CN110713767A - 一种绿色膨胀型家装防火水漆及其制备方法 - Google Patents
一种绿色膨胀型家装防火水漆及其制备方法 Download PDFInfo
- Publication number
- CN110713767A CN110713767A CN201911113999.XA CN201911113999A CN110713767A CN 110713767 A CN110713767 A CN 110713767A CN 201911113999 A CN201911113999 A CN 201911113999A CN 110713767 A CN110713767 A CN 110713767A
- Authority
- CN
- China
- Prior art keywords
- percent
- green
- home decoration
- intumescent
- water paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及涂料技术领域，提供一种绿色膨胀型家装防火水漆及其制备方法，包括水、纤维素、水性流变助剂、分散剂、抑泡剂、钛白粉、高岭土、云母粉、改性聚磷酸铵、季戊四醇、三聚氰胺、丙烯酸乳液、抗冻溶剂、成膜助剂、消泡剂、杀菌防霉剂和增稠剂，所述改性聚磷酸铵为甲基三乙氧基硅烷结合微胶囊方法包覆改性的聚磷酸铵。本发明解决了现有钢结构防火涂料所存在的弊端：漆膜耐水性差、储存不稳定、易结晶、返粗、施工宽容度低以及膨胀倍率和碳层稳定性之间的矛盾。
Description
技术领域
本发明涉及涂料技术领域，尤其涉及一种绿色膨胀型家装防火水漆及其制备方法。
背景技术
随着社会的进步，国民经济的不断提高、建筑的高层化，在建筑内部大量新型材料引入使用的同时也悄然增加了建筑发生火灾的可能性。近年火灾造成的经济损失、人员伤亡、对社会的不良影响在大幅增加，如中央电视台大火事件、上海“11.5”特大火灾事故、3.11丽江古城火灾、静安市教师公寓大火等特大事故均对社会造成了恶劣的影响。现代社会火灾发生频率居高不下，引起建筑火灾发生及扩大的原因不仅与消防设施的损坏、初期火灾扑救不及时等有关，还与使用的建筑材料有非常密切的关系。
根据火灾场景的数据统计分析，火灾中由于吸入烟气致死的人员高达85%以上。如2008年9月深圳俱乐部发生的特大火灾，死亡 44 人，受伤 88 人，其主要的原因是由于俱乐部内的聚氨酯装饰材料燃烧产生了大量的有毒有害烟气，导致人员窒息死亡。2010 年11 月上海静安区教师公寓大楼火灾事故，死亡人数高达 58 人，受伤人数 71 人， 经济损失 1.58 亿元，发生此次火灾的罪魁祸首就是外墙保温材料的燃烧而产生的大量高温的剧毒浓烟。
人们在使用科学技术不断探索火灾本质特征，在火灾的发展规律上均有了更为深刻的意识，对材料进行一定的阻燃处理是一种增大建筑材料耐火等级，减小火灾危害的有效科学方法。针对某些易燃物质，在其表面涂覆一层防火涂料可以有效提高建材的防火等级、耐火极限，改善建筑材料的防火性能、减缓热量向基材的传递速度，部分发达国家在建筑外装饰材料上较为频繁的使用防火涂料。建筑日益更新对建筑材料的要求日益增高，出于对防火效果以及环境友好的两个方面考虑。
