CN110628308A - 一种立体真石漆及其喷涂方法 - Google Patents

一种立体真石漆及其喷涂方法 Download PDF

Info

Publication number
CN110628308A
CN110628308A CN201910942752.2A CN201910942752A CN110628308A CN 110628308 A CN110628308 A CN 110628308A CN 201910942752 A CN201910942752 A CN 201910942752A CN 110628308 A CN110628308 A CN 110628308A
Authority
CN
China
Prior art keywords
parts
paint
primer
spraying
real stone
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910942752.2A
Other languages
English (en)
Inventor
王四九
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Jiunuo Building Materials Polytron Technologies Inc
Original Assignee
Jiangsu Jiunuo Building Materials Polytron Technologies Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Jiunuo Building Materials Polytron Technologies Inc filed Critical Jiangsu Jiunuo Building Materials Polytron Technologies Inc
Priority to CN201910942752.2A priority Critical patent/CN110628308A/zh
Publication of CN110628308A publication Critical patent/CN110628308A/zh
Pending legal-status Critical Current

Abstract

本发明涉及真石漆技术领域，尤其是一种立体真石漆及其喷涂方法，包括底漆、面漆和面罩漆，所述底漆的质量份组成如下：耐碱环氧乙烯树脂12‑20份、水6‑10份、改性高硬度氧化铝粉体1‑2份、防霉剂1‑2份、防腐剂1‑2份；所述面漆的质量份组成如下：改性聚丙烯酸乳液30份、天然彩石砂60‑70份、纤维素醚2‑10份、增稠剂2‑3份、增塑剂0.8‑1.2份、杀菌剂0.3‑0.4份；所述面罩漆包括A组分和B组分；本发明中的底漆使用耐碱环氧乙烯树脂和改性高硬度氧化铝粉体，提高了底漆的耐碱性和防水性，对底漆起到补强作用，提高底漆层的硬度和耐磨性，减轻了涂层固化时的提及收缩，改善涂层与基体之间的附着力；降低了纤维素醚的添加量，降低了真石漆膜的发花概率。

