CN110644226A - Production process of environment-friendly antibacterial yarn - Google Patents
Production process of environment-friendly antibacterial yarn Download PDFInfo
- Publication number
- CN110644226A CN110644226A CN201910789422.4A CN201910789422A CN110644226A CN 110644226 A CN110644226 A CN 110644226A CN 201910789422 A CN201910789422 A CN 201910789422A CN 110644226 A CN110644226 A CN 110644226A
- Authority
- CN
- China
- Prior art keywords
- parts
- yarn
- oven
- drying
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production process of environment-friendly antibacterial yarn, which comprises the following specific steps: preparing loose fibers, sending the loose fibers into cleaning equipment for cleaning, and drying the loose fibers in an oven after the loose fibers are cleaned; feeding the cleaned yarn into a dye vat for dyeing treatment, and feeding the dyed yarn into an oven for drying; putting the dyed yarns into a dipping tank for dipping treatment, and sending the yarns into a drying oven for drying after dipping; and (3) delivering the impregnated yarn into an antibacterial pool for soaking, and delivering the impregnated yarn into an oven for drying to obtain a yarn product. The production process is simple to operate, and the produced yarn is healthier and more environment-friendly and has excellent antibacterial performance.
Description
Technical Field
The invention belongs to the technical field of yarns, and particularly relates to a production process of an environment-friendly antibacterial yarn.
Background
The yarn is a product processed by various textile fibers into a certain fineness and used for weaving, rope making, thread making, knitting, embroidering and the like, along with the improvement of living standard, people pay more and more attention to the quality of textiles and require clothes to be safer, healthier and more environment-friendly.
Disclosure of Invention
In order to solve the defects of the prior art, the invention aims to provide the production process of the environment-friendly antibacterial yarn, the operation is simple, and the produced yarn is healthier and more environment-friendly and has excellent antibacterial performance.
In order to achieve the above object, the present invention adopts the following technical solutions:
the production process of the environment-friendly antibacterial yarn comprises the following specific steps:
s1, preparing loose fibers, sending the loose fibers into cleaning equipment, cleaning, drying the loose fibers in an oven after cleaning, and cooling the loose fibers to room temperature after taking out;
s2, feeding the cleaned yarn into a dye vat for dyeing, feeding the dyed yarn into an oven for drying, taking out and cooling to room temperature;
s3, putting the dyed yarns into a dipping tank for dipping treatment, after dipping for 1.5 ~ 2h, sending the yarns into an oven for drying, taking out and cooling to room temperature;
and S4, delivering the impregnated yarn into an antibacterial pool for soaking, drying the impregnated yarn in an oven, taking out, and cooling to room temperature to obtain a yarn product.
Preferably, in the foregoing step S1, the loose fibers are sprayed with clean water three times in the cleaning device, each time the spraying time is 15 ~ 20min, and the temperature of the clean water is 35 ~ 40 ℃.
Still preferably, in the step S1, the oven temperature is 50 ~ 55 ℃, and the drying time is 25 ~ 35 min.
More preferably, in the foregoing steps S2, S3 and S4, the oven temperature is 55 ~ 60 ℃ and the drying time is 15 ~ 25 min.
Further preferably, in the step S3, the steeping liquor in the steeping vat comprises 20 ~ 38 parts by weight of ethyl acetate, 15 ~ 27 parts by weight of ethylene glycol, 18 ~ 23 parts by weight of citric acid, 8 ~ 11 parts by weight of micron carbon particles, 12 ~ 19 parts by weight of glycerol and 3 ~ 7 parts by weight of n-dodecane.
Specifically, the particle size of the carbon micron particles is 0.35 ~ 0.56.56 μm.
Preferably, in the aforementioned step S4, the antibiotic liquid of the antibiotic bath includes, in parts by weight, 28 ~ 34 parts of titanium dioxide, 21 ~ 33 parts of ethylenediamine, 19 ~ 28 parts of menthol, 15 ~ 21 parts of chamomile, 11 ~ 14 parts of grapefruit peel extract, 7 ~ 9 parts of nano-silver particles, and 2 ~ 5 parts of glycerin.
Still preferably, in the step S4, the temperature of the antibacterial pool is 55 ~ 65 ℃, and the soaking time is 2 ~ 2.5.5 h.
