CN110872700B - 制备具有高碳含量的含硅膜的方法 - Google Patents

制备具有高碳含量的含硅膜的方法 Download PDF

Info

Publication number
CN110872700B
CN110872700B CN201910809682.3A CN201910809682A CN110872700B CN 110872700 B CN110872700 B CN 110872700B CN 201910809682 A CN201910809682 A CN 201910809682A CN 110872700 B CN110872700 B CN 110872700B
Authority
CN
China
Prior art keywords
silicon oxide
reactor
carbon
disilacyclobutane
oxide film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201910809682.3A
Other languages
English (en)
Chinese (zh)
Other versions
CN110872700A (zh
Inventor
雷新建
H·钱德拉
金武性
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Versum Materials US LLC
Original Assignee
Versum Materials US LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Versum Materials US LLC filed Critical Versum Materials US LLC
Publication of CN110872700A publication Critical patent/CN110872700A/zh
Application granted granted Critical
Publication of CN110872700B publication Critical patent/CN110872700B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C16/00—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes
    • C23C16/22—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes characterised by the deposition of inorganic material, other than metallic material
    • C23C16/30—Deposition of compounds, mixtures or solid solutions, e.g. borides, carbides, nitrides
    • C23C16/40—Oxides
    • C23C16/401—Oxides containing silicon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C16/00—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes
    • C23C16/22—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes characterised by the deposition of inorganic material, other than metallic material
    • C23C16/30—Deposition of compounds, mixtures or solid solutions, e.g. borides, carbides, nitrides
    • C23C16/40—Oxides
    • C23C16/401—Oxides containing silicon
    • C23C16/402—Silicon dioxide
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
    • C01B33/00—Silicon; Compounds thereof
    • C01B33/113—Silicon oxides; Hydrates thereof
    • C01B33/12—Silica; Hydrates thereof, e.g. lepidoic silicic acid
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C16/00—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes
    • C23C16/02—Pretreatment of the material to be coated
    • C23C16/0209—Pretreatment of the material to be coated by heating
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C16/00—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes
    • C23C16/22—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes characterised by the deposition of inorganic material, other than metallic material
    • C23C16/30—Deposition of compounds, mixtures or solid solutions, e.g. borides, carbides, nitrides
    • C23C16/32—Carbides
    • C23C16/325—Silicon carbide
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C16/00—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes
    • C23C16/44—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes characterised by the method of coating
    • C23C16/455—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes characterised by the method of coating characterised by the method used for introducing gases into reaction chamber or for modifying gas flows in reaction chamber
    • C23C16/45523—Pulsed gas flow or change of composition over time
    • C23C16/45525—Atomic layer deposition [ALD]
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C16/00—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes
    • C23C16/44—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes characterised by the method of coating
    • C23C16/455—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes characterised by the method of coating characterised by the method used for introducing gases into reaction chamber or for modifying gas flows in reaction chamber
    • C23C16/45523—Pulsed gas flow or change of composition over time
    • C23C16/45525—Atomic layer deposition [ALD]
    • C23C16/45527—Atomic layer deposition [ALD] characterized by the ALD cycle, e.g. different flows or temperatures during half-reactions, unusual pulsing sequence, use of precursor mixtures or auxiliary reactants or activations
    • C23C16/45536—Use of plasma, radiation or electromagnetic fields
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C16/00—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes
    • C23C16/44—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes characterised by the method of coating
    • C23C16/455—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes characterised by the method of coating characterised by the method used for introducing gases into reaction chamber or for modifying gas flows in reaction chamber
    • C23C16/45523—Pulsed gas flow or change of composition over time
    • C23C16/45525—Atomic layer deposition [ALD]