Description

一种立体真石漆及其喷涂方法
技术领域
本发明涉及真石漆技术领域，尤其是一种立体真石漆及其喷涂方法。
背景技术
真石漆采用特殊合成树脂乳液精制而成，能给墙面提供天然石材格调的立体装饰效果，具有天然石材的独特质感，并有不同格调的颜色选择，多种线格设计，能提供各种立体形状的花纹结构，能调整粗糙程度不一的表面，具有遮盖墙体表面缺陷的功能，可在异型弯曲墙面上喷涂出天然石材效果。
真石漆主要由天然彩砂配以耐候乳液、以及各种助剂调制而成，彩砂会影响真石漆的施工，有些真石漆彩砂在进行喷涂时会掉砂，甚至会四处飞溅，严重时可浪费三分之一左右，造成掉砂的原因有碎石级配不当、施工工艺不当或者涂料稠度不当，造成真石漆的施工比较复杂，如果是喷涂不均匀，容易造成发白发花，另外受天气的影响，温度过低或湿度过大都不利于外墙真石漆的施工。
发明内容
本发明的目的是：克服现有技术中不足，提供一种喷涂过程中彩砂不会出现掉砂或飞溅的立体真石漆及其喷涂方法。
为解决上述技术问题，本发明采用的技术方案如下：
一种立体真石漆，包括底漆、面漆和面罩漆，所述底漆的质量份组成如下：耐碱环氧乙烯树脂12-20份、水6-10份、改性高硬度氧化铝粉体1-2份、防霉剂1-2份、防腐剂1-2份；
所述面漆的质量份组成如下：改性聚丙烯酸乳液30份、天然彩石砂60-70份、纤维素醚2-10份、增稠剂2-3份、增塑剂0.8-1.2份、杀菌剂0.3-0.4份；
所述面罩漆包括A组分和B组分，所述A组分的质量份组成如下：聚氨酯改性环氧树脂6份、乙酸乙酯1.5-2.1份、紫外吸收剂0.8-1.2份；
所述B组分的质量份组成如下：固化剂6.6-8.4份、异氰酸酯3.2-6份、丙二醇1.2-6份。
进一步的，所述面罩漆中A组分和B组分的质量比为4-5:1。
进一步的，所述防霉剂选用AEM5700-C防霉剂、GNCE5700-C防霉剂、AEM5700-C中的一种。
进一步的，所述防腐剂选用磷酸盐防腐剂，包括磷酸铝、磷酸二氢钠、磷酸锌中的一种或几种。
进一步的，所述天然彩石砂的平均粒径大小为80-100目。
进一步的，所述增稠剂选用改性蒙脱石增稠剂、触变增稠剂AT-33、XC-69触变增稠剂中的一种。
进一步的，所述增塑剂选用邻苯二甲酸丁苄酯、邻苯二甲酸二仲辛酯、邻苯二甲酸二环己酯、邻苯二甲酸二甲酯、邻苯二甲酸二异壬酯中的一种。
进一步的，所述杀菌剂选用KLN-15B、KLN-17B、KLN-18B中的一种。
一种立体真石漆的喷涂方法，所述喷涂方法包括以下步骤：
（1）基层处理：清理墙上的碎渣和污物，刮涂腻子，厚度为2.6-2.8mm，干燥后，打磨一次，然后清灰，在墙面上画线，将墙面分割成若干块，分割线的宽度为2.1-2.8cm3，
（2）喷涂底漆：喷涂一层有色底漆，所述底漆的颜色与面漆的颜色一致，分割线上喷涂黑色底漆；
（3）喷涂面漆：待底漆干燥固化后，对底漆表面进行打磨，清灰后喷涂面漆；
（4）喷涂罩面漆：待面漆干燥固化后，对面漆进行打磨，然后清灰，喷涂罩面漆。
采用本发明的技术方案的有益效果是：
本发明中的增稠剂选用触变增稠剂，触变增稠剂的增稠机理是疏水基团之间由于憎水作用而发生聚集，使大分子链产生分子内和分子间的缔合，岁水溶液的六边形带来极大影响。在临界缔合浓度以上，形成分子间缔合为主的超分子结构，增大了流体力学体积，具有较好的增稠性。缔合增稠剂中的亲油基团可以吸附乳液颗粒和颜料颗粒，增强了漆膜强度，同时被增稠剂大分子架桥的微粒形成物理网状结构，该网状结构可以在剪切场中受到逐渐破坏，从而控制体系的流动性质，该类增稠剂，本身耐碱，不参与体系化学反应，可以明显改观真石漆喷涂时的飞砂现象，可以减少纤维素的用量，提高真石漆的耐水性，防止霉变，泛白现象，也可以明显改善施工，提高悬浮性，不分水，防沉淀。
本发明中的底漆使用耐碱环氧乙烯树脂和改性高硬度氧化铝粉体，提高了底漆的耐碱性和防水性，改性高硬度氧化铝粉体对底漆起到补强作用，提高底漆层的硬度和耐磨性，减轻了涂层固化时的提及收缩，可以防止碱性物质析出，改善涂层与基体之间的附着力。
本发明中通过采用触变性增稠剂，降低了纤维素醚的添加量，降低了真石漆膜的发花概率。
具体实施方式
为使本发明的上述目的、特征和优点能够更加明显易懂，下面结合具体实施方式对本发明作进一步详细的说明。
一种立体真石漆，包括底漆、面漆和面罩漆，所述底漆的质量份组成如下：耐碱环氧乙烯树脂12-20份、水6-10份、改性高硬度氧化铝粉体1-2份、防霉剂1-2份、防腐剂1-2份；
所述面漆的质量份组成如下：改性聚丙烯酸乳液30份、天然彩石砂60-70份、纤维素醚2-10份、增稠剂2-3份、增塑剂0.8-1.2份、杀菌剂0.3-0.4份；
