CN110618135A - 一种水洗型荧光渗透剂及其制备方法 - Google Patents

一种水洗型荧光渗透剂及其制备方法 Download PDF

Info

Publication number
CN110618135A
CN110618135A CN201910901421.4A CN201910901421A CN110618135A CN 110618135 A CN110618135 A CN 110618135A CN 201910901421 A CN201910901421 A CN 201910901421A CN 110618135 A CN110618135 A CN 110618135A
Authority
CN
China
Prior art keywords
water
penetrant
fluorescent penetrant
fluorescent
surfactant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910901421.4A
Other languages
English (en)
Inventor
高政
范从国
秦旺洋
杨建龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
According To Special Materials (suzhou) Co Ltd
Original Assignee
According To Special Materials (suzhou) Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by According To Special Materials (suzhou) Co Ltd filed Critical According To Special Materials (suzhou) Co Ltd
Priority to CN201910901421.4A priority Critical patent/CN110618135A/zh
Publication of CN110618135A publication Critical patent/CN110618135A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种水洗型荧光渗透剂，按重量份计，水洗型荧光渗透剂包括以下组分：表面活性剂30～45份；溶剂25～50份；荧光黄0.1～0.5份；荧光增白剂0.1～0.5份。本发明的水洗型荧光渗透剂，易于生物降解，对环境友好，灵敏度高，选用的原材料不含有毒有害成分，无刺激性气味；选用的表面活性剂为非离子型表面活性剂，易于生物降解，泡沫小；溶剂选用天然植物油脂，具有良好的生物降解性，并且来源广泛，价格低廉；通过加入增白剂，提高渗透剂的亮度。

Description

一种水洗型荧光渗透剂及其制备方法
技术领域
本发明涉及无损检测技术领域，具体涉及一种水洗型荧光渗透剂及其制备方法。
背景技术
渗透检测是以不损坏被检测对象的使用性能为前提，运用物理、化学、材料化学及工程学理论为基础，对各种工程材料、零部件和产品进行有效的检验，借以评价他们的完整性、连续性以及安全可靠性。渗透检测是产品制造中实现质量控制、节约原材料、改进工艺、提高劳动生产率的重要手段，也是设备维护中不可或缺的手段。
荧光渗透检测作用原理为毛细作用原理，在工件表面施涂荧光渗透剂，经过一定时间干燥后，渗透剂可以渗入到表面开口缺陷中，去除工件表面多余的渗透剂，干燥一段时间后，在黑光灯的照射下，缺陷处的渗透剂能被激发出黄绿色荧光，进而探测出缺陷的形态以及分布状态。
根据AMS2644G《美国宇航材料规范AMS2644G检测材料-渗透剂》章节1.4.1描述，渗透剂可分为着色和荧光两大类，而荧光渗透剂又可细分为A,A(W),B,C,D五种方法，本发明归属于方法A，水洗型荧光渗透剂，相比较其他方法，水洗型荧光渗透剂因自身含有表面活性剂，所以工件表面多余的渗透剂可直接用水移除。
现有技术水洗型渗透剂往往会添加烷基酚聚氧乙烯醚，醇醚，含磷阻燃剂等化学成分，生物降解性比较差，易挥发，有严重的气味问题；并且水洗型荧光渗透剂的灵敏度不佳。
发明内容
针对上述不足之处，本发明的目的在于提供一种水洗型荧光渗透剂及其制备方法，具有易于生物降解，对环境友好，灵敏度高的优势。
本发明的技术方案概述如下：
一种水洗型荧光渗透剂，其中，按重量份计，所述水洗型荧光渗透剂包括以下组分：
优选的是，所述的水洗型荧光渗透剂，其中，所述表面活性剂选自脂肪醇聚氧乙烯醚、脂肪醇烷氧基醚、脂肪酸甲酯聚氧乙烯醚中的一种或几种。
优选的是，所述的水洗型荧光渗透剂，其中，所述溶剂为天然植物油脂。
优选的是，所述的水洗型荧光渗透剂，其中，所述天然植物油脂选自棕榈油、椰子油、大豆油、花生油中的一种或者几种的混合物。
优选的是，所述的水洗型荧光渗透剂，其中，所述的荧光黄为溶剂黄145、溶剂黄98、溶剂黄185中的一种或者几种的混合物。
优选的是，所述的水洗型荧光渗透剂，其中，所述的荧光增白剂为荧光增白剂OB。
一种水洗型荧光渗透剂的制备方法，其中，包括下述步骤：
1)按比例依次加入溶剂、荧光黄、荧光增白剂、1/6～1/5质量分数的表面活性剂、搅拌2h，得到第一混合液；
2)加入剩余4/5～5/6质量分数的表面活性剂，搅拌1h，得到第二混合液；
3)将第二混合液过滤，包装得到产品。
优选的是，所述的水洗型荧光渗透剂的制备方法，其中，所述步骤3)第二混合液过滤滤网规格为1000～1200目。
本发明的有益效果是：
本发明的水洗型荧光渗透剂，易于生物降解，对环境友好，灵敏度高，选用的原材料不含有毒有害成分，无刺激性气味；选用的表面活性剂为非离子型表面活性剂，易于生物降解，泡沫小；溶剂选用天然植物油脂，具有良好的生物降解性，并且来源广泛，价格低廉；通过加入荧光增白剂，提高渗透剂在黑光灯下的亮度。
具体实施方式
下面结合实施例对本发明做进一步的详细说明，以令本领域技术人员参照说明书文字能够据以实施。
本发明提供一种水洗型荧光渗透剂，按重量份计，水洗型荧光渗透剂包括以下组分：
作为本案又一实施例，表面活性剂选自脂肪醇聚氧乙烯醚、脂肪醇烷氧基醚、脂肪酸甲酯聚氧乙烯醚中的一种或几种。
表面活性剂的类型为非离子型表面活性剂，其特点为耐电解质，易于生物降解，泡沫小，闪点高，本案优选的表面活性剂为脂肪醇聚氧乙烯醚、脂肪醇烷氧基醚、脂肪酸甲酯聚氧乙烯醚。
作为本案又一实施例，溶剂为天然植物油脂。
作为本案又一实施例，天然植物油脂选自棕榈油、椰子油、大豆油、花生油中的一种或者几种的混合物。天然植物油脂，具有易于生物降解，对环境友好的优点。
作为本案又一实施例，荧光黄为溶剂黄145、溶剂黄98、溶剂黄185中的一种或者几种的混合物。
作为本案又一实施例，荧光增白剂为荧光增白剂OB。分子式是C26H26N2O2S，中文别名：2.5-双-(5-叔丁基-2-苯并恶唑基)噻吩，可提高渗透剂的亮度。
一种水洗型荧光渗透剂的制备方法，其中，包括下述步骤：
1)按比例依次加入溶剂、荧光黄、荧光增白剂、1/6～1/5质量分数的表面活性剂、搅拌2h，得到第一混合液；
2)加入剩余4/5～5/6质量分数的表面活性剂，搅拌1h，得到第二混合液；
3)将第二混合液过滤，包装得到产品。
作为本案又一实施例，步骤3)第二混合液过滤滤网规格为1000～1200目。
表1列出具体的实施例：
表1
水洗型荧光渗透剂及其制备方法为：
(1)按比例依次加入天然植物油脂，荧光黄，荧光增白剂，少量表面活性剂、在旋桨式搅拌器搅拌2h，得到第一混合液；
(2)加入剩余表面活性剂，搅拌1h，得到第二混合液；
(3)将混合液过滤，滤网规格为1000～1200目，包装得到产品。
对实施例1、实施例2、实施例3、实施例4、实施例5的水洗型荧光渗透剂进行评估，灵敏度参照ISO3452-2《无损检测—渗透检测—渗透材料试验》，章节6.2.1.2进行测试。
实施例和对比例的性能测试结果如表2：
表2
从表2中数据可以看出，本发明的渗透剂，灵敏度高，选用的原材料不含有毒有害成分，无刺激性气味；易于生物降解，环境友好。
尽管本发明的实施方案已公开如上，但其并不仅仅限于说明书和实施方式中所列运用，它完全可以被适用于各种适合本发明的领域，对于熟悉本领域的人员而言，可容易地实现另外的修改，因此在不背离权利要求及等同范围所限定的一般概念下，本发明并不限于特定的细节。

