CN110965176A - 一种苯并三唑类抗紫外线面料的制备方法 - Google Patents

一种苯并三唑类抗紫外线面料的制备方法 Download PDF

Info

Publication number
CN110965176A
CN110965176A CN201811139910.2A CN201811139910A CN110965176A CN 110965176 A CN110965176 A CN 110965176A CN 201811139910 A CN201811139910 A CN 201811139910A CN 110965176 A CN110965176 A CN 110965176A
Authority
CN
China
Prior art keywords
fabric
fibers
resistant
preparation
benzotriazole ultraviolet
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201811139910.2A
Other languages
English (en)
Inventor
周建
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Yunfu Fashion Co Ltd
Original Assignee
Jiangsu Yunfu Fashion Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Yunfu Fashion Co Ltd filed Critical Jiangsu Yunfu Fashion Co Ltd
Priority to CN201811139910.2A priority Critical patent/CN110965176A/zh
Publication of CN110965176A publication Critical patent/CN110965176A/zh
Withdrawn legal-status Critical Current

Abstract

本发明属于面料技术领域，具体涉及一种苯并三唑类抗紫外线面料的制备方法，包括如下步骤：将经线和纬线相互编织成所需的面料，经线由锦纶纤维与棉纤维混纺编织而成，纬线由维纶纤维、涤纶纤维与汉麻纤维混纺编织而成；将编织好的面料表面通过喷涂机喷涂一层苯并三唑类抗紫外吸收剂，喷涂厚度为0.22‑0.29mm；将喷涂好的面料放入烘箱中烘干，烘干温度为25‑85℃，烘干时间为12‑18min；将烘干后的面料放入到定型机中定型，定型温度为115‑125℃，定型时间为65‑95s。即可得到抗紫外线耐磨面料。本发明提供的一种苯并三唑类抗紫外线面料的制备方法，制备好的面料具有良好的抗紫外线功能，并且其制备工艺过程简单、易操作。

