CN110682610A - 复合织物和制造方法 - Google Patents

复合织物和制造方法 Download PDF

Info

Publication number
CN110682610A
CN110682610A CN201910564848.XA CN201910564848A CN110682610A CN 110682610 A CN110682610 A CN 110682610A CN 201910564848 A CN201910564848 A CN 201910564848A CN 110682610 A CN110682610 A CN 110682610A
Authority
CN
China
Prior art keywords
fabric
composite
composite fabric
insulation
astm
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201910564848.XA
Other languages
English (en)
Other versions
CN110682610B (zh
Inventor
J·李
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
North Face Apparel Corp
Original Assignee
North Face Apparel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by North Face Apparel Corp filed Critical North Face Apparel Corp
Publication of CN110682610A publication Critical patent/CN110682610A/zh
Application granted granted Critical
Publication of CN110682610B publication Critical patent/CN110682610B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明的名称是复合织物和制造方法。一种复合织物包括第一织物层和与所述第一织物层相邻的多个隔热结构。多个隔热结构中的每一个包括限定空腔的织物外壳和位于所述空腔内的隔热材料。在其它方面，一种复合织物包括由多个间隔物分隔开的多个隔热结构。多个间隔物中的每一个包括织物材料，并且多个隔热结构中的每一个包括限定空腔的织物外壳和位于所述空腔内的隔热材料。

Description

复合织物和制造方法
技术领域
本公开涉及复合织物，并且尤其涉及包括多个隔热结构的复合织物，所述隔热结构为复合织物提供绝热(thermal insulation)。
背景技术
服装物品可以包括有包括隔热体的材料。隔热体的实例包括天然填充材料，例如羽绒(例如鹅或鸭羽毛)；和合成填充材料，例如聚酯。隔热体可以在材料内移动。举例来说，隔热体可以由于使用物品、物品穿着者移动和/或重力而移动。
另外，隔热体可能不均匀地分布在整个材料中。作为一个实例，由于隔热体在材料内移动，所述隔热体可能不均匀地分布在整个材料中。作为另一实例，由于制造材料的方法和/或将隔热体安置在材料内的方法，隔热体可能不均匀地分布在整个材料中。因此，服装物品可以具有绝热不同的区域。
这些和其它缺点由本公开的各方面解决。
发明内容
本公开的各方面涉及一种复合织物，其包括第一织物层和与所述第一织物层相邻的多个隔热结构。多个隔热结构中的每一个包括限定空腔的织物外壳和位于所述空腔内的隔热材料。