所述面罩漆包括A组分和B组分，所述A组分的质量份组成如下：聚氨酯改性环氧树脂6份、乙酸乙酯1.5-2.1份、紫外吸收剂0.8-1.2份；
所述B组分的质量份组成如下：固化剂6.6-8.4份、异氰酸酯3.2-6份、丙二醇1.2-6份。
本发明中的增稠剂选用触变增稠剂，触变增稠剂的增稠机理是疏水基团之间由于憎水作用而发生聚集，使大分子链产生分子内和分子间的缔合，岁水溶液的六边形带来极大影响。在临界缔合浓度以上，形成分子间缔合为主的超分子结构，增大了流体力学体积，具有较好的增稠性。缔合增稠剂中的亲油基团可以吸附乳液颗粒和颜料颗粒，增强了漆膜强度，同时被增稠剂大分子架桥的微粒形成物理网状结构，该网状结构可以在剪切场中受到逐渐破坏，从而控制体系的流动性质，该类增稠剂，本身耐碱，不参与体系化学反应，可以明显改观真石漆喷涂时的飞砂现象，可以减少纤维素的用量，提高真石漆的耐水性，防止霉变，泛白现象，也可以明显改善施工，提高悬浮性，不分水，防沉淀。
本发明中的底漆使用耐碱环氧乙烯树脂和改性高硬度氧化铝粉体，提高了底漆的耐碱性和防水性，改性高硬度氧化铝粉体对底漆起到补强作用，提高底漆层的硬度和耐磨性，减轻了涂层固化时的提及收缩，可以防止碱性物质析出，改善涂层与基体之间的附着力。
本发明中通过采用触变性增稠剂，降低了纤维素醚的添加量，降低了真石漆膜的发花概率。
优选的，面罩漆中A组分和B组分的质量比为4-5:1。
作为一个优选实施方式，本实施例中防霉剂选用AEM5700-C防霉剂、GNCE5700-C防霉剂、AEM5700-C中的一种。
作为一个优选实施方式，本实施例中防腐剂选用磷酸盐防腐剂，包括磷酸铝、磷酸二氢钠、磷酸锌中的一种或几种。
作为一个优选实施方式，本实施例中天然彩石砂的平均粒径大小为80-100目，将天然彩石砂的粒径大小控制在此范围内，显著降低了喷涂过程中天然彩石砂的飞砂现象。
作为一个优选实施方式，本实施例中增稠剂选用改性蒙脱石增稠剂、触变增稠剂AT-33、XC-69触变增稠剂中的一种。
作为一个优选实施方式，本实施例中增塑剂选用邻苯二甲酸丁苄酯、邻苯二甲酸二仲辛酯、邻苯二甲酸二环己酯、邻苯二甲酸二甲酯、邻苯二甲酸二异壬酯中的一种。
作为一个优选实施方式，本实施例中杀菌剂选用KLN-15B、KLN-17B、KLN-18B中的一种。
一种立体真石漆的喷涂方法，所述喷涂方法包括以下步骤：
（1）基层处理：清理墙上的碎渣和污物，刮涂腻子，厚度为2.6-2.8mm，干燥后，打磨一次，然后清灰，在墙面上画线，将墙面分割成若干块，分割线的宽度为2.1-2.8cm3，
（2）喷涂底漆：喷涂一层有色底漆，所述底漆的颜色与面漆的颜色一致，分割线上喷涂黑色底漆；
（3）喷涂面漆：待底漆干燥固化后，对底漆表面进行打磨，清灰后喷涂面漆；
（4）喷涂罩面漆：待面漆干燥固化后，对面漆进行打磨，然后清灰，喷涂罩面漆。本发明中底漆喷涂后再对底漆进行打磨一次，一方面可以起到平整基面的作用，形成一个隔离层，避免来自于墙面内部的水汽以及碱性物质造成面漆的老化，另一方面，对底漆进行打磨，可以提高表面的粗糙度，从而让面漆更好的与底漆结合。由于底漆已经起到了良好的遮盖作用，所以面漆就不用喷涂太厚，既避免了面漆的浪费，又降低了涂料开裂的几率，保证了真石漆的喷涂效果。
本发明中面漆喷涂后再进行一次打磨，让已经固化的面漆形成抛光后的效果，而再喷涂上罩面漆之后，就可以呈现出漂亮的光泽，看上去就和经过打磨抛光的天然大理石一模一样。
实施例1
一种立体真石漆，包括底漆、面漆和面罩漆，所述底漆的质量份组成如下：耐碱环氧乙烯树脂12份、水6份、改性高硬度氧化铝粉体1份、防霉剂1份、防腐剂1份；
所述面漆的质量份组成如下：改性聚丙烯酸乳液30份、天然彩石砂60份、纤维素醚2份、增稠剂2份、增塑剂0.8份、杀菌剂0.3份；
所述面罩漆包括A组分和B组分，面罩漆中A组分和B组分的质量比为4:1，所述A组分的质量份组成如下：聚氨酯改性环氧树脂6份、乙酸乙酯1.5份、紫外吸收剂0.8份；
所述B组分的质量份组成如下：固化剂6.6份、异氰酸酯3.2份、丙二醇1.2份。
其中，防霉剂选用AEM5700-C防霉剂。
其中，防腐剂选用磷酸盐防腐剂，选用磷酸铝。
其中，天然彩石砂的平均粒径大小为80-100目。
其中，增稠剂选用改性蒙脱石增稠剂。
其中，增塑剂选用邻苯二甲酸丁苄酯。
其中，杀菌剂选用KLN-15B。
实施例2
一种立体真石漆，包括底漆、面漆和面罩漆，所述底漆的质量份组成如下：耐碱环氧乙烯树脂12-20份、水6-10份、改性高硬度氧化铝粉体1-2份、防霉剂1-2份、防腐剂1-2份；
