rotating speed of 850rpm to obtain a third mixture;
step four, preparing a product: and (4) adding a formula amount of shaking auxiliary agent into the third mixture obtained in the step three, and then stirring and mixing at the rotating speed of 850rpm for 10min to obtain the water-based ready-mixed paint with good adhesive force to various types of materials.
In this example, the mass ratio of a part of water in the first step to the rest of water in the third step is 1.2: 1.
Example 4.
A water-based ready-mixed paint with good adhesive force to various types of materials comprises the following raw materials in parts by weight:
Figure BDA0002336116160000091
wherein the self-drying water-based acrylic emulsion is an acrylic emulsion which is commonly known as Coxcen 8196.
Wherein the dispersant is SN-DISPERSANT 5029 dispersant of Santanoploaceae.
Wherein the defoaming agent is DF-226 defoaming agent.
Wherein the flash rust inhibitor is FR-355 flash rust inhibitor.
Wherein the pH regulator is Dow AMP-95pH regulator.
Wherein the wetting agent is a coyen Genapol x 080 wetting agent.
Wherein the film forming aid is a composition of dipropylene glycol butyl ether, an alcohol ester dodecafilm forming aid and propylene glycol.
Wherein the swing additive is a composition of Acrysol RM-3030 swing additive, Acrysol RM-8W swing additive and Acrysol RM-12W swing additive.
The preparation method of the water-based ready-mixed paint with good adhesive force to various types of materials comprises the following steps:
step one, color paste preparation: mixing the pigment, barium sulfate, mica powder, a dispersing agent, a defoaming agent and a part of water according to the formula ratio, stirring and mixing at the rotating speed of 980rpm for 14min, and grinding until the fineness is less than or equal to 15 mu m to obtain color paste;
step two, preparing a second mixture: adding the self-drying water-based acrylic emulsion, the flash rust inhibitor, the pH regulator and the wetting agent in the formula amount into the color paste obtained in the step one, and stirring and mixing at the rotating speed of 580rpm for 11min to obtain a second mixture;
step three, preparing a third mixture: adding the film-forming aid and the rest water in the formula amount into the second mixture obtained in the step two, and stirring and mixing for 14min at the rotating speed of 780rpm to obtain a third mixture;
step four, preparing a product: and (4) adding a formula amount of shaking auxiliary agent into the third mixture obtained in the step three, and then stirring and mixing at 780rpm for 14min to obtain the water-based ready-mixed paint with good adhesion to various types of materials.
In this example, the mass ratio of a part of water in the first step to the rest of water in the third step was 0.9: 1.
Example 5.
A water-based ready-mixed paint with good adhesive force to various types of materials comprises the following raw materials in parts by weight:
Figure BDA0002336116160000101
wherein the self-drying water-based acrylic emulsion is an acrylic emulsion which is commonly known as Coxcen 8196.
Wherein the dispersant is SN-DISPERSANT 5029 dispersant of Santanoploaceae.
Wherein the defoaming agent is DF-226 defoaming agent.
Wherein the flash rust inhibitor is FR-355 flash rust inhibitor.
Wherein the pH regulator is Dow AMP-95pH regulator.
Wherein the wetting agent is a coyen Genapol x 080 wetting agent.
Wherein the film forming aid is a composition of dipropylene glycol butyl ether, an alcohol ester dodecafilm forming aid and propylene glycol.
Wherein the swing additive is a composition of Acrysol RM-3030 swing additive, Acrysol RM-8W swing additive and Acrysol RM-12W swing additive.
The preparation method of the water-based ready-mixed paint with good adhesive force to various types of materials comprises the following steps:
step one, color paste preparation: mixing the pigment, barium sulfate, mica powder, a dispersing agent, a defoaming agent and a part of water according to the formula ratio, stirring and mixing for 11min at the rotating speed of 1030rpm, and grinding until the fineness is less than or equal to 15 mu m to obtain color paste;
step two, preparing a second mixture: adding the self-drying water-based acrylic emulsion, the flash rust inhibitor, the pH regulator and the wetting agent in the formula amount into the color paste obtained in the step one, and then stirring and mixing at the rotating speed of 620rpm for 11min to obtain a second mixture;
step three, preparing a third mixture: adding the film-forming aid and the rest water in the formula amount into the second mixture obtained in the step two, and stirring and mixing at the rotating speed of 820rpm for 11min to obtain a third mixture;
step four, preparing a product: and (4) adding a formula amount of shaking auxiliary agent into the third mixture obtained in the step three, and then stirring and mixing at the rotating speed of 820rpm for 11min to obtain the water-based ready-mixed paint with good adhesive force to various types of materials.