本公开的各方面进一步涉及一种复合织物，其包括由多个间隔物分隔开的多个隔热结构。多个间隔物中的每一个包括织物材料，并且多个隔热结构中的每一个包括限定空腔的织物外壳和位于所述空腔内的隔热材料。
附图说明
在不一定按比例绘制的附图中，相似标号可以在不同视图中描述类似组件。具有不同字母后缀的相似标号可以表示类似组件的不同实例。附图通过示例而非通过限制的方式示出了本文件中所讨论的各种实施例。
图1A是根据本公开的一个方面的复合织物的顶部透视图。
图1B是图1A复合织物的一侧的照片。
图1C是图1A复合织物的另一侧的照片。
图2A是根据本公开的一个方面的复合织物的顶部透视图。
图2B是图2A复合织物的照片。
图3A是根据本公开的一个方面的复合织物的顶部透视图。
图3B是图3A复合织物的照片。
具体实施方式
通过参考以下对本公开的详细描述和其中包括的实施例，可以更容易地理解本公开。在各种方面，本公开涉及复合织物，其包括第一织物层和与所述第一织物层相邻的多个隔热结构，所述多个隔热结构中的每一个包括限定空腔的织物外壳和位于所述空腔内的隔热材料。本公开的其它方面涉及一种复合织物，其包括由多个间隔物分隔开的多个隔热结构，其中所述多个间隔物中的每一个包括织物材料，并且所述多个隔热结构中的每一个包括限定空腔的织物外壳和位于所述空腔内的隔热材料。
在公开和描述本发明化合物、组合物、物品、系统、装置和/或方法之前，应理解，除非另外指定，否则其不限于特定的合成方法，或除非另外指定，否则不限于特定的试剂，因为这类合成方法或特定试剂显然可能变化。还应理解，本文所用的术语仅用于描述特定方面的目的，而不打算是限制性的。
本公开涵盖本公开的要素的各种组合，例如来自附属于同一独立权利要求的附属权利要求的要素的组合。
此外，应理解，除非另外明确陈述，否则决不打算将本文所阐述的任何方法解释为要求以特定次序执行其步骤。因此，在方法权利要求没有实际叙述其步骤待遵循的次序，或在权利要求书或说明书中没有具体陈述所述步骤将被限制为特定次序的情况下，决不打算在任何方面推断次序。这适用于任何可能的非明确解释基础，包括：关于步骤安排或操作流程的逻辑问题；由语法组织或标点符号得出的简单含义；以及说明书中所描述的实施例的数量或类型。
本文提及的所有出版物都以引入的方式并入本文中，以公开和描述与所引用的出版物相关的方法和/或材料。
定义
还应理解，本文所用的术语仅用于描述特定方面的目的，而不打算是限制性的。如在说明书中和权利要求书中所用，术语“包含”可以包括实施例“由……组成”和“基本上由……组成”。除非另外定义，否则本文所用的所有技术和科学术语都具有与本公开所属领域的普通技术人员通常理解的相同的含义。在本说明书中和随附权利要求书中，将参考本文中所定义的多个术语。
如在说明书中和所附权利要求书中所用，除非上下文另外明确规定，否则单数形式“一(a/an)”和“所述”包括多个指示物。因此，举例来说，提及“隔热材料”包括两种或更多种隔热材料的混合物。
如本文所用，术语“组合”包括共混物\混合物\合金\反应产物等。
范围在本文中可以表述为从一个值(第一值)至另一个值(第二值)。当表述这类范围时，所述范围在一些方面包括第一值和第二值中的一个或两个。类似地，当通过使用前置词‘约’将值表述为近似值时，应理解，特定值形成另一方面。进一步应理解，每个范围的端点在与另一端点相关以及独立于另一端点的情况下都是有效的。还应理解，本文公开了许多值，并且除了所述值本身之外，每个值在本文中也公开为“约”该特定值。举例来说，如果则公开值“10”，则还公开“约10”。还应理解，还公开介于两个特定单元之间的每个单元。举例来说，如果公开10和15，则还公开11、12、13和14。