按溶剂类型，防火涂料可分为水剂型和溶剂型两类，考虑到能源的节约和环境的友好性，现阶段一般多为水剂型防火涂料。按防火机理，可分为膨胀型和非膨胀型防火涂料，非膨胀型防火涂料是根据其涂料本身的不燃性及难燃性以达到防火效果，而膨胀型防火涂料则是经过高温涂层本身可膨胀形成致密的蜂窝状炭化层，能阻止火焰与底材继续接触，从而达到防火阻燃的效果。一般使用膨胀型防火涂料能达到更显著的防火效果。然而，目前钢结构防火、饰面型防火涂料的技术指标、发展现状、使用情况并不适用于内墙涂装系统，存在薄层防火性能差，发泡倍率低，碳层结构弱、保存时间短、抑烟效果差以及耐水、耐锈性差等缺点和问题。
本发明的目的在于提供一种绿色膨胀型家装防火水漆，不含有机溶剂，通过脱水催化剂、成炭剂和发泡剂受热形成蜂窝状的碳化层，从而达到阻燃隔热的效果，解决现有技术上漆膜耐水性差，储存不稳定，施工宽容度低，易结晶、返粗以及膨胀倍率和碳层稳定性之间的矛盾。
发明内容
因此，针对上述的问题，本发明提供一种绿色膨胀型家装防火水漆及其制备方法，其克服了现有技术上膨胀型防火涂料耐水性、发泡倍率差，施工宽容度低，碳层疏松以及储存不稳定易产生结晶、氨气等问题，具有超强耐候性、阻燃、抑烟、保护基材等特点。
为解决此技术问题，本发明采取以下方案：一种绿色膨胀型家装防火水漆，包括以下重量百分比的原材料组分：
水 20-28%
纤维素 0.15-0.45%
水性流变助剂 0.2-03%
聚丙烯酸铵盐 0.2-0.6%
抑泡剂 0.1-0.3%
钛白粉 9-12%
高岭土 3-9%
云母粉 5-8%
改性聚磷酸铵 15-25%
季戊四醇 6-10%
三聚氰胺 5-9%
丙烯酸乳液 9-13%
抗冻融剂 0.6-0.8%
成膜助剂 0.6-0.9%
消泡剂 0.1-0.3%
杀菌防霉剂 0.1-0.3%
增稠剂 0.1-0.4%；
所述改性聚磷酸铵为甲基三乙氧基硅烷结合微胶囊方法包覆改性的聚磷酸铵。
进一步的，所述纤维素为羟乙基纤维素，所述水性流变助剂为有机改性精制锂蒙脱石黏土，所述抑泡剂为矿物油消泡剂和有机硅消泡剂中的一种或组合。
进一步的，所述钛白粉为金红石型钛白粉，所述高岭土为C-98煅烧高岭土，所述云母粉为绢云母。
进一步的，改性聚磷酸铵是由以下材料按质量百分比通过以下顺序步骤制备而成：
（1）将40-50%乙醇和20-26%水的复配液加入到分散器中；
（2）在300-800rpm转速下加入22-26%聚磷酸酯，接着在700-800rpm转速下加入氨水使其pH值在9.5-10.5；
（3）800-900rpm转速下加入4-10%甲基三乙氧基硅烷，并水浴加热至45℃，反应2-3h；
（4）停止加热和分散，将步骤（3）最后得到的溶液经过过滤、洗涤、干燥和冷却后得到微胶囊化的改性聚磷酸铵。
进一步的，所述丙烯酸乳液为苯乙烯/丙烯酸酯共聚而成的聚合物；所述抗冻溶剂为乙二醇；所述成膜助剂为醇酯12。
进一步的，所述季戊四醇为2000目季戊四醇；所述三聚氰胺为1250目三聚氰胺。
进一步的，所述杀菌防霉剂由5-氯-2-甲基- 4异噻唑啉-3-酮和1，2-苯并异噻唑啉-3-酮复配而成。
进一步的，所述消泡剂为有机硅消泡剂；所述增稠剂为缔合型聚氨酯类增稠剂。
一种绿色膨胀型家装防火水漆的制备方法，包括以下步骤：
（1）、在350-450r/min的转速下，将20-28%水，0.15-0.45%纤维素，0.2-0.3%水性流变助剂，0.2-0.6%分散剂和0.1-0.3%抑泡剂加入分散器中，分散2-5分钟；
（2）、将步骤（1）分散器分散完成后调整分散器转速至450-1800r/min的转速，再依次加入9-12%钛白粉、3-9%高岭土、5-8%云母粉、 15-25%改性聚磷酸铵、6-10%季戊四醇和5-9%三聚氰胺，分散20-25分钟；再将分散器调整至1800-2300r/min的转速下分散并研磨至细度<45μm；