Description

一种苯并三唑类抗紫外线面料的制备方法
技术领域
本发明属于面料技术领域，具体涉及一种苯并三唑类抗紫外线面料的制备方法。
背景技术
随着人们环保和保健意识的不断增强，越来越多的人开始关注天然纤维，棉纤维作为应用最普遍的天然纤维，被广泛应用于各类纺织品生产中。目前市场上的纱线层出不穷，材质结构各不相同，广泛应用于织布、制绳、制线等生活领域。新疆棉纤维纤维因它的柔长在纺织业中十分出名，被人们誉为绵中极品，其具有纱纰少、条干均匀光洁、可染性高的优点。然而目前市场上的棉纤维混纺纱的弹性和保暖性并不好，因此，织造完成后的织物存在保暖效果差、弹力差的缺点。
防止紫外线对人体的伤害，已经被越来越多的消费者所重视。太阳光谱中的紫外线不仅使纺织品褪色和脆化，也可使人体皮肤晒伤老化，产生黑色素和色斑，更严重的还会诱发癌变，危害人类健康。抗紫外线面料是一种人体避免过量紫外线的辐射的保护材料。
有鉴于此，亟需发展一种苯并三唑类抗紫外线面料的制备方法。
发明内容
本发明的目的是提供一种苯并三唑类抗紫外线面料的制备方法，包括如下步骤：
a、将经线和纬线相互编织成所需的面料，经线由锦纶纤维与棉纤维混纺编织而成，纬线由维纶纤维、涤纶纤维与汉麻纤维混纺编织而成；
b、将编织好的面料表面通过喷涂机喷涂一层苯并三唑类抗紫外吸收剂，喷涂厚度为0.22-0.29mm；
c、将喷涂好的面料放入烘箱中烘干，烘干温度为25-85℃，烘干时间为12-18min；
d、将烘干后的面料放入到定型机中定型，定型温度为115-125℃，定型时间为65-95s，即可得到抗紫外线耐磨面料。
优选地，所述经线中各成分所占重量百分比分别为：锦纶纤维占30-64％，棉纤维占36-70％。
优选地，所述纬线中各成分所占重量百分比分别为：维纶纤维占25-40％，涤纶纤维占15-30％，汉麻纤维占30-60％。
优选地，所述步骤b中的喷涂速度为10-15m/min。
由于采用上述技术方案，本发明具有以下优点和有益效果：
制得的面料具有良好的抗紫外线功能，并且其制备工艺过程简单、易操作。
具体实施方式
为了更清楚地说明本发明，下面结合优选实施例对本发明做进一步的说明。本领域技术人员应当理解，下面所具体描述的内容是说明性的而非限制性的，不应以此限制本发明的保护范围。
实施例1
本发明的目的是提供一种苯并三唑类抗紫外线面料的制备方法，包括如下步骤：
a、将经线和纬线相互编织成所需的面料，经线由锦纶纤维与棉纤维混纺编织而成，纬线由维纶纤维、涤纶纤维与汉麻纤维混纺编织而成；
b、将编织好的面料表面通过喷涂机喷涂一层苯并三唑类抗紫外吸收剂，喷涂厚度为0.22mm；
c、将喷涂好的面料放入烘箱中烘干，烘干温度为25℃，烘干时间为12min；
d、将烘干后的面料放入到定型机中定型，定型温度为115℃，定型时间为65s，即可得到抗紫外线耐磨面料。
所述经线中各成分所占重量百分比分别为：锦纶纤维占30％，棉纤维占70％。
所述纬线中各成分所占重量百分比分别为：维纶纤维占25％，涤纶纤维占15％，汉麻纤维占60％。
所述步骤b中的喷涂速度为10m/min。
实施例2
本发明的目的是提供一种苯并三唑类抗紫外线面料的制备方法，包括如下步骤：
a、将经线和纬线相互编织成所需的面料，经线由锦纶纤维与棉纤维混纺编织而成，纬线由维纶纤维、涤纶纤维与汉麻纤维混纺编织而成；
b、将编织好的面料表面通过喷涂机喷涂一层苯并三唑类抗紫外吸收剂，喷涂厚度为0.29mm；
c、将喷涂好的面料放入烘箱中烘干，烘干温度为85℃，烘干时间为18min；
d、将烘干后的面料放入到定型机中定型，定型温度为125℃，定型时间为95s，即可得到抗紫外线耐磨面料。
所述经线中各成分所占重量百分比分别为：锦纶纤维占64％，棉纤维占36％。
所述纬线中各成分所占重量百分比分别为：维纶纤维占40％，涤纶纤维占30％，汉麻纤维占30％。
所述步骤b中的喷涂速度为15m/min。
经检测，上述两个实施例制备的抗菌纺纱的各项指标如下表
断裂强度N（经向） 断裂强度N（纬向） 抗起毛起球性能 紫外线透过率/%
实施例1 250N 222N 4~5级 2.8
实施例2 251N 222N 4~5级 2.77
以上显示和描述了本发明的基本原理、主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等同物界定。

Claims (4)

1.一种苯并三唑类抗紫外线面料的制备方法，其特征在于，包括如下步骤：
a、将经线和纬线相互编织成所需的面料，经线由锦纶纤维与棉纤维混纺编织而成，纬线由维纶纤维、涤纶纤维与汉麻纤维混纺编织而成；
b、将编织好的面料表面通过喷涂机喷涂一层苯并三唑类抗紫外吸收剂，喷涂厚度为0.22-0.29mm；
c、将喷涂好的面料放入烘箱中烘干，烘干温度为25-85℃，烘干时间为12-18min；
d、将烘干后的面料放入到定型机中定型，定型温度为115-125℃，定型时间为65-95s，即可得到抗紫外线耐磨面料。
2.根据权利要求1所述的苯并三唑类抗紫外线面料的制备方法，其特征在于，所述经线中各成分所占重量百分比分别为：锦纶纤维占30-64％，棉纤维占36-70％。
3.根据权利要求1所述的苯并三唑类抗紫外线面料的制备方法，其特征在于，所述纬线中各成分所占重量百分比分别为：维纶纤维占25-40％，涤纶纤维占15-30％，汉麻纤维占30-60％。
4.根据权利要求1所述的苯并三唑类抗紫外线面料的制备方法，其特征在于，所述步骤b中的喷涂速度为10-15m/min。
CN201811139910.2A 2018-09-28 2018-09-28 一种苯并三唑类抗紫外线面料的制备方法 Withdrawn CN110965176A (zh)