所述面漆的质量份组成如下：改性聚丙烯酸乳液30份、天然彩石砂60-70份、纤维素醚2-10份、增稠剂2-3份、增塑剂0.8-1.2份、杀菌剂0.3-0.4份；
所述面罩漆包括A组分和B组分，面罩漆中A组分和B组分的质量比为4:1，所述A组分的质量份组成如下：聚氨酯改性环氧树脂6份、乙酸乙酯1.6份、紫外吸收剂0.9份；
所述B组分的质量份组成如下：固化剂6.8份、异氰酸酯3.5份、丙二醇1.6份。
其中，防霉剂选用AEM5700-C防霉剂。
其中，防腐剂选用磷酸盐防腐剂，选用磷酸铝。
其中，天然彩石砂的平均粒径大小为80-100目。
其中，增稠剂选用改性蒙脱石增稠剂。
其中，增塑剂选用邻苯二甲酸二仲辛酯。
其中，杀菌剂选用KLN-15B。
实施例3
一种立体真石漆，包括底漆、面漆和面罩漆，所述底漆的质量份组成如下：耐碱环氧乙烯树脂16份、水8份、改性高硬度氧化铝粉体1.5份、防霉剂1.5份、防腐剂1.5份；
所述面漆的质量份组成如下：改性聚丙烯酸乳液30份、天然彩石砂65份、纤维素醚6份、增稠剂2.5份、增塑剂1份、杀菌剂0.35份；
所述面罩漆包括A组分和B组分，面罩漆中A组分和B组分的质量比为4.5:1，所述A组分的质量份组成如下：聚氨酯改性环氧树脂6份、乙酸乙酯1.8份、紫外吸收剂1份；
所述B组分的质量份组成如下：固化剂7.2份、异氰酸酯4.8份、丙二醇3.6份。
其中，防霉剂选用GNCE5700-C防霉剂。
其中，防腐剂选用磷酸盐防腐剂，包括磷酸铝和磷酸二氢钠的混合物，其质量比为1:1。
其中，天然彩石砂的平均粒径大小为80-100目。
其中，增稠剂选用触变增稠剂AT-33。
其中，增塑剂选用邻苯二甲酸二环己酯。
其中，杀菌剂选用KLN-17B。
实施例4
一种立体真石漆，包括底漆、面漆和面罩漆，所述底漆的质量份组成如下：耐碱环氧乙烯树脂18份、水9份、改性高硬度氧化铝粉体1.8份、防霉剂1.8份、防腐剂1.8份；
所述面漆的质量份组成如下：改性聚丙烯酸乳液30份、天然彩石砂68份、纤维素醚8份、增稠剂2.8份、增塑剂1份、杀菌剂0.36份；
所述面罩漆包括A组分和B组分，面罩漆中A组分和B组分的质量比为.8:1，所述A组分的质量份组成如下：聚氨酯改性环氧树脂6份、乙酸乙酯2份、紫外吸收剂1.1份；
所述B组分的质量份组成如下：固化剂8份、异氰酸酯5份、丙二醇5份。
其中，防霉剂选用GNCE5700-C防霉剂。
其中，防腐剂选用磷酸盐防腐剂，选用磷酸二氢钠。
其中，天然彩石砂的平均粒径大小为80-100目。
其中，增稠剂选用触变增稠剂AT-33。
其中，增塑剂选用邻苯二甲酸二甲酯。
其中，杀菌剂选用KLN-17B。
实施例5
一种立体真石漆，包括底漆、面漆和面罩漆，所述底漆的质量份组成如下：耐碱环氧乙烯树脂20份、水10份、改性高硬度氧化铝粉体2份、防霉剂2份、防腐剂2份；
所述面漆的质量份组成如下：改性聚丙烯酸乳液30份、天然彩石砂70份、纤维素醚10份、增稠剂3份、增塑剂1.2份、杀菌剂0.4份；
所述面罩漆包括A组分和B组分，面罩漆中A组分和B组分的质量比为5:1，所述A组分的质量份组成如下：聚氨酯改性环氧树脂6份、乙酸乙酯2.1份、紫外吸收剂1.2份；
所述B组分的质量份组成如下：固化剂8.4份、异氰酸酯6份、丙二醇6份。
其中，防霉剂选用AEM5700-C。
其中，防腐剂选用磷酸盐防腐剂，包括磷酸锌。
其中，天然彩石砂的平均粒径大小为80-100目。
其中，增稠剂选用XC-69触变增稠剂。
其中，增塑剂选用邻苯二甲酸二异壬酯。
其中，杀菌剂选用KLN-18B。
实施例1-5中的立体真石漆的喷涂方法，包括以下步骤：
（1）基层处理：清理墙上的碎渣和污物，刮涂腻子，厚度为2.6-2.8mm，干燥后，打磨一次，然后清灰，在墙面上画线，将墙面分割成若干块，分割线的宽度为2.1-2.8cm3，
（2）喷涂底漆：喷涂一层有色底漆，所述底漆的颜色与面漆的颜色一致，分割线上喷涂黑色底漆；
（3）喷涂面漆：待底漆干燥固化后，对底漆表面进行打磨，清灰后喷涂面漆；
（4）喷涂罩面漆：待面漆干燥固化后，对面漆进行打磨，然后清灰，喷涂罩面漆。
以上述依据本发明的理想实施例为启示，通过上述的说明内容，相关工作人员完全可以在不偏离本项发明技术思想的范围内，进行多样的变更以及修改。凡在本发明的精神和原则之内，所做的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。本项发明的技术性范围并不局限于说明书上的内容，必须要根据权利要求范围来确定其技术性范围。