（3）、将步骤（2）分散并研磨好后调整分散器转速至600-900r/min的转速下再依次加入9-13%丙烯酸乳液、0.6-0.8%抗冻溶剂、0.6-0.9%成膜助剂、0.1-0.3%消泡剂、0.1-0.3%防霉剂和 0.1-0.4%流平剂，分散5-15min至混合物均匀，即可制得绿色膨胀型家装防火水漆。
进一步的，所述改性聚磷酸铵为甲基三乙氧基硅烷结合微胶囊方法包覆改性的聚磷酸铵，所述钛白粉为金红石型钛白粉，所述高岭土为C-98煅烧高岭土，所述云母粉为绢云母，所述丙烯酸乳液为苯乙烯/丙烯酸酯共聚而成的聚合物；所述抗冻溶剂为乙二醇；所述成膜助剂为醇酯12，所述季戊四醇为2000目季戊四醇；所述三聚氰胺为1250目三聚氰胺，所述杀菌防霉剂由5-氯-2-甲基- 4异噻唑啉-3-酮和1，2-苯并异噻唑啉-3-酮复配而成，所述消泡剂为有机硅消泡剂；所述增稠剂为缔合型聚氨酯类增稠剂。
通过采用前述技术方案，本发明的有益效果是：
（1）本发明采用由甲基三乙氧基硅烷改性制得的微胶囊包覆的改性聚磷酸铵，聚合度大于1000，通过微胶囊的方法对聚磷酸铵进行表面处理，聚磷酸铵表面包覆一层疏水性壳层，可以改善聚磷酸铵的耐水性，从而使漆膜耐水性得到提高；在高温阶段，硅类物质燃烧过程中在表面形成二氧化硅保护层，从而提高其热稳定性和成炭量，含硅化合物可以在凝聚相中形成碳层骨架，增强碳层的热阻和受热稳定性，从而提高了漆膜的膨胀倍率以及碳层结构的稳定性。高聚合度的改性聚磷酸铵化学链较稳定，能很大程度的减少因高温等外界条件下使其断链形成氨气或磷酸铵。
（2）本发明避开钠盐分散剂，采用聚丙烯酸铵盐分散剂，有较好的储存稳定性，且其不与改性聚磷酸铵储存中因断链形成的磷酸铵反应形成磷酸钠晶体，从而解决了水漆在储存中结晶的问题，水性流变助剂为有机改性精制锂蒙脱石黏土，有效的低剪切粘度增稠剂，展现稳定的粘度不会出现后增稠。
（3）本发明避开使用重金属含量高的重钙、硅灰石等，避免了重金属离子对聚磷酸铵的影响，从而解决了水漆在储存过程中的返粗现象。
（4）本发明加入一定量的绢云母，呈片层结构，在漆膜中形成平行的取向排列，与腐蚀性物质穿透漆膜的方向垂直，使水和其他腐蚀性物质的渗透受到强烈的阻隔，增加了穿透的路径，穿透时间能延长3倍以上，类似于迷宫效应，从而一定程度上能提高漆膜的耐水性和隔热性。
（5）因聚磷酸铵存在特殊的层层结构，形状类似于书本，存在严重的水滑性，降低体系的摩擦力，导致普通家装喷涂机无法施工，本发明配方中添加了摩擦系数较高的绢云母、煅烧土，提高了涂料体系的摩擦系数，使其适用于目前市场上普通泵压和普通流量的家装喷涂机。
（6）在体系中采用杀菌防霉剂可有效的实现杀菌、抑菌作用，环保性好，符合绿标要求；成膜助剂为醇酯12能降低乳胶漆的成膜温度、提高漆膜的光泽度、强度及抗粉化性能、增进流平性且具有无毒环保的特性、对降低涂料的VOC效果显著。
（7）钛白粉与高岭土结合使用具有良好的耐洗刷性，并能提高钛白粉的分散能力且有效地保持钛白粉的白度、遮盖力、耐候性、耐热性和化学稳定性，且都是无毒。
具体实施方式
现结合具体实施方式对本发明进一步说明。
以下实施例1-3中的各原材料分别采用以下类型原材料：所述纤维素采用美国亚跨龙HHBR250；所述水性流变助剂采用海明斯的BENTONE DY CE；所述分散剂采用大连金鼎祥化学有限公司的TRM-2400；所述抑泡剂采用海明斯的DAPRO AP 7010;所述钛白粉采用杜邦的R706；所述高岭土采用内蒙三鑫的SX-68；所述云母粉采用海扬粉体的HY-TM6；所述聚磷酸铵采用威来惠南的FR CROS 582；所述季戊四醇采用濮阳鑫鹏化工的单季季戊四醇；所述三聚氰胺采用荣盛化工的三聚氰胺；所述丙烯酸乳液采用巴德富的RS-916F；所述抗冻溶剂采用厦门正兴行提供的FT-68;所述成膜助剂采用伊士曼OE-400；所述消泡剂采用海润化工的DISPELAIR CF 18495；所述杀菌防霉剂采用鹏图化工的CM-10；所述增增稠剂采用金鼎祥的TRM-003。