    • C23C16/45527—Atomic layer deposition [ALD] characterized by the ALD cycle, e.g. different flows or temperatures during half-reactions, unusual pulsing sequence, use of precursor mixtures or auxiliary reactants or activations
    • C23C16/45536—Use of plasma, radiation or electromagnetic fields
    • C23C16/45542—Plasma being used non-continuously during the ALD reactions
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C16/00—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes
    • C23C16/44—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes characterised by the method of coating
    • C23C16/455—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes characterised by the method of coating characterised by the method used for introducing gases into reaction chamber or for modifying gas flows in reaction chamber
    • C23C16/45523—Pulsed gas flow or change of composition over time
    • C23C16/45525—Atomic layer deposition [ALD]
    • C23C16/45553—Atomic layer deposition [ALD] characterized by the use of precursors specially adapted for ALD
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C16/00—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes
    • C23C16/56—After-treatment
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10P—GENERIC PROCESSES OR APPARATUS FOR THE MANUFACTURE OR TREATMENT OF DEVICES COVERED BY CLASS H10
    • H10P14/00—Formation of materials, e.g. in the shape of layers or pillars
    • H10P14/60—Formation of materials, e.g. in the shape of layers or pillars of insulating materials
    • H10P14/63—Formation of materials, e.g. in the shape of layers or pillars of insulating materials characterised by the formation processes
    • H10P14/6326—Deposition processes
    • H10P14/6328—Deposition from the gas or vapour phase
    • H10P14/6334—Deposition from the gas or vapour phase using decomposition or reaction of gaseous or vapour phase compounds, i.e. chemical vapour deposition
    • H10P14/6336—Deposition from the gas or vapour phase using decomposition or reaction of gaseous or vapour phase compounds, i.e. chemical vapour deposition in the presence of a plasma [PECVD]
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10P—GENERIC PROCESSES OR APPARATUS FOR THE MANUFACTURE OR TREATMENT OF DEVICES COVERED BY CLASS H10
    • H10P14/00—Formation of materials, e.g. in the shape of layers or pillars
    • H10P14/60—Formation of materials, e.g. in the shape of layers or pillars of insulating materials
    • H10P14/63—Formation of materials, e.g. in the shape of layers or pillars of insulating materials characterised by the formation processes
    • H10P14/6326—Deposition processes
    • H10P14/6328—Deposition from the gas or vapour phase
    • H10P14/6334—Deposition from the gas or vapour phase using decomposition or reaction of gaseous or vapour phase compounds, i.e. chemical vapour deposition
    • H10P14/6339—Deposition from the gas or vapour phase using decomposition or reaction of gaseous or vapour phase compounds, i.e. chemical vapour deposition deposition by cyclic CVD, e.g. ALD, ALE or pulsed CVD
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10P—GENERIC PROCESSES OR APPARATUS FOR THE MANUFACTURE OR TREATMENT OF DEVICES COVERED BY CLASS H10
    • H10P14/00—Formation of materials, e.g. in the shape of layers or pillars
    • H10P14/60—Formation of materials, e.g. in the shape of layers or pillars of insulating materials
    • H10P14/65—Formation of materials, e.g. in the shape of layers or pillars of insulating materials characterised by treatments performed before or after the formation of the materials
    • H10P14/6516—Formation of materials, e.g. in the shape of layers or pillars of insulating materials characterised by treatments performed before or after the formation of the materials of treatments performed after formation of the materials
    • H10P14/6518—Formation of materials, e.g. in the shape of layers or pillars of insulating materials characterised by treatments performed before or after the formation of the materials of treatments performed after formation of the materials by introduction of substances into an already-existing insulating layer
    • H10P14/6519—Formation of materials, e.g. in the shape of layers or pillars of insulating materials characterised by treatments performed before or after the formation of the materials of treatments performed after formation of the materials by introduction of substances into an already-existing insulating layer the substance being oxygen
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10P—GENERIC PROCESSES OR APPARATUS FOR THE MANUFACTURE OR TREATMENT OF DEVICES COVERED BY CLASS H10
    • H10P14/00—Formation of materials, e.g. in the shape of layers or pillars
    • H10P14/60—Formation of materials, e.g. in the shape of layers or pillars of insulating materials