如本文所用，术语“约”和“处于或约”意味着所讨论的量或值可以是指定值、大约指定值、或与指定值约相同。如本文所用，一般理解的是，除非另外指示或推断，否则标称值指示±10％变化。所述术语打算传达，类似值促进权利要求书中所叙述的等效结果或作用。也就是说，应理解，量、大小、配方、参数和其它数量和特性并非也不必是准确的，但可以根据需要近似和/或更大或更小，从而反映公差、转换因子、四舍五入、测量误差等和本领域的技术人员已知的其它因素。一般来说，量、大小、配方、参数或其它数量或特征是“约”或“近似”，无论是否明确陈述如此。应理解，当在定量值之前使用“约”时，除非另外具体陈述，否则参数还包括特定的定量值本身。
除非本文另外相反地陈述，否则所有测试标准都是在提交本申请时有效的最新标准。
本文所公开的每种材料都可商购获得和/或其制备方法是本领域的技术人员已知的。
应理解，本文所公开的组合物具有某些功能。本文公开针对执行所公开功能的某些结构要求，并且应理解，存在可以执行与所公开结构相关的相同功能的各种结构，并且这些结构通常会实现相同的结果。
包括第一织物层和隔热结构的复合织物
参考图1A-2B，本公开的各方面涉及一种复合织物100、200，其包括第一织物层130、230和与所述第一织物层130、230相邻的多个隔热结构140、240。在一些方面，多个隔热结构140、240中的每一个包括限定空腔160、260的织物外壳150、250和位于所述空腔160、260内的隔热材料(未示出)。
第一织物层130、230可以位于织物和/或由其形成的衣物的任一侧。举例来说，在一些方面，第一织物层130、230位于复合织物100、200的身体侧，即，织物面向使用者身体的一侧。在其它方面中第一织物层130、230位于复合织物100、200的正面(face side)，即，织物背对使用者身体的一侧。在某些方面，复合织物100、200是可翻转的，以使得织物的使用者(例如，包括复合织物100、200的衣物的穿着者)可以在第一织物层130、230面向使用者或背对使用者的情况下使用所述复合织物。也如本文所用，“相邻”意味着处于上方或接近，并且不排除中间组件，包括额外的(多个)织物层、空气或流体。
参考图1A-1C，在一些方面，多个隔热结构140中的每一个附接到第一织物层130。在特定方面，多个隔热结构140中的每一个被缝合170到第一织物层(隔热结构140的底部示出为直接缝合到第一织物层130)。多个隔热结构140可以通过任何合适的方法附接到第一织物层130，例如使用粘合剂、进行缝纫、针织、焊接或缝合。
在一些方面，图1A-1C中所示的多个隔热结构140可以松散地附接(或缝合170)到第一织物层130，以使得其能自由移动。当使用(例如穿着)织物时，多个隔热结构可以抵靠第一织物层130放置(由箭头180示出)，从而在复合织物100中形成温暖的隔热层。
参考图2A和2B，在其它方面，多个隔热结构240中的每一个通过多个织物条带270保持抵靠第一织物层230。在一些方面，多个织物条带270可以以编织构造将多个隔热结构240保持抵靠第一织物层230。可以使用任何合适的编织图案。在一些方面，编织图案是平纹编织(1×1，如图所示)。在某些方面，编织图案是缎纹编织或斜纹编织(例如，1×2、1×3、2×2等)。复合织物200的组件可以具有任何合乎期望的尺寸。举例来说，在一些方面，对多个隔热结构240进行大小设定以使得当使用(例如穿着)织物时，多个隔热结构240抵靠和/或基本上覆盖第一织物层230放置(如由箭头280所示)，从而为复合织物200提供隔热层。
第一织物层130、230可以具有任何合适的织物构造。在一些方面，第一织物层130、230是编织织物。在其它方面，第一织物层130、230是针织织物、非编织织物或层压织物。在特定方面，第一织物层130、230包括塔夫绸(taffeta)，但可以使用任何其它合适的织物材料，包括但不限于棉、羊毛、尼龙、聚酯以及其组合。