实施例1：
一种绿色膨胀型家装防火水漆，它由以下原材料按以下质量配比通过以下步骤制备而成：
（1）、在400r/min的转速下，将26.9%水，0.35%纤维素，0.25%水性流变助剂，0.3%分散剂和0.2%抑泡剂加入分散器中，分散2-5分钟；
（2）、在1200r/min的转速下，依次加入10%钛白，8%高岭土，7.5%云母粉， 18%聚磷酸铵，8%季戊四醇和7.5%三聚氰胺，分散20-25分钟；调整转速在1700r/min的转速下，分散并研磨至细度<45μm；
（3）在800r/min的转速下依次加入11%丙烯酸乳液，0.7%抗冻溶剂、0.7%成膜助剂、0.2%消泡剂、0.2%防霉剂和 0.2%流平剂，分散5-15min至混合物均匀。
实施例2
一种绿色膨胀型家装防火水漆，它由以下原材料按以下质量配比通过以下步骤制备而成：
（1）、在400r/min的转速下，将22.6%水，0.3%纤维素，0.25%水性流变助剂，0.5%分散剂和0.15%抑泡剂加入分散器中，分散2-5分钟；
（2）、在1500r/min的转速下，依次加入11%钛白，6%高岭土，8%云母粉， 21%聚磷酸铵，8.5%季戊四醇和7.5%三聚氰胺，分散20-25分钟，调整转速在1900r/min的转速下，分散并研磨至细度<45μm；
（3）在800r/min的转速下依次加入12%丙烯酸乳液，0.7%抗冻溶剂、0.8%成膜助剂、0.2%消泡剂、0.2%防霉剂和 0.3%流平剂，分散5-15min至混合物均匀。
实施例3：
一种绿色膨胀型家装防火水漆，它由以下原材料按以下质量配比通过以下步骤制备而成：
（1）、在400r/min的转速下，将22.3%水，0.2%纤维素，0.25%水性流变助剂，0.4%分散剂和0.15%抑泡剂加入分散器中，分散2-5分钟；
（2）、在1500r/min的转速下，依次加入10%钛白，5%高岭土，7%云母粉， 24%聚磷酸铵，9.5%季戊四醇和8%三聚氰胺，分散20-25分钟；在1950r/min的转速下，分散并研磨至细度<45μm；
（3）在850r/min的转速下依次加入11%丙烯酸乳液，0.7%抗冻溶剂、0.8%成膜助剂、0.2%消泡剂、0.2%防霉剂和 0.3%流平剂，分散5-15min至混合物均匀。
在以上各实施例中：
所述改性聚磷酸铵由以下原料按以下质量百分配比通过以下顺序步骤制备而成：
（1）将40-50%乙醇和20-26%水的复配液加入到分散器中；
（2）在300-800rpm转速下加入22-26%APP，接着在700-800rpm转速下加入一定量的氨水使其pH值在10左右；
（3）800-900rpm转速下加入4-10%甲基三乙氧基硅烷，并水浴加热至45℃，反应2-3h；
（4）停止加热和分散，得到的溶液经过过滤、洗涤、干燥和冷却后得到微胶囊化的改性聚磷酸铵。
表1——绿色膨胀型家装防火水漆的各实施例分别在25℃、35℃、45℃和55℃中储存4周的罐内状态实验数据：
从表1中可以看出，本发明的实施例1-3储存时间都较长，按理论推断，可正常储存18个月不结晶不返粗。其中实施例1储存时间最长。
针对本申请所制备的绿色膨胀型家装防火水漆测得的膨胀倍率数据如下所示：
膨胀倍率的测试方法：在马弗炉中进行，马弗炉的电压为220V，功率为2.5KW，最高温度可达1000℃，尺寸为20cm×12cm×8cm，并装有热电偶，通过热电偶控制温度。
具体测试步骤如下：