    • H10P14/66—Formation of materials, e.g. in the shape of layers or pillars of insulating materials characterised by the type of materials
    • H10P14/668—Formation of materials, e.g. in the shape of layers or pillars of insulating materials characterised by the type of materials the materials being characterised by the deposition precursor materials
    • H10P14/6681—Formation of materials, e.g. in the shape of layers or pillars of insulating materials characterised by the type of materials the materials being characterised by the deposition precursor materials the precursor containing a compound comprising Si
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10P—GENERIC PROCESSES OR APPARATUS FOR THE MANUFACTURE OR TREATMENT OF DEVICES COVERED BY CLASS H10
    • H10P14/00—Formation of materials, e.g. in the shape of layers or pillars
    • H10P14/60—Formation of materials, e.g. in the shape of layers or pillars of insulating materials
    • H10P14/66—Formation of materials, e.g. in the shape of layers or pillars of insulating materials characterised by the type of materials
    • H10P14/668—Formation of materials, e.g. in the shape of layers or pillars of insulating materials characterised by the type of materials the materials being characterised by the deposition precursor materials
    • H10P14/6681—Formation of materials, e.g. in the shape of layers or pillars of insulating materials characterised by the type of materials the materials being characterised by the deposition precursor materials the precursor containing a compound comprising Si
    • H10P14/6682—Formation of materials, e.g. in the shape of layers or pillars of insulating materials characterised by the type of materials the materials being characterised by the deposition precursor materials the precursor containing a compound comprising Si the compound being a silane, e.g. disilane, methylsilane or chlorosilane
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10P—GENERIC PROCESSES OR APPARATUS FOR THE MANUFACTURE OR TREATMENT OF DEVICES COVERED BY CLASS H10
    • H10P14/00—Formation of materials, e.g. in the shape of layers or pillars
    • H10P14/60—Formation of materials, e.g. in the shape of layers or pillars of insulating materials
    • H10P14/69—Inorganic materials
    • H10P14/6903—Inorganic materials containing silicon
    • H10P14/6905—Inorganic materials containing silicon being a silicon carbide or silicon carbonitride and not containing oxygen, e.g. SiC or SiC:H
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10P—GENERIC PROCESSES OR APPARATUS FOR THE MANUFACTURE OR TREATMENT OF DEVICES COVERED BY CLASS H10
    • H10P14/00—Formation of materials, e.g. in the shape of layers or pillars
    • H10P14/60—Formation of materials, e.g. in the shape of layers or pillars of insulating materials
    • H10P14/69—Inorganic materials
    • H10P14/692—Inorganic materials composed of oxides, glassy oxides or oxide-based glasses
    • H10P14/6921—Inorganic materials composed of oxides, glassy oxides or oxide-based glasses containing silicon
    • H10P14/69215—Inorganic materials composed of oxides, glassy oxides or oxide-based glasses containing silicon the material being a silicon oxide, e.g. SiO2
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10P—GENERIC PROCESSES OR APPARATUS FOR THE MANUFACTURE OR TREATMENT OF DEVICES COVERED BY CLASS H10
    • H10P14/00—Formation of materials, e.g. in the shape of layers or pillars
    • H10P14/60—Formation of materials, e.g. in the shape of layers or pillars of insulating materials
    • H10P14/69—Inorganic materials
    • H10P14/692—Inorganic materials composed of oxides, glassy oxides or oxide-based glasses
    • H10P14/6921—Inorganic materials composed of oxides, glassy oxides or oxide-based glasses containing silicon
    • H10P14/6922—Inorganic materials composed of oxides, glassy oxides or oxide-based glasses containing silicon the material containing Si, O and at least one of H, N, C, F or other non-metal elements, e.g. SiOC, SiOC:H or SiONC
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2002/00—Crystal-structural characteristics
    • C01P2002/50—Solid solutions
    • C01P2002/52—Solid solutions containing elements as dopants
    • C01P2002/54—Solid solutions containing elements as dopants one element only
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C16/00—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes
    • C23C16/44—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes characterised by the method of coating
    • C23C16/4401—Means for minimising impurities, e.g. dust, moisture or residual gas, in the reaction chamber
    • C23C16/4408—Means for minimising impurities, e.g. dust, moisture or residual gas, in the reaction chamber by purging residual gases from the reaction chamber or gas lines