Claims (9)

1.一种立体真石漆，其特征在于：包括底漆、面漆和面罩漆，所述底漆的质量份组成如下：耐碱环氧乙烯树脂12-20份、水6-10份、改性高硬度氧化铝粉体1-2份、防霉剂1-2份、防腐剂1-2份；
所述面漆的质量份组成如下：改性聚丙烯酸乳液30份、天然彩石砂60-70份、纤维素醚2-10份、增稠剂2-3份、增塑剂0.8-1.2份、杀菌剂0.3-0.4份；
所述面罩漆包括A组分和B组分，所述A组分的质量份组成如下：聚氨酯改性环氧树脂6份、乙酸乙酯1.5-2.1份、紫外吸收剂0.8-1.2份；
所述B组分的质量份组成如下：固化剂6.6-8.4份、异氰酸酯3.2-6份、丙二醇1.2-6份。
2.根据权利要求1所述的一种立体真石漆，其特征在于：所述面罩漆中A组分和B组分的质量比为4-5:1。
3.根据权利要求1所述的一种立体真石漆，其特征在于：所述防霉剂选用AEM5700-C防霉剂、GNCE5700-C防霉剂、AEM5700-C中的一种。
4.根据权利要求1所述的一种立体真石漆，其特征面漆在于：所述防腐剂选用磷酸盐防腐剂，包括磷酸铝、磷酸二氢钠、磷酸锌中的一种或几种。
5.根据权利要求1所述的一种立体真石漆，其特征在于：所述天然彩石砂的平均粒径大小为80-100目。
6.根据权利要求1所述的一种立体真石漆，其特征在于：所述增稠剂选用改性蒙脱石增稠剂、触变增稠剂AT-33、XC-69触变增稠剂中的一种。
7.根据权利要求1所述的一种立体真石漆，其特征在于：所述增塑剂选用邻苯二甲酸丁苄酯、邻苯二甲酸二仲辛酯、邻苯二甲酸二环己酯、邻苯二甲酸二甲酯、邻苯二甲酸二异壬酯中的一种。
8.根据权利要求1所述的一种立体真石漆，其特征在于：所述杀菌剂选用KLN-15B、KLN-17B、KLN-18B中的一种。
9.如权利要求1-8中任一项所述的的一种立体真石漆的喷涂方法，其特征在于：所述喷涂方法包括以下步骤：
（1）基层处理：清理墙上的碎渣和污物，刮涂腻子，厚度为2.6-2.8mm，干燥后，打磨一次，然后清灰，在墙面上画线，将墙面分割成若干块，分割线的宽度为2.1-2.8cm3，
（2）喷涂底漆：喷涂一层有色底漆，所述底漆的颜色与面漆的颜色一致，分割线上喷涂黑色底漆；
（3）喷涂面漆：待底漆干燥固化后，对底漆表面进行打磨，清灰后喷涂面漆；
（4）喷涂罩面漆：待面漆干燥固化后，对面漆进行打磨，然后清灰，喷涂罩面漆。
CN201910942752.2A 2019-09-30 2019-09-30 一种立体真石漆及其喷涂方法 Pending CN110628308A (zh)