（1）用500μm湿膜制备器将绿色膨胀型家装防火水漆涂刮在型号为150mm×70mm×6mm的钢板上，待其干燥后再进行第二次涂刮。
（2）常温下养护10天，待其完全干燥后测其干膜厚度。
（3）将样板放入马弗炉中，并设置炉内温度为400℃，高温加热1小时。
（4）取出测试样板，待样板恢复常温后测其碳层厚度。
（5）膨胀倍率计算，具体计算公式如下：
P=Td/（d-Bd）
式中：
P——膨胀倍率；
Td——碳化层的厚度，cm；
d——钢板和漆膜的总厚度，cm；
Bd——钢板的厚度，cm；
表2——绿色膨胀型家装防火水漆的各实施例测得的膨胀倍率的实验数据：
从表2中可以看出，本发明的绿色膨胀型家装防火水漆的膨胀倍率都很高，碳层坚实，最优实施例2具有较高的膨胀倍率和稳定的碳化层。
表3——本发明的绿色膨胀型家装防火水漆的耐火时间检验依据《南烽一号安全水漆》Q/FJNF 001-2019，进行检验，测得的试验数据：
从表3中可以看出，本发明的实施例1-3的隔热效果都很好，隔热等级都能达到6星级。
表4——检验依据《南烽一号安全水漆》Q/FJNF 001-2019，进行检验，测得的试验
数据如下：
| 序号 | 项目 | 技术指标 | 实施例1 | 实施例2 | 实施例3 |
| 1 | 容器中状态 | 无硬块，搅拌后呈均匀状态 | 符合要求 | 符合要求 | 符合要求 |
| 2 | 施工性 | 涂刷二道无障碍 | 符合要求 | 符合要求 | 符合要求 |
| 3 | 低温稳定性（4次循环） | 不变质 | 不变质 | 不变质 | 不变质 |
| 4 | 涂膜外观 | 正常 | 正常 | 正常 | 正常 |
| 5 | 耐水性 | 经24h试验，涂膜不起皱、不剥落 | 合格 | 合格 | 合格 |
| 6 | 干燥时间/表干（h） | ≤2 | 1.5 | 1.6 | 1.6 |
| 7 | 挥发性有机化合物含量（VOC） | ≤7（g/L） | 未检出 | 未检出 | 未检出 |
| 8 | 苯、甲苯、乙苯、二甲苯总和/（mg/kg） | ≤45 | 18 | 18 | 20 |
| 9 | 游离甲醛/（mg/kg） | ≤5 | 未检出 | 未检出 | 未检出 |
注：耐水性检验依据《饰面型防火涂料》GB 12441-2018.
从表4中可以看出，本发明的实施例1-3的低温稳定性高，耐水性好、干燥时间短，容器中的状态、施工性以及涂膜外观都正常，VOC、苯系物以及游离甲醛的含量都非常低。
综上所述，本发明所制备的绿色膨胀型家装防火水漆储存时间可达18个月以上，隔热性好，克服了现有技术上漆膜耐水性差，储存不稳定，易结晶、返粗，以及膨胀倍率和碳层稳定性之间的矛盾。
本发明中各组份的重量百分配比以以下配比为宜：水20-28%，纤维素0.15-0.45%，水性流变助剂0.2-03%，聚丙烯酸铵盐0.2-0.6%，抑泡剂0.1-0.3%，钛白粉9-12%，高岭土3-9%，云母粉5-8%，改性聚磷酸铵15-25%，季戊四醇6-10%，三聚氰胺5-9%，丙烯酸乳液9-13%，抗冻融剂0.6-0.8%，成膜助剂0.6-0.9%，消泡剂0.1-0.3%，杀菌防霉剂0.1-0.3%，增稠剂0.1-0.4%。其中所述改性聚磷酸铵为甲基三乙氧基硅烷结合微胶囊方法包覆改性的聚磷酸铵，所述钛白粉为金红石型钛白粉，所述高岭土为C-98煅烧高岭土，所述云母粉为绢云母，所述丙烯酸乳液为苯乙烯/丙烯酸酯共聚而成的聚合物；所述抗冻溶剂为乙二醇；所述成膜助剂为醇酯12，所述季戊四醇为2000目季戊四醇；所述三聚氰胺为1250目三聚氰胺，所述杀菌防霉剂由5-氯-2-甲基- 4异噻唑啉-3-酮和1，2-苯并异噻唑啉-3-酮复配而成，所述抑泡剂为矿物油消泡剂和有机硅消泡剂中的一种或组合；所述增稠剂为缔合型聚氨酯类增稠剂。