Claims (8)

1.一种水洗型荧光渗透剂，其特征在于，按重量份计，所述水洗型荧光渗透剂包括以下组分：
2.根据权利要求1所述的水洗型荧光渗透剂，其特征在于，所述表面活性剂选自脂肪醇聚氧乙烯醚、脂肪醇烷氧基醚、脂肪酸甲酯聚氧乙烯醚中的一种或几种。
3.根据权利要求1所述的水洗型荧光渗透剂，其特征在于，所述溶剂为天然植物油脂。
4.根据权利要求3所述的水洗型荧光渗透剂，其特征在于，所述天然植物油脂选自棕榈油、椰子油、大豆油、花生油中的一种或者几种的混合物。
5.根据权利要求1所述的水洗型荧光渗透剂，其特征在于，所述的荧光黄为溶剂黄145、溶剂黄98、溶剂黄185中的一种或者几种的混合物。
6.根据权利要求1所述的水洗型荧光渗透剂，其特征在于，所述的荧光增白剂为荧光增白剂OB。
7.根据权利要求1～6任一项所述的水洗型荧光渗透剂的制备方法，其特征在于，包括下述步骤：
1)按比例依次加入溶剂、荧光黄、荧光增白剂、1/6～1/5质量分数的表面活性剂，搅拌2h，得到第一混合液；
2)加入剩余4/5～5/6质量分数的表面活性剂，搅拌1h，得到第二混合液；
3)将第二混合液过滤，包装得到产品。
8.根据权利要求7所述的水洗型荧光渗透剂的制备方法，其特征在于，所述步骤3)第二混合液过滤滤网规格为1000～1200目。
CN201910901421.4A 2019-09-23 2019-09-23 一种水洗型荧光渗透剂及其制备方法 Pending CN110618135A (zh)