The invention has the advantages that: the production process of the environment-friendly antibacterial yarn is simple to operate, and the produced yarn is healthier and more environment-friendly and has excellent antibacterial performance; a layer of film can be formed on the surface of the dyed yarn by dipping in a dipping tank, and micron carbon particles, glycerol and n-dodecane are added into a dipping solution, so that the film can be formed more uniformly, the wear resistance of the yarn can be improved, the fading condition of the yarn is reduced, the quality of the yarn is improved, and the harm to the body of a user can be avoided; by adding the menthol, the chamomile and the shaddock peel extract into the antibacterial liquid, the antibacterial property of the yarn can be improved, the yarn has natural plant fragrance, and a user feels more comfortable.
Detailed Description
The present invention will be described in detail with reference to the following embodiments.
Example 1
The production process of the environment-friendly antibacterial yarn comprises the following specific steps:
s1, preparing loose fibers, sending the loose fibers into cleaning equipment for cleaning, and spraying the loose fibers in the cleaning equipment for three times by using clean water, wherein the spraying time is 15min each time, and the temperature of the clean water is 35 ℃; cleaning, drying in an oven at 50 deg.C for 25min, and cooling to room temperature;
s2, feeding the cleaned yarn into a dye vat for dyeing, feeding the dyed yarn into an oven for drying, wherein the oven temperature is 55 ℃, the drying time is 15min, and taking out the yarn and cooling the yarn to room temperature;
s3, putting the dyed yarn into a dipping tank for dipping treatment, wherein the dipping solution comprises the following components in parts by weight: 20 parts of ethyl acetate, 15 parts of ethylene glycol, 18 parts of citric acid, 8 parts of micrometer carbon particles, 12 parts of glycerol and 3 parts of n-dodecane, wherein the particle size of the micrometer carbon particles is 0.35 mu m; after dipping for 1.5h, sending the yarn into an oven for drying, wherein the oven temperature is 55 ℃, the drying time is 15min, and cooling to room temperature after taking out;
s4, feeding the yarn after being soaked into an antibacterial pool for soaking, wherein the antibacterial solution comprises the following components in parts by weight: 28 parts of titanium dioxide, 21 parts of ethylenediamine, 19 parts of menthol, 15 parts of chamomile, 11 parts of a shaddock peel extract, 7 parts of nano-silver particles and 2 parts of glycerol; and (3) the temperature of the antibacterial pool is 55 ℃, the soaking time is 2 hours, the soaked yarn enters an oven to be dried, the oven temperature is 55 ℃, the drying time is 15 minutes, and the yarn is taken out and cooled to room temperature to obtain a yarn product.
Example 2
The production process of the environment-friendly antibacterial yarn comprises the following specific steps:
s1, preparing loose fibers, sending the loose fibers into cleaning equipment for cleaning, and spraying the loose fibers in the cleaning equipment for three times by using clean water, wherein the spraying time is 20min each time, and the temperature of the clean water is 40 ℃; cleaning, drying in an oven at 55 deg.C for 35min, and cooling to room temperature;
s2, feeding the cleaned yarn into a dye vat for dyeing, feeding the dyed yarn into an oven for drying, wherein the oven temperature is 60 ℃, the drying time is 25min, and taking out the yarn and cooling the yarn to room temperature;
s3, putting the dyed yarn into a dipping tank for dipping treatment, wherein the dipping solution comprises the following components in parts by weight: 38 parts of ethyl acetate, 27 parts of ethylene glycol, 23 parts of citric acid, 11 parts of micrometer carbon particles, 19 parts of glycerol and 7 parts of n-dodecane, wherein the particle size of the micrometer carbon particles is 0.56 mu m; after dipping for 2h, sending the yarns into an oven for drying, wherein the temperature of the oven is 60 ℃, the drying time is 25min, and cooling to room temperature after taking out;
s4, feeding the yarn after being soaked into an antibacterial pool for soaking, wherein the antibacterial solution comprises the following components in parts by weight: 34 parts of titanium dioxide, 33 parts of ethylenediamine, 28 parts of menthol, 21 parts of chamomile, 14 parts of shaddock peel extract, 9 parts of nano-silver particles and 5 parts of glycerol; and (3) the temperature of the antibacterial pool is 65 ℃, the soaking time is 2.5h, the soaked yarn enters an oven to be dried, the oven temperature is 60 ℃, the drying time is 25min, and the yarn is taken out and cooled to room temperature to obtain a yarn product.