本明的绿色膨胀型家装防火水漆的制备方法中步骤（1）对各材料的分散容器以在350-450r/min的转速下分散25分钟为宜，步骤（2）在450-1800r/min的转速下加入9-12%钛白粉、3-9%高岭土、5-8%云母粉、 15-25%改性聚磷酸铵、6-10%季戊四醇和5-9%三聚氰胺分散20-25分钟为宜，之后调整转速至1800-2300r/min的转速下分散并研磨至细度<45μm为佳，步骤（3）在600-900r/min的转速下依次加入9-13%丙烯酸乳液、0.6-0.8%抗冻溶剂、0.6-0.9%成膜助剂、0.1-0.3%消泡剂、0.1-0.3%防霉剂和 0.1-0.4%流平剂，分散5-15min为宜。
与现有的放火涂料相比本发明通过采用以上方案具有以下优势：
（1）本发明采用由甲基三乙氧基硅烷改性制得的微胶囊包覆的改性聚磷酸铵，聚合度大于1000，通过微胶囊的方法对聚磷酸铵进行表面处理，聚磷酸铵表面包覆一层疏水性壳层，可以改善聚磷酸铵的耐水性，从而使漆膜耐水性得到提高；在高温阶段，硅类物质燃烧过程中在表面形成二氧化硅保护层，从而提高其热稳定性和成炭量，含硅化合物可以在凝聚相中形成碳层骨架，增强碳层的热阻和受热稳定性，从而提高了漆膜的膨胀倍率以及碳层结构的稳定性。高聚合度的改性聚磷酸铵化学链较稳定，能很大程度的减少因高温等外界条件下使其断链形成氨气或磷酸铵。
（2）本发明避开钠盐分散剂，采用聚丙烯酸铵盐分散剂，有较好的储存稳定性，且其不与改性聚磷酸铵储存中因断链形成的磷酸铵反应形成磷酸钠晶体，从而解决了水漆在储存中结晶的问题，水性流变助剂为有机改性精制锂蒙脱石黏土，有效的低剪切粘度增稠剂，展现稳定的粘度不会出现后增稠。
（3）本发明避开使用重金属含量高的重钙、硅灰石等，避免了重金属离子对聚磷酸铵的影响，从而解决了水漆在储存过程中的返粗现象。
（4）本发明加入一定量的绢云母，呈片层结构，在漆膜中形成平行的取向排列，与腐蚀性物质穿透漆膜的方向垂直，使水和其他腐蚀性物质的渗透受到强烈的阻隔，增加了穿透的路径，穿透时间能延长3倍以上，类似于迷宫效应，从而一定程度上能提高漆膜的耐水性和隔热性。
（5）因聚磷酸铵存在特殊的层层结构，形状类似于书本，存在严重的水滑性，降低体系的摩擦力，导致普通家装喷涂机无法施工，本发明配方中添加了摩擦系数较高的绢云母、煅烧土，提高了涂料体系的摩擦系数，使其适用于目前市场上普通泵压和普通流量的家装喷涂机。
（6）在体系中采用杀菌防霉剂可有效的实现杀菌、抑菌作用，环保性好，符合绿标要求；成膜助剂为醇酯12能降低乳胶漆的成膜温度、提高漆膜的光泽度、强度及抗粉化性能、增进流平性且具有无毒环保的特性、对降低涂料的VOC效果显著。
（7）钛白粉与高岭土结合使用具有良好的耐洗刷性，并能提高钛白粉的分散能力且有效地保持钛白粉的白度、遮盖力、耐候性、耐热性和化学稳定性，且都是无毒。
尽管结合优选实施方案具体展示和介绍了本发明，但所属领域的技术人员应该明白，在不脱离所附权利要求书所限定的本发明的精神和范围内，在形式上和细节上可以对本发明做出各种变化，均为本发明的保护范围。
Claims (10)
1.一种绿色膨胀型家装防火水漆，其特征在于：包括以下重量百分比的原材料组分：
水 20-28%
纤维素 0.15-0.45%
水性流变助剂 0.2-03%
聚丙烯酸铵盐 0.2-0.6%
抑泡剂 0.1-0.3%
钛白粉 9-12%
高岭土 3-9%
云母粉 5-8%
改性聚磷酸铵 15-25%
季戊四醇 6-10%
