CN110628091A - 一种耐穿刺工程实心轮胎 - Google Patents

一种耐穿刺工程实心轮胎 Download PDF

Info

Publication number
CN110628091A
CN110628091A CN201910840774.8A CN201910840774A CN110628091A CN 110628091 A CN110628091 A CN 110628091A CN 201910840774 A CN201910840774 A CN 201910840774A CN 110628091 A CN110628091 A CN 110628091A
Authority
CN
China
Prior art keywords
parts
agent
resistant
puncture
carbon black
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910840774.8A
Other languages
English (en)
Inventor
程平
吴喜林
王化勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu Jituo Solid Tyre Co Ltd
Original Assignee
Wuhu Jituo Solid Tyre Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Jituo Solid Tyre Co Ltd filed Critical Wuhu Jituo Solid Tyre Co Ltd
Priority to CN201910840774.8A priority Critical patent/CN110628091A/zh
Publication of CN110628091A publication Critical patent/CN110628091A/zh
Pending legal-status Critical Current

Abstract

本发明的目的是提供一种耐穿刺工程实心轮胎，采用天然橡胶、沉淀法二氧化硅、炭黑、白炭黑、芳烃油、抗撕裂树脂、氧化锌、硬脂酸、硫磺、促进剂的配合，并且还包括有撕裂剂AT‑KL、芳纶浸胶短纤维、高性能分子材料HR‑801抗撕裂剂、防老剂DPA、抗硫化返原剂，一系列抗撕裂耐穿刺材料的适应，使得该配方制得的实心轮胎大幅度提高轮胎的在恶劣环境下的耐穿刺能力。

Description

一种耐穿刺工程实心轮胎
技术领域
本发明涉及实心轮胎领域，尤其涉及一种耐穿刺工程实心轮胎。
背景技术
实心轮胎是与充气轮胎（空心轮胎）对应的一种轮胎，其胎体是实心的，不用帘线作骨架，不必充气，故不需内胎或气密层。最早的轮胎就是实心轮胎。实心轮胎目前仅用于低速行驶的高负荷车辆或机械，也用于固定位置的机械。实心轮胎需要在有刺的场合使用，因此需要具有很好的耐穿刺性能，目前的实心轮胎配方耐穿刺效果不佳。因此解决这一问题就显得十分必要了。
发明内容
为解决上述问题，本发明提供一种耐穿刺工程实心轮胎，采用天然橡胶、沉淀法二氧化硅、炭黑、白炭黑、芳烃油、抗撕裂树脂、氧化锌、硬脂酸、硫磺、促进剂的配合，并且还包括有撕裂剂AT-KL、芳纶浸胶短纤维、高性能分子材料HR-801抗撕裂剂、防老剂DPA、抗硫化返原剂，一系列抗撕裂耐穿刺材料的适应，使得该配方制得的实心轮胎大幅度提高轮胎的在恶劣环境下的耐穿刺能力，解决了背景技术中出现的问题。
本发明的目的是提供一种耐穿刺工程实心轮胎，包括有以下质量份数的组分料：
天然橡胶80-120份、沉淀法二氧化硅15-25份、炭黑25-35份、白炭黑10-20份、芳烃油3-9份、抗撕裂树脂8-12份、氧化锌5-10份、硬脂酸1-3份、硫磺1-5份、促进剂 3-9份、撕裂剂AT-KL 5-10份、芳纶浸胶短纤维5-10份、高性能分子材料HR-801抗撕裂剂2-5份、防老剂DPA5-10份、抗硫化返原剂5-10份。
进一步改进在于：所述促进剂为秋兰姆促进剂。
本发明的有益效果：本发明采用天然橡胶、沉淀法二氧化硅、炭黑、白炭黑、芳烃油、抗撕裂树脂、氧化锌、硬脂酸、硫磺、促进剂的配合，并且还包括有撕裂剂AT-KL、芳纶浸胶短纤维、高性能分子材料HR-801抗撕裂剂、防老剂DPA、抗硫化返原剂，一系列抗撕裂耐穿刺材料的适应，使得该配方制得的实心轮胎大幅度提高轮胎的在恶劣环境下的耐穿刺能力。
具体实施方式
为了加深对本发明的理解，下面将结合实施例对本发明作进一步详述，该实施例仅用于解释本发明，并不构成对本发明保护范围的限定。
实施例一
本实施例提供一种耐穿刺工程实心轮胎，包括有以下质量份数的组分料：天然橡胶80份、沉淀法二氧化硅15份、炭黑25份、白炭黑10份、芳烃油3份、抗撕裂树脂8份、氧化锌5份、硬脂酸1份、硫磺1份、促进剂 3份。还包括有撕裂剂AT-KL 5份、芳纶浸胶短纤维5份、高性能分子材料HR-801抗撕裂剂2份、防老剂DPA 5份、抗硫化返原剂5份。所述促进剂为秋兰姆促进剂。
实施例二
本实施例提供一种耐穿刺工程实心轮胎，包括有以下质量份数的组分料：天然橡胶100份、沉淀法二氧化硅20份、炭黑30份、白炭黑15份、芳烃油5份、抗撕裂树脂10份、氧化锌7份、硬脂酸2份、硫磺2.5份、促进剂 4.5份。还包括有撕裂剂AT-KL 5-10份、芳纶浸胶短纤维8份、高性能分子材料HR-801抗撕裂剂3份、防老剂DPA 7份、抗硫化返原剂7份。所述促进剂为秋兰姆促进剂。
实施例三
本实施例提供一种耐穿刺工程实心轮胎，包括有以下质量份数的组分料：天然橡胶120份、沉淀法二氧化硅25份、炭黑35份、白炭黑20份、芳烃油9份、抗撕裂树脂12份、氧化锌10份、硬脂酸3份、硫磺5份、促进剂9份。还包括有撕裂剂AT-KL 10份、芳纶浸胶短纤维10份、高性能分子材料HR-801抗撕裂剂5份、防老剂DPA 10份、抗硫化返原剂10份。所述促进剂为秋兰姆促进剂。
以上实施例采用天然橡胶、沉淀法二氧化硅、炭黑、白炭黑、芳烃油、抗撕裂树脂、氧化锌、硬脂酸、硫磺、促进剂的配合，并且还包括有撕裂剂AT-KL、芳纶浸胶短纤维、高性能分子材料HR-801抗撕裂剂、防老剂DPA、抗硫化返原剂，一系列抗撕裂耐穿刺材料的适应，使得该配方制得的实心轮胎大幅度提高轮胎的在恶劣环境下的耐穿刺能力。

Claims (2)

1.一种耐穿刺工程实心轮胎，其特征在于：包括有以下质量份数的组分料：
天然橡胶80-120份、沉淀法二氧化硅15-25份、炭黑25-35份、白炭黑10-20份、芳烃油3-9份、抗撕裂树脂8-12份、氧化锌5-10份、硬脂酸1-3份、硫磺1-5份、促进剂 3-9份、撕裂剂AT-KL 5-10份、芳纶浸胶短纤维5-10份、高性能分子材料HR-801抗撕裂剂2-5份、防老剂DPA5-10份、抗硫化返原剂5-10份。
2.如权利要求1所述一种耐穿刺工程实心轮胎，其特征在于：所述促进剂为秋兰姆促进剂。
CN201910840774.8A 2019-09-06 2019-09-06 一种耐穿刺工程实心轮胎 Pending CN110628091A (zh)