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Organic Chemistry (AREA)
  • Metallurgy (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • General Chemical & Material Sciences (AREA)
  • Inorganic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Plasma & Fusion (AREA)
  • Electromagnetism (AREA)
  • Chemical Vapour Deposition (AREA)
  • Formation Of Insulating Films (AREA)
CN201910809682.3A 2018-08-29 2019-08-29 制备具有高碳含量的含硅膜的方法 Active CN110872700B (zh)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US201862724109P 2018-08-29 2018-08-29
US62/724,109 2018-08-29
US16/553,080 US20200071819A1 (en) 2018-08-29 2019-08-27 Methods For Making Silicon Containing Films That Have High Carbon Content
US16/553,080 2019-08-27

Publications (2)

Publication Number Publication Date
CN110872700A CN110872700A (zh) 2020-03-10
CN110872700B true CN110872700B (zh) 2022-11-08

Family

ID=67809388

Family Applications (1)

Application Number Title Priority Date Filing Date
CN201910809682.3A Active CN110872700B (zh) 2018-08-29 2019-08-29 制备具有高碳含量的含硅膜的方法

Country Status (7)

Country Link
US (2) US20200071819A1 (OSRAM)
EP (1) EP3620550B1 (OSRAM)
JP (2) JP6999620B2 (OSRAM)
KR (3) KR20200026148A (OSRAM)
CN (1) CN110872700B (OSRAM)
SG (1) SG10201907962WA (OSRAM)
TW (1) TWI762809B (OSRAM)

Families Citing this family (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20180033614A1 (en) * 2016-07-27 2018-02-01 Versum Materials Us, Llc Compositions and Methods Using Same for Carbon Doped Silicon Containing Films
TWI764068B (zh) * 2019-01-11 2022-05-11 日商國際電氣股份有限公司 半導體裝置之製造方法、基板處理方法、基板處理裝置及程式
WO2021053756A1 (ja) * 2019-09-18 2021-03-25 株式会社Ｋｏｋｕｓａｉ Ｅｌｅｃｔｒｉｃ 半導体装置の製造方法、基板処理装置およびプログラム
CN111453695B (zh) * 2020-06-16 2020-10-16 中芯集成电路制造(绍兴)有限公司 氧化硅层的刻蚀方法、mems器件及其形成方法
CN115867689A (zh) * 2020-06-23 2023-03-28 恩特格里斯公司 硅前体化合物及形成含硅膜的方法
KR20230046303A (ko) 2020-07-24 2023-04-05 버슘머트리얼즈 유에스, 엘엘씨 조성물 및 게르마늄 시드층을 위한 이의 사용 방법
US20220091513A1 (en) * 2020-09-18 2022-03-24 Applied Materials, Inc. Film structure for electric field assisted bake process
JP7754923B2 (ja) * 2020-09-30 2025-10-15 ジェレスト， インコーポレイテッド 炭化ケイ素薄膜及びその蒸着方法
KR20250162947A (ko) * 2021-01-26 2025-11-19 엔테그리스, 아이엔씨. 고 처리율 침착 방법
EP4284960A4 (en) * 2021-03-02 2024-10-16 Versum Materials US, LLC Compositions and methods using same for films comprising silicon and boron
JP2024508893A (ja) * 2021-03-02 2024-02-28 バーサム マテリアルズ ユーエス，リミティド ライアビリティ カンパニー シリコン誘電体膜の選択的堆積
WO2023220650A1 (en) * 2022-05-13 2023-11-16 Versum Materials Us, Llc Compositions and methods using same for carbon doped silicon containing films
US20240087881A1 (en) * 2022-08-26 2024-03-14 Applied Materials, Inc. Systems and methods for depositing low-k dielectric films
US20250357107A1 (en) * 2024-05-16 2025-11-20 Applied Materials, Inc. Rf pulsing assisted low-k material deposition with high density

Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102487035A (zh) * 2010-12-01 2012-06-06 中芯国际集成电路制造(上海)有限公司 具有多孔结构的超低介电常数的层间介质的淀积方法