在某些方面，第一织物层130、230是高度透气的或具有空气透过性。空气透过率可以根据ASTM D737来加以测定，并且以立方英尺/分钟(cubic feet per minute，CFM)为单位报告。在一些方面，当根据ASTM D737测试时，第一织物层130、230的空气透过率为约40CFM至约80CFM。在特定方面，当根据ASTM D737测试时，第一织物层130、230的空气透过率为约50CFM至约60CFM。第一织物层130、230的较高空气透过率为复合织物100、200提供允许水分穿过的透气层。
织物外壳150、250可以具有任何合适的织物构造。在一些方面，织物外壳150、250是编织织物、针织织物、非编织织物或层压织物。在特定方面，织物外壳150、250包括塔夫绸，但可以使用任何其它合适的织物材料，包括但不限于棉、羊毛、聚酯、尼龙以及其组合。
在一些方面，可能期望织物外壳150、250对于空气基本上不可渗透或透过率极低。在特定方面，当根据ASTM D737测试时，织物外壳150、250的空气透过率为0CFM至约5CFM。在其它方面，当根据ASTM D737测试时，织物外壳150、250的空气透过率为0CFM至约2CFM。将不可渗透或基本上不可渗透的织物用于织物外壳150、250为织物提供温暖，并且将隔热材料包封在空腔160、260中以防止所述隔热材料在复合织物100、200内迁移或移动或使所述迁移或移动减到最少。
如所提到的，多个隔热结构140、240中的每一个包括限定空腔160、260的织物外壳150、250和位于所述空腔160、260内的隔热材料。可以使用任何合适的隔热材料，包括天然隔热材料、合成隔热材料或其组合。在特定方面，隔热材料包括至少一种天然隔热材料，包括羽绒(例如鹅或鸭羽毛)。可用于复合织物100、200中的其它天然隔热材料包括但不限于棉和羊毛。在其它方面，隔热材料包括至少一种合成隔热材料，包括聚酯。可以在复合织物100、200中使用的其它合成隔热材料包括但不限于
Figure BDA0002109253990000061
新雪丽TM(ThinsulateTM)、
Figure BDA0002109253990000062
ThermoBallTM、聚对苯二甲酸乙二酯、聚丙烯、丙烯酸类以及其组合。可以通过任何常规方法将隔热材料插入到空腔中，包括但不限于吹气、插入、注射和剑杆插入。另外，隔热材料可以呈任何形式。在一些方面，隔热材料是松散纤维；在其它方面；隔热材料成形(例如以管状形式)。
包括隔热结构和间隔物的复合织物
参考图3A和3B，本公开的各方面进一步涉及一种复合织物300，其包括由多个间隔物320分隔开的多个隔热结构310。多个间隔物320中的每一个包括织物材料，并且多个隔热结构310中的每一个包括限定空腔340的织物外壳330和位于所述空腔340内的隔热材料。
在某些方面，复合织物300是可翻转的，以使得织物的使用者(例如，包括复合织物300的衣物的穿着者)可以在任一侧面向使用者或背对使用者的情况下使用所述复合织物300。
多个间隔物320可以具有任何合适的织物构造。在一些方面，多个间隔物320是编织织物。在其它方面，多个间隔物320是针织织物、非编织织物或层压织物。在特定方面，多个间隔物320包括塔夫绸，但可以使用任何其它合适的织物材料，包括但不限于棉、羊毛、聚酯、尼龙以及其组合。多个间隔物320可以具有任何合乎期望的尺寸。在一些方面，如图所示，多个间隔物320是织物条带。
多个间隔物320和织物外壳330可以具有任何合适的尺寸。在某个方面，多个间隔物320的宽度为约1英寸(1")，并且织物外壳330的宽度为约5"至约6"。另外，多个间隔物320和/或织物外壳330可以在同一复合织物300内具有不同尺寸。可以对多个间隔物320进行大小设定以使得当使用(例如穿着)织物时，多个隔热结构310抵靠和/或基本上重叠或覆盖多个间隔物320放置(如由箭头350所示)，从而为复合织物300提供隔热层。