Example 3
The production process of the environment-friendly antibacterial yarn comprises the following specific steps:
s1, preparing loose fibers, sending the loose fibers into cleaning equipment for cleaning, and spraying the loose fibers in the cleaning equipment for three times by using clean water, wherein the spraying time is 18min each time, and the temperature of the clean water is 37 ℃; cleaning, drying in an oven at 53 deg.C for 30min, and cooling to room temperature;
s2, feeding the cleaned yarn into a dye vat for dyeing, feeding the dyed yarn into an oven for drying, wherein the oven temperature is 57 ℃, the drying time is 20min, and taking out the yarn and cooling the yarn to room temperature;
s3, putting the dyed yarn into a dipping tank for dipping treatment, wherein the dipping solution comprises the following components in parts by weight: 29 parts of ethyl acetate, 20 parts of ethylene glycol, 20 parts of citric acid, 9 parts of micrometer carbon particles, 15 parts of glycerol and 5 parts of n-dodecane, wherein the particle size of the micrometer carbon particles is 0.4 mu m; after dipping for 1.8h, sending the yarns into an oven for drying, wherein the oven temperature is 57 ℃, the drying time is 20min, and taking out the yarns and cooling the yarns to room temperature;
s4, feeding the yarn after being soaked into an antibacterial pool for soaking, wherein the antibacterial solution comprises the following components in parts by weight: 31 parts of titanium dioxide, 27 parts of ethylenediamine, 24 parts of menthol, 18 parts of chamomile, 13 parts of shaddock peel extract, 8 parts of nano-silver particles and 4 parts of glycerol; and (3) the temperature of the antibacterial pool is 60 ℃, the soaking time is 2.2h, the soaked yarn enters an oven to be dried, the oven temperature is 58 ℃, the drying time is 20min, and the yarn is taken out and cooled to room temperature to obtain a yarn product.
The foregoing shows and describes the general principles, features and advantages of the present invention. It should be understood by those skilled in the art that the above embodiments do not limit the present invention in any way, and all technical solutions obtained by using equivalent alternatives or equivalent variations fall within the scope of the present invention.
Claims (8)
1. The production process of the environment-friendly antibacterial yarn is characterized by comprising the following specific steps of:
s1, preparing loose fibers, sending the loose fibers into cleaning equipment, cleaning, drying the loose fibers in an oven after cleaning, and cooling the loose fibers to room temperature after taking out;
s2, feeding the cleaned yarn into a dye vat for dyeing, feeding the dyed yarn into an oven for drying, taking out and cooling to room temperature;
s3, putting the dyed yarns into a dipping tank for dipping treatment, after dipping for 1.5 ~ 2h, sending the yarns into an oven for drying, taking out and cooling to room temperature;
and S4, delivering the impregnated yarn into an antibacterial pool for soaking, drying the impregnated yarn in an oven, taking out, and cooling to room temperature to obtain a yarn product.
2. The process of claim 1, wherein in step S1, the loose fibers are sprayed with clean water three times in a cleaning device, each time the spraying time is 15 ~ 20min, and the temperature of the clean water is 35 ~ 40 ℃.
3. The process for producing environment-friendly antibacterial yarn according to claim 1, wherein in the step S1, the oven temperature is 50 ~ 55 ℃ and the drying time is 25 ~ 35 min.
4. The process for producing environment-friendly antibacterial yarn according to claim 1, wherein in the steps S2, S3 and S4, the oven temperature is 55 ~ 60 ℃ and the drying time is 15 ~ 25 min.
5. The process of claim 1, wherein in step S3, the steeping liquor in the steeping vat comprises 20 ~ 38 parts by weight of ethyl acetate, 15 ~ 27 parts by weight of ethylene glycol, 18 ~ 23 parts by weight of citric acid, 8 ~ 11 parts by weight of micron carbon particles, 12 ~ 19 parts by weight of glycerol and 3 ~ 7 parts by weight of n-dodecane.
6. The process for producing environment-friendly antibacterial yarn as claimed in claim 5, wherein the particle size of the micrometer carbon particles is 0.35 ~ 0.56.56 μm.
7. The process of claim 1, wherein in step S4, the antimicrobial solution in the antimicrobial pool comprises, by weight, 28 ~ 34 parts of titanium dioxide, 21 ~ 33 parts of ethylenediamine, 19 ~ 28 parts of menthol, 15 ~ 21 parts of chamomile, 11 ~ 14 parts of pomelo peel extract, 7 ~ 9 parts of nano-silver particles, and 2 ~ 5 parts of glycerin.
8. The process of claim 1, wherein in step S4, the temperature of the antibacterial bath is 55 ~ 65 ℃ and the soaking time is 2 ~ 2.5.5 h.