In this example, the mass ratio of a part of water in the first step to the rest of water in the third step was 1.1: 1.
Finally, it should be noted that the above embodiments are only used for illustrating the technical solutions of the present invention, and not for limiting the protection scope of the present invention, although the present invention is described in detail with reference to the preferred embodiments, it should be understood by those skilled in the art that modifications or equivalent substitutions can be made on the technical solutions of the present invention without departing from the spirit and scope of the technical solutions of the present invention.

Claims (10)

1. The water-based ready-mixed paint with good adhesive force to various types of materials is characterized in that: the composite material comprises the following raw materials in parts by weight:
Figure FDA0002336116150000011
2. the water-based ready-mixed paint with good adhesion to various types of materials as claimed in claim 1, wherein: the composite material comprises the following raw materials in parts by weight:
Figure FDA0002336116150000012
Figure FDA0002336116150000021
3. the water-based ready-mixed paint with good adhesion to various types of materials as claimed in claim 1, wherein: the composite material comprises the following raw materials in parts by weight:
Figure FDA0002336116150000022
4. the water-based ready-mixed paint with good adhesion to various types of materials as claimed in claim 1, wherein: the self-drying water-based acrylic emulsion is an acrylic emulsion which is commonly known as Coxcen 8196.
5. The water-based ready-mixed paint with good adhesion to various types of materials as claimed in claim 1, wherein: the dispersant is SN-DISPERSANT 5029 dispersant of Santonopodaceae;
the defoaming agent is a common DF-226 defoaming agent;
the flash rust inhibitor is an FR-355 flash rust inhibitor.
6. The water-based ready-mixed paint with good adhesion to various types of materials as claimed in claim 1, wherein: the pH regulator is a Dow AMP-95pH regulator;
the wetting agent is a coyen Genapol x 080 wetting agent;
the film-forming aid is a composition of dipropylene glycol butyl ether, alcohol ester dodecafilm-forming aid and propylene glycol;
the shake change assistant is a composition of Acrysol RM-3030 shake change assistant, Acrysol RM-8W shake change assistant and Acrysol RM-12W shake change assistant.
7. A method for preparing a water-based ready-mixed paint with good adhesion to various types of materials according to any one of claims 1 to 6, which is characterized in that: it comprises the following steps:
step one, color paste preparation: mixing the pigment, barium sulfate, mica powder, a dispersing agent, a defoaming agent and a part of water according to the formula ratio, stirring and mixing for a certain time at a certain rotating speed, and grinding to a certain fineness to obtain a color paste;
step two, preparing a second mixture: adding the formula amounts of the self-drying water-based acrylic emulsion, the flash rust inhibitor, the pH regulator and the wetting agent into the color paste obtained in the step one, and then stirring and mixing for a certain time at a certain rotating speed to obtain a second mixture;
step three, preparing a third mixture: adding the film-forming aid and the rest water in the formula amount into the second mixture obtained in the step two, and stirring and mixing for a certain time at a certain rotating speed to obtain a third mixture;
step four, preparing a product: and (4) adding a formula amount of shaking auxiliary agent into the third mixture obtained in the step three, and stirring and mixing for a certain time at a certain rotating speed to obtain the water-based ready mixed paint with good adhesive force to various types of materials.
8. The method for preparing the water-based ready-mixed paint with good adhesion to various types of materials according to claim 7, wherein the method comprises the following steps: in the first step, stirring and mixing at the rotating speed of 950-1050 rpm for 10-15 min, and grinding until the fineness is less than or equal to 15 mu m to obtain color paste;
and in the second step, stirring and mixing for 10-15 min at the rotating speed of 550-650 rpm to obtain a second mixture.
9. The method for preparing the water-based ready-mixed paint with good adhesion to various types of materials according to claim 7, wherein the method comprises the following steps: in the third step, stirring and mixing for 10-15 min at the rotating speed of 750-850 rpm to prepare a third mixture;
and in the fourth step, stirring and mixing at the rotating speed of 750-850 rpm for 10-15 min to obtain the water-based ready-mixed paint with good adhesive force to various types of materials.
10. The method for preparing the water-based ready-mixed paint with good adhesion to various types of materials according to claim 7, wherein the method comprises the following steps: the mass ratio of part of water in the first step to the rest of water in the third step is 0.8-1.2: 1.
CN201911356662.1A 2019-12-25 2019-12-25 Water-based ready-mixed paint with good adhesive force to various types of materials and preparation method thereof Pending CN111040543A (en)