在某些方面，多个间隔物320具有高度空气透过性。在一些方面，当根据ASTM D737测试时，多个间隔物320的空气透过率为约40CFM至约80CFM。在特定方面，当根据ASTM D737测试时，多个间隔物320的空气透过率为约50CFM至约60CFM。多个间隔物320的较高空气透过率为复合织物300提供允许水分穿过的透气组件。
织物外壳330可以具有任何合适的织物构造。在一些方面，织物外壳330是编织织物、针织织物、非编织织物或层压织物。在特定方面，织物外壳330包括塔夫绸，但可以使用任何其它合适的织物材料，包括但不限于棉、羊毛、聚酯、尼龙以及其组合。
在一些方面，可能期望织物外壳330对于空气基本上不可渗透或透过率极低。在特定方面，当根据ASTM D737测试时，织物外壳330的空气透过率为0CFM至约5CFM。在其它方面，当根据ASTM D737测试时，织物外壳330的空气透过率为0CFM至约2CFM。将不可渗透或基本上不可渗透的织物用于织物外壳330为织物提供温暖，并且将隔热材料包封在空腔340中以防止所述隔热材料在复合织物300内迁移或移动或使所述迁移或移动减到最少。
如所提到的，多个隔热结构310中的每一个包括限定空腔340的织物外壳330和位于所述空腔340内的隔热材料。可以使用任何合适的隔热材料，包括天然隔热材料、合成隔热材料或其组合。在特定方面，隔热材料包括至少一种天然隔热材料，包括羽绒(例如鹅或鸭羽毛)。可用于复合织物300中的其它天然隔热材料包括但不限于棉和羊毛。在其它方面，隔热材料包括至少一种合成隔热材料，包括聚酯。可以在复合织物300中使用的其它合成隔热材料包括但不限于
Figure BDA0002109253990000081
新雪丽TM、
Figure BDA0002109253990000082
ThermoBallTM、聚对苯二甲酸乙二酯、聚丙烯、丙烯酸类以及其组合。可以通过任何常规方法将隔热材料插入到空腔中，包括但不限于吹气、插入、注射和剑杆插入。另外，隔热材料可以呈任何形式。在一些方面，隔热材料是松散纤维；在其它方面；隔热材料成形(例如以管状形式)。
复合织物100、200、300和其组件可以根据常规方法(例如，常规缝合、编织和针织方法)来形成。
本文所描述的复合织物100、200、300可以并入到织物中并且用于制造物品。示例性物品包括服装物品，例如夹克、裤子、帽子、手套、连身衣和其它外衣。其它示例性物品包括但不限于毯子、运动装备(例如头盔的衬里)和户外装备。
本公开涵盖本公开的要素的各种组合，例如来自附属于同一独立权利要求的附属权利要求的要素的组合。
本公开的各方面
在各种方面，本公开涉及并且包括至少以下方面。
方面1.一种复合织物，其包含：
第一织物层；和
与所述第一织物层相邻的多个隔热结构，所述多个隔热结构中的每一个包含限定空腔的织物外壳和位于所述空腔内的隔热材料。
方面2.根据方面1所述的复合织物，其中所述多个隔热结构中的每一个附接到所述第一织物层。
方面3.根据方面1或2所述的复合织物，其中所述多个隔热结构中的每一个缝合到所述第一织物层。
方面4.根据方面1所述的复合织物，其中所述多个隔热结构中的每一个通过多个织物条带保持抵靠所述第一织物层。
方面5.根据方面4所述的复合织物，其中所述多个织物条带以编织构造将所述多个隔热结构保持抵靠所述第一织物层。
方面6.根据方面1至5中任一个所述的复合织物，其中所述第一织物层包含编织织物或针织织物。
方面7.根据方面1至6中任一个所述的复合织物，其中当根据ASTM D737测试时，所述第一织物层的空气透过率为约40立方英尺/分钟(CFM)至约80CFM。
方面8.根据方面1至6中任一个所述的复合织物，其中当根据ASTM D737测试时，所述第一织物层的空气透过率为约50CFM至约60CFM。
方面9.根据方面1至8中任一个所述的复合织物，其中所述织物外壳包含编织织物、针织织物、非编织织物或层压织物。