三聚氰胺 5-9%
丙烯酸乳液 9-13%
抗冻融剂 0.6-0.8%
成膜助剂 0.6-0.9%
消泡剂 0.1-0.3%
杀菌防霉剂 0.1-0.3%
增稠剂 0.1-0.4%；
所述改性聚磷酸铵为甲基三乙氧基硅烷结合微胶囊方法包覆改性的聚磷酸铵。
2.根据权利要求1所述的绿色膨胀型家装防火水漆，其特征在于：所述纤维素为羟乙基纤维素，所述水性流变助剂为有机改性精制锂蒙脱石黏土，所述抑泡剂为矿物油消泡剂和有机硅消泡剂中的一种或组合。
3.根据权利要求1所述的绿色膨胀型家装防火水漆，其特征在于：所述钛白粉为金红石型钛白粉，所述高岭土为C-98煅烧高岭土，所述云母粉为绢云母。
4.根据权利要求1所述的绿色膨胀型家装防火水漆，其特征在于：改性聚磷酸铵是由以下材料按质量百分比通过以下顺序步骤制备而成：
（1）将40-50%乙醇和20-26%水的复配液加入到分散器中；
（2）在300-800rpm转速下加入22-26%聚磷酸酯，接着在700-800rpm转速下加入氨水使其pH值在9.5-10.5；
（3）800-900rpm转速下加入4-10%甲基三乙氧基硅烷，并水浴加热至45℃，反应2-3h；
（4）停止加热和分散，将步骤（3）最后得到的溶液经过过滤、洗涤、干燥和冷却后得到微胶囊化的改性聚磷酸铵。
5.根据权利要求1所述的绿色膨胀型家装防火水漆，其特征在于：所述丙烯酸乳液为苯乙烯/丙烯酸酯共聚而成的聚合物；所述抗冻溶剂为乙二醇；所述成膜助剂为醇酯12。
6.根据权利要求1所述的绿色膨胀型家装防火水漆，其特征在于：所述季戊四醇为2000目季戊四醇；所述三聚氰胺为1250目三聚氰胺。
7.根据权利要求1所述的绿色膨胀型家装防火水漆，其特征在于：所述杀菌防霉剂由5-氯-2-甲基- 4异噻唑啉-3-酮和1，2-苯并异噻唑啉-3-酮复配而成。
8.根据权利要求1所述的绿色膨胀型家装防火水漆，其特征在于：所述消泡剂为有机硅消泡剂；所述增稠剂为缔合型聚氨酯类增稠剂。
9.一种绿色膨胀型家装防火水漆的制备方法，其特征在于：包括以下步骤：
（1）、在350-450r/min的转速下，将20-28%水，0.15-0.45%纤维素，0.2-0.3%水性流变助剂，0.2-0.6%分散剂和0.1-0.3%抑泡剂加入分散器中，分散2-5分钟；
（2）、将步骤（1）分散器分散完成后调整分散器转速至450-1800r/min的转速，再依次加入9-12%钛白粉、3-9%高岭土、5-8%云母粉、 15-25%改性聚磷酸铵、6-10%季戊四醇和5-9%三聚氰胺，分散20-25分钟；再将分散器调整至1800-2300r/min的转速下分散并研磨至细度<45μm；
（3）、将步骤（2）分散并研磨好后调整分散器转速至600-900r/min的转速下再依次加入9-13%丙烯酸乳液、0.6-0.8%抗冻溶剂、0.6-0.9%成膜助剂、0.1-0.3%消泡剂、0.1-0.3%防霉剂和 0.1-0.4%流平剂，分散5-15min至混合物均匀，即可制得绿色膨胀型家装防火水漆。
10.根据权利要求9所述的绿色膨胀型家装防火水漆的制备方法，其特征在于：所述改性聚磷酸铵为甲基三乙氧基硅烷结合微胶囊方法包覆改性的聚磷酸铵，所述钛白粉为金红石型钛白粉，所述高岭土为C-98煅烧高岭土，所述云母粉为绢云母，所述丙烯酸乳液为苯乙烯/丙烯酸酯共聚而成的聚合物；所述抗冻溶剂为乙二醇；所述成膜助剂为醇酯12，所述季戊四醇为2000目季戊四醇；所述三聚氰胺为1250目三聚氰胺，所述杀菌防霉剂由5-氯-2-甲基- 4异噻唑啉-3-酮和1，2-苯并异噻唑啉-3-酮复配而成，所述消泡剂为有机硅消泡剂；所述增稠剂为缔合型聚氨酯类增稠剂。