Family Cites Families (24)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2614338B2 (ja) 1990-01-11 1997-05-28 株式会社東芝 液体ソース容器
US5465766A (en) 1993-04-28 1995-11-14 Advanced Delivery & Chemical Systems, Inc. Chemical refill system for high purity chemicals
WO1998027247A1 (en) 1996-12-17 1998-06-25 Advanced Technology Materials, Inc. Reagent supply vessel for chemical vapor deposition
US6953047B2 (en) 2002-01-14 2005-10-11 Air Products And Chemicals, Inc. Cabinet for chemical delivery with solvent purging
EP1504138A2 (en) * 2002-05-08 2005-02-09 Applied Materials, Inc. Method for using low dielectric constant film by electron beam
US8241624B2 (en) 2008-04-18 2012-08-14 Ecolab Usa Inc. Method of disinfecting packages with composition containing peracid and catalase
JP5421736B2 (ja) * 2009-11-13 2014-02-19 株式会社日立国際電気 半導体装置の製造方法、基板処理装置、及びプログラム
JP5530744B2 (ja) * 2010-02-15 2014-06-25 大陽日酸株式会社 絶縁膜のダメージ回復方法及びダメージが回復された絶縁膜
US9040127B2 (en) 2010-09-24 2015-05-26 Applied Materials, Inc. Low temperature silicon carbide deposition process
KR20130135261A (ko) * 2010-11-03 2013-12-10 어플라이드 머티어리얼스, 인코포레이티드 실리콘 카바이드 및 실리콘 카보나이트라이드 막들을 증착하기 위한 장치 및 방법들
WO2013039881A2 (en) 2011-09-13 2013-03-21 Applied Materials, Inc. Carbosilane precursors for low temperature film deposition
US8722546B2 (en) 2012-06-11 2014-05-13 Asm Ip Holding B.V. Method for forming silicon-containing dielectric film by cyclic deposition with side wall coverage control
US9234276B2 (en) 2013-05-31 2016-01-12 Novellus Systems, Inc. Method to obtain SiC class of films of desired composition and film properties
KR20150121217A (ko) 2013-03-01 2015-10-28 어플라이드 머티어리얼스, 인코포레이티드 ＳｉＣＮ 또는 ＳｉＣＯＮ을 포함하는 필름의 저온 원자층 증착
JP5864637B2 (ja) 2013-03-19 2016-02-17 株式会社日立国際電気 半導体装置の製造方法、基板処理装置、プログラム及び記録媒体
JP6112928B2 (ja) 2013-03-19 2017-04-12 株式会社日立国際電気 半導体装置の製造方法、基板処理装置及びプログラム
JP6155063B2 (ja) 2013-03-19 2017-06-28 株式会社日立国際電気 半導体装置の製造方法、基板処理装置及びプログラム
US9796739B2 (en) * 2013-06-26 2017-10-24 Versum Materials Us, Llc AZA-polysilane precursors and methods for depositing films comprising same
JP6125946B2 (ja) 2013-08-08 2017-05-10 株式会社日立国際電気 半導体装置の製造方法、基板処理装置及びプログラム
US10023958B2 (en) * 2013-11-22 2018-07-17 Applied Materials, Inc. Atomic layer deposition of films comprising silicon, carbon and nitrogen using halogenated silicon precursors
JP5883049B2 (ja) * 2014-03-04 2016-03-09 株式会社日立国際電気 半導体装置の製造方法、基板処理装置、プログラムおよび記録媒体
EP3254303B1 (en) * 2015-02-06 2018-12-05 Versum Materials US, LLC Method for formation of carbon doped silicon containing films
US9455138B1 (en) 2015-11-10 2016-09-27 Asm Ip Holding B.V. Method for forming dielectric film in trenches by PEALD using H-containing gas
US20180033614A1 (en) * 2016-07-27 2018-02-01 Versum Materials Us, Llc Compositions and Methods Using Same for Carbon Doped Silicon Containing Films

Patent Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102487035A (zh) * 2010-12-01 2012-06-06 中芯国际集成电路制造(上海)有限公司 具有多孔结构的超低介电常数的层间介质的淀积方法

Also Published As

Publication number Publication date
TWI762809B (zh) 2022-05-01
US20220145453A1 (en) 2022-05-12
SG10201907962WA (en) 2020-03-30
CN110872700A (zh) 2020-03-10
US20200071819A1 (en) 2020-03-05
KR20250034358A (ko) 2025-03-11
JP2022008973A (ja) 2022-01-14
JP6999620B2 (ja) 2022-01-18
KR20200026148A (ko) 2020-03-10
EP3620550B1 (en) 2024-05-01
KR20220137605A (ko) 2022-10-12
JP2020036013A (ja) 2020-03-05
EP3620550A1 (en) 2020-03-11
TW202012682A (zh) 2020-04-01

Similar Documents

Publication Publication Date Title
US11742200B2 (en) Composition and methods using same for carbon doped silicon containing films
TWI762809B (zh) 具有高碳含量的含矽膜的製造方法
EP3460827B1 (en) Compositions and methods using same for carbon doped silicon containing films
TWI882336B (zh) 用於碳摻雜的含矽膜的組合物及使用其的方法
TWI884773B (zh) 氯甲矽烷基取代的矽環烷烴及其用於形成包含矽和氧的膜的用途
KR20240054222A (ko) 실리콘 및 붕소를 포함하는 필름을 위한 조성물 및 이의 사용 방법

Legal Events

Date Code Title Description
PB01 Publication
PB01 Publication
SE01 Entry into force of request for substantive examination
SE01 Entry into force of request for substantive examination
GR01 Patent grant
GR01 Patent grant