方面10.根据方面1至9中任一个所述的复合织物，其中当根据ASTM D737测试时，所述织物外壳的空气透过率为0CFM至约5CFM。
方面11.根据方面1至10中任一个所述的复合织物，其中当根据ASTM D737测试时，所述织物外壳的空气透过率为0CFM至约2CFM。
方面12.根据方面1至11中任一个所述的复合织物，其中所述隔热材料包含天然隔热材料、合成隔热材料或其组合。
方面13.根据方面12所述的复合织物，其中所述天然隔热材料包含羽绒、棉、羊毛或其组合。
方面14.根据方面12所述的复合织物，其中所述合成隔热材料包含聚酯、聚对苯二甲酸乙二酯、聚丙烯、丙烯酸类、新雪丽TM、
Figure BDA0002109253990000102
ThermoBallTM以及其组合。
方面15.一种复合织物，其包含由多个间隔物分隔开的多个隔热结构，其中所述多个间隔物中的每一个包含织物材料，并且所述多个隔热结构中的每一个包含限定空腔的织物外壳和位于所述空腔内的隔热材料。
方面16.根据方面15所述的复合织物，其中所述织物材料包含编织织物、针织织物、非编织织物或层压织物。
方面17.根据方面15或16所述的复合织物，其中当根据ASTM D737测试时，所述织物材料的空气透过率为约40CFM至约80CFM。
方面18.根据方面15至17中任一个所述的复合织物，其中当根据ASTM D737测试时，所述织物材料的空气透过率为约50CFM至约60CFM。
方面19.根据方面15至18中任一个所述的复合织物，其中所述织物外壳包含编织织物、针织织物、非编织织物或层压织物。
方面20.根据方面15至19中任一个所述的复合织物，其中当根据ASTM D737测试时，所述织物外壳的空气透过率为0CFM至约5CFM。
方面21.根据方面15至20中任一个所述的复合织物，其中当根据ASTM D737测试时，所述织物外壳的空气透过率为0CFM至约2CFM。
方面22.根据方面15至21中任一个所述的复合织物，其中所述隔热材料包含天然隔热材料、合成隔热材料或其组合。
方面23.根据方面22所述的复合织物，其中所述天然隔热材料包含羽绒、棉、羊毛或其组合。
方面24.根据方面23所述的复合织物，其中所述合成隔热材料包含聚酯、聚对苯二甲酸乙二酯、聚丙烯、丙烯酸类、
Figure BDA0002109253990000111
新雪丽TM、
Figure BDA0002109253990000112
Figure BDA0002109253990000113
ThermoBallTM以及其组合。
本文所描述的方法实例可至少部分地由机器或计算机实施。一些实例可以包括编码有指令的计算机可读介质或机器可读介质，所述指令可操作以配置电子装置来执行如在上文实例中所描述的方法。这类方法的实施可以包括代码，例如微代码、汇编语言代码、更高级语言代码等。这类代码可以包括用于执行各种方法的计算机可读指令。代码可以形成计算机程序产品的一部分。此外，在一个实例中，代码可以有形地存储在一个或多个易失性、非暂时性或非易失性有形计算机可读介质上，例如在执行期间或在其它时间存储。这些有形计算机可读介质的实例可以包括但不限于硬盘、可移动磁盘、可移动光盘(例如，光盘和数字视频磁盘)、盒式磁带、存储卡或棒、随机存取存储器(RAM)、只读存储器(ROM)等。
上文描述打算是说明性的，而不是限定性的。举例来说，上文所描述的实例(或其一个或多个方面)可以彼此组合使用。在查阅上文描述后，例如本领域的普通技术人员可以使用其它实施例。提供摘要以符合37C.F.R.§1.72(b)，以允许读者迅速确定技术公开内容的性质。在理解以下内容的情况下进行提交：其将不会用于解释或限制权利要求书的范围或含义。此外，在上文详细描述中，可以将各种特征分组在一起以简化本公开。这不应解释为希望未要求的公开特征对于任何权利要求是必不可少的。相反，本发明主题可以在于特定公开实施例的少于全部特征。因此，以下权利要求书特此作为实例或实施例并入详细描述中，其中每个权利要求自身作为单独的实施例，并且预期这类实施例可以彼此组合成各种组合或排列。应参考所附权利要求书以及授予这类权利要求书的等同物的完整范围来确定本发明的范围。

Claims (24)

1.一种复合织物，其包含：
第一织物层；和
与所述第一织物层相邻的多个隔热结构，所述多个隔热结构中的每一个包含限定空腔的织物外壳和位于所述空腔内的隔热材料。
2.根据权利要求1所述的复合织物，其中所述多个隔热结构中的每一个附接到所述第一织物层。
3.根据权利要求1或2所述的复合织物，其中所述多个隔热结构中的每一个缝合到所述第一织物层。
4.根据权利要求1所述的复合织物，其中所述多个隔热结构中的每一个通过多个织物条带保持抵靠所述第一织物层。
5.根据权利要求4所述的复合织物，其中所述多个织物条带以编织构造将所述多个隔热结构保持抵靠所述第一织物层。
6.根据权利要求1至5中任一项所述的复合织物，其中所述第一织物层包含编织织物或针织织物。
7.根据权利要求1至6中任一项所述的复合织物，其中当根据ASTM D737测试时，所述第一织物层的空气透过率为约40立方英尺/分钟(CFM)至约80CFM。
8.根据权利要求1至6中任一项所述的复合织物，其中当根据ASTM D737测试时，所述第一织物层的空气透过率为约50 CFM至约60 CFM。
9.根据权利要求1至8中任一项所述的复合织物，其中所述织物外壳包含编织织物、针织织物、非编织织物或层压织物。
10.根据权利要求1至9中任一项所述的复合织物，其中当根据ASTM D737测试时，所述织物外壳的空气透过率为0 CFM至约5 CFM。
11.根据权利要求1至10中任一项所述的复合织物，其中当根据ASTMD737测试时，所述织物外壳的空气透过率为0 CFM至约2 CFM。
12.根据权利要求1至11中任一项所述的复合织物，其中所述隔热材料包含天然隔热材料、合成隔热材料或其组合。
13.根据权利要求12所述的复合织物，其中所述天然隔热材料包含羽绒、棉、羊毛或其组合。
14.根据权利要求12所述的复合织物，其中所述合成隔热材料包含聚酯、聚对苯二甲酸乙二酯、聚丙烯、丙烯酸类以及其组合。
15.一种复合织物，其包含由多个间隔物分隔开的多个隔热结构，其中所述多个间隔物中的每一个包含织物材料，并且所述多个隔热结构中的每一个包含限定空腔的织物外壳和位于所述空腔内的隔热材料。
16.根据权利要求15所述的复合织物，其中所述织物材料包含编织织物、针织织物、非编织织物或层压织物。
17.根据权利要求15或16所述的复合织物，其中当根据ASTM D737测试时，所述织物材料的空气透过率为约40 CFM至约80 CFM。
18.根据权利要求15至17中任一项所述的复合织物，其中当根据ASTM D737测试时，所述织物材料的空气透过率为约50 CFM至约60 CFM。
19.根据权利要求15至18中任一项所述的复合织物，其中所述织物外壳包含编织织物、针织织物、非编织织物或层压织物。
20.根据权利要求15至19中任一项所述的复合织物，其中当根据ASTM D737测试时，所述织物外壳的空气透过率为0 CFM至约5 CFM。
21.根据权利要求15至20中任一项所述的复合织物，其中当根据ASTM D737测试时，所述织物外壳的空气透过率为0 CFM至约2 CFM。
22.根据权利要求15至21中任一项所述的复合织物，其中所述隔热材料包含天然隔热材料、合成隔热材料或其组合。
23.根据权利要求22所述的复合织物，其中所述天然隔热材料包含羽绒、棉、羊毛或其组合。
24.根据权利要求23所述的复合织物，其中所述合成隔热材料包含聚酯、聚对苯二甲酸乙二酯、聚丙烯、丙烯酸类以及其组合。
CN201910564848.XA 2018-07-05 2019-06-27 复合织物和制造方法 Active CN110682610B (zh)